CN106082651A - The coloured glaze that a kind of firing temperature is low - Google Patents
The coloured glaze that a kind of firing temperature is low Download PDFInfo
- Publication number
- CN106082651A CN106082651A CN201610671462.5A CN201610671462A CN106082651A CN 106082651 A CN106082651 A CN 106082651A CN 201610671462 A CN201610671462 A CN 201610671462A CN 106082651 A CN106082651 A CN 106082651A
- Authority
- CN
- China
- Prior art keywords
- parts
- coloured glaze
- low
- firing temperature
- flux
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the coloured glaze that a kind of firing temperature is low, it is to be grouped into by the one-tenth of following mass fraction, including: quartz sand 80 85 parts, soda 20 30 parts, clarifier 15 20 parts, oxidant 5 10 parts, flux 15 18 parts, coloring agent 15 20 parts, 5 10 parts of firming agent.Described flux is the mixture of sodium carbonate, potassium carbonate, sodium carbonate and potassium nitrate.By the way, the present invention can reduce the fusing point of coloured glaze, fires at a lower temperature, thus optimized production process, reduce production cost.
Description
Technical field
The present invention relates to coloured glaze field, particularly relate to the coloured glaze that a kind of firing temperature is low.
Background technology
Fine work colored glaze product fires it is generally required to the hot conditions of 1400 DEG C, and clarifying temp needs to arrive 1600-especially
1800 DEG C, owing to temperature requirement is the highest, and the time that coloured glaze fires needs consuming is the longest, is always maintained at high-temperature firing, to combustion
How material, the suitable height of requirement of equipment, reduce the firing temperature of colored glaze product, thus reduce production cost, reduce expense, be
One problem preparing research.
Summary of the invention
The technical problem that present invention mainly solves is to provide one, it is possible to reduce the fusing point of coloured glaze, at a lower temperature
Fire, thus optimized production process, reduce production cost.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide the coloured glaze that a kind of firing temperature is low
Glass, is to be grouped into by the one-tenth of following mass fraction, including: quartz sand 80-85 part, soda 20-30 part, clarifier 15-20 part, oxygen
Agent 5-10 part, flux 15-18 part, coloring agent 15-20 part, firming agent 5-10 part.Described flux is sodium carbonate, carbonic acid
Potassium, sodium carbonate and the mixture of potassium nitrate.
In a preferred embodiment of the present invention, the coloured glaze that described firing temperature is low, is by the one-tenth of following mass fraction
It is grouped into, including: quartz sand 80 parts, soda 25 parts, clarifier 16 parts, oxidant 7 parts, flux 15 parts, coloring agent 17 parts, solid
Agent 8 parts.
In a preferred embodiment of the present invention, the coloured glaze that described firing temperature is low, is by the one-tenth of following mass fraction
It is grouped into, including: quartz sand 85 parts, soda 24 parts, clarifier 17 parts, oxidant 9 parts, flux 16 parts, coloring agent 19 parts, solid
Agent 6 parts.
The invention has the beneficial effects as follows: the present invention can reduce the fusing point of coloured glaze, fires at a lower temperature, thus excellent
Metaplasia production. art, reduces production cost.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
Embodiment 1:
The coloured glaze that a kind of firing temperature is low, is to be grouped into by the one-tenth of following mass fraction, including: quartz sand 80 parts, soda 25 parts,
Clarifier 16 parts, oxidant 7 parts, flux 15 parts, coloring agent 17 parts, 8 parts of firming agent.
Embodiment 2:
The coloured glaze that a kind of firing temperature is low, is to be grouped into by the one-tenth of following mass fraction, including: quartz sand 85 parts, soda 24 parts,
Clarifier 17 parts, oxidant 9 parts, flux 16 parts, coloring agent 19 parts, 6 parts of firming agent.
By using sodium carbonate, potassium carbonate, the sodium carbonate mixture with potassium nitrate as flux, effective fall can be reduced
The fusing point of low coloured glaze, thus reduce the effect of firing temperature.
The coloured glaze that described firing temperature is low, its preparation process is as follows: weigh raw material；Raw material refines；Raw material preheats, in advance
Heating-up temperature is maintained at 250-300 DEG C, continues 2-3 hour；Raw material melts, and melt temperature controls at 1100 DEG C, continues 20 hours；
High temperature is clarified, and clarifying temp is 1300 DEG C, continues 18 hours；Mould molding；Cooling refine；Annealing, annealing temperature controls 500
DEG C, continue 5 hours；Secondary refine.
The present invention can reduce the fusing point of coloured glaze, fires at a lower temperature, thus optimized production process, reduce and produce
Cost.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description and content are made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. the coloured glaze that a firing temperature is low, it is characterised in that be to be grouped into by the one-tenth of following mass fraction, including: quartz sand
80-85 part, soda 20-30 part, clarifier 15-20 part, oxidant 5-10 part, flux 15-18 part, coloring agent 15-20 part, solid
Agent 5-10 part.
2. flux described in is the mixture of sodium carbonate, potassium carbonate, sodium carbonate and potassium nitrate.
The coloured glaze that firing temperature the most according to claim 1 is low, it is characterised in that be to be grouped by the one-tenth of following mass fraction
Become, including: quartz sand 80 parts, soda 25 parts, clarifier 16 parts, oxidant 7 parts, flux 15 parts, coloring agent 17 parts, firming agent
8 parts.
The coloured glaze that firing temperature the most according to claim 1 is low, it is characterised in that be to be grouped by the one-tenth of following mass fraction
Become, including: quartz sand 85 parts, soda 24 parts, clarifier 17 parts, oxidant 9 parts, flux 16 parts, coloring agent 19 parts, firming agent
6 parts.