CN106085028A - A kind of Yellow luminous water paint of LED luminous plaque - Google Patents

A kind of Yellow luminous water paint of LED luminous plaque Download PDF

Info

Publication number
CN106085028A
CN106085028A CN201610609198.2A CN201610609198A CN106085028A CN 106085028 A CN106085028 A CN 106085028A CN 201610609198 A CN201610609198 A CN 201610609198A CN 106085028 A CN106085028 A CN 106085028A
Authority
CN
China
Prior art keywords
parts
yellow
water paint
luminous
led
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610609198.2A
Other languages
Chinese (zh)
Inventor
王玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Chuben Electronic Technology Co Ltd
Original Assignee
Kunshan Chuben Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Chuben Electronic Technology Co Ltd filed Critical Kunshan Chuben Electronic Technology Co Ltd
Priority to CN201610609198.2A priority Critical patent/CN106085028A/en
Publication of CN106085028A publication Critical patent/CN106085028A/en
Pending legal-status Critical Current

Abstract

The Yellow luminous water paint of a kind of LED luminous plaque disclosed by the invention, it is characterized in that, comprise each component of following mass parts: emulsion polymerization 30 ~ 50 parts, light-accumulating luminous material 10 ~ 50 parts, yellow composite pigment 10 ~ 50 parts, dispersant 0.3 ~ 0.8 part, thickening agent 0.5 ~ 1.0 part, coalescents 4 ~ 8 parts, anti-settling agent 1.0 2.0 parts, preservative 0.1 ~ 0.3 part, defoamer 0.2 ~ 0.4 part, 10 ~ 60 parts of water.The beneficial effect that the present invention is reached: the LED that the Yellow luminous water paint of the present invention prepares, can be relieved in child's view, ensure that child preserves from when carrying out nocturnalism, and colour-fast under artificial light irradiates, salt fog, chemical substance, steam there are is preferable stability.

Description

A kind of Yellow luminous water paint of LED luminous plaque
Technical field
The present invention relates to the Yellow luminous water paint of a kind of LED luminous plaque, belong to technical field of polymer materials.
Background technology
Light-storing and emitting material is that a kind of reception can store and permissible in the case of gauge without light source irradiates after light source irradiates The material of continuous illumination a period of time, this material has occurred, the legendary luminous pearl, the luminous wine glass that are known are A kind of light-storing and emitting material.
The view designed for child, first has to the physical qualification in view of child, can be used for constituting child's view Material definitely child can not be caused any negative effect, the damage to human eye retina, any high-octane light irradiates Or the light application time process of specific wavelength under threshold energy, all can cause damage in various degree.Because of light-storing and emitting material Luminous safety and can be with continuous illumination, brightness prolongation in time constantly reduces, and not keeps peak brightness, completely may be used To ensure to preserve from when child carries out nocturnalism, and the safety problem of child is paid much attention to by people now so that should Material application in child's view has very big market.
Summary of the invention
Present invention solves the technical problem that the Yellow luminous water paint being to provide a kind of LED luminous plaque, use this Bright Yellow luminous water paint prepare LED, can be relieved in child's view, it is ensured that child carrying out night live Preserve from time dynamic, and colour-fast under artificial light irradiates, salt fog, chemical substance, steam there are is preferable stability.
In order to realize above-mentioned target, the present invention adopts the following technical scheme that:
The Yellow luminous water paint of a kind of LED luminous plaque, it is characterised in that comprise each component of following mass parts:
Emulsion polymerization 30 ~ 50 parts, light-accumulating luminous material 10 ~ 50 parts, yellow composite pigment 10 ~ 50 parts, dispersant 0.3 ~ 0.8 part, thickening agent 0.5 ~ 1.0 part, coalescents 4 ~ 8 parts, anti-settling agent 1.0-2.0 part, preservative 0.1 ~ 0.3 part, defoamer 0.2 ~ 0.4 part, 10 ~ 60 parts of water.
Described emulsion polymerization is one or more in styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.
Described light-accumulating luminous material is alkaline earth aluminate salt system, silicate systems or zinc sulfide system.
Described dispersant be ammonium polyacrylate salt, Quadrafos, polycarboxylate sodium one or more.
Described thickening agent be methylcellulose, modified poly-third dash forward olefin(e) acid sodium, containing in many carboxylated polypropylenes acids polymers A kind of.
Described coalescents is the one in Oleum Terebinthinae, ethylene glycol, benzyl alcohol.
Described yellow composite pigment comprises each component of following mass parts: titanium dioxide 420 ~ 500 parts, ferrum oxide 20 ~ 25 Part, aluminium oxide 30 ~ 35 parts, antimony oxide 30 ~ 35 parts.
The beneficial effect that the present invention is reached: the LED that the Yellow luminous water paint of the present invention prepares, can be relieved In child's view, it is ensured that child preserves from when carrying out nocturnalism and colour-fast, to salt under artificial light irradiates Mist, chemical substance, steam have preferable stability.
Detailed description of the invention
In conjunction with specific examples below, the present invention is described in further detail, and following example are only used for more clear Chu's ground explanation technical scheme, and can not limit the scope of the invention with this.
Embodiment 1:
The Yellow luminous water paint of a kind of LED luminous plaque, comprises each component of following mass parts:
Emulsion polymerization 30 parts, light-accumulating luminous material 10 parts, yellow composite pigment 10 parts, dispersant 0.3 part, thickening agent 0.5 part, coalescents 4 parts, anti-settling agent 1.0 parts, preservative 0.1 part, defoamer 0.2 part, 10 parts of water.
Preferably, one or more during emulsion polymerization is styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.
Preferably, light-accumulating luminous material is alkaline earth aluminate salt system, silicate systems or zinc sulfide system.
Preferably, dispersant be ammonium polyacrylate salt, Quadrafos, polycarboxylate sodium one or more.
Preferably, thickening agent be methylcellulose, modified poly-third dash forward olefin(e) acid sodium, containing in many carboxylated polypropylenes acids polymers One.
Further, the one during coalescents is Oleum Terebinthinae, ethylene glycol, benzyl alcohol.
Further, yellow composite pigment comprises each component of following mass parts: titanium dioxide 420 parts, ferrum oxide 02 Part, aluminium oxide 30 parts, antimony oxide 30 parts.
Embodiment 2:
The Yellow luminous water paint of a kind of LED luminous plaque, it is characterised in that comprise each component of following mass parts:
Emulsion polymerization 40 parts, light-accumulating luminous material 25 parts, yellow composite pigment 30 parts, dispersant 0.5 part, thickening agent 0.8 part, coalescents 6 parts, anti-settling agent 1.5 parts, preservative 0.2 part, defoamer 0.3 part, 40 parts of water.
Preferably, one or more during emulsion polymerization is styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.
Preferably, light-accumulating luminous material is alkaline earth aluminate salt system, silicate systems or zinc sulfide system.
Preferably, dispersant be ammonium polyacrylate salt, Quadrafos, polycarboxylate sodium one or more.
Preferably, thickening agent be methylcellulose, modified poly-third dash forward olefin(e) acid sodium, containing in many carboxylated polypropylenes acids polymers One.
Further, the one during coalescents is Oleum Terebinthinae, ethylene glycol, benzyl alcohol.
Further, yellow composite pigment comprises each component of following mass parts: titanium dioxide 450 parts, ferrum oxide 20 Part, aluminium oxide 32 parts, antimony oxide 35 parts.
Embodiment 3:
The Yellow luminous water paint of a kind of LED luminous plaque, it is characterised in that comprise each component of following mass parts:
Emulsion polymerization 50 parts, light-accumulating luminous material 50 parts, yellow composite pigment 50 parts, dispersant 0.8 part, thickening agent 1.0 parts, coalescents 8 parts, anti-settling agent 2.0 parts, preservative 0.3 part, defoamer 0.4 part, 60 parts of water.
Preferably, one or more during emulsion polymerization is styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.
Preferably, light-accumulating luminous material is alkaline earth aluminate salt system, silicate systems or zinc sulfide system.
Preferably, dispersant be ammonium polyacrylate salt, Quadrafos, polycarboxylate sodium one or more.
Preferably, thickening agent be methylcellulose, modified poly-third dash forward olefin(e) acid sodium, containing in many carboxylated polypropylenes acids polymers One.
Further, the one during coalescents is Oleum Terebinthinae, ethylene glycol, benzyl alcohol.
Further, yellow composite pigment comprises each component of following mass parts: titanium dioxide 500 parts, ferrum oxide 25 Part, aluminium oxide 35 parts, antimony oxide 35 parts.
By titanium dioxide, ferrum oxide, aluminium oxide and four kinds of raw material mixing of antimony oxide, it is ground, after grinding uniformly Carrying out high-temperature calcination, finally dry grinding obtains yellow composite pigment.
First part formulation water is put in dispersator, be sequentially added under the low speed preservative, half coalescents, one Half thickening agent, dispersant, half defoamer, after mix homogeneously, be slowly added into impeller by light-accumulating luminous material, yellow composite pigment In the whirlpool stirred, after adding, improve wheel speed and evenly spread to solution to light-accumulating luminous material and yellow composite pigment In, impeller proceed to low speed be gradually added into emulsion polymerization, half coalescents, half defoamer, anti-settling agent, water and The thickening agent of half, the most remaining other half thickening agent adds after being made into 10% aqueous solution, just makes this after being uniformly dispersed Bright Yellow luminous water paint.
The present invention the above be only the preferred embodiment of the present invention, it is noted that common for the art For technical staff, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvement and deformation, these improve Also protection scope of the present invention is should be regarded as with deformation.

Claims (7)

1. the Yellow luminous water paint of a LED luminous plaque, it is characterised in that comprise each component of following mass parts:
Emulsion polymerization 30 ~ 50 parts, light-accumulating luminous material 10 ~ 50 parts, yellow composite pigment 10 ~ 50 parts, dispersant 0.3 ~ 0.8 part, thickening agent 0.5 ~ 1.0 part, coalescents 4 ~ 8 parts, anti-settling agent 1.0-2.0 part, preservative 0.1 ~ 0.3 part, defoamer 0.2 ~ 0.4 part, 10 ~ 60 parts of water.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described height Molecularly Imprinted Polymer emulsion is one or more in styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described storage Light luminescent material is alkaline earth aluminate salt system, silicate systems or zinc sulfide system.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described point Powder be ammonium polyacrylate salt, Quadrafos, polycarboxylate sodium one or more.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described increasing Thick dose be methylcellulose, modified poly-third dash forward olefin(e) acid sodium, containing the one in many carboxylated polypropylenes acids polymers.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described one-tenth Film auxiliary agent is the one in Oleum Terebinthinae, ethylene glycol, benzyl alcohol.
The Yellow luminous water paint of a kind of LED luminous plaque the most according to claim 1, it is characterised in that described Huang Color composite pigment comprises each component of following mass parts: titanium dioxide 420 ~ 500 parts, ferrum oxide 20 ~ 25 parts, aluminium oxide 30 ~ 35 Part, antimony oxide 30 ~ 35 parts.
CN201610609198.2A 2016-07-29 2016-07-29 A kind of Yellow luminous water paint of LED luminous plaque Pending CN106085028A (en)