CN106010098B - It is coated with the film of anti-aging coating - Google Patents
It is coated with the film of anti-aging coating Download PDFInfo
- Publication number
- CN106010098B CN106010098B CN201610402818.5A CN201610402818A CN106010098B CN 106010098 B CN106010098 B CN 106010098B CN 201610402818 A CN201610402818 A CN 201610402818A CN 106010098 B CN106010098 B CN 106010098B
- Authority
- CN
- China
- Prior art keywords
- parts
- aging
- coating
- powder
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of film for being coated with anti-aging coating, technical solution uses following material mixture ratio:Epoxy polyester powder, polyester polyol, solvent, diisocyanate, silane coupling agent, dispersant, luminescent powder and antioxidant are mixed and made into anti-aging coating;Again by anti-aging coating be made antiaging coatings be applied to PE layers, aluminium foil layer, anti-aging pet layer form film on;By the way that the film is pasted on the surfaces such as building, ornament, the film of antiaging coatings is coated with by pasting, improves its anti-aging property and service life, reduce the degree of its jaundice, increase the performance attractive in appearance of building.
Description
Technical field
The present invention relates to technical field of coatings, more specifically, it relates to a kind of film for being coated with anti-aging coating.
Background technology
With the continuous development of science and technology, structure material kind is varied, but its anti-aging phase is short, more or less
Ground there are some such as easy to aging, peelings, it is easy to fall off, can change colour, weatherability is poor, toxic has the defects of taste, construction is inconvenient;And
In outdoor buildings, its service life is short, therefore some products are only limitted to indoor use, and since its raw material is mostly using new
Section bar material causes production cost higher;Nowadays more universal in membrane structure building, they have strong stylishness and artistic feeling.
At present, the Chinese patent of Publication No. CN204845048U discloses a kind of low concentration brine salt film for anti-aging, packet
Film casing play is included, antiaging coatings is provided with above film casing play, antibiotic layer is provided with below film casing play,
A graphene layer is also coated in the outer surface of the antibiotic layer, the thickness of the antiaging coatings is 0.03~0.04mm, described
The thickness of film casing play is 0.05~0.08mm, and the thickness of the antibiotic layer is 0.02~0.03mm.
It is outer by erosions such as sunlight, ultraviolet light irradiation and sleet due to being exposed to, along with China's environmental condition also very
It is undesirable, the salt film in use the moment by extraneous various pollutions, as floated in air dust, in industry
The smog of oiliness is carried in city, the substance with oiliness or acidity that fuel oil and coal combustion equipment volatilize also has in vehicle exhaust
Containing big black particle, in addition acid rain, mist etc., can all be polluted by multiple channel and form, in addition salt film is easy in itself
It is corroded, the too fast loss of internal plasticizer makes the easy aging of salt film, oxidation, the jaundice etc., influences making for roofing film
Use the service life.
Invention content
In view of the deficiencies of the prior art, the present invention intends to provide a kind of anti-aging coating of service life length.
To achieve the above object, the present invention provides following technical solutions:
A kind of anti-aging coating, the coating is counted in parts by weight, including following raw materials according:30-60 parts of epoxy polyester powder,
30-50 parts of polyester polyol, 30-50 parts of solvent, 0.5-0.9 parts of diisocyanate, 0.3-0.8 parts of silane coupling agent, dispersant
0.3-0.7 parts, 0.2-0.5 parts of luminescent powder, 0.15-0.4 parts of antioxidant.
So set, epoxy polyester powder is the matrix of thermosetting powder coating, use epoxy resin and polyester resin for
Main raw material(s) is prepared, and is provided simultaneously with the respective special performance of the two so that the film produced has extremely good stream
Levelling, dicoration, mechanical performance and stronger corrosion resistance are widely applied to the application of various indoor metal products.
Polyester polyol be typically by Dicarboxylic Acids (acid anhydrides or ester) and polyalcohol (including glycol) condensation (or ester hand over
Change) or formed by lactone and polymerization, because intramolecular contains more ester group, amino isopolarity group, cohesive strength and
Strong adhesive force has higher intensity, wearability, and acid-fast alkali-proof polyester polyol is selected as in the present invention, improves not on the same day
The outdoor applicable performance of the coating under gas and environment.
Diisocyanate, that is, aliphatic and alicyclic diisocyanate (ADI) are a kind of spies with-N=C=O functional groups
Different chemicals is mainly used as the raw material of manufacture polyurethane material, and polyurethane material is by diisocyanate and polyether polyol or polyester
Polyalcohol is aggregated and obtained, one of basis as the invention coating, improves the non yellowing of the coating and good application performance.
Solvent is a kind of liquid that can be dissolved solid, be dissolved in liquid, when active compound is processed into pulvis or in order to make it
Convenient for spraying the inert substance being diluted added in, solvent is added in reduce its viscosity and convenient for being processed further,
Using to during adhesive for reducing adhesive viscosity, the power of impregnation having had, modified technique performance, while adhesive can also be reduced
Activity, so as to extend the compound of the validity period of adhesive;It dissolves sizing frequently with solvent for the ease of gluing and adjusts
Required viscosity;Add in solvent purpose be mainly technologic requirement, because solvent addition can the corresponding viscosity of coating, and
Suitable solvent can weld polymer and play adhesive effect.
Generally there are three types of methods for the application of silane coupling agent:First, the surface conditioning agent as framework material;Second is that it adds in
Into bonding agent, three are directly added in high molecular material;Silane coupling agent is a kind of in the molecule while containing there are two types of not
With the organo-silicon compound of chemical property group, having simultaneously in the molecule thereof can be with inanimate matter material (such as glass, silica sand, gold
Belong to etc.) chemically combined reactive group and with organic material (synthetic resin etc.) chemically combined reactive group, on the one hand may be used
For surface treatment, improve the bond properties of compo, while also greatly improve the intensity of the coating, electrical, water resistant, resist
The performances such as weather, even if in hygrometric state, its raising to coating property, effect is also very significantly;Filler is carried out in advance simultaneously
Surface treatment, can also be directly added into resin, can improve dispersibility and bonding force of the filler in resin, improve inorganic filler with
Compatibility between resin improves processing performance and improves the performances such as its weatherability;On the other hand it can be improved as tackifier
The performances such as adhesive strength, water-fast, weatherability, can not be bonded since solving the problems, such as certain materials, action principle
Being itself, there are two types of groups:A kind of group can be combined with by viscous framework material;And another group then can be with high score
Sub- material or bonding agent combine, and so as to form the higher chemical bond of strength in bonding interface, substantially improve the adhesive strength of coating.
Antioxidant is used in high molecular polymer prevent the invention coating from losing intensity and tough due to oxidative degradation
Property, it prevents or coating is delayed to aoxidize, the additive of the stability for improving coating and the coating for extending storage period, such as antioxidant
1010th, antioxidant 1076, irgasfos 168, antioxidant 164, antioxidant DNP, anti-oxidant DLTP, antioxidant MB, antioxidant TNP
Deng improving the antioxygenic property of coating.
Dispersant be it is a kind of in the molecule while there is the interfacial agents of two kinds of opposite natures of lipophile and hydrophily, can
Those are uniformly dispersed to be poorly soluble in the inorganic of liquid, the solid and liquid particles of organic pigment, while can also prevent particle
Sedimentation and cohesion, form the amphipathic reagent needed for stable suspension, improve and improve solid or liquid material dispersion performance
Auxiliary agent has fatty acid, aliphatic amide, esters, paraffin class, metal soap and low molecule wax class etc.;In epoxy polyester powder
End and polyalcohol add in dispersant when mixing, and particle is contributed to crush and prevents broken particle cohesion and keeps dispersion
Stablize, oil-based liquid not soluble in water is dispersed into the liquid pearl of very little under high shear force stirring, after stopping stirring, at interface
It is layered under the action of power, and is stirred after adding in dispersant quickly, then can form stable emulsion, main function is to reduce
Interfacial tension between liquid-liquid and solid-liquid, thus dispersant is also surfactant;Also have simultaneously and promote the invention coating
Gloss, increase levelling effect gloss actually it is main depend on coating surface to the scattering of light, prevent floating, improve tinting strength, tinting power
Paying attention to tinting strength, tinting power, not the higher the better in automatic color regulating system, reduces viscosity, increases pigment loading, reduces flocculation, increases
Storage-stable increases color developing, increases color saturation, increases transparency or the advantages that covering power.
Luminescent powder is powdered photic light-accumulating luminous material, and lighting function is realized, and can be more by absorbing various visible rays
Secondary recycling without radioactive element, can be used as a kind of additive, and in the appearance colour of bright place's presentation itself, and dark place is then
The light of different colours is sent out, the function of good low emergency lighting, sign and decoration is presented, usually with the pigment
Manufactured various light emitting articles.
The invention coating using the epoxy polyester powder that acid-fast alkali-proof polyalcohol and epoxy resin and polyester resin are made as
Raw material, makes the basic material of preparation have good anti-aging and stability, has non yellowing and good application adding in
The diisocyanate of performance, then dissolve sizing by adding in silane coupling agent, solvent and dispersant and adjust required glutinous
Degree, antioxidant can prevent polymer material from losing intensity and toughness due to oxidative degradation, prevent or coating is delayed to aoxidize, and improve
The stability of coating and extension storage period, a small amount of luminescent powder is additionally added, realizes lighting functions by absorbing various visible rays, be in
The function of existing good low emergency lighting, sign and decoration, improves the functionality of the coating, makes anti-aging coating
Anti-aging, anti-jaundice property acid-fast alkali-proof, high temperature resistant and resistance to light in a variety of contexts gets a promotion, and it is corresponding to increase it
Multiple performances, the colleague for improving the service life of building such as anti-aging of building can also increase its service life.
Further setting:The coating is counted in parts by weight, including following raw materials according:40 parts of epoxy polyester powder, polyester is more
First 30 parts of alcohol, 30 parts of solvent, 0.6 part of diisocyanate, 0.5 part of silane coupling agent, 0.4 part of dispersant, 0.3 part of luminescent powder resist
0.2 part of oxidant.
So set, under proportioning in the range, the anti-aging property of the invention coating is effectively improved.
Further setting:The solvent is using one or more in MIKB, DMF, butanone, ethyl acetate.
So set, the full name Chinese of MIKB is referred to as methyl-isobutyl (first) ketone or methylisobutylketone or 4- methyl -2- penta
Ketone is a kind of colourless transparent liquid, has similar camphor smell, is dissolved in ethyl alcohol, benzene, ether etc., and be slightly soluble in water, as the coating
In solvent have good conformability and economic performance;DMF, that is, dimethylformamide is both that a kind of purposes is extremely wide
Industrial chemicals and a kind of excellent solvent having many uses;Butanone also known as methyl ethyl ketone, colourless transparent liquid have similar
Acetone smell, it is volatile, it, can be with ethyl alcohol, ether, benzene, chloroform, oils due to the active hydrogen adjacent with carbonyl and with carbonyl
It is miscible, therefore various reactions easily occur, as acrylic resin, coating, etc. solvent;Ethyl acetate as industrial solvent,
For coating its with excellent dissolubility, quick-drying, it is widely used, be a kind of very important Organic Chemicals and fabulous
Solvent;For the mixing such as resin and powder, the purpose for adding in diluent is mainly technologic requirement, because of adding for diluent
Entering can be as the interim measure for reducing polymer viscosity, so that Polymer Processing, into product, suitable diluent can weld
Polymer and rise adhesive effect.
Further setting:The luminescent powder is using one or more in fluorescent powder, night black luminescent powder, magnetic powder, aluminium powder.
So set, fluorescent powder is generally divided into two class of photo-induced energy storage luminescent powder and luminescent powder with radionuclide, photic storage
Can luminescent powder be fluorescent powder after by irradiations such as natural light, daylight light, ultraviolet lights, luminous energy is stored, stop light
After irradiation, then slowly release in a manner of fluorescence, so at night or dark, remain to see it is luminous, when continuing
Between be up to a few houres to ten a few houres;Luminescent powder with radionuclide is that radioactive substance is mixed in fluorescent powder, utilizes radiation
The ray excitated fluorescent powder that property substance is constantly sent out shines, and this kind of luminescent powder fluorescent lifetime is very long;Night, black luminescent powder was powdered
Photic light-accumulating luminous material realizes lighting function by absorbing various visible rays, can be used as a kind of additive, present good low
Spend the function of emergency lighting, sign and decoration, the usually various light emitting articles made of the pigment;Magnetic powder is one kind
Magnetic paint is made in the single domain particle of hard magnetic, it and adhesive, solvent etc., has high dispersibility and fillibility in magnetic paint, works as residence
In temperature to reach more than a certain numerical value, make the intensity of magnetization vary with temperature relatively slowly, when interior can vehicle interior temperature it is relatively low when, have
The coating carries out extinction to light source, reaches the raised effect of temperature;Aluminium powder is also known as the metallic pigments of " silver powder ", i.e. silver color, with pure
Aluminium foil adds in a small amount of lubricant, through pounding crushing as squamous powder, then polished forms;Aluminium powder is light, and floating force is high, covering power
By force, the 60%-90% of visible ray, ultraviolet light and infrared light can be reflected, with the paint spraying object containing aluminium powder, surface silvery white
Light has the feature of good reflection light;By adding in corresponding luminescent powder, the corresponding function of coating can be increased,
Increase the performance of coating.
In addition, it is a further object of the invention to provide a kind of film with above-mentioned coating, to improve building
Anti-aging property.
A kind of film, from inside to outside successively including PE layers, aluminium foil layer, anti-aging pet layer and above-mentioned anti-aging coating
Manufactured antiaging coatings are connected between the antiaging coatings and anti-aging pet layer by articulamentum.
So set, using PE layers as internal layer, directly Nian Jie with roof or object roofing, PE layers with good stability
Can, play the chemical stability for enhancing film;And PE layers are arranged between aluminium foil layer and contact surface, can avoid PE layers directly with
Light contacts, while aluminium foil layer can play good heat conduction and dissipate to strong anaclasis, reduce because being generated during strong illumination
The increase effect of temperature, and aluminium foil layer is between PE layers and anti-aging pet layer substantially and atmospheric isolation, avoids aoxidizing
And colour-darkening;Antiaging coatings can be played to the good protecting effect of anti-aging pet layer, which has anti-aging
The double effects of performance and refraction astigmatism, it is therefore desirable to be arranged on outermost layer, can directly and light contacts, make full use of the property of coating
The anti-aging property of related building can be protected and reduce building because the time for a long time caused by object plane jaundice, the degree that comes off.
Further setting:The articulamentum is mixed by epoxy resin, acrylic acid, antioxidant and binder resin.
So set, its epoxy resin is to refer to the organic compound containing two or more epoxy groups in molecule
Object, to contain active epoxy group in strand as its feature, epoxy group can positioned at the end of strand, centre or into
Cyclic structure has good physics, chemical property, it is strong with excellent bonding to the surface of metal and nonmetallic materials
Degree, dielectric properties are good, and deformation retract rate is small, and product size stability is good, and hardness is high, and flexibility is preferable, to alkali and major part
Solvent-stable, thus be widely used in making in coating;Acrylic acid has the water suction of superpower property for one of important source material of coating
Agent, the basis as coating preparation;Antioxidant has and can prevent or delay the oxidation of material, improve material stability and
Service life, binder resin have the characteristics that strong tough and tensile, flexibility, binding force, wear-resisting, oil resistant, water-fast, antienzyme bacterium;The articulamentum
Using epoxy resin as matrix, acrylic acid is as the basis prepared, in addition antioxidant can improve its oxidation resistance, plus
Binder resin increases its adhesive strength, and coating is made to pass through articulamentum and is connect with aluminium foil layer, and is bonded on articulamentum, reaching refraction
The effect given out light.
Further setting:PE layers described, aluminium foil layer is connected with anti-aging pet layer by adhesive layer between any two.
So set, by being connected between any two by adhesive, whole compactedness can be increased, while glue-line was both
There is certain flexibility, the film is made to improve the performance of film convenient for bending.
Further setting:The adhesive layer uses EVA hot-melt adhesive.
So set, EVA hot-melt adhesive be it is a kind of be not required to solvent, moisture-free, 100% solid meltability polymer,
It is at normal temperatures solid, heating melting becomes to flow to a certain extent and has the liquid adhesive of certain viscosity, after melting
For light brown translucent body or this white;Hot melt adhesive main component is that ethylene is copolymerized under high pressure with vinyl acetate, then
It is equipped with tackifier, viscosity modifier, antioxidant etc. and hot melt adhesive is made;It is low, viscous with quick solidifying, public hazards when being bonded with other layers
Put forth effort the characteristics of strong, while entirety had not only remain certain flexibility, hardness but also had certain toughness, while can also be again after connection
Heating melting, becomes that adherent is Nian Jie with adherend again again, has the characteristics that viscosity again centainly.
Further setting:Thickness PE layers described is 12-40 microns, and the thickness of the aluminium foil layer is 7-15 microns, described
The thickness of anti-aging pet layer is 40-150 microns, and the thickness of the articulamentum is 2-10 microns, the thickness of the antiaging coatings
It is 4-20 microns.
So set, since film after a variety of layers of bonding by having certain thickness, the thickness of each layer of setting makes film
Integral thickness in a suitable range, do not influence to use and effect under the premise of ensure using for the film.
By using above-mentioned technical proposal, the present invention compares compared with the prior art:By the way that epoxy polyester powder, polyester is more
First alcohol, solvent, diisocyanate, silane coupling agent, dispersant, luminescent powder and antioxidant are mixed and made into anti-aging coating;
Again by anti-aging coating be made antiaging coatings be applied to PE layers, aluminium foil layer, anti-aging pet layer form film on;Pass through
The film is pasted on the surfaces such as building, ornament, the film of antiaging coatings is coated with by pasting, improves its ageing resistance
Energy and service life reduce the degree of its jaundice and building excoriation degree, increase the performance attractive in appearance of building.
Description of the drawings
Fig. 1 is the sectional view of film side.
In figure:1st, PE layers;2nd, aluminium foil layer;3rd, anti-aging pet layer;4th, antiaging coatings;5th, articulamentum;6th, adhesive layer.
Specific embodiment
It is following to fight aged coatings and be described further with the film of the coating.
Embodiment 1:Anti-aging coating, is counted in parts by weight, including following raw materials according:20 parts of epoxy polyester powder, polyester is more
First 20 parts of alcohol, MIKB20 parts, 0.4 part of diisocyanate, 0.2 part of silane coupling agent, stearmide and higher alcohol and with 0.2 part,
0.1 part of fluorescent powder, 0.1 part of antioxidant.
Embodiment 2:Anti-aging coating, is counted in parts by weight, including following raw materials according:25 parts of epoxy polyester powder, polyester is more
First 25 parts of alcohol, 25 parts of butanone, 0.45 part of diisocyanate, 0.25 part of silane coupling agent, 0.25 part of hexenyl bis-stearamides, night
Black 0.15 part of luminescent powder, 0.12 part of antioxidant 1010.
Embodiment 3:Anti-aging coating, is counted in parts by weight, including following raw materials according:30 parts of epoxy polyester powder, polyester is more
First 30 parts of alcohol, 30 parts of ethyl acetate, 0.5 part of diisocyanate, 0.3 part of silane coupling agent, 0.3 part of glyceryl monostearate, magnetic
0.2 part of powder, 0.15 part of antioxidant 1076.
Embodiment 4:Anti-aging coating, is counted in parts by weight, including following raw materials according:40 parts of epoxy polyester powder, polyester is more
First 30 parts of alcohol, DMF30 parts, 0.6 part of diisocyanate, 0.5 part of silane coupling agent, 0.4 part of polyethylene wax, 0.3 part of aluminium powder, 0.2
The irgasfos 168 of part.
Embodiment 5:Anti-aging coating, is counted in parts by weight, including following raw materials according:50 parts of epoxy polyester powder, polyester is more
First 40 parts of alcohol, MIKB20 parts, DMF20 parts, 0.75 part of diisocyanate, 0.7 part of silane coupling agent, 0.55 part of polyethylene glycol
200,0.2 part of aluminium powder, 0.2 part of magnetic powder, 0.3 part of antioxidant DNP.
Embodiment 6:Anti-aging coating, is counted in parts by weight, including following raw materials according:60 parts of epoxy polyester powder, polyester is more
First 50 parts, 20 parts of MIKB, 20 parts of DMF of alcohol, 10 parts of ethyl acetate, 0.9 part of diisocyanate, 0.8 part of silane coupling agent,
0.7 part of polyethylene glycol 400,0.1 part of night black luminescent powder, 0.2 part of aluminium powder, 0.2 part of magnetic powder, 0.4 part of anti-oxidant DLTP.
Embodiment 7:Articulamentum 5 is counted in parts by weight, including following raw materials according:35 parts of epoxy resin, resists 45 parts of acrylic acid
10 parts of oxidant, 10 parts of binder resin are mixed.
Embodiment 8:As shown in Figure 1, a kind of film, includes PE layers 1, aluminium foil layer 2, anti-aging pet layer successively from inside to outside
3rd, antiaging coatings 4 made of anti-aging coating described in embodiment 1 and the articulamentum 5 described in embodiment 7.
Embodiment 9:A kind of film includes PE layers 1, aluminium foil layer 2, anti-aging pet layer 3,2 institute of embodiment successively from inside to outside
Antiaging coatings 4 made of the anti-aging coating stated and the articulamentum 5 described in embodiment 7.
Embodiment 10:A kind of film includes PE layers 1, aluminium foil layer 2, anti-aging pet layer 3, embodiment 3 successively from inside to outside
Antiaging coatings 4 made of the anti-aging coating and the articulamentum 5 described in embodiment 7.
Embodiment 11:A kind of film includes PE layers 1, aluminium foil layer 2, anti-aging pet layer 3, embodiment 4 successively from inside to outside
Antiaging coatings 4 made of the anti-aging coating and the articulamentum 5 described in embodiment 7.
Embodiment 12:A kind of film includes PE layers 1, aluminium foil layer 2, anti-aging pet layer 3, embodiment 5 successively from inside to outside
Antiaging coatings 4 made of the anti-aging coating and the articulamentum 5 described in embodiment 7.
Embodiment 13:As shown in Figure 1, a kind of film, includes PE layers 1, aluminium foil layer 2, anti-aging pet layer successively from inside to outside
3rd, antiaging coatings 4 made of the anti-aging coating described in embodiment 6 and the articulamentum 5 described in embodiment 7.
In embodiment 8-13, connected between antiaging coatings 4 and anti-aging pet layer 3 by articulamentum 5;PE layers 1,
Aluminium foil layer 2 and anti-aging pet layer 3 are connected between any two by adhesive layer 6, and adhesive layer 6 is glued using EVA hot-melt adhesive mode
It closes;PE layers 1 use HDPE;The thickness of PE layers 1 is 25 microns, and the thickness of aluminium foil layer 2 is 12 microns, the thickness of anti-aging pet layer 3
It it is 75 microns, the thickness of the articulamentum 5 is 7 microns, and the thickness of antiaging coatings 4 is 12 microns.
Embodiment 14:Anti-aging Strength Changes experiment
Subjects:Using the film in above-described embodiment 8-13 as test sample, using anti-aging film common on the market as
Comparative example 15 is used as control sample.
Content of the test:Each film is cut into the square of onesize (50cm*50cm), the film cut is distinguished
Be pasted on the roofing under equal conditions or the buildings such as roof on, the side according to as defined in national standard (GB/T3978-94)
Method:Under the environment such as identical illumination, humidity, uniformly to irradiate anti-aging film, detect to be made under different ratio
Anti-aging coating anti-aging film anti-aging intensity.
Result of the test:Through being tested for the property under the environment such as identical illumination, humidity to film, acid resistance, resistance to height
The results are shown in Table 1 for the value of chromatism of the anti-aging experiment of artificial climate under temperature, humidity, light shine, salt spray resistance and different time.
Table 1
From result above and comparative example 15 as can be seen that anti-aging coating provided by the invention than comparative example 15 have compared with
For good performance, wherein acid resistance, high temperature resistant and the salt spray resistance performance under suitable proportioning reaches 1500h coatings
Surface is without exception, and light shine reaches that 2000h is without exception, and salt spray resistance is also without exception in general, old in artificial climate
It can be controlled below 0.32 when changing experiment difference 3000h;Therefore the present invention has very good anti-under suitable proportioning
Ageing properties and good stability, in above example, anti-aging painting that the preparation proportioning of wherein embodiment 11 obtains
The anti-aging property that antiaging coatings are made in material is best, therefore as optimal embodiment.
Simultaneously during the present invention is studied, some exploratory experiments are carried out, in order to verify the reliable of instant component
Property, with embodiment 11 for control, corresponding component is eliminated under study for action, and result and effect clearly, therefore illustrate this
The component that invention provides has good correspondence, carries out specific PROCESS OVERVIEW below.
By taking embodiment 11 as an example, during anti-aging coating is prepared, do not add in diisocyanate, other components with
Embodiment 11 is identical, as a result carries out anti-aging property test to the coating, and as a result in light shine test, 1500h rear films apply
There is more slight yellowing phenomenon on the surface of layer, while also has the phenomenon that slightly wrinkling, therefore shows diisocyanate for applying
The resistance to light of material plays an important roll.
It is control with embodiment 11, during anti-aging coating is prepared, does not add in silane coupling agent, as a result cause
In the experiment of humidity, after irradiating 1500h, the surface of film coating has apparent obscission and has slight yellowing to show
As showing that silane coupling agent can improve the adhesion of coatings of the coating and the performance that surface is smooth.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of film for being coated with anti-aging coating, it is characterised in that:From inside to outside successively include PE layers (1), aluminium foil layer (2),
Anti-aging pet layer (3) and antiaging coatings (4) pass through between the antiaging coatings (4) and anti-aging pet layer (3) and connect
Layer (5) connection, PE layers described (1), aluminium foil layer (2), anti-aging pet layer (3) are connected between any two by adhesive layer (6), institute
The thickness for stating PE layers (1) is 12-40 microns, and the thickness of the aluminium foil layer (2) is 7-15 microns, the antiaging coatings (3)
Thickness is 40-150 microns, and the thickness of the articulamentum (5) is 2-10 microns, and the thickness of the antiaging coatings (4) is 4-20
Micron;Antiaging coatings (4) the moderate resistance aged coatings are counted in parts by weight, including following raw materials according:Epoxy polyester powder 25-50
Part, 25-40 parts of polyester polyol, 25-40 parts of solvent, 0.45-0.75 parts of diisocyanate, 0.25-0.7 parts of silane coupling agent,
0.25-0.55 parts of dispersant, 0.15-0.4 parts of luminescent powder, 0.12-0.3 parts of antioxidant.
2. the film according to claim 1 for being coated with anti-aging coating, it is characterised in that:The coating is in parts by weight
Meter, including following raw materials according:40 parts of epoxy polyester powder, 30 parts of polyester polyol, 30 parts of solvent, 0.6 part of diisocyanate, silane
0.5 part of coupling agent, 0.4 part of dispersant, 0.3 part of luminescent powder, 0.2 part of antioxidant.
3. the film according to claim 1 or 2 for being coated with anti-aging coating, it is characterised in that:The solvent using MIKB,
It is one or more in DMF, butanone, ethyl acetate.
4. the film according to claim 1 or 2 for being coated with anti-aging coating, it is characterised in that:The luminescent powder is using glimmering
It is one or more in light powder, night black luminescent powder, magnetic powder, aluminium powder.
5. the film according to claim 1 for being coated with anti-aging coating, it is characterised in that:The articulamentum (5) is by epoxy
Resin, acrylic acid, antioxidant and binder resin are mixed.
6. the film according to claim 1 for being coated with anti-aging coating, it is characterised in that:The adhesive layer (6) is using EVA
Hot melt adhesive.