CN106011887A - Steel surface oil and rust removing agent and preparation method thereof - Google Patents
Steel surface oil and rust removing agent and preparation method thereof Download PDFInfo
- Publication number
- CN106011887A CN106011887A CN201610496381.6A CN201610496381A CN106011887A CN 106011887 A CN106011887 A CN 106011887A CN 201610496381 A CN201610496381 A CN 201610496381A CN 106011887 A CN106011887 A CN 106011887A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel surface
- surface oil
- rust
- removing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a steel surface oil and rust removing agent and a preparation method thereof. The steel surface oil and rust removing agent is prepared by the following raw materials in parts by weight: 11-14 parts of sodium tripolyphosphate, 6-12 parts of methylene metformin, 4-7 parts of ethylene diamine tetraacetic acid, 10-14 parts of sodium alginate, 6-9 parts of konjac glucomannan, 8-12 parts of acetic acid, 5-8 parts of copper sulfate, 1-6 parts of petroleum barium sulfonate, 6-9 parts of methyl nonyl copper, 8-12 parts of sulfurized isobutylene, 3-6 parts of zinc dialkyl dithiophosphate, 4-7 parts of lupeol palitate, and 30-35 parts of de-ionized water. The prepared steel surface oil and rust removing agent is reasonable in formula, excellent in rust removing effect and high in rust removing efficiency, and can quickly remove oil stains and rust marks on metal surfaces without generating the steel corrosion phenomenon; all the components in the rust removing liquid are environment-friendly and non-toxic; and the preparation method is simple and low in cost.
Description
Technical field
The present invention relates to a kind of steel surface oil-removing rust-removing agent and preparation method thereof.
Background technology
Iron and steel is to use most metals in human history, grows with each passing day the demand of iron and steel especially into the mankind after industrialization.Now, the storage level of verifying of iron and steel is very limited, and the yield of the mankind remains high, and this conflict can not get alleviating, and largely will restrict the further development of the mankind.And the iron and steel caused because of corrosion every year loses the most surprising, cause the waste of ample resources.Iron and steel, during production process or finished product use, runs into that there was dampness in the air and during the rainy day, and easily oxidation and rusting affects product appearance quality.And preventing iron and steel simplest method of getting rusty is to make iron and steel and water, air exclusion, often keep being dried and clean of steel surface.The measure being usually taken is: is coated with mineral oils and fats on the surface of steel product, paints or cover enamel, plastics etc..Can also be coated with, at steel surface, the metal that last layer is difficult to be corroded by methods such as plating, hot dip, spraying platings.If conventional galvanized iron sheet is exactly at one layer of zinc of steel-sheet plated surface, the tinplate making canned food is exactly at steel-sheet plated surface last layer stannum.The steel ring of bicycle is exactly the chromium corrosion-resistant, wear-resisting with electric plating method plating last layer and nickel.But said method only just uses when a small amount of ferrous materials, cannot use in a large number during stock's steel substantial amounts of to steel production enterprise and marketer;Using antirust oil and steel surface plating, need to consume substantial amounts of oil plant raw material and anti-rust metal, energy resource consumption aggravates, and increases cost.And along with the progress of technology, increasing employing antirust agent prevents iron and steel from getting rusty, antirust agent is the most antirust depends on the protection to metal surface, thus stops or postponing moisture, oxygen and the invasion of other impurity.Antirust agent selects high-quality anticorrosion raw material and multiple auxiliary agent to process, and surface can be protected not encroached on by moisture, chemicals, air and other corrosives.Can be widely used for iron and steel, rustless steel, steel alloy article assembly and the rust prevention during manufacture of material in many industries.The material such as steel, ferrum can be effectively protected, prevent from getting rusty.According to the difference of rust-proof life requirement, and water is used in mixed way by a definite proportion, and the antirust time limit can reach several days to several months, if having certain damp-proof outer package condition or leaving dry environment condition in, antirust time was up to more than 1 year.And having easy and simple to handle, technique is simple, postorder easy cleaning, processes postorder without features such as impacts, low price simultaneously, and rust-proof effect is preferable, is increasingly favored by numerous clients.In order to adapt to the market competition needs of fast development, improving the quality of rust remover, reduce energy consumption cost, technical process simplification, functionalization etc. become current development trend, therefore develop the oil-removing rust-removing agent with multifunction.But mostly oil-removing rust-removing agent the most on the market is to use strong basicity hot solution, and (energy consumption is high, pollute weight, processed part is caused secondary oil to pollute by the oil slick on working solution surface), or with strong acid, or with organic solvent inflammable, explosive, virulent, produce the toxic deep-etching heavily contaminated of the gas, liquid, solid three wastes.To this end, we set about from formula and the technique of product, it is provided that a kind of steel surface oil-removing rust-removing agent and preparation method thereof.
Summary of the invention
It is an object of the invention to provide a kind of steel surface oil-removing rust-removing agent and preparation method thereof.
To achieve these goals, the invention provides a kind of steel surface oil-removing rust-removing agent, raw material includes following component by weight: prepared by the raw material of following weight portion: sodium tripolyphosphate 11-14 part, methylene biguanide 6-12 part, disodiumedetate 4-7 part, sodium alginate 10-14 part, Konjac glucomannan 6-9 part, acetic acid 8-12 part, copper sulfate 5-8 part, barium mahogany sulfonate 1-6 part, methyl nonyl ketone 6-9 part, sulfide isobutene 8-12 part, zinc dialkyl dithiophosphate 3-6 part, lupeol cetylate 4-7 part, deionized water 30-35 part.
It is possibly together with decanedioic acid 20-24 part.
It is possibly together with octadecyl trimethyl ammonium chloride 3-6 part.
It is possibly together with sodium xylene sulfonate 2-6 part.
The preparation method of a kind of steel surface oil-removing rust-removing agent, comprises the following steps: weighs each component, then mix and blend according to above-mentioned weight fraction ratio, stirs and make each component be completely dissolved, obtains described steel surface oil-removing rust-removing agent.
The method have the advantages that the steel surface degreasing and rust removal agent prescription that the present invention prepares is reasonable, eliminate rust effective, efficiency of derusting is high, can quickly remove metal surface greasy dirt, rusty stain, steel are occurred without corrosion phenomenon, and each component environmental protection in this antirust solution, nontoxic, and preparation method is simple, low cost.
Detailed description of the invention
Embodiment
1
The steel surface oil-removing rust-removing agent of the present embodiment, is prepared by the component of following weight portion: sodium tripolyphosphate 11 parts, methylene biguanide 6 parts, disodiumedetate 4 parts, sodium alginate 10 parts, Konjac glucomannan 6 parts, acetic acid 8 parts, 5 parts of copper sulfate, barium mahogany sulfonate 1 part, methyl nonyl ketone 6 parts, sulfide isobutene 8 parts, zinc dialkyl dithiophosphate 3 parts, lupeol cetylate 4 parts, deionized water 30 parts.
Weigh each component, then mix and blend according to above-mentioned weight fraction ratio, stir and make each component be completely dissolved, obtain described steel surface oil-removing rust-removing agent.
The steel surface oil-removing rust-removing agent of the present embodiment can use directly immersion, the method for spraying that surface of the work is carried out processing of rust removing.
Embodiment
2
The steel surface oil-removing rust-removing agent of the present embodiment, is prepared by the component of following weight portion: sodium tripolyphosphate 14 parts, methylene biguanide 12 parts, disodiumedetate 7 parts, sodium alginate 14 parts, Konjac glucomannan 9 parts, acetic acid 12 parts, 8 parts of copper sulfate, barium mahogany sulfonate 6 parts, methyl nonyl ketone 9 parts, sulfide isobutene 12 parts, zinc dialkyl dithiophosphate 6 parts, lupeol cetylate 7 parts, deionized water 35 parts, decanedioic acid 24 parts.
Weigh each component, then mix and blend according to above-mentioned weight fraction ratio, stir and make each component be completely dissolved, obtain described steel surface oil-removing rust-removing agent.
The steel surface oil-removing rust-removing agent of the present embodiment can use directly immersion, the method for spraying that surface of the work is carried out processing of rust removing.
Embodiment
3
The steel surface oil-removing rust-removing agent of the present embodiment, is prepared by the component of following weight portion: sodium tripolyphosphate 11 parts, methylene biguanide 6 parts, disodiumedetate 4 parts, sodium alginate 10 parts, Konjac glucomannan 6 parts, acetic acid 8 parts, 5 parts of copper sulfate, barium mahogany sulfonate 1 part, methyl nonyl ketone 6 parts, sulfide isobutene 8 parts, zinc dialkyl dithiophosphate 3 parts, lupeol cetylate 4 parts, deionized water 30 parts, decanedioic acid 20 parts, octadecyl trimethyl ammonium chloride 3 parts.
Weigh each component, then mix and blend according to above-mentioned weight fraction ratio, stir and make each component be completely dissolved, obtain described steel surface oil-removing rust-removing agent.
The steel surface oil-removing rust-removing agent of the present embodiment can use directly immersion, the method for spraying that surface of the work is carried out processing of rust removing.
Embodiment
4
The steel surface oil-removing rust-removing agent of the present embodiment, is prepared by the component of following weight portion: sodium tripolyphosphate 14 parts, methylene biguanide 12 parts, disodiumedetate 7 parts, sodium alginate 14 parts, Konjac glucomannan 9 parts, acetic acid 12 parts, 8 parts of copper sulfate, barium mahogany sulfonate 6 parts, methyl nonyl ketone 9 parts, sulfide isobutene 12 parts, zinc dialkyl dithiophosphate 6 parts, lupeol cetylate 7 parts, deionized water 35 parts, decanedioic acid 24 parts, octadecyl trimethyl ammonium chloride 6 parts, sodium xylene sulfonate 6 parts.
Weigh each component, then mix and blend according to above-mentioned weight fraction ratio, stir and make each component be completely dissolved, obtain described steel surface oil-removing rust-removing agent.
The steel surface oil-removing rust-removing agent of the present embodiment can use directly immersion, the method for spraying that surface of the work is carried out processing of rust removing.
Embodiment
5
The rust remover of above-described embodiment 1-4 gained is used for workpiece rust cleaning, and rust cleaning efficiency is high, and a few minutes can complete the metal works invariant color after the descaling process of general workpiece, and rust cleaning, without dust, without hydrogen embrittlement.
The above is only the optimal way of the present invention, it is noted that to those skilled in the art, without departing from the concept of the premise of the invention, it is also possible to make some similar deformation and improvement, within these also should be regarded as protection scope of the present invention.
Claims (5)
1. a steel surface oil-removing rust-removing agent, it is characterised in that prepared by the raw material of following weight portion: sodium tripolyphosphate 11-14 part, methylene biguanide 6-12 part, disodiumedetate 4-7 part, sodium alginate 10-14 part, Konjac glucomannan 6-9 part, acetic acid 8-12 part, copper sulfate 5-8 part, barium mahogany sulfonate 1-6 part, methyl nonyl ketone 6-9 part, sulfide isobutene 8-12 part, zinc dialkyl dithiophosphate 3-6 part, lupeol cetylate 4-7 part, deionized water 30-35 part.
2. according to the steel surface oil-removing rust-removing agent described in claim 1, it is characterised in that: it is possibly together with decanedioic acid 20-24 part.
3. according to the steel surface oil-removing rust-removing agent described in claim 2, it is characterised in that: it is possibly together with octadecyl trimethyl ammonium chloride 3-6 part.
4. according to the steel surface oil-removing rust-removing agent described in claim 3, it is characterised in that: it is possibly together with sodium xylene sulfonate 2-6 part.
5. according to the preparation method of the steel surface oil-removing rust-removing agent according to any one of claim 1-4, it is characterized in that comprising the following steps: weigh each component according to above-mentioned weight fraction ratio, then mix and blend, stirs and makes each component be completely dissolved, and obtains described steel surface oil-removing rust-removing agent.