CN106012294A - Manufacturing method of vehicle wiping towel - Google Patents
Manufacturing method of vehicle wiping towel Download PDFInfo
- Publication number
- CN106012294A CN106012294A CN201610496452.2A CN201610496452A CN106012294A CN 106012294 A CN106012294 A CN 106012294A CN 201610496452 A CN201610496452 A CN 201610496452A CN 106012294 A CN106012294 A CN 106012294A
- Authority
- CN
- China
- Prior art keywords
- manufacture method
- melt
- base fabric
- towel
- vehicle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a vehicle wiping towel, and relates to the technical field of textile production. The method includes the following steps of conducting opening, even mixing, carding, mesh overlapping and spun-lacing procedures on active carbon fiber and viscose in the weight part ratio of (5-6):1 to prepare base cloth, drying the base cloth at a temperature of 140-160 DEG C for 15-30 min, conducting cooling to the room temperature, and melt-blowing superfine fiber on the surface of the base cloth at a melt-blowing extrusion temperature of 200-250 DEG C, extrusion pressure of 2.5-3.5 MPa and a receiving distance of 15-20 cm. The problem that a vehicle wiping towel is high in cost is solved.
Description
Technical field
The present invention relates to textile production technical field, especially a kind of.
Background technology
Automobile is outdoor vehicles, thus car surface easily occurs dirty, needs often to clean surface, and the turner tool of wiping used the earliest is exactly general towel, but the wiping effect of towel is the best, is also easy to abrade car surface.Raising and the quickening of rhythm of life along with people's Living Water product, for the ease of trip, more and more people become clan owning cars, wipe garage's industry to rise the most therewith, thus emerge the most professional more and more wiping turner tool, such as instead of the vehicle scrubbing towel of towel, existing vehicle scrubbing towel has superfine fibre, chamois leather, suede nap, flock suede etc..The vehicle scrubbing towel that chamois leather, suede nap, flock suede make is very easy to dirty, and cleans and need to rub dirty place with the mixed liquor of ethanol and ammonia, until after Gan Jing, also scrubbing with clear water, cleans trouble.Use the vehicle scrubbing towel that superfine fibre makes, because superfine fibre silk can increase the layer structure of silk, thus increase specific surface area and capillary effect, make fibrous inside reflection light can adsorb the dust of own wt 7 times, granule, liquid at the finer and smoother superfine fibre of surface distributed, it has superpower cleaning capacity, but the fiber number of superfine fibre is less than 0.3 danier, actual production is more difficult, thus price is high, electrostatic phenomenon is the most more serious, need careful and skilled when post processing, the degree of depth of dyeing and fastness reduce.
Summary of the invention
It is an object of the invention to provide the manufacture method of a kind of vehicle scrubbing towel, the problem that problem vehicle scrubbing towel cost that it can solve the problem that is high.
In order to solve the problems referred to above, the technical solution used in the present invention is: the manufacture method of a kind of vehicle scrubbing towel comprises the following steps:
(1), by active carbon fibre peacekeeping viscose rayon that weight portion is 5~6:1 through shredding, mixing, combing, folded net and spun lacing operation, base fabric is made;
(2), base fabric being dried, drying temperature is 140~160 DEG C, and the time is 15~30min;
(3), be cooled to room temperature after, at scrim surfaces melt-blown micro fibre, melt-blown extrusion temperature is 200~250 DEG C, and extrusion pressure is 2.5-3.5MPa, and receiving range is 15~20cm.
In the technical scheme of the manufacture method of above-mentioned plastics vehicle scrubbing towel, more specifically technical scheme is it may also is that the specific surface area of base fabric is 600~1000m2/g。
Further, a diameter of the 4~12um of described NACF.
Further, the fineness of described viscose rayon is 3~5D.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that low cost, easily cleans, and intensity is high, and service life is long;By the spacing base fabric made of activated carbon fiber and viscose glue, and at scrim surfaces melt-blown micro fibre, forming nethike embrane at scrim surfaces, the vehicle scrubbing towel specific surface area that cooperated technique for producing prepares is big, the energy large and small molecular substance of quick adsorption and particulate matter, and easily desorption.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail:
Embodiment 1
The manufacture method of the present embodiment vehicle scrubbing towel comprises the following steps:
(1), prepare a diameter of 4~7um the viscose rayon that active carbon fibre peacekeeping fineness is 3~4D, by active carbon fibre peacekeeping viscose rayon that weight portion is 5:1 through shredding, mixing, combing, folded net and spun lacing operation, making specific surface area is 600m2The base fabric of/g;
(2), base fabric being dried, drying temperature is 140 DEG C, and the time is 30min;
(3), be cooled to room temperature after, at scrim surfaces melt-blown micro fibre, melt-blown extrusion temperature is 200 DEG C, and extrusion pressure is 2.5MPa, and receiving range is 15cm.
Embodiment 2
The manufacture method of the present embodiment vehicle scrubbing towel comprises the following steps:
(1), prepare a diameter of 6~10um the viscose rayon that active carbon fibre peacekeeping fineness is 3.5~5D, by active carbon fibre peacekeeping viscose rayon that weight portion is 5.6:1 through shredding, mixing, combing, folded net and spun lacing operation, making specific surface area is 800m2The base fabric of/g;
(2), base fabric being dried, drying temperature is 155 DEG C, and the time is 25min;
(3), be cooled to room temperature after, at scrim surfaces melt-blown micro fibre, melt-blown extrusion temperature is 230 DEG C, and extrusion pressure is 3MPa, and receiving range is 18cm.
Embodiment 3
The manufacture method of the present embodiment vehicle scrubbing towel comprises the following steps:
(1), prepare a diameter of 9~12um the viscose rayon that active carbon fibre peacekeeping fineness is 4~5D, by active carbon fibre peacekeeping viscose rayon that weight portion is 6:1 through shredding, mixing, combing, folded net and spun lacing operation, making specific surface area is 1000m2The base fabric of/g;
(2), base fabric being dried, drying temperature is 160 DEG C, and the time is 15min;
(3), be cooled to room temperature after, at scrim surfaces melt-blown micro fibre, melt-blown extrusion temperature is 250 DEG C, and extrusion pressure is 3.5MPa, and receiving range is 20cm.
Claims (4)
1. the manufacture method of a vehicle scrubbing towel, it is characterised in that comprise the following steps:
(1), by active carbon fibre peacekeeping viscose rayon that weight portion is 5~6:1 through shredding, mixing, combing, folded net and spun lacing operation, base fabric is made;
(2), base fabric being dried, drying temperature is 140~160 DEG C, and the time is 15~30min;
(3), be cooled to room temperature after, at scrim surfaces melt-blown micro fibre, melt-blown extrusion temperature is 200~250 DEG C, and extrusion pressure is 2.5-3.5MPa, and receiving range is 15~20cm.
The manufacture method of vehicle scrubbing towel the most according to claim 1, it is characterised in that: the specific surface area of base fabric is 600~1000m2/g。
The manufacture method of vehicle scrubbing towel the most according to claim 2, it is characterised in that: a diameter of the 4 of described NACF~12um.
4. according to the manufacture method of vehicle scrubbing towel described in any one of claims 1 to 3, it is characterised in that:
The fineness of described viscose rayon is 3~5D.