CN106084959A - A kind of high light corrosion-resistant based aluminum pigment of high stable - Google Patents
A kind of high light corrosion-resistant based aluminum pigment of high stable Download PDFInfo
- Publication number
- CN106084959A CN106084959A CN201610595078.1A CN201610595078A CN106084959A CN 106084959 A CN106084959 A CN 106084959A CN 201610595078 A CN201610595078 A CN 201610595078A CN 106084959 A CN106084959 A CN 106084959A
- Authority
- CN
- China
- Prior art keywords
- minute
- add
- aluminium powder
- times amount
- obtains
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high light corrosion-resistant based aluminum pigment of high stable, it is made up of the raw material of following weight portion: flake aluminum 40 45, isopropanol 100 110, copper sulfate crystal 0.3 0.35, deionized water is appropriate, 2, 2-Oxydiphenol type phosphate ester 4 4.5, dehydrated alcohol is appropriate, tetraethyl orthosilicate 9 10, VTES 67, concentration is the ammonia 9 10 of 20wt%, butyl acetate 200 220, acrylic acid 56, methacrylic acid 56, dibenzoyl peroxide 0.6 0.65, propylene glycol monomethyl ether 13 15, polyvinyl alcohol 1.2 1.5, sodium polyacrylate 0.3 0.4, nano antimony tin oxide 67, dimethicone 1.2 1.4, polydimethylsiloxane 0.8 1.The product that the present invention makes is not corroded in water-based system, and stability is strong.
Description
Technical field
The present invention relates to pigment technology field, particularly relate to a kind of high light corrosion-resistant based aluminum pigment of high stable.
Background technology
Aluminum pigment is one of important metallic pigments, because of aesthetic and the anti-corrosive properties of its uniqueness, is coated with in anticorrosion in recent years
Material, industrial coating, car paint, architecture indoor exterior decoration coating, paint for domestic electric appliance, printing-ink and Plastics Processing Industry obtain
Obtain and extensively apply.Along with constantly strengthening and government's environmental regulation the most perfect of people's environmental consciousness, conventional organic solvents
Type coating will necessarily be replaced by environment-friendlywater-based water-based paint, the aluminum pigment of the aluminum pigment used by water paint and solvent based coating
Having different requirements: first, surface of pigments must be hydrophilic, can be effectively dispersed in water, secondly must keep in aqueous medium
Higher chemical stability.But, the chemical property of aluminum is relatively more active, easily reacts with oxygen or water, and this not only corrodes
Aluminum surface of pigments, have impact on metallic luster and the stability of aluminum, the most also can cause blast, bring unsafe factor to production.
Therefore the Water-borne modification research of aluminum pigment becomes focus, and achieved with certain progress.
In " copper ion alumina powder strengthens the phosphate ester corrosion inhibition to aluminum pigment " literary composition, use copper ion alumina powder
Realizing aluminium powder surface hydroxylation, then using 2, 2-Oxydiphenol type phosphate ester as corrosion inhibiter, preparation method is simple, is harmful to without to organism
Chromate, molybdate, the composition such as nitrite, have certain affinity with aluminum surface of pigments, rate of metal corrosion can be made bright
Aobvious reduction.Although the method adding inhibitor in aluminum pigments system can suppress the corrosion rate of aluminum, but corrosion mitigating effect has
Limit, extends and contacts with water-based system coating, ink etc., and aluminum pigment still can cause certain corrosion, reduces metallic luster
There is also potential safety hazard simultaneously.This is accomplished by the basis of original inhibitor modification being modified, and improves aluminum pigment further
Corrosion resistance, thus improve application in the product such as water paint, ink.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of high light high stable corrosion-resistant aqueous aluminum
Pigment.
The present invention is achieved by the following technical solutions:
A kind of high light corrosion-resistant based aluminum pigment of high stable, is made up of the raw material of following weight portion: flake aluminum 40-
45, isopropanol 100-110, copper sulfate crystal 0.3-0.35, deionized water is appropriate, 2, 2-Oxydiphenol type phosphate ester 4-4.5, dehydrated alcohol suitable
Amount, tetraethyl orthosilicate 9-10, VTES 6-7, concentration are the ammonia 9-10 of 20wt%, butyl acetate 200-
220, acrylic acid 5-6, methacrylic acid 5-6, dibenzoyl peroxide 0.6-0.65, propylene glycol monomethyl ether 13-15, polyvinyl alcohol
1.2-1.5, sodium polyacrylate 0.3-0.4, nano antimony tin oxide 6-7, dimethicone 1.2-1.4, polydimethylsiloxane
0.8-1。
Described a kind of high light corrosion-resistant based aluminum pigment of high stable, is made up of step in detail below:
(1) flake aluminum is put in reactor, add isopropanol, 2, 2-Oxydiphenol type phosphate ester, be heated to 40-50 DEG C, stirring reaction
60-80 minute, copper sulfate crystal is dissolved in the deionized water of 40-50 times amount formation solution and is slowly added to above-mentioned reaction system
In, controlling to add for 15-20 minute, constant temperature stirs 90-120 minute, sucking filtration, is vacuum dried at 55-60 DEG C, obtains inhibition modified
Aluminium powder;
(2) tetraethyl orthosilicate is mixed with VTES, add the dehydrated alcohol of total amount 2-2.5 times amount, formed
Mixed liquor A is stand-by;In the ammonia that concentration is 20wt%, add the deionized water of 1.5-2 times amount, the dehydrated alcohol of 3-4 times amount, stir
Mix that to be formed uniformly mixed liquid B stand-by;Is added the dehydrated alcohol of 10-12 times amount, so in the inhibition modified aluminium powder that step (1) is obtained
After be warming up to 50-60 DEG C, mixed liquor A and B drip are added in reaction system, are incubated 4-5 hour after dropping, stop adding
Heat, filters, and uses absolute ethanol washing product, is finally vacuum dried at 50-60 DEG C, obtains monolayer cladding aluminium powder;
(3) acrylic acid, methacrylic acid, dibenzoyl peroxide are added the formation that stirs in the butyl acetate of half amount mixed
Conjunction liquid is stand-by;The butyl acetate adding surplus in once cladding aluminium powder step (2) obtained is total, ultrasonic disperse 120-150
Minute, be subsequently adding above-mentioned mixed liquor, with 350-400 turn/speed of part is stirred and heated to 85 DEG C, insulation reaction 5-6 hour,
It is cooled to sucking filtration after room temperature, is vacuum dried at 55-60 DEG C, obtains dual cladding aluminium powder;
(4) will in nano antimony tin oxide add 8-10 times amount deionized water, dispersed with stirring add the most afterwards polyvinyl alcohol, poly-third
Olefin(e) acid sodium, after continuing to stir 50-60 minute with the speed of 300-400 rev/min, ultrasonic disperse 30-40 minute, is finally spray-dried,
Obtain modified oxidized stannum antimony powder end;Modified oxidized stannum antimony powder end is put in high speed mixer, add except propylene glycol monomethyl ether it
Remaining outer residual components, stirs 15-20 minute with the speed of 800-1000 rev/min, discharging, pulverizes, and crosses 200 mesh sieves, obtains
Add auxiliary agent;
(5) the interpolation auxiliary agent that dual cladding aluminium powder step (3) obtained obtains with step (4) mixes, and adds propylene glycol list first
Ether, puts in kneader and mediates 30-40 minute, be finally vacuum dried, obtain the present invention.
The invention have the advantage that the present invention first passes through copper ion aluminium oxide and realizes aluminium powder surface hydroxylation, can adsorb
2, 2-Oxydiphenol type phosphate ester, has certain corrosion inhibition;Then by a series of technique by silicon dioxide and polyacrylate
Be respectively coated by inhibition modified aluminium powder surface, form fine and close nucleocapsid structure, can effectively shield aluminium powder core, prevent aluminum pigment with
Water or air dielectric come in contact reaction, and dual cladding significantly improves the corrosion resistance of aluminum pigment;The aluminum pigment of preparation is applied to be coated with
Good dispersion property in material, appearance of film flat smooth, glossiness is good, good to the adhesive force of coating.
The present invention adds the nano antimony tin oxide powder of modification in the preparation of aluminum pigment, and light transmittance is good, does not interferes with aluminum
The bright property of pigment, enhances the stability of aluminum pigment simultaneously so that the product made is not corroded in water-based system, stable
Property is strong.
Detailed description of the invention
A kind of high light corrosion-resistant based aluminum pigment of high stable, is made up of the raw material of following weight portion (kilogram): sheet
Shape aluminium powder 40, isopropanol 100, copper sulfate crystal 0.3, deionized water are appropriate, 2, 2-Oxydiphenol type phosphate ester 4, dehydrated alcohol silicon appropriate, positive
Acetoacetic ester 9, VTES 6, concentration are the ammonia 9 of 20wt%, butyl acetate 200, acrylic acid 5, methacrylic acid
5, dibenzoyl peroxide 0.6, propylene glycol monomethyl ether 13, polyvinyl alcohol 1.2, sodium polyacrylate 0.3, nano antimony tin oxide 6, two
Methyl-silicone oil 1.2, polydimethylsiloxane 0.8.
Described a kind of high light corrosion-resistant based aluminum pigment of high stable, is made up of step in detail below:
(1) flake aluminum is put in reactor, add isopropanol, 2, 2-Oxydiphenol type phosphate ester, be heated to 40 DEG C, stirring reaction 60 points
Clock, is dissolved in copper sulfate crystal in the deionized water of 40 times amount formation solution and is slowly added in above-mentioned reaction system, control 15 points
Clock adds, and constant temperature stirs 90 minutes, sucking filtration, is vacuum dried, obtains inhibition modified aluminium powder at 55 DEG C;
(2) tetraethyl orthosilicate is mixed with VTES, add the dehydrated alcohol of total amount 2 times amount, form mixing
Liquid A is stand-by;Adding the deionized water of 1.5 times amount, the dehydrated alcohol of 3 times amount in the ammonia that concentration is 20wt%, stir shape
Become mixed liquid B stand-by;Is added in the inhibition modified aluminium powder that step (1) is obtained the dehydrated alcohol of 10 times amount, then heats to 50
DEG C, mixed liquor A and B drip are added in reaction system, after dropping, are incubated 4 hours, stop heating, filter, with anhydrous
Washing with alcohol product, is finally vacuum dried at 50 DEG C, obtains monolayer cladding aluminium powder;
(3) acrylic acid, methacrylic acid, dibenzoyl peroxide are added the formation that stirs in the butyl acetate of half amount mixed
Conjunction liquid is stand-by;The butyl acetate adding surplus in once cladding aluminium powder step (2) obtained is total, ultrasonic disperse 120 minutes,
It is subsequently adding above-mentioned mixed liquor, is stirred and heated to 85 DEG C with the speed of 350 turns/part, insulation reaction 5 hours, it is cooled to room temperature
Rear sucking filtration, is vacuum dried at 55 DEG C, obtains dual cladding aluminium powder;
(4) will add the deionized water of 8 times amount in nano antimony tin oxide, dispersed with stirring adds polyvinyl alcohol, polypropylene the most afterwards
Acid sodium, after continuing to stir 50 minutes with the speed of 300 revs/min, ultrasonic disperse 30 minutes, is finally spray-dried, obtains modified oxidized
Stannum antimony powder end;Modified oxidized stannum antimony powder end is put in high speed mixer, adds remaining residue in addition to propylene glycol monomethyl ether
Composition, stirs 15 minutes with the speed of 800 revs/min, discharging, pulverizes, and crosses 200 mesh sieves, obtains adding auxiliary agent;
(5) the interpolation auxiliary agent that dual cladding aluminium powder step (3) obtained obtains with step (4) mixes, and adds propylene glycol list first
Ether, puts in kneader and mediates 30 minutes, be finally vacuum dried, obtain the present invention.
Through inspection, product of the present invention good dispersion in water-based system, inhibition efficiency is 97.5%, and coating gloss is
109.8Gs。
Claims (2)
1. the one kind high light corrosion-resistant based aluminum pigment of high stable, it is characterised in that be made up of the raw material of following weight portion:
Flake aluminum 40-45, isopropanol 100-110, copper sulfate crystal 0.3-0.35, deionized water are appropriate, 2, 2-Oxydiphenol type phosphate ester 4-
4.5, dehydrated alcohol is appropriate, tetraethyl orthosilicate 9-10, VTES 6-7, concentration are 20wt% ammonia 9-10,
Butyl acetate 200-220, acrylic acid 5-6, methacrylic acid 5-6, dibenzoyl peroxide 0.6-0.65, propylene glycol monomethyl ether
13-15, polyvinyl alcohol 1.2-1.5, sodium polyacrylate 0.3-0.4, nano antimony tin oxide 6-7, dimethicone 1.2-1.4, poly-
Dimethyl siloxane 0.8-1.
A kind of high light corrosion-resistant based aluminum pigment of high stable, it is characterised in that by detail below
Step is made:
(1) flake aluminum is put in reactor, add isopropanol, 2, 2-Oxydiphenol type phosphate ester, be heated to 40-50 DEG C, stirring reaction
60-80 minute, copper sulfate crystal is dissolved in the deionized water of 40-50 times amount formation solution and is slowly added to above-mentioned reaction system
In, controlling to add for 15-20 minute, constant temperature stirs 90-120 minute, sucking filtration, is vacuum dried at 55-60 DEG C, obtains inhibition modified
Aluminium powder;
(2) tetraethyl orthosilicate is mixed with VTES, add the dehydrated alcohol of total amount 2-2.5 times amount, formed
Mixed liquor A is stand-by;In the ammonia that concentration is 20wt%, add the deionized water of 1.5-2 times amount, the dehydrated alcohol of 3-4 times amount, stir
Mix that to be formed uniformly mixed liquid B stand-by;Is added the dehydrated alcohol of 10-12 times amount, so in the inhibition modified aluminium powder that step (1) is obtained
After be warming up to 50-60 DEG C, mixed liquor A and B drip are added in reaction system, are incubated 4-5 hour after dropping, stop adding
Heat, filters, and uses absolute ethanol washing product, is finally vacuum dried at 50-60 DEG C, obtains monolayer cladding aluminium powder;
(3) acrylic acid, methacrylic acid, dibenzoyl peroxide are added the formation that stirs in the butyl acetate of half amount mixed
Conjunction liquid is stand-by;The butyl acetate adding surplus in once cladding aluminium powder step (2) obtained is total, ultrasonic disperse 120-150
Minute, be subsequently adding above-mentioned mixed liquor, with 350-400 turn/speed of part is stirred and heated to 85 DEG C, insulation reaction 5-6 hour,
It is cooled to sucking filtration after room temperature, is vacuum dried at 55-60 DEG C, obtains dual cladding aluminium powder;
(4) will in nano antimony tin oxide add 8-10 times amount deionized water, dispersed with stirring add the most afterwards polyvinyl alcohol, poly-third
Olefin(e) acid sodium, after continuing to stir 50-60 minute with the speed of 300-400 rev/min, ultrasonic disperse 30-40 minute, is finally spray-dried,
Obtain modified oxidized stannum antimony powder end;Modified oxidized stannum antimony powder end is put in high speed mixer, add except propylene glycol monomethyl ether it
Remaining outer residual components, stirs 15-20 minute with the speed of 800-1000 rev/min, discharging, pulverizes, and crosses 200 mesh sieves, obtains
Add auxiliary agent;
(5) the interpolation auxiliary agent that dual cladding aluminium powder step (3) obtained obtains with step (4) mixes, and adds propylene glycol list first
Ether, puts in kneader and mediates 30-40 minute, be finally vacuum dried, obtain the present invention.