CN106011552A - Nanometer titania reinforced aluminum magnesium alloy material for automobile electronic packaging and preparation method of nanometer titania reinforced aluminum magnesium alloy material - Google Patents
Nanometer titania reinforced aluminum magnesium alloy material for automobile electronic packaging and preparation method of nanometer titania reinforced aluminum magnesium alloy material Download PDFInfo
- Publication number
- CN106011552A CN106011552A CN201610550285.5A CN201610550285A CN106011552A CN 106011552 A CN106011552 A CN 106011552A CN 201610550285 A CN201610550285 A CN 201610550285A CN 106011552 A CN106011552 A CN 106011552A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- titanium oxide
- nano titanium
- magnesium alloy
- hydronalium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nanometer titania reinforced aluminum magnesium alloy material for automobile electronic packaging. The alloy material comprises, by weight, 5% to 6% of magnesium, 3% to 4% of titanium, 1% to 2% of nickel, 3% to 5% of silicon, 0.5% to 1% of copper, 40% to 50% of nanometer titania sol, 1% to 2% of a pore forming agent, 0.5% to 1% of absolute ethyl alcohol and the balance aluminum.
Description
Technical field
The present invention relates to electronic package material technical field, particularly relate to a kind of automotive electronics encapsulation nano titanium oxide and strengthen hydronalium and preparation method thereof.
Background technology
Automotive electronics is the general name of electronic control device for vehicle and vehicular automotive electronic device, and automotive electronics occupies vital position in automotive engineering, is exploitation new model, improves the most important technical measures of automotive performance.Owing to automotive interior exists the adverse circumstances factors such as extreme operating temperature range, strong mechanical vibration and spot be more, automobile electronics performance to be guaranteed is interference-free, must carry out the encapsulation work of product, the encapsulating material chosen is to realize the technology trends such as industry lower cost, higher function, higher reliability.
Preferably electronic package material thermal coefficient of expansion to be possessed is low, high heat conduction, air-tightness is good, enough strength and stiffness, it is easy to the advantage such as machine-shaping and welding and lightweight light weight, the most conventional a few class wrapper materials mainly have plastic encapsulant, ceramic packaging material, Materials for Metal Packaging and several big class of metal-base composites, wherein metal-based compound electronics encapsulating material has intensity height, the advantages such as heat conductivity is good become the focus of industry research, especially aluminium based metal material, the advantage of its lightweight is extensively favored at automotive field, the combination property improving aluminum-based packaging material is also study hotspot." vacuum heating-press sintering method prepares diamond/Al-Cu based composites ", a literary composition utilized the mode of vacuum heating-press sintering to improve the interface untoward reaction of diamond and aluminum, it is simultaneously introduced Cu powder and improves performance, this method uses micron-sized diamond powder body, although obtaining the composite of high heat conductance, but the intensity of alloy material, plasticity reduce the most to a certain extent, range is limited, nano grade inorganic material has prominent advantage in terms of improving alloy property, but the dispersibility that nanometer materials are in the alloy is the most not fully up to expectations.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of automotive electronics encapsulation nano titanium oxide strengthens hydronalium and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of automotive electronics encapsulation nano titanium oxide strengthens hydronalium, and this alloy material is made up of the raw material of following weight portion: magnesium 5-6%, titanium 3-4%, nickel 1-2%, silicon 3-5%, copper 0.5-1%, nano titanic oxide sol 40-50%, pore creating material 1-2%, dehydrated alcohol 0.5-1, surplus are aluminum.
Described nano titanic oxide sol is formulated by following methods: Dodecyl trimethyl ammonium chloride put in dehydrated alcohol, and stirring puts into nano titanium oxide, sonic oscillation dispersion 5-10h to it after being completely dissolved, to obtain final product;Wherein nano titanium oxide, dehydrated alcohol, the weight ratio of Dodecyl trimethyl ammonium chloride three are 1:5:0.1.
Described pore creating material is the one in sodium chloride, sodium carbonate, spherical carbamide.
Described a kind of automotive electronics encapsulation nano titanium oxide strengthens hydronalium preparation method and comprises the following steps:
(1) first by aluminum, magnesium, titanium, nickel, silicon, copper, pore creating material, dehydrated alcohol mixes, with 150-200 turn/rotating speed of min mixes powder 10-15min, gained mixed material obtains green compact through compacting densification, subsequently green compact are put in mould Thermocompressed sintering and forming under vacuum, sintering process is: system is warming up to 600-650 DEG C with the programming rate of 15-20 DEG C/min, pressurize when temperature reaches 550 DEG C, pressure is 60-80MPa, heat preservation sintering 20-30min, naturally cool to release after room temperature subsequently, products obtained therefrom is put in water and is dried after dissolution pore creating material, obtain Al-Mg alloy foam prefabricated component standby;
(2) the Al-Mg alloy foam prefabricated component of step (1) gained is put in mould, it is subsequently added nano titanic oxide sol, long-pending 50-60min is oozed under-0.01--0.05MPa, process recovers normal pressure after terminating, and takes out prefabricated component, dried 2-3h in 80-100 DEG C of baking oven, subsequently prefabricated component is placed again in mould, 800-850 DEG C, again sinter 20-30min under 20-30MPa pressure, release of finally lowering the temperature, i.e. obtain described encapsulation alloy material after being cooled to room temperature.
The invention have the advantage that
(1) encapsulating material of the present invention is using almag as base material, and blend the raw materials such as titanium, nickel, silicon, copper wherein, obtain the alloy material with excellent comprehensive mechanical property, this alloy material has lightweight, the advantage such as high-strength, high-elastic, has prominent application advantage in automobile component field.
(2) alloy powder is first processed into Al-Mg alloy foam prefabricated component in technique by the present invention, and nano titanium oxide oozed with the form vacuum of colloidal sol amass in alloy components, finished product is prepared again after double sintering, this technological process improves the phenomenon that nano titanium oxide is easily reunited, improve its dispersibility in the alloy, reach the effect efficiently strengthened, refining alloy tissue, improve the anticorrosive of alloy material surface, mar proof, the most this processing method also changes alloy internal structure, improve the damping of alloy material, electronic device stability after encapsulation is high, good operation can be continued, reduce the negative effect of external environment.
Detailed description of the invention
A kind of automotive electronics encapsulation nano titanium oxide strengthens hydronalium, and this alloy material is made up of the raw material of following weight portion: magnesium 5%, titanium 3%, nickel 1%, silicon 3%, copper 0.5%, nano titanic oxide sol 40%, pore creating material 1%, dehydrated alcohol 0.5, surplus are aluminum.
Described nano titanic oxide sol is formulated by following methods: Dodecyl trimethyl ammonium chloride put in dehydrated alcohol, and stirring puts into nano titanium oxide, sonic oscillation dispersion 5h to it after being completely dissolved, to obtain final product;Wherein nano titanium oxide, dehydrated alcohol, the weight ratio of Dodecyl trimethyl ammonium chloride three are 1:5:0.1.
Pore creating material is spherical carbamide.
The preparation method of this alloy material comprises the following steps:
(1) first by aluminum, magnesium, titanium, nickel, silicon, copper, pore creating material, dehydrated alcohol mixes, powder 10min is mixed with the rotating speed of 150 turns/min, gained mixed material obtains green compact through compacting densification, subsequently green compact are put in mould Thermocompressed sintering and forming under vacuum, sintering process is: system is warming up to 600 DEG C with the programming rate of 15 DEG C/min, pressurize when temperature reaches 550 DEG C, pressure is 60MPa, heat preservation sintering 20min, naturally cool to release after room temperature subsequently, products obtained therefrom is put in water and is dried after dissolution pore creating material, obtain Al-Mg alloy foam prefabricated component standby;
(2) the Al-Mg alloy foam prefabricated component of step (1) gained is put in mould, it is subsequently added nano titanic oxide sol, long-pending 60min is oozed under-0.01MPa, process recovers normal pressure after terminating, and takes out prefabricated component, dried 3h in 80 DEG C of baking ovens, subsequently prefabricated component is placed again in mould, 800 DEG C, again sinter 30min under 30MPa pressure, release of finally lowering the temperature, i.e. obtain described encapsulation alloy material after being cooled to room temperature.
Taking obtained material and prepare standard specimen, carry out performance test according to relevant criterion, test result is:
Density: 2.72g/cm3;Bending strength: 40MPa;Thermal conductivity: 168W/m.k;Thermal coefficient of expansion: 3.42 × 10-6m/k;The most solderable: to be.
Claims (4)
1. an automotive electronics encapsulation nano titanium oxide strengthens hydronalium, it is characterized in that, this alloy material is made up of the raw material of following weight portion: magnesium 5-6%, titanium 3-4%, nickel 1-2%, silicon 3-5%, copper 0.5-1%, nano titanic oxide sol 40-50%, pore creating material 1-2%, dehydrated alcohol 0.5-1, surplus are aluminum.
2. a kind of automotive electronics encapsulation nano titanium oxide as claimed in claim 1 strengthens hydronalium, it is characterized in that, described nano titanic oxide sol is formulated by following methods: Dodecyl trimethyl ammonium chloride put in dehydrated alcohol, stirring puts into nano titanium oxide after being completely dissolved to it, sonic oscillation dispersion 5-10h, to obtain final product;Wherein nano titanium oxide, dehydrated alcohol, the weight ratio of Dodecyl trimethyl ammonium chloride three are 1:5:0.1.
3. a kind of automotive electronics encapsulation nano titanium oxide as claimed in claim 1 strengthens hydronalium, it is characterised in that described pore creating material is the one in sodium chloride, sodium carbonate, spherical carbamide.
4. a kind of automotive electronics encapsulation nano titanium oxide as claimed in claim 1 strengthens hydronalium preparation method, it is characterised in that described preparation method comprises the following steps:
(1) first by aluminum, magnesium, titanium, nickel, silicon, copper, pore creating material, dehydrated alcohol mixes, with 150-200 turn/rotating speed of min mixes powder 10-15min, gained mixed material obtains green compact through compacting densification, subsequently green compact are put in mould Thermocompressed sintering and forming under vacuum, sintering process is: system is warming up to 600-650 DEG C with the programming rate of 15-20 DEG C/min, pressurize when temperature reaches 550 DEG C, pressure is 60-80MPa, heat preservation sintering 20-30min, naturally cool to release after room temperature subsequently, products obtained therefrom is put in water and is dried after dissolution pore creating material, obtain Al-Mg alloy foam prefabricated component standby;
(2) the Al-Mg alloy foam prefabricated component of step (1) gained is put in mould, it is subsequently added nano titanic oxide sol, long-pending 50-60min is oozed under-0.01--0.05MPa, process recovers normal pressure after terminating, and takes out prefabricated component, dried 2-3h in 80-100 DEG C of baking oven, subsequently prefabricated component is placed again in mould, 800-850 DEG C, again sinter 20-30min under 20-30MPa pressure, release of finally lowering the temperature, i.e. obtain described encapsulation alloy material after being cooled to room temperature.