CN106008861A - 一种用于制作地灯面板的复合材料及其制备方法 - Google Patents
一种用于制作地灯面板的复合材料及其制备方法 Download PDFInfo
- Publication number
- CN106008861A CN106008861A CN201610438137.4A CN201610438137A CN106008861A CN 106008861 A CN106008861 A CN 106008861A CN 201610438137 A CN201610438137 A CN 201610438137A CN 106008861 A CN106008861 A CN 106008861A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite
- polymer
- good
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于制作地灯面板的复合材料,包含如下重量份的原料:丙烯酸羟丙脂25‑30份、丙烯酸丁脂15‑20份、甲基丙烯酸0.5‑1份、十一烯酸1‑1.5份、苯乙烯15‑20份、二丙二醇甲醚30‑35份、酚醛树脂20‑25份、环氧树脂6‑8份、甲基丙烯酸四氟丙脂12‑15份、过氧化苯甲酰1‑2份,本发明中聚合物含氟侧链向空气中伸展,大大降低了聚合物的表面能,赋予聚合物良好的疏水性能,同时稳定的碳氟键包覆着主链,对聚合物内部形成良好的屏障作用,使得本发明的聚合物具有良好的耐候性和耐摩擦性。该聚合物表明致密且光洁,具有良好的反射阳光的作用,即使在太阳下暴晒数小时,表面温度也维持在人体可接受的范围内。
Description
技术领域
本发明涉及一种灯具制作材料,更确切地说,是一种用于制作地灯面板的复合材料及其制备方法。
背景技术
地灯又称地埋灯或藏地灯,是镶嵌在地面上的照明设施。地灯对地面、地上植被等进行照明,能使景观更美丽,行人通过更安全。现多用LED节能光源,表面为不锈钢抛光或铝合金面板,优质的防水接头,硅胶密封圈,钢化玻璃,可防水、防尘、防漏电且耐腐蚀。
对于一些安装在人行道路上的景观地灯,面板多为不锈钢抛光或铝合金面板,这些面板表面光洁美观。但是,在盛夏光照很强烈的情况下,这些金属的地灯面板表面温度太高,过往行人不慎接触到则容易被烫伤。如果有一种材料,既具有较高的光洁度和耐磨性,太阳暴晒后也不会温度太高,则用这种材料制作地灯面板更加合适。
发明内容
本发明主要是解决现有技术所存在的技术问题,从而提供一种用于制作地灯面板的复合材料,用该复合材料制成的地灯面板表面光洁 耐磨,太阳暴晒后温度不会太高。
本发明的上述技术问题主要是通过下述技术方案得以解决的:
一种用于制作地灯面板的复合材料,包含如下重量份的原料:
本发明还公开了一种该用于制作地灯面板的复合材料的制备方法,包含如下步骤:
①按照重量份比将丙烯酸羟丙脂、甲基丙烯酸、苯乙烯、酚醛树脂、环氧树脂、二丙二醇甲醚加入搅拌机,以80-90转/分的速度搅拌,同时将混合物加热到80-85℃,维持15-20分钟;
②按照重量份比将丙烯酸丁脂、十一烯酸加入继续搅拌,温度降低到75-80℃,维持25-30分钟;
③按照重量份比加入甲基丙烯酸四氟丙脂,充分搅拌后维持温度70-75℃静置反应2-2.5小时;
④按照重量份比在混合物中加入过氧化苯甲酰,充分搅拌后维持温度70-75℃静置反应2.5-3小时;
⑤冷却至室温出料,得标的产物。
本发明中聚合物含氟侧链向空气中伸展,大大降低了聚合物的表面能,赋予聚合物良好的疏水性能,同时稳定的碳氟键包覆着主链,对聚合物内部形成良好的屏障作用,使得本发明的聚合物具有良好的耐候性和耐摩擦性。该聚合物表面致密且光洁,具有良好的反射阳光的作用,即使在太阳下暴晒数小时,表面温度也维持在人体可接受的范围内。
具体实施方式
下面对本发明的优选实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界 定。
[实施例1]
取如下原材料:
制作地灯面板:
将丙烯酸羟丙脂、甲基丙烯酸、苯乙烯、环氧树脂、二丙二醇甲醚加入搅拌机,以80转/分的速度搅拌,同时将混合物加热到80℃,维持15分钟;将丙烯酸丁脂、十一烯酸加入继续搅拌,温度降低到75℃,维持25分钟;加入甲基丙烯酸四氟丙脂,充分搅拌后维持温度70℃静置反应2小时;混合物中加入过氧化苯甲酰,充分搅拌后维持温度70℃静置反应2.5小时;冷却至室温出料,得标的产物;将标的产物制成2cm厚板材备用。
[实施例2]
取如下原材料:
制作地灯面板:
将丙烯酸羟丙脂、甲基丙烯酸、苯乙烯、环氧树脂、二丙二醇甲醚加入搅拌机,以90转/分的速度搅拌,同时将混合物加热到85℃,维持20分钟;将丙烯酸丁脂、十一烯酸加入继续搅拌,温度降低到80℃,维持30分钟;加入甲基丙烯酸四氟丙脂,充分搅拌后维持温度75℃静置反应2.5小时;混合物中加入过氧化苯甲酰,充分搅拌后维持温度75℃静置反应3小时;冷却至室温出料,得标的产物;将标的产物制成2cm厚板材备用。
[实施例3]
取如下原材料:
制作地灯面板:
将丙烯酸羟丙脂、甲基丙烯酸、苯乙烯、环氧树脂、二丙二醇甲醚加入搅拌机,以85转/分的速度搅拌,同时将混合物加热到82℃,维持18分钟;将丙烯酸丁脂、十一烯酸加入继续搅拌,温度降低到78℃,维持27分钟;加入甲基丙烯酸四氟丙脂,充分搅拌后维持温度73℃静置反应2.2小时;混合物中加入过氧化苯甲酰,充分搅拌后维持温度73℃静置反应2.7小时;冷却至室温出料,得标的产物; 将标的产物制成2cm厚板材备用。
将实施例1~3制成的板材与相同厚度的不锈钢板材、铝合金板材进行对比测试,测试结果如下:
检测项目 | 实施例1 | 实施例2 | 实施例3 | 不锈钢板材 | 铝合金板材 |
硬度(HB) | 181 | 184 | 178 | 176 | 147 |
动摩擦系数 | 0.35 | 0.39 | 0.37 | 0.42 | 0.48 |
表面温度(109Lux,1H) | 41℃ | 43℃ | 42℃ | 78℃ | 72℃ |
测试结果显示:本发明复合材料制成的地灯面板表明更加光洁耐磨,特别是经过长时间剧烈光照后表面温度较低,在人体可接受范围内,不会被烫伤。
以上仅仅以3个实施方式来说明本发明的设计思路,在系统允许的情况下,本发明可以扩展为同时外接更多的功能模块,从而最大限度扩展其功能。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (2)
1.一种用于制作地灯面板的复合材料,其特征在于,包含如下重量份的原料:
2.一种如权利要求1所述用于制作地灯面板的复合材料的制备方法,其特征在于,包含如下步骤:
①按照重量份比将丙烯酸羟丙脂、甲基丙烯酸、苯乙烯、酚醛树脂、环氧树脂、二丙二醇甲醚加入搅拌机,以80-90转/分的速度搅拌,同时将混合物加热到80-85℃,维持15-20分钟;
②按照重量份比将丙烯酸丁脂、十一烯酸加入继续搅拌,温度降低到75-80℃,维持25-30分钟;
③按照重量份比加入甲基丙烯酸四氟丙脂,充分搅拌后维持温度70-75℃静置反应2-2.5小时;
④按照重量份比在混合物中加入过氧化苯甲酰,充分搅拌后维持温度70-75℃静置反应2.5-3小时;
⑤冷却至室温出料,得标的产物。