CN106009822A - Acrylic-modified polyester resin varnish for coating of light industrial products - Google Patents
Acrylic-modified polyester resin varnish for coating of light industrial products Download PDFInfo
- Publication number
- CN106009822A CN106009822A CN201610464285.3A CN201610464285A CN106009822A CN 106009822 A CN106009822 A CN 106009822A CN 201610464285 A CN201610464285 A CN 201610464285A CN 106009822 A CN106009822 A CN 106009822A
- Authority
- CN
- China
- Prior art keywords
- polyester resin
- acrylic acid
- light industrial
- weight
- modified polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses acrylic-modified polyester resin varnish for coating of light industrial products. The varnish is prepared from acrylic-modified oxalic acid, neopentyl glycol, amino resin and solvent dimethylbenzene through mixing. The varnish has the advantages of being light in color, rapid to dry, high in hardness, good in gloss, excellent in gloss retention and the like and is applicable to coating of the high-grade light industrial products.
Description
Technical field
The present invention relates to paint technology field, be specifically related to a kind of light industrial goods application use-propylene
Acid modified polyester resin varnish.
Background technology
The clothing of light industrial goods, such as leather, furniture in use, are often subject to friction,
Long-term friction can cause leather to damage, and in order to extend its service life, the coating being used for is also
There is higher requirement.
Summary of the invention
For above-mentioned, it is an object of the invention to provide a kind of light industrial goods application-acrylic acid and change
Property polyester resin varnish.
The present invention adopts the technical scheme that:
A kind of light industrial goods application use-acrylic acid modified polyester resin varnish, is changed by acrylic acid series
Property ethanedioic acid, neopentyl glycol, amino resins, solvent xylene mixing composition.
Further, described light industrial goods application use-acrylic acid modified polyester resin varnish,
By the modified ethanedioic acid of 5-10 parts by weight of acrylic acid system, 5-10 weight portion neopentyl glycol, 5-10
Weight portion amino resins, 15-25 parts by weight solvent dimethylbenzene mixing composition.
It is further preferred that described light industrial goods application use-acrylic acid modified polyester resin is clear
Paint, by the modified ethanedioic acid of 7.5 parts by weight of acrylic acid systems, 7.5 weight portion neopentyl glycols, 7.5
Weight portion amino resins, 20 parts by weight solvent dimethylbenzene mixing compositions.
Technical specification:
The invention has the beneficial effects as follows: the varnish of the present invention that there is of light color, fast drying, hard
The advantages such as degree height, good luster, gloss retention are good, it is adaptable to the covering with paint of high-grade light industrial goods.
Detailed description of the invention
Below embodiments of the invention are described in detail, so that advantages and features of the invention
Can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made more
Explicit defines.
Embodiment 1
A kind of light industrial goods application use-acrylic acid modified polyester resin varnish, by 5 weight portions third
The ethanedioic acid of olefin(e) acid system modification, 5 weight portion neopentyl glycols, 5 weight portion amino resins, 15 weights
Amount part solvent xylene mixing composition.
Embodiment 2
A kind of light industrial goods application use-acrylic acid modified polyester resin varnish, by 7.5 weight portions
The modified ethanedioic acid of acrylic acid series, 7.5 weight portion neopentyl glycols, 7.5 weight portion amino resins,
20 parts by weight solvent dimethylbenzene mixing compositions.
Embodiment 3
A kind of light industrial goods application use-acrylic acid modified polyester resin varnish, by 10 weight portions third
The modified ethanedioic acid of olefin(e) acid system, 10 weight portion neopentyl glycols, 10 weight portion amino resins, 25
Parts by weight solvent dimethylbenzene mixing composition.
Claims (3)
1. a light industrial goods application use-acrylic acid modified polyester resin varnish, it is characterised in that
By the ethanedioic acid of acrylic acid series modification, neopentyl glycol, amino resins, solvent xylene mixing group
Become.
Light industrial goods application use-acrylic acid modified polyester resin the most according to claim 1
Varnish, it is characterised in that by the modified ethanedioic acid of 5-10 parts by weight of acrylic acid system, 5-10 weight
Part neopentyl glycol, 5-10 weight portion amino resins, 15-25 parts by weight solvent dimethylbenzene mixing group
Become.
Light industrial goods application use-acrylic acid modified polyester resin the most according to claim 2
Varnish, by the modified ethanedioic acid of 7.5 parts by weight of acrylic acid systems, 7.5 weight portion neopentyl glycols,
7.5 weight portion amino resins, 20 parts by weight solvent dimethylbenzene mixing compositions.