CN102899957A - Production method for lining paper for cigarette - Google Patents
Production method for lining paper for cigarette Download PDFInfo
- Publication number
- CN102899957A CN102899957A CN2012104119078A CN201210411907A CN102899957A CN 102899957 A CN102899957 A CN 102899957A CN 2012104119078 A CN2012104119078 A CN 2012104119078A CN 201210411907 A CN201210411907 A CN 201210411907A CN 102899957 A CN102899957 A CN 102899957A
- Authority
- CN
- China
- Prior art keywords
- pulp
- weight
- production method
- paper
- lining paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production method for a lining paper for a cigarette. The production method comprises the following steps: A) preparing grinding pulp, and then allocating the pulp which contains 15-30 wt.% of bleached needle bush pulp, 55-75 wt.% of bleached hardwood pulp and 10-15 wt.% of straw pulp, separately pulping, and then mixing the grinding pulp, and controlling pulp intensity at 30-40 OSR and wet weight being 2.5-5.5g; B) adding padding and a degassing agent before primarily slushing the pulp, and then entering into multi-stage deslagging; C) adding pulp glue and starting the secondary slushing; D) after ending the secondary slushing, adding a sizing agent, placing into a pressure screen for treating, and adding a retention agent at an outlet of the pressure screen; E) pouring the pulp into a pulp flowing box, loading a net and preparing paper with the pulp; F) extracting and dewatering; G) drying; H) performing soft calendaring dual-pressing treatment; and I) coiling, rewinding and cutting, packaging and putting into a storage. The lining paper for the cigarette produced according to the production method has the beneficial effects: the paper sheet uniformity is excellent; the horizontal width rated difference is small; the tensile force is high; the lining paper is easy to cut; the front surface of the paper sheet has higher smoothness; and the back surface of the paper sheet has certain smoothness.
Description
Technical field
The present invention relates to a kind of tobacco lining paper production method.
Background technology
Existing vacuum aluminium-plated paper and moistureproof paper are widely used in cigarette, food, daily use chemicals, decoration industry, owing to the quality reason, vertical stretching resistance of vacuum aluminium-plated paper and moistureproof paper is poor, be only suitable for using on the production line of low speed, especially be not suitable for using at the high-speed cigarette machine of tobacco business, otherwise disconnected paper phenomenon occurs easily.As improvement, in the prior art, by aluminum foil backing paper and the compound rear formation composite aluminium foil paper of rolling aluminum foil, this composite aluminium foil paper is compared with moistureproof paper with vacuum aluminium-plated paper larger advantage, particularly can be used as tobacco lining paper uses at high-speed cigarette machine, but the technique that composite aluminium foil paper is produced is different, and the composite aluminium foil paper of producing also has different performances.
Summary of the invention
The invention provides a kind of production method of tobacco lining paper, by increasing a certain amount of filler auxiliary agent and selecting suitable adding point to guarantee that the reliable in quality of product is stable, on integrated performance index, more be better than the tobacco lining paper of producing with prior art.
Technical scheme of the present invention is:
A kind of production method of tobacco lining paper comprises the steps:
A, preparation are carried out with slurry behind the defibrination, and wherein, bleaching needle-point leaf pulp is 15-30%(weight), bleached hardwood pulp is 55-75%(weight), straw pulp is 10-15%(weight), separately mix defibrination after the making beating, control degree of beating 30-40
ZeroSR, weight in wet base 2.5-5.5g;
B, slurry enter once and add filler, degasser before the punching slurry, enter afterwards the multistage slagging-off;
Glue enters secondary punching slurry in C, the adding slurry;
D, go out to add behind the secondary punching slurry sizing agent and enter pressurized screen and process, add retention agent in the pressurized screen exit;
E, slurry enter the head box online and manufacture paper with pulp;
F, press dewatering;
G, drying and processing;
H, the two pressure of soft calendaring are processed;
I, batch rewind slitting, packing warehouse-in.
Among the described step B, the optional calcium carbonate of filler or talcum powder, consumption 1.1-2.8%(weight); Degasser consumption 0.011-0.013%(weight).
Among the described step B, slagging-off has three sections at least.
Need to prove that every section slagging-off is equipped with scummer.
Among the described step C, glue consumption 0.06-0.08%(weight in the slurry).
Among the described step D, sizing agent is selected alkyl ketene dimer, consumption 0.03-0.06%(weight), retention agent consumption 0.003-0.004%(weight).
In the described step e, the concentration that online is manufactured paper with pulp is 0.6-0.8%(weight), the wet end dehydrating amount is 75-80%(weight).
In the described step F, the dehydrating amount of squeezing is 8-12%(weight).
In the described step F, behind the drying and processing, the moisture of page is 4-6%(weight).
Among the described step H, the pressure of soft calendaring is 100-150 kN/ m
2, roll surface temperature is 110-160 ℃.
The tobacco lining paper of producing with this method has following beneficial effect: formation of sheet is good, Substance, thickness, moisture uniformity; Quantitative difference of banner is little, banner moisture is consistent, with guarantee in the recombination process lining paper both sides degree of tightness unanimously, foldover not; Higher pulling force is arranged, and machine direction tensile strength can reach more than the 3kN/m, and to adapt to the high speed cigarette machined of cigarette factory, the disconnected paper of avoiding the high speed pulling force to cause, cross direction tensile strength can reach more than the 2.5kN/m, easily cuts off simultaneously; There is higher smoothness in the paper front, and to guarantee the glossiness of composite aluminium foil paper, reverse side has certain smoothness, makes composite aluminium foil paper better existing outward, has certain air permeability, tightness moderate.
The specific embodiment
Below by embodiment, specify production method of the present invention.
Embodiment 1:
Press bleaching needle-point leaf pulp 15%, hardwood pulp 75%, the ratio of straw pulp 10% is separately mixed defibrination after the making beating, the control degree of beating 30
ZeroSR, weight in wet base 2.5g, add talcum powder 2.0% behind the defibrination, degasser 0.013% enters fan pump punching slurry one time, again to three sections scummer slagging-off, add the interior glue 0.08% of slurry and enter secondary fan pump punching slurry, add afterwards alkyl ketene dimer 0.04% and enter pressurized screen, go out and add retention agent 0.0035%(weight behind the pressurized screen) enter the head box online and manufacture paper with pulp, be 8-12%(weight by wet end, dehydrating amount) press section, oven dry section obtain moisture at the page of 4-6%, enter the two nips of soft calendaring, controlled pressure 150 kN/ m
2, roll surface temperature is 130 ℃ and carries out surface finish; Batch at last rewind slitting, packing warehouse-in.More than listed ratio all with respect to the paper pulp total amount.
Embodiment 2:
Press bleaching needle-point leaf pulp 30%, hardwood pulp 55%, the ratio of straw pulp 15% is separately mixed defibrination after the making beating, the control degree of beating 40
ZeroSR, weight in wet base 5.5g, add calcium carbonate 2.8% behind the defibrination, degasser 0.011% enters fan pump punching slurry one time, again to four sections scummer slagging-off, add the interior glue 0.06% of slurry and enter secondary fan pump punching slurry, add afterwards alkyl ketene dimer 0.06% and enter pressurized screen, go out and add retention agent 0.003%(weight behind the pressurized screen) enter the head box online and manufacture paper with pulp, be 8-12%(weight by wet end, dehydrating amount) press section, oven dry section obtain moisture at the page of 4-6%, enter the two nips of soft calendaring, controlled pressure 100 kN/ m
2, roll surface temperature is 160 ℃ and carries out surface finish; Batch at last rewind slitting, packing warehouse-in.More than listed ratio all with respect to the paper pulp total amount.
Embodiment 3:
Press bleaching needle-point leaf pulp 20%, hardwood pulp 68%, the ratio of straw pulp 12% is separately mixed defibrination after the making beating, the control degree of beating 34
ZeroSR, weight in wet base 3.5g, add calcium carbonate 1.1% behind the defibrination, degasser 0.012% enters fan pump punching slurry one time, again to four sections scummer slagging-off, add the interior glue 0.065% of slurry and enter secondary fan pump punching slurry, add afterwards alkyl ketene dimer 0.03% and enter pressurized screen, go out and add retention agent 0.004%(weight behind the pressurized screen) enter the head box online and manufacture paper with pulp, be 8-12%(weight by wet end, dehydrating amount) press section, oven dry section obtain moisture at the page of 4-6%, enter the two nips of soft calendaring, controlled pressure 130 kN/ m
2, roll surface temperature is 110 ℃ and carries out surface finish; Batch at last rewind slitting, packing warehouse-in.More than listed ratio all with respect to the paper pulp total amount.
The above is preferred embodiment of the present invention only, does not limit the present invention with this, all any modifications of doing within the spirit and principles in the present invention, is equal to and replaces and improvement etc., all should be included within protection scope of the present invention.
Claims (9)
1. the production method of a tobacco lining paper is characterized in that, comprises the steps:
A, preparation are carried out with slurry behind the defibrination, and wherein, bleaching needle-point leaf pulp is 15-30%(weight), bleached hardwood pulp is 55-75%(weight), straw pulp is 10-15%(weight), separately mix defibrination after the making beating, control degree of beating 30-40
ZeroSR, weight in wet base 2.5-5.5g;
B, slurry enter once and add filler, degasser before the punching slurry, enter afterwards the multistage slagging-off;
Glue enters secondary punching slurry in C, the adding slurry;
D, go out to add behind the secondary punching slurry sizing agent and enter pressurized screen and process, add retention agent in the pressurized screen exit;
E, slurry enter the head box online and manufacture paper with pulp;
F, press dewatering;
G, drying and processing;
H, the two pressure of soft calendaring are processed;
I, batch rewind slitting, packing warehouse-in.
2. the production method of a kind of tobacco lining paper as claimed in claim 1 is characterized in that: among the described step B, and the optional calcium carbonate of filler or talcum powder, consumption 1.1-2.8%(weight); Degasser consumption 0.011-0.013%(weight).
3. the production method of a kind of tobacco lining paper as claimed in claim 2 is characterized in that: among the described step B, slagging-off has three sections at least.
4. the production method of a kind of tobacco lining paper as claimed in claim 1 is characterized in that: among the described step C, starch interior glue consumption 0.06-0.08%(weight).
5. the production method of a kind of tobacco lining paper as claimed in claim 1, it is characterized in that: among the described step D, sizing agent is selected alkyl ketene dimer, consumption 0.03-0.06%(weight), retention agent consumption 0.003-0.004%(weight).
6. the production method of a kind of tobacco lining paper as claimed in claim 1 is characterized in that: in the described step e, the concentration that online is manufactured paper with pulp is 0.6-0.8%(weight), the wet end dehydrating amount is 75-80%(weight).
7. the production method of a kind of tobacco lining paper as claimed in claim 1, it is characterized in that: in the described step F, the dehydrating amount of squeezing is 8-12%(weight).
8. the production method of a kind of tobacco lining paper as claimed in claim 1, it is characterized in that: in the described step F, behind the drying and processing, the moisture of page is 4-6%(weight).
9. the production method of a kind of tobacco lining paper as claimed in claim 1, it is characterized in that: among the described step H, the pressure of soft calendaring is 100-150 kN/ m
2, roll surface temperature is 110-160 ℃.