CN106084904A - A kind of inorganic oxygen bar solid-state paint formula - Google Patents
A kind of inorganic oxygen bar solid-state paint formula Download PDFInfo
- Publication number
- CN106084904A CN106084904A CN201610394201.3A CN201610394201A CN106084904A CN 106084904 A CN106084904 A CN 106084904A CN 201610394201 A CN201610394201 A CN 201610394201A CN 106084904 A CN106084904 A CN 106084904A
- Authority
- CN
- China
- Prior art keywords
- grams
- powder
- agent
- dry powder
- inorganic oxygen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of inorganic oxygen bar solid-state paint formula, raw material components including following weight portion percentage ratio: calcination kieselguhr: 8 10%, calcium oxide 35% 45%, sodium rice titanium dioxide 4 6%, Pulvis Talci 2 4%, dry powder 18 22%, powdered polyvinyl alcohol 2 4%, mica powder 2 4%, latex powder 18 22%, methylcellulose 0.5% 0.7%, defoamer 0.3% 0.5%, inorganic thixotropic agent 0.3% 0.5%, fluorescent whitening agent 0.1% 0.2%, dry powder antifungus agent 0.1% 0.2%.It is solid-state that the present invention changes the liquid of original paint, and the water adding 1.5 2 times of weight during use is adjusted the most static 30 minutes and can construct, to reduce production, cost of transportation.Change the formula of original paint to reach the effect of environmental protection.
Description
Technical field
The invention belongs to chemical technology field, a kind of inorganic oxygen bar solid-state paint formula.
Background technology
In existing oil paint, a lot of paint have used benzene class, ketone and esters equal solvent in process of production, this
A little solvent highly volatiles, also can spray workman's to job site to environment during producing and using
Health causes harm in various degree.At present, the taste after a procedure of paint on the market is very big, about two weeks to be breathed freely
Just can move in, contain that to paint the air of taste harmful.And after part drying varniss, still remain molten in paint film
Agent, can directly influence the health of user.And liquid paint the most on the market is for transport, the use of northern area has pole
Big inconvenience, is limited to the impact in terms of form, causes freezing of liquid paint to bring the most not on using as temperature is on the low side
Just, environmental constraints, transport is too high with production cost makes remote districts, the north almost nil for the use of liquid paint.Additionally this
Solid-state paint can be allocated according to engineering usage amount, reaches to avoid waste, and (liquid paint is opened one barrel and is necessary for using in the effect of reduction cost
Complete, often produce waste).Therefore selecting the solid-state paint to human body and environment non-hazardous, develop a set of inorganic oxygen bar solid-state paint has very much
Necessary.
Summary of the invention
It is an object of the invention to provide a kind of inorganic oxygen bar solid-state paint formula, solve the problem in background technology.
The present invention realizes by the following technical solutions:
A kind of inorganic oxygen bar solid-state paint formula, including the raw material components of following weight portion percentage ratio:
Calcination kieselguhr: 8-10%
Calcium oxide 35%-45%
Sodium rice titanium dioxide 4-6%
Dry powder 18-22%
Mica powder 2-4%
Pulvis Talci 2-4%
Powdered polyvinyl alcohol 2-4%
Latex powder 18-22%
Methylcellulose 0.5%-0.7%
Defoamer 0.3%-0.5%
Thixotropic agent 0.3%-0.5%
Fluorescent whitening agent 0.1%-0.2%.
Dry powder antifungus agent 0.1%-0.2%
A kind of inorganic oxygen bar solid-state paint formula, including the raw material components of following weight: every 1000 grams of content are
Calcination kieselguhr: 100 grams
Calcium oxide 500 grams
Sodium rice titanium dioxide 50 grams
Dry powder 100 grams
Mica powder 10 grams
Latex powder 120 grams
Pulvis Talci 50 grams
Powdered polyvinyl alcohol 50 grams
Methylcellulose 6.0 grams
Defoamer 4.0 grams
Thixotropic agent 6.0 grams
Fluorescent whitening agent 2.0 grams.
Dry powder antifungus agent 2.0 grams
In the present invention, described calcination kieselguhr is white calcination kieselguhr.
The preparation technology of a kind of inorganic oxygen bar solid-state paint is: weigh raw material by weight percentage, then will calcination kieselguhr,
Calcium oxide, sodium rice titanium dioxide, dry powder, mica powder, Pulvis Talci super micron mill is pulverized, and is subsequently adding powder polyethylene
Alcohol, latex powder, methylcellulose, defoamer, thixotropic agent, fluorescent whitening agent stir evenly and i.e. obtain a kind of inorganic oxygen bar solid-state paint.
In the present invention, calcium oxide and be calcined diatomaceous use, utilize calcium oxide add water allotment after absorbing carbon dioxide, produce
Expand in raw, make lacquer painting tempering, can water-fast, moisture resistance, scrubbing resistance.Calcination kieselguhr increases absorbability, simultaneously energy releasing oxygen,
Reach the function of inorganic oxygen bar.
Beneficial effect: the present invention is solid-state paint, changes the form of original paint to reduce production, cost of transportation.Change
The formula of original paint is to reach the effect of environmental protection.Inorganic oxygen bar solid-state paint and the difference of generic latex paint: 1, decompose elimination formaldehyde,
Benzene, ammonia harmful gas；2, anion releasing and far infrared, regulates microcirculation in human body, improves sleep quality；3, remove contamination self-cleaning,
Water-fast, can clean；4, fire protection flame retarding, can be high temperature resistant, and the most molten point does not has burning-point；5, color eye protection, absorptance is strong, makes reflection
Light soft；6, damping sterilization, may absorb moisture content, can discharge hydrone damping when air is dried during indoor moisture；7、
Overlong service life, does not falls off, colour-fast, resistance to fosterization；8, easy construction, the function of existing diatom ooze, there is again the construction letter of emulsion paint
Just.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of inorganic oxygen bar solid-state paint formula, including the raw material components of following weight portion percentage ratio: calcination kieselguhr: 8-
10%, calcium oxide 35%-45%, sodium rice titanium dioxide 4-6%, dry powder 18-22%, mica powder 2-4%, Pulvis Talci 2-4%,
Powdered polyvinyl alcohol 2-4%, latex powder 18-22%, methylcellulose 0.5%-0.7%, defoamer 0.3%-0.5%, thixotroping
Agent 0.3%-0.5%, fluorescent whitening agent 0.1%-0.2%, dry powder antifungus agent 0.1%-0.2%.A kind of inorganic oxygen bar solid-state paint
Preparation technology be: weigh raw material by weight percentage, then will calcination kieselguhr, calcium oxide, sodium rice titanium dioxide, round trip flight
Powder, mica powder, Pulvis Talci super micron mill is pulverized, and is subsequently adding powdered polyvinyl alcohol, latex powder, methylcellulose, froth breaking
Agent, thixotropic agent, fluorescent whitening agent, dry powder antifungus agent stir evenly and i.e. obtain a kind of inorganic oxygen bar solid-state paint.
Embodiment 2
A kind of inorganic oxygen bar solid-state paint formula, including the raw material components of following weight: calcination kieselguhr: 100 grams, calcium oxide
500 grams, sodium rice titanium dioxide 50 grams, dry powder 100 grams, mica powder 10 grams, Pulvis Talci 50 grams, powdered polyvinyl alcohol 50 grams, breast
Rubber powder 120 grams, methylcellulose 6.0 grams, defoamer 4.0 grams, thixotropic agent 4.0 grams, fluorescent whitening agent 2.0 grams, dry powder antifungus agent 2
Gram.Described calcination kieselguhr is white calcination kieselguhr.The preparation technology of a kind of inorganic oxygen bar solid-state paint is: by weight percentage
Weigh raw material, then by calcination kieselguhr, calcium oxide, sodium rice titanium dioxide, dry powder, mica powder, Pulvis Talci micronizing
Machine pulverize, be subsequently adding powdered polyvinyl alcohol, latex powder, methylcellulose, defoamer, thixotropic agent, fluorescent whitening agent, dry powder prevent
Mould dose stirs evenly and i.e. obtains a kind of inorganic oxygen bar solid-state paint.
The ultimate principle of the present invention and principal character and advantages of the present invention, the technology of the industry have more than been shown and described
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both fall within scope of the claimed invention, claimed scope by appending claims and
Equivalent defines.
Claims (3)
1. an inorganic oxygen bar solid-state paint formula, it is characterised in that include the raw material components of following weight portion percentage ratio:
Calcination kieselguhr: 8-10%
Calcium oxide 35%-45%
Sodium rice titanium dioxide 4-6%
Dry powder 18-22%
Mica powder 2-4%
Pulvis Talci 2-4%
Powdered polyvinyl alcohol 2-4%
Latex powder 18-22%
Methylcellulose 0.5%-0.7%
Defoamer 0.3%-0.5%
Thixotropic agent 0.3%-0.5%
Fluorescent whitening agent 0.1%-0.2%.
Dry powder antifungus agent 0.1%-0.2%.
One the most according to claim 1 inorganic oxygen bar solid-state paint formula, it is characterised in that include the raw material of following weight
Component: every 1000 grams of content
Calcination kieselguhr: 100 grams
Calcium oxide 500 grams
Sodium rice titanium dioxide 50 grams
Dry powder 100 grams
Mica powder 10 grams
Latex powder 120 grams
Pulvis Talci 50 grams
Powdered polyvinyl alcohol 50 grams
Methylcellulose 6.0 grams
Defoamer 4.0 grams
Thixotropic agent 6.0 grams
Fluorescent whitening agent 2.0 grams.
Dry powder antifungus agent 2.0 grams.
3. the preparation technology of an inorganic oxygen bar solid-state paint, it is characterised in that weigh raw material by weight percentage, then will calcination
Kieselguhr, calcium oxide, sodium rice titanium dioxide, dry powder, mica powder, Pulvis Talci super micron mill is pulverized, and is subsequently adding powder
Polyvinyl alcohol, latex powder, methylcellulose, defoamer, thixotropic agent, fluorescent whitening agent stir evenly and i.e. obtain a kind of inorganic oxygen bar solid-state
Paint.