CN106009861A - Storage battery joint protective agent and preparation method thereof - Google Patents
Storage battery joint protective agent and preparation method thereof Download PDFInfo
- Publication number
- CN106009861A CN106009861A CN201610354281.XA CN201610354281A CN106009861A CN 106009861 A CN106009861 A CN 106009861A CN 201610354281 A CN201610354281 A CN 201610354281A CN 106009861 A CN106009861 A CN 106009861A
- Authority
- CN
- China
- Prior art keywords
- storage battery
- parts
- protective agent
- battery joint
- joint protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a storage battery joint protective agent and a preparation method thereof. The storage battery joint protective agent is prepared from the following components in parts by volume: 25-30 parts of transparent rust inhibitor, 40-50 parts of chloroform, 5-10 parts of trichloroethylene, 5-10 parts of antioxidant, 6-10 parts of oil-soluble toner, 4-6 parts of benzotriazole, 10-15 parts of metal corrosion inhibitor and 5-10 parts of ethyl acetate. The storage battery joint protective agent has the characteristics of oxidation resistance, wear resistance, corrosion resistance and the like, and can prolong the service life of the storage battery.
Description
Technical field
The invention belongs to protective agent field, be specifically related to a kind of storage battery joint protective agent and preparation method thereof.
Background technology
Storage battery is also called accumulator, is the equipment that chemical energy changes into electric energy.Its effect is supplied with electric motor car electricity consumption, and when vehicle prepares to start, accumulator can be discharged provides electric power to starter, and by starter flywheel driven, crank rotation, thus start vehicle.Electromotor electricity shortage or not actuated time for car in electrical appliance such as sound system, illuminator etc. provide power supply, after electromotor starts normal power supply, accumulator then can be collected and store electric energy, in case use in the future, accumulator is during using, battery head is affected by outside environmental elements can occur the problems such as corrosion, oxidation, thus causes time-dependent current, reduces contact resistance, reduces the service life of battery.
Summary of the invention
Goal of the invention: present invention aims to the deficiencies in the prior art, it is provided that a kind of storage battery joint protective agent and preparation method thereof.
Technical scheme: in order to reach foregoing invention purpose; the present invention is specifically achieved like this: a kind of storage battery joint protective agent, score ratio is by measure: transparent antirust agent 25-30 part, chloroform 40-50 part, trichloro ethylene 5-10 part, antioxidant 5-10 part, oil-soluble toner 6-10 part, BTA 4-6 part, metal inhibitor 10-15 part, ethyl acetate 5-10 part.
Preferably, one or more during described metal inhibitor is bi-imidazoline quaternary ammonium salt and oil acid based imidazolines.
Preferably, described antioxidant is dibenzylatiooluene or tert-butyl hydroquinone.
A kind of protectant preparation method of storage battery joint, comprises the following steps:
1) first, being stirred by transparent antirust agent, oil-soluble toner, BTA, metal inhibitor and ethyl acetate addition high-speed mixer, mixing time is 25-30 minute;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 40-50 degree, and the response time is 15-20 minute, is then cooled to room temperature;Reheating, temperature is 15-20 degree, and the response time is 5-10 minute;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, is then stirred by chloroform, trichloro ethylene and antioxidant addition high-speed mixer, and mixing time is 5-10 minute;
4) dispersion, disperses 8-10 minute in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.
The beneficial effects of the present invention is: the made protective agent of the present invention is developed specifically for protection storage battery joint; make its joint from erosion; and affect electric energy transmission, it is mainly used in the storage battery in vehicle, boats and ships and uninterrupted power supply (UPS); joint line; terminal, the equipment such as folder, there is antioxidation; wear-resistant, that the multiple additives such as anti-corrosion refines protective agent;Without lead protection film, quickly parch, form one layer of coloured mantle;It is effective against oxidation, corrosion, it is provided that protect in time, electromotor easy in starting up, extends the storage battery life-span.
Detailed description of the invention
Embodiment 1:
A kind of storage battery joint protective agent, score ratio is by measure: transparent antirust agent 25 parts, chloroform 40 parts, trichloro ethylene 5 parts, dibenzylatiooluene 5 parts, oil-soluble toner 6 parts, BTA 4 parts, bi-imidazoline quaternary ammonium salt 10 parts, ethyl acetate 5 parts.
A kind of protectant preparation method of storage battery joint, comprises the following steps:
1) first, being stirred by transparent antirust agent, oil-soluble toner, BTA, bi-imidazoline quaternary ammonium salt and ethyl acetate addition high-speed mixer, mixing time is 25 minutes;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 40 degree, and the response time is 15 minutes, is then cooled to room temperature;Reheating, temperature is 15 degree, and the response time is 5 minutes;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, is then stirred by chloroform, trichloro ethylene and antioxidant addition high-speed mixer, and mixing time is 5 minutes;
4) dispersion, disperses 8 minutes in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.
Embodiment 2:
A kind of storage battery joint protective agent, score ratio is by measure: transparent antirust agent 28 parts, chloroform 45 parts, trichloro ethylene 7 parts, butylhydroquinone 7 parts, oil-soluble toner 8 parts, BTA 5 parts, oil acid based imidazolines 13 parts, ethyl acetate 7 parts.
A kind of protectant preparation method of storage battery joint, comprises the following steps:
1) first, transparent antirust agent, oil-soluble toner, BTA, oil acid based imidazolines and ethyl acetate being added high-speed mixer and is stirred, mixing time is 28 minutes;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 45 degree, and the response time is 18 minutes, is then cooled to room temperature;Reheating, temperature is 18 degree, and the response time is 7 minutes;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, then chloroform, trichloro ethylene and butylhydroquinone is added high-speed mixer and is stirred, and mixing time is 8 minutes;
4) dispersion, disperses 9 minutes in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.
Embodiment 3:
A kind of storage battery joint protective agent, score ratio is by measure: transparent antirust agent 30 parts, chloroform 50 parts, trichloro ethylene 10 parts, dibenzylatiooluene 10 parts, oil-soluble toner 10 parts, BTA 6 parts, bi-imidazoline quaternary ammonium salt 15 parts, ethyl acetate 10 parts.
A kind of protectant preparation method of storage battery joint, comprises the following steps:
1) first, being stirred by transparent antirust agent, oil-soluble toner, BTA, bi-imidazoline quaternary ammonium salt and ethyl acetate addition high-speed mixer, mixing time is 30 minutes;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 50 degree, and the response time is 20 minutes, is then cooled to room temperature;Reheating, temperature is 20 degree, and the response time is 10 minutes;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, is then stirred by chloroform, trichloro ethylene and dibenzylatiooluene addition high-speed mixer, and mixing time is 10 minutes;
4) dispersion, disperses 10 minutes in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.
Embodiment 4:
A kind of storage battery joint protective agent, score ratio is by measure: transparent antirust agent 27 parts, chloroform 43 parts, trichloro ethylene 6 parts, tert-butyl hydroquinone 8 parts, oil-soluble toner 8 parts, BTA 5 parts, bi-imidazoline quaternary ammonium salt 5 parts, oil acid based imidazolines 5 parts, ethyl acetate 9 parts.
A kind of protectant preparation method of storage battery joint, comprises the following steps:
1) first, transparent antirust agent, oil-soluble toner, BTA, bi-imidazoline quaternary ammonium salt, oil acid based imidazolines and ethyl acetate being added high-speed mixer and is stirred, mixing time is 30 minutes;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 48 degree, and the response time is 20 minutes, is then cooled to room temperature;Reheating, temperature is 20 degree, and the response time is 10 minutes;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, is then stirred by chloroform, trichloro ethylene and tert-butyl hydroquinone addition high-speed mixer, and mixing time is 10 minutes;
4) dispersion, disperses 10 minutes in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.
The above is only the preferred embodiment of the present invention, it is noted that for those skilled in the art, under the premise without departing from the principles of the invention, it is also possible to make some improvement, and these improvement also should be regarded as protection scope of the present invention.
Claims (4)
1. a storage battery joint protective agent, it is characterised in that: score ratio is by measure: transparent antirust agent 25-30 part, chloroform 40-50 part, trichloro ethylene 5-10 part, antioxidant 5-10 part, oil-soluble toner 6-10 part, BTA 4-6 part, metal inhibitor 10-15 part, ethyl acetate 5-10 part.
A kind of storage battery joint protective agent the most according to claim 1, it is characterised in that: described metal inhibitor is one or more in bi-imidazoline quaternary ammonium salt and oil acid based imidazolines.
A kind of storage battery joint protective agent the most according to claim 1, it is characterised in that: described antioxidant is dibenzylatiooluene or tert-butyl hydroquinone.
4. the protectant preparation method of the storage battery joint as described in claim 1-3 is arbitrary, it is characterised in that: comprise the following steps:
1) first, being stirred by transparent antirust agent, oil-soluble toner, BTA, metal inhibitor and ethyl acetate addition high-speed mixer, mixing time is 25-30 minute;
2) heating, the mixed solution first step obtained adds in stirring at low speed heater, and heating-up temperature is 40-50 degree, and the response time is 15-20 minute, is then cooled to room temperature;Reheating, temperature is 15-20 degree, and the response time is 5-10 minute;
3) secondary mix and blend, the mixed solution obtained by second step is again added in high-speed mixer, is then stirred by chloroform, trichloro ethylene and antioxidant addition high-speed mixer, and mixing time is 5-10 minute;
4) dispersion, disperses 8-10 minute in the liquid that the 3rd step obtains adds to scuffing of cylinder bore, then carries out fill and obtain storage battery joint protective agent goods.