CN1060690A - A kind of vacuum aluminium plating cigarette box line paper - Google Patents
A kind of vacuum aluminium plating cigarette box line paper Download PDFInfo
- Publication number
- CN1060690A CN1060690A CN 90106276 CN90106276A CN1060690A CN 1060690 A CN1060690 A CN 1060690A CN 90106276 CN90106276 CN 90106276 CN 90106276 A CN90106276 A CN 90106276A CN 1060690 A CN1060690 A CN 1060690A
- Authority
- CN
- China
- Prior art keywords
- paper
- pulp
- layer
- coated
- cigarette
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of vacuum aluminium-plated paper that is used for the little tympan sheet of cigarette.Its principal character is to cover to mould the layer of polyethylene film on body paper, and coating one deck alcohol dissolubility pre-treating adhesive on polyethylene film carries out vacuum aluminum-coatedly on the coating of pre-treating adhesive, forms one deck aluminizer.This paper has original paper layer, covers and mould layer, rubberised layer and aluminium coated.The moistureproof flavor property of protecting is good, and aluminium powder does not come off, and can be used for internal liner package of foods.
Description
The invention belongs to the vacuum aluminium-plated paper category, especially for the interior lining paper and the food wrapper of cigarette inner wrapping.
The interior lining paper that is used for the cigarette inner wrapping in the prior art as the paper of QB849-83 regulation, when little package operation of cigarette-packaging machine and use, produces the aluminium powder obscission, causes the pollution of metal dust, and the moistureproof flavor performance of protecting is affected.Japanese Patent Laid communique (A), clear 61-215793 disclose a kind of artistic paper of be used to chart printing and external packing.The formation of its paper is that body paper+vistanex+acrylic resin (or polyester based resin)+aluminium is steaming layer+acrylic acid series (or polyester system) resin.The paper of above-mentioned formation is effective as label printing paper and overwrap, but as cigarette and internal liner package of foods paper, because coating and the used material of top coat are organic macromolecule resin under it, are solvent with benzene class and vinyl chloride, and be improper for the internal liner package of food and cigarette.And body paper will use high-grade paper such as matter paper, glassine paper, artistic paper, and is therefore, improper as the liner inner wrapping paper of cigarette.
The purpose of this invention is to provide a kind of cigarette lining parcel paper and internal liner package of foods paper of being applicable to.
The objective of the invention is to reach like this, at the compound layer of polyethylene thin layer of the one side of body paper, coated one deck preliminary treatment glued membrane on this thin layer, the top of preliminary treatment glued membrane plates one deck aluminium coated with vacuum coating equipment.It promptly is the interior lining paper that is used for cigarette package of the present invention.
The used body paper of tympan sheet of the present invention can be pure wood pulp paper, and its main characteristics is not only to use wood pulp paper, can also be with the paper of the mixed pulp system of homemade straw pulp and wood pulp, and grass, cotton, the paper of wood pulp mixed pulp and the paper of Populus deltoides slurry mixed pulp, ratio can be from 0.5: 9.5 to 9.5: 0.5.Even the body paper of poor quality, also can reach every index request such as tension, anti tear of standard-required after compound, and compare with the little cylinder-packing of cigarette wraparound of the original use paper of aluminizing that to have a moisture resistance good, it is good to protect the fragrant flavor performance of protecting, the characteristics of the aluminium powder that do not come off.Compare with the artistic paper among the clear 61-215793, even the aluminium coated of appearance does not have external coating to have good printing drawing performance yet, and the pollution of organic solvent-free volatilization, can be used as internal liner package of foods paper and use.
Provided the enlarged diagram of the section structure of tympan sheet of the present invention in the accompanying drawing.
Below tympan sheet of the present invention is described in detail. In the accompanying drawings, 1. body paper is 2. moulded layer, 3. preliminary treatment glue-line, 4. aluminium coated again. Once did in the past after moulding again on the body paper and directly aluminize, consequently aluminized paper is curling, can't normally use on bag cigarette machine, and the quality of paper is also bad. Original technology is consolidated coating as the sealing in paper hole and the pre-treating adhesive before aluminizing with the height of pure dissolubility. Aluminized paper does not take place curling, and still, aluminium powder comes off seriously. The present invention proposes in order to improve above-mentioned deficiency just.
The body paper of the usefulness of aluminizing, quantitative target is at 45～120g/m2All can. According to experience in the past, original paper quality is more good, and the quality of aluminized paper is also more good. Simple when using high solid coating, the straw pulp ratio in the body paper reaches 70% when above, and the quality of aluminized paper just is difficult for assurance. In the paper structure of the present invention, first coated layer of polyethylene plastic sheeting on body paper, the thickness of this layer is decided on the quality of body paper, generally between 8～50um, be preferably between 10～25um, quantitatively low body paper coating is thinner, and quantitatively high body paper coated bed thickness is a little. The polyethylene that adopts is that melt index 2～8 extrusion moldings are coated with replica, preferably adopts 1F7B and 1C7A type. Multiple molding machine can use the multiple molding machine of TNK1050EX type or other models.
Body paper is after moulding operation again, and the rewinding rolling enters painting process, at the multiple high solid coating of good poly surface-coated one deck alcohol dissolubility, high solid coating can use provide in the Chinese patent 86106862 give processing glue. Also can use the glue made from additive method, solids content all can between 5～80%. But best to use pure dissolubility in 86106862 to give to process glue. Q-1000 type or H5211-∏ type coating machine are used in the coating apparatus suggestion, and Painting effect is best, and is simple to operate, easy to use. The alcohol dissolubility gives the use amount of processing glue and does solid amount between 2～10g, thickness 2～10um with every square metre. Be coated with complete after, with rewinding good through once mould again and once coating have one deck original paper layer after what handle well, one deck is moulded layer again, one deck coating is given the treatment paper of giving of the rubberised layer of processing glue and is carried out vacuum aluminum-coated. It may be noted that once mould again and once coating can satisfy vacuum aluminum-coated requirement, if again row to repeat to mould again and be coated be insignificant repetition and waste.
Vacuum aluminum-coated suggestion is carried out on H4411 ∏-ZD type devices of coiled vacuum coating machine, or use GALILEOA-AL type vacuum coating equipment to require to operate according to the operation of vacuum coating equipment, make that at glued membrane surface evaporation one layer thickness that gives processing glue through giving processing be 1 * 10
-8～3 * 10
-8The aluminium film of m.Can obtain tympan sheet of the present invention through above-mentioned working procedure processing process, promptly can be used as little tympan sheet of cigarette or packaging for foodstuff lining paper after cutting packaging process through moisture regain again, as through mould again, gluing, the 120g/m that aluminizes
2The ox-hide body paper can be used as the inside lining packing paper of tealeaves.
Below provide specific embodiment:
Get and quantitatively be 45g/m
2Body paper, the straw pulp ratio is 5%, the polyethylene thickness of moulding layer again is 10um, the giving of rubberised layer handled glue and quantitatively is 8g/m
2, aluminum layer thickness is 1 * 10
-8M can obtain the tympan sheet that cigarette is used.
Get and quantitatively be 45g/m
2Body paper, the straw pulp ratio is 30%, moulds the polyethylene thickness 15um of layer again, what the giving of rubberised layer handled glue quantitatively is 10g/m
2, aluminum layer thickness is 1.5 * 10
-8M can obtain the tympan sheet that cigarette is used.
Get and quantitatively be 45g/m
2Body paper, the straw pulp ratio is 50%, moulds the polyethylene thickness 20um of layer again, what the giving of rubberised layer handled glue quantitatively is 12g/m
2, aluminum layer thickness is 2 * 10
-8M can obtain the cigarette tympan sheet.
Get and quantitatively be 45g/m
2Body paper, the straw pulp ratio is 70%, moulds the polyethylene thickness 20um of layer again, what the giving of rubberised layer handled glue quantitatively is 14g/m
2, aluminum layer thickness is 2.5 * 10
-8M can obtain the cigarette tympan sheet.
Embodiment 5
Get and quantitatively be 45g/m
2Body paper, the straw pulp ratio is 95%, moulds the polyethylene thickness 25um of layer again, what the giving of rubberised layer handled glue quantitatively is 16g/m
2, aluminum layer thickness is 2.5 * 10
-8～3 * 10
-8M can obtain the cigarette tympan sheet.
Need particularly point out, the straw pulp ratio in the above embodiments and the thickness of aluminium coated and mould again the layer thickness and the quantitative target of rubberised layer can exchange, promptly the 45g/m among the embodiment 1
2Quantitative body paper, after 5% the straw pulp ratio and the body paper of the straw pulp ratio 95% among the embodiment 5 exchanged, all the other indexs were constant, can obtain qualified cigarette tympan sheet fully.
Embodiment 6
Be 120g/m quantitatively
2Body paper, the straw pulp ratio is 50%, moulds layer thickness 25um again, rubberised layer to give the quantitative target of handling glue be 15g/m
2, aluminum layer thickness is 2.5 * 10
-8M can obtain good tealeaves inside lining packing paper.
Be 65g/m quantitatively
2Body paper, all the other indexs are identical with embodiment 6, can obtain qualified food inside lining packing paper.
Embodiment 8
Get and quantitatively be 80g/m
2Body paper, all the other indexs are identical with embodiment 6, promptly can obtain qualified food liner (outer lining) wrapping paper.
Wrapping paper of the present invention can be used as the use of label printing paper fully.If use pure wood pulp paper, better effects if.
Reference examples:
Get and quantitatively be 45g/m
2Body paper, straw pulp ratio 0, rubberised layer is handled glue-line (CN86106862 number) for giving, aluminum layer thickness is 1 * 10
-8～3 * 10
-8M all can.The cigarette package that the is former explained hereafter paper of aluminizing.
Straw pulp in embodiment 1～8, wood pulp mixed pulp paper can change straw pulp, cotton pulp, wood pulp mixed pulp paper into, reach cotton pulp, wood pulp mixed pulp paper, and effect is constant.
The regulation among the QB849-83 is pressed in contrast.
1. moisture permeability: index embodiment reference examples
50g/m
2·24h 5～15 50
2. adhesive force: index embodiment reference examples
The dealuminzation powder aluminium powder that do not come off does not come off seriously
Claims (3)
1, a kind of on a surface of body paper the vacuum aluminium-plated paper of compound layer of polyethylene film, it is characterized in that between polyethylene film and aluminium coated coated one deck alcohol dissolubility cigarette tympan sheet that gives the rubberised layer composition of handling glue before vacuum aluminum-coated.
2, according to the described tympan sheet of claim 1, it is characterized in that said body paper is the mixed slurry paper of straw pulp and wood pulp and the mixed pulp paper of wood pulp and straw pulp cotton pulp, and the mixed pulp paper of cotton pulp and wood pulp.
3, according to the described tympan sheet of claim 1, it is characterized in that said polyethylene film is that melt index 2～8 extrusion moldings are coated with the replica polyethylene, the multiple molding machine of warp is compounded in the thin film on the body paper.