CN102719182A - Luminescent coating for shoes - Google Patents
Luminescent coating for shoes Download PDFInfo
- Publication number
- CN102719182A CN102719182A CN201210169770XA CN201210169770A CN102719182A CN 102719182 A CN102719182 A CN 102719182A CN 201210169770X A CN201210169770X A CN 201210169770XA CN 201210169770 A CN201210169770 A CN 201210169770A CN 102719182 A CN102719182 A CN 102719182A
- Authority
- CN
- China
- Prior art keywords
- parts
- luminescent coating
- shoes
- coating
- footwear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a luminescent coating for shoes. The luminescent coating for the shoes comprises the following components in part by mass: 20 to 24 parts of medium-oil alkyd resin, 2 to 3 parts of phosphorescent pigment, 0.01 to 0.02 part of manganese naphthenate, 0.01 to 0.02 part of zinc palmitate, 0.5 to 1 part of zinc sulfide, 1 to 2 parts of ethyl acetate, 10 to 15 parts of chloroprene rubber and 15 to 20 parts of carboxymethyl cellulose sodium. The luminescent coating for the shoes can keep the luminescence for 4 to 6 hours after being irradiated at one time for 30 seconds, and can be adhered to various kinds of vamp materials; and the phosphorescent pigment is seldomly used, and the zinc sulfide is added at the same time, so that the performance of the coating is improved, and the cost is reduced.
Description
Technical field
The invention belongs to footwear and use technical field of coatings, particularly footwear are used luminescent coating.
Background technology
When night, road was walked, because light is dark, pedestrian's safety lacked effective guarantee always.Though existing light reflecting material can produce eye-catching effect under light-illuminating, after light was removed, it acted on also completely dissolve and is difficult for coming to light.Existing fluorescent material owing to have radioactivity, therefore can not on conventional shoe, use, and noctilucent material can be decayed owing to light, and cost is high, therefore also seldom is applied on the conventional shoe.
Summary of the invention
The technical problem that solves:
The present invention is directed to the prior art defective, provide a kind of footwear to use luminescent coating, this coating can make shoes after by irradiate light, and is luminous naturally, and fall time is long, and preparation cost is low.
Technical scheme:Footwear are used fluorescent coating, comprise by mass parts: 20～24 parts of medium oil alkyds, 2～3 parts of phosphorescent pigments; 0.01～0.02 part of manganese naphthenate; 0.01～0.02 part of zinc palmitate, 0.5～1 part in zinc sulphide, 1～2 part in ETHYLE ACETATE; 10～15 parts of X 050s, 15～20 parts of sodium cellulose glycolates.
20 parts of said medium oil alkyds.0.02 part of said manganese naphthenate.20 parts of said sodium cellulose glycolates.
Beneficial effect:Footwear provided by the invention are used luminescent coating, after 30 seconds, can keep luminous 4～6 hours at once irradiating, and be suitable for being attached to all kinds of vamp materials, and less use phosphorescent pigments cooperates zinc sulphide simultaneously, has improved coating property, has reduced cost.
Embodiment
Embodiment 1
Footwear are used fluorescent coating, comprise by mass parts: 24 parts of medium oil alkyds, 2 parts of phosphorescent pigments, 0.01 part of manganese naphthenate, 0.01 part of zinc palmitate, 1 part in zinc sulphide, 2 parts in ETHYLE ACETATE, 10 parts of X 050s, 15～20 parts of sodium cellulose glycolates.Footwear provided by the invention are used luminescent coating, after 30 seconds, can keep luminous 4 hours at once irradiating, and be suitable for being attached to all kinds of vamp materials, and less use phosphorescent pigments cooperates zinc sulphide simultaneously, has improved coating property, has reduced cost.
Embodiment 2
Footwear are used fluorescent coating, comprise by mass parts: 20 parts of medium oil alkyds, 3 parts of phosphorescent pigments, 0.02 part of manganese naphthenate, 0.01 part of zinc palmitate, 1 part in zinc sulphide, 1.5 parts in ETHYLE ACETATE, 12 parts of X 050s, 20 parts of sodium cellulose glycolates.Footwear provided by the invention are used luminescent coating, after 30 seconds, can keep luminous 5 hours at once irradiating, and be suitable for being attached to all kinds of vamp materials, and less use phosphorescent pigments cooperates zinc sulphide simultaneously, has improved coating property, has reduced cost.
Embodiment 3
Footwear are used fluorescent coating, comprise by mass parts: 20 parts of medium oil alkyds, 2.5 parts of phosphorescent pigments, 0.01 part of manganese naphthenate, 0.01 part of zinc palmitate, 0.5 part in zinc sulphide, 1 part in ETHYLE ACETATE, 10 parts of X 050s, 20 parts of sodium cellulose glycolates.Footwear provided by the invention are used luminescent coating, after 30 seconds, can keep luminous 3 hours at once irradiating, and be suitable for being attached to all kinds of vamp materials, and less use phosphorescent pigments cooperates zinc sulphide simultaneously, has improved coating property, has reduced cost.This material can keep the luminous intensity decay faint after illumination repeatedly simultaneously, and test result reaches 4 years for guaranteeing property at present.
Claims (4)
1. footwear are used fluorescent coating, it is characterized in that comprising by mass parts: 20～24 parts of medium oil alkyds, 2～3 parts of phosphorescent pigments; 0.01～0.02 part of manganese naphthenate; 0.01～0.02 part of zinc palmitate, 0.5～1 part in zinc sulphide, 1～2 part in ETHYLE ACETATE; 10～15 parts of X 050s, 15～20 parts of sodium cellulose glycolates.
2. footwear according to claim 1 are used fluorescent coating, and its characteristic is by 20 parts of the said medium oil alkyds of mass parts.
3. footwear according to claim 1 are used fluorescent coating, and its characteristic is by 0.02 part of the said manganese naphthenate of mass parts.
4. footwear according to claim 1 are used fluorescent coating, and its characteristic is by 20 parts of the said sodium cellulose glycolates of mass parts.