CN106009725A - Odorless waste tire rubber powder modifying agent easy to melt - Google Patents
Odorless waste tire rubber powder modifying agent easy to melt Download PDFInfo
- Publication number
- CN106009725A CN106009725A CN201610441619.5A CN201610441619A CN106009725A CN 106009725 A CN106009725 A CN 106009725A CN 201610441619 A CN201610441619 A CN 201610441619A CN 106009725 A CN106009725 A CN 106009725A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber powder
- agent
- modifying agent
- waste tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an odorless waste tire rubber powder modifying agent easy to melt. The odorless waste tire rubber powder modifying agent easy to melt has the advantages that the novel odorless waste tire rubber powder modifying agent easy to melt solves the problems that in the prior art, rubber powder modified asphalt releases pungent stink in the production and construction process, the production temperature is 180-190 DEG C and is relatively high, energy consumption and viscosity are high, a high temperature is also needed in construction, and rubber powder serves as the core of rubber powder modified asphalt and is the reason for the high temperature and stink in production and construction; the odorless waste tire rubber powder modifying agent easy to melt is prepared by carrying out desulfuration treatment on common rubber powder and carrying out pre-soaking with a solvent, and diffusion of stink is greatly relieved when the modifying agent is used for producing rubber modified asphalt; besides, the viscosity of rubber modified asphalt is effectively reduced under the same condition, so that the production and construction temperature is reduced, energy consumption is reduced accordingly, cost is reduced, and harm to the environment is relieved.
Description
Technical field
The present invention relates to rubber powder preparation method field, specially one and easily melt odorless rubber powder of waste tire modifying agent.
Background technology
Desulfurizing agent refers generally to remove the free sulphur in fuel, raw material or unclassified stores or the medicament of sulphur compound;The control and process of pollutant refer mainly to remove the medicament used by removing exhaust gas sulphur oxide, various alkali compoundss all can be as desulfurizing agent, remove the desulfurizing agent of sulfur dioxide in stack gases, using most is cheap Calx, limestone and the alkaline solution with the preparation of calcium carbonate medicament, desulfurizing agent can absorb most sulfur dioxide in flue gas and be fixed in waste fuel, chemical plant, smeltery etc. process the tail gas containing sulfur dioxide frequently with the solution such as sodium carbonate, basic aluminum sulfate as desulfurizing agent, and can desorbing recycle.
In prior art, rubber powder modified asphalt can discharge pungent stink during production and construction, produces temperature and is 180-190 DEG C, and temperature is of a relatively high, and power consumption is relatively big, and viscosity is relatively big, is also required to higher temperature during construction, and this runs counter to its environmental protection concept.
Summary of the invention
It is an object of the invention to provide one and easily melt odorless rubber powder of waste tire modifying agent, with the problem solving to propose in above-mentioned background technology.
It is an object of the invention to be achieved by following technical proposals: one easily melts odorless rubber powder of waste tire modifying agent, it is characterised in that it is prepared by the raw material of following parts by weight: degradation inhibitor 2-3 part, organic sulfur adsorbent 1-4 part, cosolvent 2-5 part, limestone 3-6 part, ammonia 2-5 part, desulfurizing agent 3-6 part, mononuclear aromatics 2-7 part, organic acid 4-6 part, metal chloride 1-4 part, mineral acid 2-4 part, regeneration activity agent 3-5 part, rubber powder 1-3 part, emulsifying agent 2-3 part, softening agent 1-4 part, activator 2-5 part.
Above-mentioned organic acid is prepared by the raw material of following parts by weight: formic acid 0.2-0.5%, acetic acid 0.1-0.3%, sulphuric acid 0.2-0.4%, benzoic acid 0.6-0.8%, monoxone 0.1-0.3%, carboxyl 0.2-0.5%, by raw material placing response still merges, obtain organic acid.
Above-mentioned metal chloride is prepared by the raw material of following parts by weight: zinc chloride 0.4-0.6%, iron chloride 0.5-0.7%, aluminum chloride 0.4-0.6%, Phosphorous chloride. 0.2-0.5%, by merging in raw material placing response still, obtains metal chloride.
Above-mentioned regeneration activity agent is prepared by the raw material of following parts by weight: ethoxy-dithioformic acid fat 0.5-0.7%, formic acid 0.2-0.6%, by merging in raw material placing response still, obtains regeneration activity agent.
Above-mentioned by the degradation inhibitor weighed 2 parts, organic sulfur adsorbent 3 parts, cosolvent 2 parts, limestone 4 parts, ammonia 4 parts, desulfurizing agent 4 parts, mononuclear aromatics 3 parts, organic acid 5 parts, metal chloride 2 parts, mineral acid 3 parts, regeneration activity agent 4 parts, rubber powder 2 parts, emulsifying agent 3 parts, softening agent 2 parts and 3 parts of activator are put in agitator tank and are stirred, keep 2 hours, the most again by the steam of 0.9 ~ 0.98MPa (9 ~ 10kgf/cm), 80 DEG C of warm water is injected as heat transfer medium in tank, then dilute alkaline soln it is slowly added into, make pasty state, add water dilution, reciprocal 2 times, extract under the vacuum environment of 2.0Mpa afterwards, obtain modifying agent.
nullThe invention has the beneficial effects as follows: this novel one easily melts odorless rubber powder of waste tire modifying agent,Solve rubber powder modified asphalt in prior art and can discharge pungent stink during production and construction,Produce temperature and be 180-190 DEG C,Temperature is of a relatively high,Consume energy bigger,And viscosity is bigger,Higher temperature it is also required to during construction,The core of rubber modified asphalt is exactly rubber powder,Higher and stink the reason of production and construction temperature is all because rubber powder,General Purpose Rubber powder is carried out desulfurization process,And presoak solvent and prepare one and easily melt odorless rubber powder of waste tire modifying agent,This modifying agent is used to greatly reduce distributing of stink when producing rubber modified asphalt,And effectively reduce the viscosity of rubber modified asphalt under equal conditions,Thus reduce production and construction temperature,And then reduce power consumption,Cost-effective,Reduce the harm to environment.
Detailed description of the invention
Below in conjunction with detailed description of the invention further instruction, but following detailed description should not be understood to the restriction to body invention, various changes that those of ordinary skill in the art can make the most apparently and change, it should all within the scope of invention.
Embodiment 1: the degradation inhibitor 2 parts that will weigh, organic sulfur adsorbent 3 parts, cosolvent 2 parts, limestone 4 parts, ammonia 4 parts, desulfurizing agent 4 parts, mononuclear aromatics 3 parts, organic acid 5 parts, metal chloride 2 parts, mineral acid 3 parts, regeneration activity agent 4 parts, rubber powder 2 parts, emulsifying agent 3 parts, softening agent 2 parts and 3 parts of activator are put in agitator tank and are stirred, keep 2 hours, the most again by the steam of 0.9 ~ 0.98MPa (9 ~ 10kgf/cm), 80 DEG C of warm water is injected as heat transfer medium in tank, then dilute alkaline soln it is slowly added into, make pasty state, add water dilution, reciprocal 2 times, extract under the vacuum environment of 2.0Mpa afterwards, obtain modifying agent.
Embodiment 2: the degradation inhibitor 3 parts that will weigh, organic sulfur adsorbent 5 parts, cosolvent 1 part, limestone 5 parts, ammonia 3 parts, desulfurizing agent 1 part, mononuclear aromatics 2 parts, organic acid 3 parts, metal chloride 1 part, mineral acid 5 parts, regeneration activity agent 6 parts, rubber powder 1 part, emulsifying agent 4 parts, softening agent 1 part and 4 parts of activator are put in agitator tank and are stirred, keep 3 hours, the most again by the steam of 0.9 ~ 0.98MPa (9 ~ 10kgf/cm), 85 DEG C of warm water is injected as heat transfer medium in tank, then dilute alkaline soln it is slowly added into, make pasty state, add water dilution, reciprocal 2 times, extract under the vacuum environment of 4.0Mpa afterwards, obtain modifying agent.
Embodiment 3: the degradation inhibitor 2 parts that will weigh, organic sulfur adsorbent 3 parts, cosolvent 2 parts, limestone 2 parts, ammonia 3 parts, desulfurizing agent 6 parts, mononuclear aromatics 6 parts, organic acid 2 parts, metal chloride 1 part, mineral acid 2 parts, regeneration activity agent 6 parts, rubber powder 1 part, emulsifying agent 1 part, softening agent 4 parts and 5 parts of activator are put in agitator tank and are stirred, keep 1 hour, the most again by the steam of 0.9 ~ 0.98MPa (9 ~ 10kgf/cm), 100 DEG C of warm water is injected as heat transfer medium in tank, then dilute alkaline soln it is slowly added into, make pasty state, add water dilution, reciprocal 2 times, extract under the vacuum environment of 5.0Mpa afterwards, obtain modifying agent.
Above description is only the preferred embodiment of the application and the explanation to institute's application technology principle, skilled artisan would appreciate that, invention scope involved in the application, it is not limited to the technical scheme of the particular combination of above-mentioned technical characteristic, also should contain in the case of without departing from described inventive concept simultaneously, other technical scheme being carried out combination in any by above-mentioned technical characteristic or its equivalent feature and being formed, such as features described above are with disclosed herein
(
But it is not limited to
)
The technical characteristic with similar functions is replaced mutually and the technical scheme that formed.
Claims (5)
1. one kind easily melts odorless rubber powder of waste tire modifying agent, it is characterised in that it is prepared by the raw material of following parts by weight: degradation inhibitor 2-3 part, organic sulfur adsorbent 1-4 part, cosolvent 2-5 part, limestone 3-6 part, ammonia 2-5 part, desulfurizing agent 3-6 part, mononuclear aromatics 2-7 part, organic acid 4-6 part, metal chloride 1-4 part, mineral acid 2-4 part, regeneration activity agent 3-5 part, rubber powder 1-3 part, emulsifying agent 2-3 part, softening agent 1-4 part, activator 2-5 part.
2. one as claimed in claim 1 easily melts odorless rubber powder of waste tire modifying agent, it is characterized in that organic acid is prepared by the raw material of following parts by weight: formic acid 0.2-0.5%, acetic acid 0.1-0.3%, sulphuric acid 0.2-0.4%, benzoic acid 0.6-0.8%, monoxone 0.1-0.3%, carboxyl 0.2-0.5%, by raw material placing response still merges, obtain organic acid.
3. one as claimed in claim 1 easily melts odorless rubber powder of waste tire modifying agent, it is characterized in that metal chloride is prepared by the raw material of following parts by weight: zinc chloride 0.4-0.6%, iron chloride 0.5-0.7%, aluminum chloride 0.4-0.6%, Phosphorous chloride. 0.2-0.5%, by raw material placing response still merges, obtain metal chloride.
4. one as claimed in claim 1 easily melts odorless rubber powder of waste tire modifying agent, it is characterized in that regeneration activity agent is prepared by the raw material of following parts by weight: ethoxy-dithioformic acid fat 0.5-0.7%, formic acid 0.2-0.6%, by raw material placing response still merges, obtain regeneration activity agent.
5. one as claimed in claim 1 easily melts odorless rubber powder of waste tire modifying agent, it is characterized in that the degradation inhibitor 2 parts that will weigh, organic sulfur adsorbent 3 parts, cosolvent 2 parts, limestone 4 parts, ammonia 4 parts, desulfurizing agent 4 parts, mononuclear aromatics 3 parts, organic acid 5 parts, metal chloride 2 parts, mineral acid 3 parts, regeneration activity agent 4 parts, rubber powder 2 parts, emulsifying agent 3 parts, softening agent 2 parts and 3 parts of activator are put in agitator tank and are stirred, keep 2 hours, the most again by the steam of 0.9 ~ 0.98MPa (9 ~ 10kgf/cm), 80 DEG C of warm water is injected as heat transfer medium in tank, then dilute alkaline soln it is slowly added into, make pasty state, add water dilution, reciprocal 2 times, extract under the vacuum environment of 2.0Mpa afterwards, obtain modifying agent.