CN106087101A - A kind of fire-resistant antistatic polyester fiber - Google Patents
A kind of fire-resistant antistatic polyester fiber Download PDFInfo
- Publication number
- CN106087101A CN106087101A CN201610418708.8A CN201610418708A CN106087101A CN 106087101 A CN106087101 A CN 106087101A CN 201610418708 A CN201610418708 A CN 201610418708A CN 106087101 A CN106087101 A CN 106087101A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- fire
- main body
- fire retardant
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-resistant antistatic polyester fiber, including: polyester fiber main body and the fire retardant being added in described polyester fiber main body and antistatic additive, calculate by mass percentage, the content of described polyester fiber main body is 85% 90%, the content of described fire retardant is 9% 12%, the content of described antistatic additive is 1% 3%, described fire-resistant antistatic polyester fiber is to use the fire retardant of above-mentioned formula and antistatic additive to add in polyester fiber main body, then prepare through melt spinning method, and described fire retardant is added with inorganic nano material.By the way, the present invention, by adding fire retardant and the antistatic additive of rational formula amount in polyester fiber main body, makes the fiber prepared have anti-flammability and the antistatic behaviour of excellence, has good water absorption and pleasant softness simultaneously.
Description
Technical field
The present invention relates to fire resistance fibre field, particularly relate to a kind of fire-resistant antistatic polyester fiber.
Background technology
Along with increasing considerably of textile demand, textile the disaster hidden-trouble caused is consequently increased.To by fire
The result of the death by accident investigation that calamity causes shows, the fire that textile causes holds pride of place.Therefore, for preventing sending out of fire
Raw, flame retardant textiles is increasingly subject to people's attention, and the research to fire resistance fibre also becomes the emphasis that current textile is studied
Problem.
Combustible needs enough temperature and oxygen, burning to be difficult to degree can to pass through limited oxygen index (LOI) and characterize.Logical
In the case of Chang, air oxygen concentration is 21%, therefore, as LOI > 21%, i.e. shows that this material is difficult to burn in atmosphere, polyester
Generally 18%-20%, i.e. its fire resistance are poor for the LOI value of fiber, and polyester fiber is the most also deposited that water absorption is poor, easily adsorbed in addition
Dust, it is easily generated the defects such as electrostatic.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of fire-resistant antistatic polyester fiber, has the anti-flammability of excellence
And antistatic behaviour, there is good water absorption and pleasant softness simultaneously.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of fire-resistant antistatic polyester
Fiber, including: polyester fiber main body and the fire retardant being added in described polyester fiber main body and antistatic additive, by quality hundred
Proportion by subtraction calculates, and the content of described polyester fiber main body is 85%-90%, the content of described fire retardant is 9%-12%, described antistatic
The content of agent is 1%-3%, and described fire-resistant antistatic polyester fiber is to use the fire retardant of above-mentioned formula and antistatic additive to add to
In polyester fiber main body, then prepare through melt spinning method, and described fire retardant is added with inorganic nano material.
In a preferred embodiment of the present invention, described fire retardant is microencapsulated red phosphorus flame retardant.
In a preferred embodiment of the present invention, described inorganic nano material is nano silicon.
In a preferred embodiment of the present invention, the addition of described inorganic nano material accounts for polyester fiber body weight
5%-10%。
The invention has the beneficial effects as follows: the present invention by polyester fiber main body add rational formula amount fire retardant and
Antistatic additive, makes the fiber prepared have anti-flammability and the antistatic behaviour of excellence, has good water absorption simultaneously and feel is soft
Soft.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
A kind of fire-resistant antistatic polyester fiber, including: polyester fiber main body and be added in described polyester fiber main body fire-retardant
Agent and antistatic additive, calculate by mass percentage, and the content of described polyester fiber main body is 85%-90%, the containing of described fire retardant
Amount is 1%-3% for 9%-12%, the content of described antistatic additive, and described fire-resistant antistatic polyester fiber is the resistance using above-mentioned formula
Combustion agent and antistatic additive add in polyester fiber main body, then prepare through melt spinning method, and add in described fire retardant
Added with inorganic nano material.
Wherein, described fire retardant is microencapsulated red phosphorus flame retardant, has Halogen, non-volatile, Heat stability is good, flame retarding efficiency
High feature.
Described inorganic nano material is nano silicon, adds nanometer titanium dioxide in described microencapsulated red phosphorus flame retardant
Silicon, can improve flame retardant effect, can improve the mechanical property of fiber simultaneously.
Preferably, the addition of described inorganic nano material accounts for the 5%-10% of polyester fiber body weight.
Embodiment one:
(1) fire retardant is prepared: after taking microencapsulated red phosphorus flame retardant 12kg, nano silicon 4.5kg mixing, put into comminutor,
Make the powdery flame retardent of particle diameter≤5 μm;
(2) fire-resistant antistatic polyester fiber is prepared: take polyester fiber main body 85kg, take above-mentioned prepared powdery flame retardent
16kg, antistatic additive 3kg, prepare described flame-retardant and anti-static polyester fiber through spinning-drawing machine melt spinning after mixing.
Embodiment two:
(1) fire retardant is prepared: put into comminutor after taking microencapsulated red phosphorus flame retardant 10kg, nano silicon 7kg mixing, system
Become the powdery flame retardent of particle diameter≤5 μm;
(2) fire-resistant antistatic polyester fiber is prepared: take polyester fiber main body 87kg, take above-mentioned prepared powdery flame retardent
16.5kg, antistatic additive 3kg, prepare described flame-retardant and anti-static polyester fiber through spinning-drawing machine melt spinning after mixing.
Embodiment three:
(1) fire retardant is prepared: put into comminutor after taking microencapsulated red phosphorus flame retardant 9kg, nano silicon 9kg mixing, system
Become the powdery flame retardent of particle diameter≤5 μm;
(2) fire-resistant antistatic polyester fiber is prepared: take polyester fiber main body 90kg, take above-mentioned prepared powdery flame retardent
18kg, antistatic additive 1kg, prepare described flame-retardant and anti-static polyester fiber through spinning-drawing machine melt spinning after mixing.
Present invention is disclosed a kind of fire-resistant antistatic polyester fiber, by adding rational formula amount in polyester fiber main body
Fire retardant and antistatic additive, make the fiber prepared have excellence anti-flammability and antistatic behaviour, there is good water suction simultaneously
Property and pleasant softness.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. a fire-resistant antistatic polyester fiber, it is characterised in that including: polyester fiber main body and to be added on described polyester fine
Dimension main body in fire retardant and antistatic additive, calculate by mass percentage, the content of described polyester fiber main body be 85%-90%,
The content of described fire retardant is 9%-12%, the content of described antistatic additive is 1%-3%, and described fire-resistant antistatic polyester fiber is to adopt
Fire retardant and antistatic additive with above-mentioned formula add in polyester fiber main body, then prepare through melt spinning method, and
Described fire retardant is added with inorganic nano material.
Fire-resistant antistatic polyester fiber the most according to claim 1, it is characterised in that described fire retardant is microcapsule red phosphorus
Fire retardant.
Fire-resistant antistatic polyester fiber the most according to claim 1, it is characterised in that described inorganic nano material is nanometer
Silicon dioxide.
Fire-resistant antistatic polyester fiber the most according to claim 1, it is characterised in that the interpolation of described inorganic nano material
Amount accounts for the 5%-10% of polyester fiber body weight.