CN106010756A - Water displacement type steel plate lubrication and rust prevention oil - Google Patents
Water displacement type steel plate lubrication and rust prevention oil Download PDFInfo
- Publication number
- CN106010756A CN106010756A CN201610414595.4A CN201610414595A CN106010756A CN 106010756 A CN106010756 A CN 106010756A CN 201610414595 A CN201610414595 A CN 201610414595A CN 106010756 A CN106010756 A CN 106010756A
- Authority
- CN
- China
- Prior art keywords
- oil
- rust prevention
- steel plate
- water displacement
- type steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water displacement type steel plate lubrication and rust prevention oil. The water displacement type steel plate lubrication and rust prevention oil is obtained by adding an antirust agent, a lubricant, a pour point reducer and an antioxidant to mineral oil, and used for sealing storage of cold-rolled steel coils and rust prevention of intermediate processes. The greatest advantage of the water displacement type steel plate lubrication and rust prevention oil is high water displacement property; by the adoption of the water displacement type steel plate lubrication and rust prevention oil, a small amount of moisture left on a leveled cold-rolled sheet can be separated from the sheet by means of an antirust additive with high adsorbability and small surface tension, so that a rust prevention effect is well realized; meanwhile, degreasing can also be achieved, degreasing rate reaches 80%, and follow-up processing can not be affected; rust prevention time is long, no oil patch residue is left, low temperature resistance is realized, environment friendliness is realized, no odor is generated, cost is reasonable, price is moderate, and extensive use can be conducted; the frequency of rust prevention maintenance can be reduced, maintenance cost can be reduced, environment friendliness and safety are realized, and three-waste emission is avoided in production and use.
Description
Technical field
The present invention relates to IPC classification C10M lubricating composition, especially water displaced type steel plate lubricating anticorrosive oil.
Background technology
Steel plate through cold rolled annealed smooth after, antirust oil need to be coated to guarantee will not get rusty in sealing transportation up for safekeeping, but,
After smooth, leveling precision has and remains on steel plate on a small quantity, if except unclean, directly coating general steel plate and prevent
Rust oil, may result in local and gets rusty, affect serviceability.
Antirust oil has the not reactivity of water substituting and corrosive deposit, plays rustless property, produces to block to corrosive environment and makees
With.Metal covering attachment rust-inhibiting additive, molecule forms adsorbed film, forms the oil reservoir structure of water proofing property above.The oil of adsorbed film
The additive molecule that membrane molecule and oil are planted is mixed to form mutually adsorbed film, and adsorption layer hinders the corrosion factor material such as water and oxygen patch
Nearly metal surface, corrosion factor is played the effect of suppression by upper strata oil film.
The solvent-borne type mantle that displacing type rust preventive oil is made up of petroleum solvent, dehydrant, antirust agent, anti-blushing agent, preservative etc.
Antirust oil, without consuming atmospheric ozone and atmospheric warming effect material, to human non-toxic's side effect, nuisanceless to environment, belong to
Environmentally friendly machine.
Water displacement antirust oil has water substituting matter, when needing antirust material surface to be the most thoroughly dried, is coated with general antirust
After oil is antirust, still it is susceptible to corrosion problem.It is coated with general antirust oil surface to be dried, and is coated with water displacement antirust oil, material list
Face has some moisture content, water displacement antirust oil moisture content can be cemented out, and oil completely attaches to material surface, and rustless property is preferable.
Water displacement antirust oil also has replacement of human sweat, and hand perspiration easily makes metal surface corrosion, water displacement antirust oil to solve.
Water displacement antirust oil and the difference of common antirust oil be, water displacement antirust oil has water substituting, water substituting to be exactly can be
Moisture on metal surface cements out, say, that even if having a small amount of moisture content on surface, in the middle of steam, or technique
Fingerprint hand perspiration etc. need not dry directly smear water displacement antirust oil.
Related art scheme discloses less, and Chinese patent application 201110099905.5 Changzhou Shuguang Chemical Factory discloses one
The preparation method of displacing type rust preventive oil, by weight percentage, with the lanoline of 25-33%, the sulphuric acid of 3-10%, 4-8%'s
Calcium hydroxide, the solvent naphtha of 3-10%, the mineral oil of 50-60% is raw material, after lanoline is taken off water, is cooled to 30-45 DEG C
In the range of, it being slowly added dropwise sulphuric acid and carry out sulfonating reaction, sulfonation temperature controls in the range of 30-50 DEG C, sulfonation 4-7h；Treat sulphur
It is to slowly warm up to 60-75 DEG C after change, is slowly added to calcium hydroxide and reacts in the range of 60-110 DEG C, be incubated 2-3
Hour；Finally add mineral oil, solvent naphtha carries out dissolving and allocates to the most uniformly, obtains required displacing type rust preventive oil.
Autobody sheet lubricating anticorrosive oil disclosed in Chinese patent application 201210540576.8 Jing Jiang Hengfeng Chemical Co., Ltd. adds
Adding agent, each raw materials by weight is: dimerization oleic acid monoester 3-15%, rust-inhibiting additive alkyl benzene calcium sulfonate 5-20%,
Film former 2-10%, antioxidant additive BHT0.5-3%, matal deactivator BTA 0.10-2%, rust-inhibiting additive cycloalkanes
Acid zinc 0-8%, rust-inhibiting additive dodecenylsuccinic acid or dodecenylsuccinic acid monoesters 0-5%, oil based on remaining.
Chinese patent application 201510490118.1 Wuxi Yanggong Machinery Manufacturing Co., Ltd discloses a kind of outside electromotor
The displacing type rust preventive oil of shell, is made up of the component of following parts by weight: barium mahogany sulfonate 5.4-6.3 part, lanoline 3.1-3.5
Part, oxidized petrolatum barium soap 2.3-2.8 part, petroleum sodium sulfonate 1.5-1.8 part, benzotriazole 0.1-0.4 part, machinery
Oil 18-25 part, kerosene 30-40 part.
Summary of the invention
It is an object of the invention to provide a kind of water displaced type steel plate lubricating anticorrosive oil, overcome the deficiencies in the prior art, improve rust cleaning
Effect.
The purpose of the present invention will be realized by techniques below measure: formula is:
Production method is:
Rust-inhibiting additive, antioxidant are added in mineral oil together with extreme pressure agent, is heated to 85 ± 5 DEG C of stir about 60 ± 5min
Confirm that solution is transparent, then in this solution, add pour-point depressant and another kind of mineral oil, then at 40 ± 5 DEG C stir about 20 ±
5min, is packaged in bucket after QC detection is qualified and seals up for safekeeping.
Especially,
Advantages of the present invention and effect: can be by adsorptivity is strong, surface tension is little rust-inhibiting additive by moisture and steel plate
Separate, reach rust-proof effect completely.Being simultaneously introduced antioxidant makes product be not easy corruption, it is ensured that the length of product
For a long time ruggedness, corrupt will not occur odor impact service life.Adding pour-point depressant is the freezing point in order to reduce product, it is ensured that
Can also normally use at low temperatures, minimum temperature can reach 40 degrees below zero simultaneously, it is ensured that the most all can make in China
With.Adding extreme pressure agent is the greasy property in order to strengthen product.This product is without while solvent naphtha, it is ensured that viscosity is relatively
Low, flash-point is higher, and volatile material is few, is the environmentally friendly product of a kind of odorless, tasteless.Take into account defat performance simultaneously,
Defat reaches 80%, does not affect follow-up processing.Antirust time is long, remains without oil mark, low temperature resistant, and cost is reasonable, valency
Lattice are moderate, can use in a large number.The number of times of antirust maintenance can be reduced, reduce maintenance cost, Environmental Safety, produce and make
Three-waste free discharge during with.
Detailed description of the invention
The principle of the invention is, mainly antirust agent, lubricant, pour-point depressant and antioxidant is joined in mineral oil
Make, for cold-rolled steel coils seal up for safekeeping and intermediate step is antirust, the great advantage of this product is to have good water substituting energy,
A small amount of moisture content of residual on cold-reduced sheet after flattened can be separated with sheet material, so make oil film be completely covered by sheet material it
On, prevent it from thoroughly not getting rusty because of moisture drying.
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1: formula is:
Production method is:
Rust-inhibiting additive, antioxidant are added in mineral oil together with extreme pressure agent, is heated to 85 ± 5 DEG C of stir about 60 ± 5min
Confirm that solution is transparent, then in this solution, add pour-point depressant and another kind of mineral oil, then at 40 ± 5 DEG C stir about 20 ±
5min, is packaged in bucket after QC detection is qualified and seals up for safekeeping.
In aforementioned, rust-inhibiting additive is sulfonate.
In the present embodiment, the water displaced type steel plate lubricating anticorrosive oil qualitative characteristics prepared is, it is allowed to have a small amount of water on steel plate
The residual of part, the requirement that steel plate is dried less than harshness, so that procedure calls reduces, save the energy, use
Effect is, to reaching in surface of steel plate a period of time to be entirely prevented from getting rusty.
The present invention is suitable for the antirust of the metal materials such as steel, steel alloy, cast steel, copper, aluminum and alloy thereof, it is adaptable to machinery adds
Rust prevention during manufacture in the metallic element course of processing of the industries such as work, automobile, electronics, iron and steel, metallurgy, aviation and in,
Short-term stock is antirust.
The present invention operating process when application is:
1, water displaced type steel plate lubricating anticorrosive oil of the present invention will be immersed after drying with the metallic element after water rinsed clean, leaching
The angle of incidence is 2-3 minute, for having the parts of aperture, gap and inner chamber it is noted that stir, to ensure that oiling is complete.
2, checking whether metallic element surface has blister, bubble, oil film attachment is the most uniformly, completely.
4, the parts that need not clean can be used spray, soak, the mode that is coated with directly carries out antirust treatment.
5, implement nature by technological requirement to drain.
6, subsequent handling is implemented by technological requirement.
Embodiments of the present invention have been described in detail above, but this is only to facilitate the example that understands and lift, is not construed as
Limit the scope of the present invention.Equally, any person of ordinary skill in the field all can be according to technical scheme
And the description of preferred embodiment, make various possible equivalent and change or replace, but all these change or replacement all should belong to
In the protection domain that this practicality invention requires.
Claims (2)
1. water displaced type steel plate lubricating anticorrosive oil, it is characterised in that formula is:
Production method is:
Rust-inhibiting additive, antioxidant are added in mineral oil together with extreme pressure agent, is heated to 85 ± 5 DEG C of stir about 60 ± 5min
Confirm that solution is transparent, then in this solution, add pour-point depressant and another kind of mineral oil, then at 40 ± 5 DEG C stir about 20 ±
5min, is packaged in bucket after QC detection is qualified and seals up for safekeeping.
2. water displaced type steel plate lubricating anticorrosive oil as claimed in claim 1, it is characterised in that formula is:
Production method is:
Rust-inhibiting additive, antioxidant are added in mineral oil together with extreme pressure agent, is heated to 85 ± 5 DEG C of stir about 60 ± 5min true
Recognize solution transparent, then in this solution, add pour-point depressant and another kind of mineral oil, then at 40 ± 5 DEG C stir about 20 ±
5min, is packaged in bucket after QC detection is qualified and seals up for safekeeping.