CN106046591A - Polyvinyl chloride foamed pipe - Google Patents
Polyvinyl chloride foamed pipe Download PDFInfo
- Publication number
- CN106046591A CN106046591A CN201510974591.7A CN201510974591A CN106046591A CN 106046591 A CN106046591 A CN 106046591A CN 201510974591 A CN201510974591 A CN 201510974591A CN 106046591 A CN106046591 A CN 106046591A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- parts
- chloride pipe
- foam polyvinyl
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a polyvinyl chloride foamed pipe, comprising inner and outer solid-wall layers and a middle foamed core layer. The inner and outer solid-wall layers are prepared from, by mass, 100 parts of polyvinyl chloride A, 2 to 4 parts of a stabilizing agent, 0.2 to 1 part of an inner lubricant, 0.2 to 1 part of an outer lubricant, 1 to 2 parts of a processing aid, 2 to 6 parts of an impact modifier, 11 to 15 parts of a filling material and 0.2 to 2 parts of pigment. The middle foamed core layer is prepared from, by mass, 100 parts of polyvinyl chloride B, 2 to 4 parts of a stabilizing agent, 0.2 to 1 part of an inner lubricant, 0.2 to 1 part of an outer lubricant, 4 to 6 parts of a processing aid, 2 to 6 parts of an impact modifier, 0.5 to 0.8 part of an AC foaming agent, 5 to 15 parts of a filling material and 0.2 to 2 parts of pigment. The polyvinyl chloride foamed pipe provided by the invention is corrosion-resistant, light, heat-insulating and shock-resistant; the circumferential rigidity of the polyvinyl chloride foamed pipe is about 8 times higher than the circumferential rigidity of common UPVC pipes; and compared with solid-wall pipes, the polyvinyl chloride foamed pipe provided by the invention saves raw materials by more than 25% and reduces noise by 2 to 3 db, having a substantial noise reduction function.
Description
Technical field
The present invention relates to a kind of tubing, in particular it relates to a kind of foam polyvinyl chloride pipe
Background technology
Plastic conduit in traditional handicraft, is mainly used in using to, draining.But due to inner wall smooth, pouring
Time be easy to produce the loudest singing of the stream.
In traditional technique, often using UPVC, it is the aggregated reaction of Vinyl Chloride Monomer and the nothing made
Amorphous thermoplastic resin adds certain additive (such as stabilizer, lubricant, filler etc.) composition.Except
With outside additive, additionally use and carry out the way of blending and modifying with other resin so that it is there is obvious practicality
It is worth.These resins have CPVC, PE, ABS, EVA, MBS etc..The melt viscosity of UPVC is high, mobility
Difference, even if improving injection pressure and melt temperature, the change of mobility is the most little.
It addition, the forming temperature of resin and heat decomposition temperature very close to, it is possible to the temperature range being shaped is very
Narrow, it is a kind of material being difficult to molding.
Additionally, existing tubing the most all exist corrosion resistance more weak, thick and heavy and insulation, shockproof effect
The best, manufacturing cost is the highest, be not appropriate for modernization commercial production needs.
Summary of the invention
It is contemplated that overcome drawbacks described above, manufacture a kind of PVC PVC core layer foaming tube, in the middle of it be
Relative density is a kind of novel tube of 0.7-0.9 low ratio foamed layer, and itself is except corrosion-resistant, light weight, protects
Temperature, shockproof outside, its hoop rigidity the most at least exceeds about 8 times of common UPVC pipe, compared with existing tubing
Can at least conservation more than 25%, decrease of noise functions is the most notable, at least can reduce and make an uproar compared with existing tubing
Sound 2~3db.
The invention provides a kind of foam polyvinyl chloride pipe, it is characterised in that: sent out by interior exterior-excess parietal layer and centre
Bubble sandwich layer composition,
Wherein, interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
Middle foamed core layer is fabricated by by the component of following mass fraction:
During manufacturing, above-mentioned formula passes through extruder, interior exterior-excess parietal layer and middle foamed core layer is divided
After other extrusion molding, then co-extruding mould composite molding completes.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned polrvinyl chloride A
It is the resin of 1000-1200 selected from the degree of polymerization;The above-mentioned polrvinyl chloride B degree of polymerization is the resin of 600-750.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that aforementioned stable agent is selected
From lead salts complex stabilizer, terres rares is compound, the mixture of one or more in metal soap stabilizer.
Lead salts is selected from lead sulfate tribasic, dibasic lead phosphite, dibasic lead stearate, stearic acid
Lead, 2 ethyl acetic acid lead, lead salicylate, tribasic lead stearate, Dythal, three salt
Base Malaysia lead plumbate (tribasic maleic acid lead).
Metal soap can be fatty acid (lauric acid, stearic acid, aphthenic acids etc.) metal (lead, barium,
Cadmium, zinc, calcium etc.) salt, wherein the most commonly used with stearate.As: barium stearate, Osmanthus tragranscv.Aurantiacu acid barium, castor
Fiber crops acid barium, cadmium stearate, cadmium ricinoleate, calcium stearate, calcium ricinoleate, zinc stearate, magnesium stearate.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned in-lubricant
The mixture of one or more in paraffin, stearic acid and its esters, PE, PTFE, PP.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned external lubricant
The mixture of one or more in paraffin, Tissuemat E, stearate lubrication prescription.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned processing aid
Selected from plasticizer, lubricant, heat stabilizer, impact modifier, processing aid etc..It is preferably acrylate
Class.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned impact modified
Agent be selected from chlorinated polyethylene, ethylene/acetic acid ethylene copolymer, one or more in ACR impact modifier
Mixture.
Additionally, the foam polyvinyl chloride pipe that the present invention provides, also have a characteristic that above-mentioned filler is selected from
Wood powder, potter's clay, calcium carbonate, graphite, magnetic powder, Muscovitum, white carbon black, silicon dioxide, titanium dioxide, Pulvis Talci,
The mixture of one or more in calcium carbonate, barium sulfate.
The effect of the present invention and effect
The foam polyvinyl chloride pipe that the present invention provides is made up of with intermediate core layer two-layer inside and outside one, and centre is phase
Being a kind of novel tube of 0.7-0.9 low ratio foamed layer to density, itself is except corrosion-resistant, light weight, insulation,
Outside shockproof, its hoop rigidity also exceeds about 8 times of common UPVC pipe, can save former compared with solid-wall pipe
Material more than 25%, decrease of noise functions is the most notable, can reduce noise 2~3db compared with solid-wall pipe.
Specifically, the foam polyvinyl chloride pipe that the present invention provides is by interior exterior-excess parietal layer and middle foamed core layer group
Becoming, the material of interior exterior-excess parietal layer, in addition to requiring good processing characteristics, possesses PVC-U again
Strength character.
Therefore, pointing out in the present invention, preferably selecting intermediate molecular weight on polyvinyl chloride resin selects, the degree of polymerization is
The resin of about 1000, such as, SG5.And core material wants the preferable low-molecular-weight of selecting liquidity, the degree of polymerization
Being the resin of about 750, such as, SG7, the resin of the type not only can be conducive to the raising of foaming quality, also
In being conducive to, exterior-excess parietal layer combines with the fine of sandwich layer.
Additionally, be to improve the processing characteristics of this product, should add a part of processing aid improves, as, third
Olefin(e) acid lipid (ACR).The addition of the type auxiliary agent not only can improve the plasticizing of PVC compound, moreover it is possible to improves
The melt strength of polyvinyl chloride resin, is unlikely to sandwich layer material and can't stand that gas pressure causes because holding in foaming process
Cell collapse, causes the effect that abscess subsides.Rationally add the consumption of ACR, foam structure can be carried out
Control.
Additionally, due to the plastic pipe impact strength that polrvinyl chloride is made is relatively low, the present invention is additionally added some and resists
Impact modifier improves its fragility and the quick sex chromosome mosaicism of breach.Preferably having, anti-impact agent has chlorinated polyethylene (CPE),
Ethylene/acetic acid ethylene copolymer (EVA), ACR impact modifier etc..
It addition, in the PVC-U plastic pipe course of processing, because the decomposition temperature of Corvic is close to it
Processing temperature, for suppression extrusion time Corvic affected and phenomenon of decomposing by processing temperature, this
Invention is additionally added a certain amount of heat stabilizer.Such as lead salts complex stabilizer, terres rares complex stabilizer etc..
Facts have proved along with lead salts complex stabilizer adds the increase the most substantially reduction AC foaming agent decomposition temperature of number
The effect of degree.
It addition, during manufacturing, in order to reduce the friction between polymer and equipment, paraffin can be added,
Tissuemat E is adjusted.Meanwhile, in order to reduce the friction of molecular resin interchain, improve inside resin
Flowing, stearate lubrication prescription also should add in right amount.
It addition, in the present invention preferably inserts be mesh number about 800 light active calcium carbonate, should
Inserts can promote foaming, improves gas forming amount and cell density, useful to the stability of regulation foaming structure.
Addition controls between 10~20 parts, becomes big beyond this scope sandwich layer abscess, and pipe ring stiffness also can reduce.
Utilizing the product that above-mentioned formula obtains, lightweight, low cost, corrosion-resistant, insulation, shockproof, hoop is firm
Property strong, also there is outstanding noise reduction characteristics, it is believed that this product can need heat insulation liquid pipeline in draining, conveying
In be widely used.Along with China's degree of progress speed to security housing, drainage pipeline usage amount is year by year
It is incremented by, the kind that in various plastic conduit, consumption figure is maximum will be become.
Specific embodiment
Embodiment one, foam polyvinyl chloride pipe 1#
Interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
PVC-SG5 type | 100 |
Lead sulfate tribasic | 2 |
Paraffin | 0.2 |
Paraffin | 0.2 |
ACR-201 | 1 |
CPE130A | 2 |
800 mesh calcium carbonate | 15 |
Titanium dioxide | 0.1 |
Ultramarine | 0.1 |
Middle foamed core layer is fabricated by by the component of following mass fraction:
Embodiment two, foam polyvinyl chloride pipe 2#
Interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
PVC-SG5 type | 100 |
Barium stearate | 2 |
Paraffin | 1 |
Stearic acid 1801 | 1 |
ACR-901 | 2 |
EVA | 6 |
Carbon black | 15 |
Titanium dioxide | 0.3 |
Ultramarine | 0.3 |
Middle foamed core layer is fabricated by by the component of following mass fraction:
PVC-SG7 type | 100 |
CZ-108 | 3 |
Paraffin | 0.2 |
Stearic acid 1801 | 0.2 |
ACR-401 | 4 |
CPE130A | 6 |
AC-1500 | 0.8 |
Carbon black | 15 |
Titanium dioxide | 0.2 |
Ultramarine | 0.2 |
Embodiment three, foam polyvinyl chloride pipe 3#
Interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
PVC-SG5 type | 100 |
CZ-108 | 3 |
Stearic acid 1500 | 1 |
Tissuemat E | 0.7 |
ACR-201 | 2 |
EVA | 4 |
White carbon | 7 |
White carbon black | 1 |
Middle foamed core layer is fabricated by by the component of following mass fraction:
PVC-SG7 type | 100 |
CZ-108 | 4 |
Tissuemat E | 0.5 |
Stearic acid 1500 | 0.5 |
ACR-201 | 5 |
CPE130A | 2.5 |
AC-1500 | 0.6 |
White carbon | 10 |
White carbon black | 0.2 |
Embodiment four, foam polyvinyl chloride pipe 4#
Interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
Middle foamed core layer is fabricated by by the component of following mass fraction:
PVC-SG7 type | 100 |
Lead sulfate tribasic/Osmanthus tragranscv.Aurantiacu acid barium (50/50) | 4 |
Paraffin | 0.7 |
Tissuemat E | 0.7 |
ACR-II | 4 |
MBS | 6 |
AC foaming agent | 0.7 |
800 mesh calcium carbonate | 10 |
Titanium dioxide | 2 |
Iron oxide red | 0.2 |
Embodiment five, foam polyvinyl chloride pipe 5#
Interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
PVC-SG5 type | 100 |
WP01 | 3 |
Paraffin | 0.2~1 |
Tissuemat E | 0.2~1 |
ACR-301 | 1~2 |
CPE140B | 2~6 |
800 mesh calcium carbonate | 10 |
Titanium dioxide | 2 |
Phthalocyanine blue | 0.1 |
Middle foamed core layer is fabricated by by the component of following mass fraction:
PVC-SG7 type | 100 |
WP01 | 3 |
Tissuemat E | 0.4 |
Stearic acid 1500 | 0.4 |
ACR-901 | 5 |
CPE140B | 2 |
AC-1500 | 0.5 |
800 mesh calcium carbonate | 10 |
Titanium dioxide | 0.2 |
Phthalocyanine blue | 0.1 |
Claims (8)
1. a foam polyvinyl chloride pipe, it is characterised in that: it is made up of interior exterior-excess parietal layer and middle foamed core layer,
Wherein, described interior exterior-excess parietal layer is fabricated by by the component of following mass fraction:
Described middle foamed core layer is fabricated by by the component of following mass fraction:
2. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Described polrvinyl chloride A is the resin of 1000-1200 selected from the degree of polymerization;
The described polrvinyl chloride B degree of polymerization is the resin of 600-750.
3. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Described stabilizer is selected from lead salts complex stabilizer, terres rares is compound, one in metal soap stabilizer or
Several mixture.
4. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Mixing of one or more in paraffin, stearic acid and its esters, PE, PTFE, PP of described in-lubricant
Compound.
5. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
The described external lubricant mixture of one or more in paraffin, Tissuemat E, stearate lubrication prescription.
6. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Described processing aid is acrylics.
7. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Described impact modifying agent is selected from chlorinated polyethylene, and ethylene/acetic acid ethylene copolymer, in ACR impact modifier
The mixture of one or more.
8. a kind of foam polyvinyl chloride pipe as claimed in claim 1, it is characterised in that:
Described filler is selected from wood powder, potter's clay, calcium carbonate, graphite, magnetic powder, Muscovitum, white carbon black, silicon dioxide, titanium
The mixture of one or more in white lead, Pulvis Talci, calcium carbonate, barium sulfate.