CN106051158B - A kind of sealing drilled packing ring and its production method - Google Patents

A kind of sealing drilled packing ring and its production method Download PDF

Info

Publication number
CN106051158B
CN106051158B CN201610482405.2A CN201610482405A CN106051158B CN 106051158 B CN106051158 B CN 106051158B CN 201610482405 A CN201610482405 A CN 201610482405A CN 106051158 B CN106051158 B CN 106051158B
Authority
CN
China
Prior art keywords
low
friction coefficient
packing ring
flexible material
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610482405.2A
Other languages
Chinese (zh)
Other versions
CN106051158A (en
Inventor
黄新明
马信凯
陶海军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO AITUO SEALING TECHNOLOGY Co.,Ltd.
Original Assignee
Zhejiang Honglulan Textile Printing & Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Honglulan Textile Printing & Dyeing Co Ltd filed Critical Zhejiang Honglulan Textile Printing & Dyeing Co Ltd
Priority to CN201610482405.2A priority Critical patent/CN106051158B/en
Publication of CN106051158A publication Critical patent/CN106051158A/en
Application granted granted Critical
Publication of CN106051158B publication Critical patent/CN106051158B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of sealing drilled packing ring and its production method, belong to the sealing ring technical field made with metal.A kind of low-friction coefficient sealing drilled packing ring includes：If dried layer sheet metal and sheet low-friction coefficient flexible material, the top and the bottom of the sealing drilled packing ring are the sheet metal, multiple projecting apertures and the multiple shrinkage pools for being evenly distributed with that spurt processing is formed on one layer of sheet low-friction coefficient flexible material, the sheet metal are provided between sheet metal described in adjacent two layers.The low-friction coefficient sealing drilled packing ring coefficient of friction is smaller, can avoid occurring the problem of the frictional force caused by frock or other reasonses increases.

Description

A kind of sealing drilled packing ring and its production method
Technical field
The present invention relates to a kind of sealing drilled packing ring, belong to the sealing ring technical field made with metal.
Background technology
In the prior art, the less axle class sealing drilled packing ring of static or linear velocity is generally used for, is with single flexibility Material is constituted, and the structural strength of material is relatively low, it is impossible to resist the operating mode of elevated pressures, easily in use material by medium Blowout is worn and torn, and also have increases metal backup shoe or complexed metal litzendraht wire to improve material strength problem in filler ring surface, but Metal backup shoe is that smooth steel pool and flexible sealing material adhesion are poor, easily comes off during installation and occurs leakage when using and asks Topic, while metal backup shoe only exists surface, improves very limited to intensity, and metal knitted line similarly has that intensity is not high to ask Topic, and when somewhere frock problem occurs and causes that frictional force is excessive between contact surface, can run out bearing, or even can be to packing ring in itself Structure brings influence.
The content of the invention
The technical problem to be solved in the present invention is, in view of the shortcomings of the prior art, proposing a kind of low-friction coefficient airtight and watertight padding Ring.The present invention is that the technical scheme for solving above-mentioned technical problem proposition is：A kind of low-friction coefficient sealing drilled packing ring includes：It is some Layer sheet metal and sheet low-friction coefficient flexible material, the top and the bottom of the sealing drilled packing ring are the metal foil One layer of sheet low-friction coefficient flexible material, the metal foil are provided between piece, sheet metal described in adjacent two layers Multiple projecting apertures and multiple shrinkage pools that spurt processing is formed are evenly distributed with piece.
The sheet low-friction coefficient flexible material is made up of following mass percent raw material：20%~40% plant is fine Dimension, 20%~30% inanimate matter, 5%~10% size, 5%~15% lubricant, 5%~15% thickener；Wherein, the string The mass percent of each component is 10%~60% castor-oil plant line, 15%~40% linen thread, 0~20% ramie and 0~20% jute；It is described The mass percent of inanimate matter each component is 35%~65% graphite, 0~35% molybdenum disulfide and 0~35% silica, and the nothing The particle diameter of machine matter is 2500 mesh；The size is trimethoxy silane, silmethylene or the ptfe emulsion of purity 99% In one kind；The lubricant is one kind in castor-based lubricating oil, mineral base oil or the poly- ɑ olefin oils of PAO；It is described to increase Thick dose be natural polymer and its derivative, including：Starch, gelatin, sodium alginate, casein, guar gum, chitosan, I One or more in uncle's natural gum, xanthans, soybean protein glue, natural rubber, lanolin, agar.
The sheet low-friction coefficient flexible material is prepared as follows according to said components：
（1）The string normal temperature is immersed in the size 24~48 hours；
（2）Take out step（1）The string of middle infiltration carries out chopping processing, and the plant fiber length after chopping is less than 5mm；
（3）Add the inanimate matter and the lubricant successively into the first Scattered Kettle, 800 revs/min of high-speed stirreds are mixed Close uniform 10~15min；
（4）String and step after into the second Scattered Kettle, addition is shredded successively（3）The mixture of middle acquisition, fully Mixing, after 800 revs/min of high-speed stirreds, then adds into the second Scattered Kettle thickener and with 50~150 revs/min of low speed Stirring is until between the two without obvious layering；
（5）By step（4）In obtained mixture be evaporated processing with 50~80 DEG C so that final mixture reclaimed water Mass percent is between 13%~25%.What the sheet metal and flexible material layer were connected is partially submerged into the projecting apertures and recessed Kong Zhong.
The foil material is one or more combination in stainless steel, galvanized sheet, copper.The shrinkage pool and projecting apertures interval Arrangement.
It is of the invention to be using the beneficial effect of above-mentioned technical proposal：This hair is by airtight and watertight padding by the common structure of multilayer ring structure Into, sheet low-friction coefficient flexible material internal layer and outer layer be provided for support rib act on and styling sheet metal Layer, makes low-friction coefficient material not deformed because of extruding or the influence of other active forces, and filled out relative to existing Ring, its coefficient of friction between filler is smaller does not influence the normal operation of pump.
Brief description of the drawings
Fig. 1 is the schematic cross-section of the present embodiment.
Embodiment
Embodiment
The low-friction coefficient sealing drilled packing ring of the present embodiment, as shown in figure 1, low by four layers of sheet metal 1 and three-layer tablet shape Coefficient of friction flexible material 2 is constituted, and the top and the bottom of sealing drilled packing ring are sheet metal 1, and adjacent double layer of metal is thin One layer of sheet low-friction coefficient flexible material 2 is provided between piece 1, it can be seen that the double layer of metal of inner side is thin The skeleton function that piece is 1,1 styling of sheet metal in outside limits whole low-friction coefficient flexible material 2 and constituted, gold It is evenly distributed with spurt multiple projecting apertures 3 for being formed of processing and multiple shrinkage pools 4 on category thin slice 1, projecting apertures 3 and shrinkage pool 4 are by metal foil Piece 1 is fitted close with low-friction coefficient flexible material 2.
Sheet metal 1 is partially submerged into projecting apertures 3 and shrinkage pool 4 with what sheet low-friction coefficient flexible material 2 was connected.
The one or more in stainless steel, galvanized sheet, copper of sheet metal 1 are made.
Shrinkage pool 4 and projecting apertures 3 are spaced.
Sheet low-friction coefficient flexible material is made up of following mass percent raw material：20%~40% string, 20% ~30% inanimate matter, 5%~10% size, 5%~15% lubricant, 5%~15% thickener；Wherein, the matter of string each component It is 10%~60% castor-oil plant line, 15%~40% linen thread, 0~20% ramie and 0~20% jute to measure percentage；Inanimate matter each component Mass percent is 35%~65% graphite, 0~35% molybdenum disulfide and 0~35% silica, and the particle diameter of inanimate matter is 2500 Mesh；Size is one kind in trimethoxy silane, silmethylene or the ptfe emulsion of purity 99%；Lubricant is castor One kind in numb based lubricating oil, mineral base oil or the poly- ɑ olefin oils of PAO；Thickener be natural polymer and its derivative, Including：Starch, gelatin, sodium alginate, casein, guar gum, chitosan, gum arabic, xanthans, soybean protein glue, day One or more in right rubber, lanolin, agar；
Sheet low-friction coefficient flexible material is prepared as follows according to said components：
（1）The string normal temperature is immersed in the size 24~48 hours；
（2）Take out step（1）The string of middle infiltration carries out chopping processing, and the plant fiber length after chopping is less than 5mm；
（3）Add inanimate matter and lubricant successively into the first Scattered Kettle, 800 revs/min of high-speed stirreds are well mixed 10 ~15min；
（4）String and step after into the second Scattered Kettle, addition is shredded successively（3）The mixture of middle acquisition, fully Mixing, after 800 revs/min of high-speed stirreds, then adds into the second Scattered Kettle thickener and with 50~150 revs/min of low speed Stirring is until between the two without obvious layering；
（5）By step（4）In obtained mixture be evaporated processing with 50~80 DEG C so that final mixture reclaimed water Mass percent is between 13%~25%.
The present invention is not limited to above-described embodiment.The technical scheme of all use equivalent substitution formation, all falling within the present invention will The protection domain asked.

Claims (1)

1. a kind of production method of low-friction coefficient sealing drilled packing ring, it is characterised in that the sealing drilled packing ring includes：Four layers of metal Thin slice and three-layer tablet shape low-friction coefficient flexible material, the top and the bottom of the sealing drilled packing ring are the metal foil One layer of sheet low-friction coefficient flexible material, the metal foil are provided between piece, sheet metal described in adjacent two layers It is evenly distributed with spurt multiple projecting apertures for being formed of processing and multiple shrinkage pools on piece, projecting apertures and shrinkage pool are by sheet metal and low friction Coefficient flexible material is fitted close；
The sheet low-friction coefficient flexible material is made up of following mass percent raw material：It is 40% string, 30% inorganic Matter, 5%~10% size, 5%~15% lubricant, 5%~15% thickener；Wherein, the quality hundred of the string each component Fraction is 60% castor-oil plant line, 15%~40% linen thread, 0~20% ramie and 0~20% jute；The quality of the inanimate matter each component Percentage is 35%~65% graphite, 0~35% molybdenum disulfide and 0~35% silica, and the particle diameter of the inanimate matter is 2500 mesh；
The size is the ptfe emulsion of purity 99%；The lubricant is mineral base oil；The thickener is soybean Protein adhesive；
The sheet low-friction coefficient flexible material is prepared as follows according to said components：
（1）The string normal temperature is immersed in the size 24~48 hours；
（2）Take out step（1）The string of middle infiltration carries out chopping processing, and the plant fiber length after chopping is less than 5mm；
（3）Add the inanimate matter and the lubricant successively into the first Scattered Kettle, 800 revs/min of high-speed stirreds, mixing is equal Even 10~15min；
（4）String and step after into the second Scattered Kettle, addition is shredded successively（3）The mixture of middle acquisition, it is fully mixed Close, after 800 revs/min of high-speed stirreds, then add thickener into the second Scattered Kettle and stirred with 50~150 revs/min of low speed Mix until between the two without obvious layering；
（5）By step（4）In obtained mixture be evaporated processing with 50~80 DEG C so that the quality of final mixture reclaimed water Percentage is between 13%~25%.
CN201610482405.2A 2014-07-30 2014-07-30 A kind of sealing drilled packing ring and its production method Active CN106051158B (en)