CN106012529A - PLA fiber-silk interwoven fabric - Google Patents
PLA fiber-silk interwoven fabric Download PDFInfo
- Publication number
- CN106012529A CN106012529A CN201610361403.8A CN201610361403A CN106012529A CN 106012529 A CN106012529 A CN 106012529A CN 201610361403 A CN201610361403 A CN 201610361403A CN 106012529 A CN106012529 A CN 106012529A
- Authority
- CN
- China
- Prior art keywords
- silk
- corn fiber
- fabric
- pretreatment
- silk interlaced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PLA (Polylactic Acid) fiber-silk interwoven fabric, which is prepared by the following steps: (1) pretreatment: 83dtexPLA/88dtex PLA fiber-silk interwoven fabric is selected, put into a pretreatment solution, completely immersed, and maintained at 30-40 DEG C for 30-40 min, wherein the pretreatment solution is composed of 1% of trehalose, 0.05% of water-soluble chitosan and the balance of pure water; (2) compound enzyme treatment: the PLA fiber-silk interwoven fabric after pretreatment is immersed in a compound enzyme, wherein the process conditions of the enzyme treatment are as follows: 1 U/mL Bromelain, 6 U/mL phytase, 20-25 U/mL catechol oxidase, pH 7, temperature of 38 DEG C, time of 20-30 min, and a bath ratio of 1: 10; and (3) washing after-treatment: the PLA fiber-silk interwoven fabric after the enzyme treatment of step (2) is subjected to soaping treatment at 60-80 DEG C for 15-25 min at the bath ratio of 1:5.
Description
Technical field
The present invention relates to a kind of silk interlaced fabric of corn fiber and preparation technology thereof, belong to field of textile.
Background technology
Acid fiber by polylactic (polylactic acid, be called for short PLA) is by the starch-containing material such as Semen Maydis, Semen Tritici aestivi, the fermented lactic acid that is converted into, then the fiber that aggregated, spinning is made, also referred to as acid fiber by polylactic, is commonly called as corn fiber.It has biodegradation character, and catabolite is carbon dioxide and water, thus be a kind of can the novel environment-friendlyfiber fiber of Natural Circulation completely.Owing to corn fiber has comfortable skin sense of touch and feel, drapability is good, good thermostability and anti-ultraviolet function, and wearability is good.Development corn fiber through in recent years has been applied to multiple fields such as ribbon, clothing, home textile, is received by increasing people and likes.
PLA fibrous material compares with polyster fibre, has good clothing processability, and its general characteristic parameter is as follows: fiber number 1. 5 dtex/38 mm, intensity 30~35 cN/tex, percentage elongation 50%~60%, regain 0. 4%~0. 6%, density 1. 25 g/cm3, fusing point 170 DEG C.
The silk interlaced fabric of PLA is suitable for making necktie, but much bigger than real silk of PLA temperature influence, when 120 DEG C, PLA shrinkage factor has reached 10 %, and real silk is only less than 3 %, PLA and silk interlaced at one piece, it is wrinkling that shrinkage factors different in iron process will result in cloth cover, causes the gross distortion of finished product necktie, and prior art is processed by preshrunk and solves this problem.
It is desirable to provide a kind of silk interlaced fabric of novel corn fiber and preparation technology thereof, make the silk interlaced fabric of corn fiber modified need not preshrunk process, directly just become heat-resisting being difficult to shrink, the hygroscopicity additionally allowing corn fiber is greatly improved, there is pearlescent gloss, almost the same with real silk, substantially increase the class of product, the wrinkle resistance of silk tie, drapability can be improved again;The present invention passes through the lot of experiment validation the most optimized parameter of technique, and bromelain, phytase are the most also used in combination, and catechol-oxydase fabric silk interlaced to corn fiber processes, and such technique have not been reported.
Summary of the invention
The technical problem existed based on background technology, the shortcoming that the present invention is directed to current corn fiber, provide a kind of silk interlaced fabric of novel corn fiber and preparation technology thereof so that the silk interlaced fabric of corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks, the hygroscopicity additionally allowing corn fiber is greatly improved, there is pearlescent gloss, almost the same with real silk, substantially increase the class of product, the wrinkle resistance of silk tie, drapability can be improved again;The present invention passes through the lot of experiment validation the most optimized parameter of technique, and bromelain, phytase are the most also used in combination, and catechol-oxydase fabric silk interlaced to corn fiber processes, and such technique have not been reported.
Polyphenol oxidase is a kind of cupric enzyme that in nature, distributed pole is wide, can be formed the quinone of correspondence by catalysis oxidation phenol or polyphenolic substance, cause further and react with other primary amines, form more stable coalition.Polyphenol oxidase includes monophenol oxidase (tryrosinase), bis-phenol oxidase (catechol-oxydase) and laccase, during wherein catechol-oxydase is mainly distributed on plant, catechol-oxydase (catechol oxidase, EC. 1. 10. 3. 2) being the polyphenol oxidase being prevalent in plant, it is so that the main cause of plant brown stain.In plant (such as Fructus Mali pumilae, Fructus Litchi, Herba Spinaciae, Rhizoma Solani tuber osi etc.) tissue, catechol-oxydase combines with interior utricule film, native state does not has activity, but after being organized into homogenate or damage, catechol-oxydase is activated, thus shows activity.In fruit and vegerable cell tissue, the position that catechol-oxydase exists is variant because of the difference of the kind of raw material, kind and Maturity.
Technical scheme is as follows:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 30-40 DEG C to process 30-40min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 20-25 U/mL, pH 7, temperature 38 DEG C, time 20-30min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 60~80 DEG C, soap process 15~25min, bath raio 1: 5.
The invention have benefit that:
1, enzyme process reaction condition is used to relax: to carry out the compound enzyme modification of the silk interlaced fabric of corn fiber under low temperature near-neutral sulfite deinking, there is the advantage that energy consumption is low, process process safety environmental protection, look for deeply and while fastness improving dye, be truly realized green ecological environmental protection;
2, make the silk interlaced fabric of corn fiber modified need not preshrunk process, directly just become heat-resisting being difficult to shrink, the hygroscopicity additionally allowing corn fiber is greatly improved, there is pearlescent gloss, almost the same with real silk, substantially increase the class of product, the wrinkle resistance of silk tie, drapability can be improved again.
Detailed description of the invention
Embodiment
1
:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 30 DEG C to process 40min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 20 U/mL, pH 7, temperature 38 DEG C, time 30min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 60 DEG C, soap process 25min, bath raio 1: 5.
Result:
When 120 DEG C, PLA shrinkage factor is 2.8%, and real silk shrinkage factor is 3.0 %, and the silk interlaced fabric of such corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;
The hygroscopicity additionally allowing corn fiber is greatly improved 25%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
Embodiment
2
:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 40 DEG C to process 30min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 25 U/mL, pH 7, temperature 38 DEG C, time 20min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 80 DEG C, soap process 15min, bath raio 1: 5.
Result:
When 120 DEG C, PLA shrinkage factor is 3.3%, and real silk shrinkage factor is 2.5 %, and the silk interlaced fabric of such corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;
The hygroscopicity additionally allowing corn fiber is greatly improved 43%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
Embodiment
3
:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 31 DEG C to process 39min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 21 U/mL, pH 7, temperature 38 DEG C, time 29min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 61 DEG C, soap process 24min, bath raio 1: 5.
Result:
When 120 DEG C, PLA shrinkage factor is 2.9%, and real silk shrinkage factor is 2.9 %, and the silk interlaced fabric of such corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;
The hygroscopicity additionally allowing corn fiber is greatly improved 26%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
Embodiment
4
:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 38 DEG C to process 31min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 24 U/mL, pH 7, temperature 38 DEG C, time 21min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 79 DEG C, soap process 16min, bath raio 1: 5.
Result:
When 120 DEG C, PLA shrinkage factor is 3.2%, and real silk shrinkage factor is 2.6 %, and the silk interlaced fabric of such corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;
The hygroscopicity additionally allowing corn fiber is greatly improved 42%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
Embodiment 5:
A kind of silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose the silk interlaced fabric of corn fiber of 83dtexPLA/ 88dtex, put in pretreatment fluid, be totally submerged, keep 32 DEG C to process 38min;
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 22 U/mL, pH 7, temperature 38 DEG C, time 28min, bath raio 1: 10;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 70 DEG C, soap process 20min, bath raio 1: 5.
Result:
When 120 DEG C, PLA shrinkage factor is 3.0%, and real silk shrinkage factor is 2.8 %, and the silk interlaced fabric of such corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;
The hygroscopicity additionally allowing corn fiber is greatly improved 30%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
As can be seen here, the present invention uses enzyme process reaction condition to relax: carried out the compound enzymatic pretreatment of PLA/cotton blended fabric under low temperature near-neutral sulfite deinking, there is the advantage that energy consumption is low, process process safety environmental protection, look for deeply and while fastness improving dye, be truly realized green ecological environmental protection;The silk interlaced fabric of corn fiber is modified need not preshrunk process, the most just becomes heat-resisting being difficult to and shrinks;The hygroscopicity additionally allowing corn fiber is greatly improved 25-43%, and has pearlescent gloss, almost the same with real silk, substantially increases the class of product, can improve again the wrinkle resistance of silk tie, drapability.
The above; it is only the present invention preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; any those familiar with the art is in the technical scope that the invention discloses; according to technical scheme and inventive concept equivalent or change in addition thereof, all should contain within protection scope of the present invention.
Claims (3)
1. the silk interlaced fabric of novel corn fiber, it is prepared from by the following method:
(1) pretreatment:
Choose 83dtexPLA/
The silk interlaced fabric of corn fiber of 88dtex, puts in pretreatment fluid, is totally submerged, and keeps 30-40 DEG C to process 30-40min;
(2) compound enzyme processes:
After pretreatment, by silk interlaced for corn fiber fabric impregnation process in compound enzyme;
Wherein, enzyme treatment process condition is: bromelain L, phytase, catechol-oxydase Combined Treatment;
(3) washing post processing: the silk interlaced fabric of corn fiber after step (2) ferment treatment is carried out, at 60~80 DEG C, soap process 15~25min, bath raio 1: 5.
2. the silk interlaced fabric of corn fiber described in claim 1, it is characterised in that:
Wherein, enzyme treatment process condition is: bromelain 1U/mL, phytase 6U/mL, catechol-oxydase 20-25 U/mL, pH 7, temperature 38 DEG C, time 20-30min, bath raio 1: 10.
3. the silk interlaced fabric of corn fiber described in claim 1, it is characterised in that:
The formula of described pretreatment fluid is: 1% trehalose, 0.05% water-soluble chitosan, and remaining is pure water.