CN106042118A - 一种增强增韧柳编用柳条溶胶‑凝胶表面处理剂及其制备方法 - Google Patents
一种增强增韧柳编用柳条溶胶‑凝胶表面处理剂及其制备方法 Download PDFInfo
- Publication number
- CN106042118A CN106042118A CN201610550851.2A CN201610550851A CN106042118A CN 106042118 A CN106042118 A CN 106042118A CN 201610550851 A CN201610550851 A CN 201610550851A CN 106042118 A CN106042118 A CN 106042118A
- Authority
- CN
- China
- Prior art keywords
- wicker
- sol
- parts
- gel surface
- treating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种增强增韧柳编用柳条溶胶‑凝胶表面处理剂,其是由下述重量份的原料制得:甘草1‑2,陈皮1‑2,苦参0.5‑1,皂角0.5‑1,无患子0.5‑1,正硅酸乙酯3‑5,纳米硼纤维0.1‑0.15,十八烷基三乙氧基硅烷0.1‑0.15,柠檬酸0.5‑1,无水乙醇10‑15,聚乙二醇2‑4,松油醇0.5‑1,果胶0.3‑0.5,水80‑100。本发明的柳条表面处理剂能起到优良的增强、增韧效果,有效改善柳编工艺品的力学性能和可塑性,增强产品的色泽,无菌无毒、不霉腐,效用持续时间长、耐储藏,而且绿色环保。
Description
技术领域
本发明涉及工艺品处理剂领域,尤其涉及一种增强增韧柳编用柳条溶胶-凝胶表面处理剂及其制备方法。
背景技术
柳条柔软易弯、粗细匀称、色泽高雅,通过新颖的设计,可以编织成各种朴实自然、造型美观、轻便耐用的实用工艺品。柳编是中国民间传统手工艺品之一,在古代人们只是作为普通的日常实用品。近年来,柳编工艺不断发展并且柳编工艺品开始出口,产业有了较大发展。随着柳编工艺品技术附加值和艺术附加值的升高,升值空间巨大。
由于柳编的原料柳条属于植物纤维类材料,其力学性能尤其是强度、韧性不够,造成使用性能不佳、使用寿命缩短等问题,因此,柳条在使用前需要进行处理,目前多使用浸泡处理。专利201410287551.0公开了一种含花椒叶的藤条用改性浸泡液,其有效成分经过长时间浸泡渗透入纤维质后,能够有效的软化材质,达到软化、增韧的功效。然而此方法效用时间有限,无法长时间维持材料的良好力学性能和耐用性,为需要对其改进。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种性能优异、效果持久的增强增韧柳编用柳条溶胶-凝胶表面处理剂及其制备方法。
本发明是通过以下技术方案实现的:
一种增强增韧柳编用柳条溶胶-凝胶表面处理剂,其是由下述重量份的原料制得:
甘草1-2,陈皮1-2,苦参0.5-1,皂角0.5-1,无患子0.5-1,正硅酸乙酯3-5,纳米硼纤维0.1-0.15,十八烷基三乙氧基硅烷0.1-0.15,柠檬酸0.5-1,无水乙醇10-15,聚乙二醇2-4,松油醇0.5-1,果胶0.3-0.5,水80-100。
一种增强增韧柳编用柳条溶胶-凝胶表面处理剂的制备方法,包括以下步骤:
(1)按重量称取原料,先将正硅酸乙酯和柠檬酸加入无水乙醇中常温搅拌均匀,然后加入纳米硼纤维和松油醇继续搅拌分散均匀,最后缓慢滴加十八烷基三乙氧基硅烷并继续搅拌0.5-1h,然后静置1-2h,得复合溶胶;
(2)将甘草、陈皮、苦参、皂角、无患子混合均匀后加入水中80-90℃煎煮1-2h,冷却后过滤,得提取液;
(3)将(1)中的复合溶胶缓慢加入(2)中的提取液中并搅拌0.5-1h,然后加入其余原料混合搅拌均匀,即得增强增韧柳编用柳条溶胶-凝胶表面处理剂。
本发明的优点是:
本发明通过水提充分提取中药有效成分,既能起到杀菌防腐的功效,又有利于改善表面处理剂的渗透性能以及与柳条的结合性能;同时利用正硅酸乙酯、十八烷基三乙氧基硅烷和纳米硼纤维通过溶胶-凝胶法得到的溶胶相复合,起到优良的防水、增强效果,改善柳条的力学性能和耐久性;同时,通过其余原料的复配,使得到的柳条表面处理剂能起到优良的增强、增韧效果,有效改善柳编工艺品的力学性能和可塑性,增强产品的色泽,无菌无毒、不霉腐,效用持续时间长、耐储藏,而且绿色环保。
具体实施方式
一种增强增韧柳编用柳条溶胶-凝胶表面处理剂,由下列重量(kg)的组分原料制备而成:
甘草1,陈皮1,苦参0.5,皂角0.5,无患子0.5,正硅酸乙酯3,纳米硼纤维0.1,十八烷基三乙氧基硅烷0.1,柠檬酸0.5,无水乙醇10,聚乙二醇2,松油醇0.5,果胶0.3,水80。
一种增强增韧柳编用柳条溶胶-凝胶表面处理剂的制备方法,包括以下步骤:
(1)按重量称取原料,先将正硅酸乙酯和柠檬酸加入无水乙醇中常温搅拌均匀,然后加入纳米硼纤维和松油醇继续搅拌分散均匀,最后缓慢滴加十八烷基三乙氧基硅烷并继续搅拌0.5h,然后静置1h,得复合溶胶;
(2)将甘草、陈皮、苦参、皂角、无患子混合均匀后加入水中80℃煎煮1h,冷却后过滤,得提取液;
(3)将(1)中的复合溶胶缓慢加入(2)中的提取液中并搅拌0.5h,然后加入其余原料混合搅拌均匀,即得增强增韧柳编用柳条溶胶-凝胶表面处理剂。
经过上述制得的处理剂处理过的柳条较同批次未处理柳条的抗压强度平均提高36%,抗弯强度平均提高32%,编织成的产品承重力平均提高47%。
Claims (2)
1.一种增强增韧柳编用柳条溶胶-凝胶表面处理剂,其特征在于,其是由下述重量份的原料制得:
甘草1-2,陈皮1-2,苦参0.5-1,皂角0.5-1,无患子0.5-1,正硅酸乙酯3-5,纳米硼纤维0.1-0.15,十八烷基三乙氧基硅烷0.1-0.15,柠檬酸0.5-1,无水乙醇10-15,聚乙二醇2-4,松油醇0.5-1,果胶0.3-0.5,水80-100。
2.根据权利要求1所述的一种增强增韧柳编用柳条溶胶-凝胶表面处理剂的制备方法,其特征在于,包括以下步骤:
(1)按重量称取原料,先将正硅酸乙酯和柠檬酸加入无水乙醇中常温搅拌均匀,然后加入纳米硼纤维和松油醇继续搅拌分散均匀,最后缓慢滴加十八烷基三乙氧基硅烷并继续搅拌0.5-1h,然后静置1-2h,得复合溶胶;
(2)将甘草、陈皮、苦参、皂角、无患子混合均匀后加入水中80-90℃煎煮1-2h,冷却后过滤,得提取液;
(3)将(1)中的复合溶胶缓慢加入(2)中的提取液中并搅拌0.5-1h,然后加入其余原料混合搅拌均匀,即得增强增韧柳编用柳条溶胶-凝胶表面处理剂。