CN1060482A - Make the method for artistic articles of imitation ivory - Google Patents
Make the method for artistic articles of imitation ivory Download PDFInfo
- Publication number
- CN1060482A CN1060482A CN 91109299 CN91109299A CN1060482A CN 1060482 A CN1060482 A CN 1060482A CN 91109299 CN91109299 CN 91109299 CN 91109299 A CN91109299 A CN 91109299A CN 1060482 A CN1060482 A CN 1060482A
- Authority
- CN
- China
- Prior art keywords
- add
- talcum powder
- resin
- unsaturated polyester
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is the imitative ivories of a kind of manufacturing, the method of artistic articles of imitation ivory particularly, adopt unsaturated polyester resin, add solidifying agent and promotor, curing molding in pattern, demoulding finishing again, its inventive point is, cast and/or brush raw-material on pattern and mainly consist of: unsaturated polyester resin, talcum powder, its ratio is 1: (0.5～2.0); The raw-material set-up procedure of cast and/or brushing usefulness is: the surface tension modifier that 1) adds 1～5% weight resin in unsaturated polyester resin continuously or intermittently; 2) discoloring agent of adding 1～5% weight resin; 3) add talcum powder with above-mentioned ratio, the emulation degree height of the imitative ivories that present method produces, not only can imitate the ivory true qualities, and can imitate out effect after the ivory decolouring, method is also easier, the percentage of A-class goods height in the making processes, to resin raw material require low, be particularly suitable for making the smallclothes artistic articles of imitation ivory, and the price of goods is low.
Description
The present invention relates to a kind of making method of imitative ivories, particularly artistic articles of imitation ivory.The category that belongs to the Handicraft decorative technology.
CN1046743 and CN1032946A disclose a kind of composite for luminous sculptures and manufacture method thereof, unsaturated polyester resin and filler talcum powder (5～15%) have wherein been used, for reaching the effect of imitative ivory and imitative jade, (main in the effect aspect the density) also imbeds ironcasting in goods, the main drawback of this technology is that the imitative ivory effect of goods is bad, the percentage of A-class goods is low, and cost is also higher, especially is not suitable for making the artwork of smallclothes.
The objective of the invention is to overcome the deficiencies in the prior art, and the method for the imitative ivories of a kind of better production is provided.
Ivories is imitated in a kind of manufacturing, the method of artistic articles of imitation ivory particularly, adopt unsaturated polyester resin, add solidifying agent and promotor, solidifying formation in pattern, demoulding finishing again, cast and/or brush raw-material on pattern and mainly consist of: unsaturated polyester resin, talcum powder, its ratio are 1: (0.5～2.0); The raw-material set-up procedure of cast and/or brushing usefulness is:
A, in unsaturated polyester resin, add the surface tension modifier of 1～5% weight resin continuously or intermittently;
The discoloring agent of b, adding 1～5% weight resin;
C, add talcum powder with above-mentioned ratio,
The emulation degree height of the imitative ivories that this method is made, not only can imitate the ivory true qualities, and can imitate out effect after the ivory decolouring, method is also easier, percentage of A-class goods height in the making processes, to resin raw material require lowly, be particularly suitable for making the smallclothes artistic articles of imitation ivory, and the price of goods is low.
Ivories is imitated in this manufacturing, the method of artistic articles of imitation ivory particularly, adopt unsaturated polyester resin, add solidifying agent and promotor, solidifying formation in pattern, the method for the prior art of demoulding finishing again, its inventive point is, cast and/or brush raw-material on pattern and mainly consist of: unsaturated polyester resin, talcum powder, its ratio is 1: (0.5～2.0); The raw-material set-up procedure of cast and/or brushing usefulness is:
A, in unsaturated polyester resin, add the surface tension modifier of 1～5% weight resin continuously or intermittently;
The discoloring agent of b, adding 1～5% weight resin;
C, add talcum powder with above-mentioned ratio.
The technology that can use cast in the method for the present invention or brush is made, and perhaps uses two kinds of technologies simultaneously.
The surface tension modifier that adds in the insatiable hunger youngster alkyd resin can be for once adding, also can divide secondary to add, the time phase difference that secondary adds is more than half an hour, the amount that adds for the first time is 0.5～3%, the amount that adds for the second time is 0.5～2%, the employing secondary adds, can eliminate the bubble that resin is sneaked into better in whipping process, for the first time add surface tension modifier, in fact play the effect of foaming, secondary adding, in fact play the effect that issued bubble is eliminated, the goods core that obtains like this is few, and the finishing process amount descends greatly, and percentage of A-class goods rate can reach more than 99%.
In adding the talcum powder step, preceding or simultaneously or add the titanium dioxide (TiO of 1～5% weight resin in the back
2) and/or orpiment, add the effect after titanium dioxide can be imitated out the ivory decolouring merely, add orpiment or add titanium dioxide more simultaneously, can imitate out the ivory true qualities, increase the effect of emulation, the granularity of talcum powder, titanium stone flour should be more than 300 orders.
Above-mentioned unsaturated polyester resin adopts the resin of 191 or 196 or 103 models, or they are made up arbitrarily, for increasing mechanical performance of products, can in the resin of above-mentioned model, call in the resin of 10～30% 192 or 197 models or it makes up arbitrarily, these belong to the ordinary skill of unsaturated polyester resin application facet, in this necessity that does not elaborate.
Above-mentioned discoloring agent can be after adding talcum powder, add in the raw material with solidifying agent, perhaps in manufacturing processed according to the color of raw materials such as resin, in resin, added discoloring agent mixes later on 1～2% weight resin again in solidifying agent discoloring agent, to increase the effect of decolouring.
Can after adding talcum powder, add the surface tension modifier of 1～3% weight resin again,, improve yield rate to eliminate the bubble in the raw material better.
Preferred surface tension modifier is a methyl-silicone oil, and preferred discoloring agent is a potassium permanganate, adds with the solution shape.
The releasing agent that aforesaid method adopts is suds, can reduce the cost of goods like this.
Claims (13)
1, the imitative ivories of a kind of manufacturing, the method of artistic articles of imitation ivory particularly, adopt unsaturated polyester resin, add solidifying agent and promotor, solidifying formation in pattern, demoulding finishing again, it is characterized in that, cast and/or brush raw-material on pattern and mainly consist of: unsaturated polyester resin, talcum powder, its ratio is 1:(0.5～2.0); The raw-material set-up procedure of cast and/or brushing usefulness is:
A, in unsaturated polyester resin, add the surface tension modifier of 1～5% weight resin continuously or intermittently;
The discoloring agent of b, adding 1～5% weight resin;
C, add talcum powder with above-mentioned ratio.
2, method according to claim 1 is characterized in that, the surface tension modifier that adds in the insatiable hunger youngster alkyd resin is that secondary adds, and time phase difference is more than half an hour, and the amount that adds for the first time is 0.5～3%, and the amount that adds for the second time is 0.5～2%.
3, method according to claim 1 is characterized in that, in adding the talcum powder step, preceding or simultaneously or add the titanium dioxide (TiO of 1～5% weight resin in the back
2).
4, method according to claim 1 is characterized in that, in adding the talcum powder step, preceding or simultaneously or add the orpiment of 1～5% weight resin in the back.
5, method according to claim 3 is characterized in that, the granularity of talcum powder, titanium dioxide is more than 300 orders.
6, method according to claim 1 is characterized in that, above-mentioned unsaturated polyester resin adopt 191 196 or 103 or its make up arbitrarily.
7, method according to claim 1 is characterized in that, can call in the above-mentioned unsaturated polyester resin 10～30% 192 197 or its make up arbitrarily.
8, method according to claim 1 is characterized in that, above-mentioned discoloring agent can add in the raw material with solidifying agent after adding talcum powder.
9, method according to claim 1 is characterized in that, mixes the discoloring agent of 1～2% weight resin in solidifying agent.
10, method according to claim 1 is characterized in that, after adding talcum powder, adds the surface tension modifier of 1～3% weight resin again.
According to claim 1 or 2 or 10 described methods, it is characterized in that 11, above-mentioned surface tension modifier is a methyl-silicone oil.
According to claim 1 or 8 or 9 described methods, it is characterized in that 12, above-mentioned discoloring agent is a potassium permanganate, add with the solution shape.
According to the method for claim 1, it is characterized in that 13, releasing agent adopts suds.