CN106005748A - Packaging box of precision part - Google Patents
Packaging box of precision part Download PDFInfo
- Publication number
- CN106005748A CN106005748A CN201610488880.0A CN201610488880A CN106005748A CN 106005748 A CN106005748 A CN 106005748A CN 201610488880 A CN201610488880 A CN 201610488880A CN 106005748 A CN106005748 A CN 106005748A
- Authority
- CN
- China
- Prior art keywords
- packing box
- precision parts
- elastic layer
- unsaturated
- inner housing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of packaging, and in particular to a packaging box of a precision part. The packaging box comprises an outer shell and an inner shell, wherein the outer shell and the inner shell are connected by using a first damping mechanism; the inner shell includes a supporting layer, a buffering layer and an elastic layer which are sequentially disposed from outside to inside; the supporting layer is a rigid board; the buffering layer includes a plurality of a second damping mechanism disposed between the supporting layer and the elastic layer. The packaging box of the precision part can effectively guarantee intactness of a precise instrument in a transportation process.
Description
Technical field
The present invention relates to packaging field, particularly to the packing box of a kind of precision parts.
Background technology
Packing box is generally used for the circulation of goods, facilitates the turnover of goods, also exists most important in our life
Effect.Packing box has certain storage space, is commonly used to pack food that is multiple frangible or that be not easy to collision or object, works as bag
After in mounted box, article fill up, can only rely in case between article to bear against formation stable, but when when between article, space is more loose just
Can produce and rock, can cause the damage of article, existing conventional way time serious is to add vibrationproof implant, though operation is not multiple
Miscellaneous, but take time and effort, it is unfavorable for the saving of cost, the especially packaging to precision instrument.
In all items, precision instrument is the instrument that a class is higher to instrument precision requirement, and every precision instrument is going out
All through the test of performance during factory, but precision instrument can be rocked or clash into, seriously by various in the process selling transport
Affect the accurate performance of instrument.
In order to solve that the problems referred to above prior art has pointed out related art scheme, such as Chinese patent CN 105151482A
Disclosing " a kind of shock-proof packaging box ", including casing and case lid, described casing includes internal box and outer case, the sidewall of internal box
And gap is arranged between the sidewall of outer case, at least side sidewall of internal box be can the elastic plate that expands outwardly of arc-shaped deformation, institute
State shock-proof packaging box and also include the outer draw piece for drawing elastic plate to make it deform outward;Also include that the diapire being arranged on internal box is with outer
Between the diapire of casing and for the air spring of vibration damping.But its main purpose be article after being to make to be placed in packing box with
Having the metastable power of bearing against between article, form relatively stable placement effect, article will not form shifting relatively to each other
Move and produce collision, thus prevent from damaging.Also Chinese patent CN105151531A is had to disclose " a kind of packaging having shock-proof effect
Transport case ", including outer case be arranged in outer case and for the internal box of storing, the diapire of outer case and the end of internal box
It is provided with between wall for the damper unit to internal box longitudinal damping;It is additionally provided with on the sidewall of outer case outside internal box is formed
Wrapping and be used for the vibration-damped component to internal box oscillation crosswise vibration damping, vibration-damped component includes along the outer casing that outer case sidewall is circumferentially disposed
Be wrapped in outer casing in and stand tightly against in the damping body of outer case sidewall.
Both technical schemes above-mentioned the most effectively slow down the problem that article rock in casing, but such scheme all simply solves
Article do not rock relative to internal box, it is adaptable to the parts of decomposition, and the precision instrument assembled for local is the most inapplicable.
How to keep the standing of article not rock in the case of internal box is also had weak vibrations by prior art, then there is no correlation technique
Means.
Summary of the invention
In order to solve above-mentioned technical problem, the present invention provides the packing box of a kind of precision parts, and it can be effectively ensured essence
Close instrument standing intact in transportation.
For realizing above-mentioned technical purpose, the concrete technological means that the present invention takes is, the packaging of a kind of precision parts
Box, including shell body and inner housing, uses the first damper mechanism to be connected between shell body with inner housing;Described inner housing include from
Supporting layer, cushion and the elastic layer set gradually in arriving outward;Described supporting layer is hard plate;Described cushion includes several
The second damper mechanism being uniformly arranged between supporting layer and elastic layer.
The technical scheme improved as the present invention, the inwall of shell body and the outer wall of inner housing are correspondingly arranged several and install
Groove;Described first damper mechanism installation by adhering is in mounting groove, and the thickness/height of described first damper mechanism is more than outward
The spacing of the mounting groove being correspondingly arranged in inner walls and inner housing outer wall.
The technical scheme improved as the present invention, described first damper mechanism is shock-absorbing spring, air cushion or elastic ball;The
Two damper mechanisms are shock-absorbing spring, air cushion or elastic ball.
The technical scheme improved as the present invention, also includes that several sponge liquid glue, described sponge liquid glue are positioned over
In gap between precision component and elastic layer.
The technical scheme improved as the present invention, described hard plate is PVC hard plate.
The technical scheme improved as the present invention, described elastic layer is that each material using following weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 1-4 part
EVA resin 4-16 part
Ethylenically unsaturated polyisocyanate 4-16 part
Polyether polyols ester 4-16 part
Unsaturated polyester resin 2-8 part.
The technical scheme improved as the present invention, in described EVA resin, VA content is 30%-50%.
The technical scheme improved as the present invention, described protecting film uses following steps to be prepared from, particularly as follows: a,
At a temperature of 100-150 DEG C, after melted for EVA resin, add unsaturated group cage-type silsesquioxane, obtain pre-after mix homogeneously
Goods;B, ethylenically unsaturated polyisocyanate and polyether polyol are simultaneously introduced mixing and stirring in prefabrication, and
React 0.5-5h under the vacuum of 120-130 DEG C, obtain intermediate products;C, it is 60-90 DEG C in 1.5-2 normal atmosphere, temperature
Under conditions of unsaturated polyurethanes added in intermediate products and mix homogeneously, after standing 3-5h, compression molding obtains protecting film.
Beneficial effect
The present invention, by arranging the first damper mechanism between shell body and inner housing, effectively slows down outside to packing box inner housing
Vibration, cushion and the elastic layer in inner housing positioned inside avoids the vibration of inner housing to precision parts the most completely
Vibration.
Detailed description of the invention
Purpose and technical scheme for making the embodiment of the present invention are clearer, below the technical scheme to the embodiment of the present invention
It is clearly and completely described.Obviously, described embodiment is a part of embodiment of the present invention rather than whole realities
Execute example.Based on described embodiments of the invention, those of ordinary skill in the art are institute on the premise of without creative work
The every other embodiment obtained, broadly falls into the scope of protection of the invention.
Those skilled in the art of the present technique are appreciated that unless otherwise defined, and all terms used herein (include technology art
Language and scientific terminology) have with the those of ordinary skill in art of the present invention be commonly understood by identical meaning.Also should
Being understood by, those terms defined in such as general dictionary should be understood that the meaning having with the context of prior art
The meaning that justice is consistent, and unless defined as here, will not explain by idealization or the most formal implication.
The implication of heretofore described " inside and outside " refers to relative to equipment itself, the side within sensing equipment
To for interior, otherwise it is outward, rather than the specific restriction to assembly of the invention mechanism.
The implication of heretofore described " connection " can be being directly connected between parts can also be to pass through between parts
Being indirectly connected with of other parts.
Embodiment 1
The packing box of a kind of precision parts, including shell body and inner housing, uses the first vibration damping between shell body and inner housing
Mechanism connects;Described inner housing includes supporting layer, cushion and the elastic layer set gradually from outside to inside;Described supporting layer is hard
Scutum;Described cushion includes several the second damper mechanisms being uniformly arranged between supporting layer and elastic layer.
And in order to improve damping efficiency, the second damper mechanism between shell body and inner housing is evenly distributed with some
Individual, when so making shell local vibration, the first damper mechanism can locally carry out vibration damping, and overall inner shell is the most motionless;The most existing skill
For the damper mechanism of the integral type in art, when local vibration, damper mechanism entirety can occur elastic shape for slowing down vibration
Become, cause rocking of inner shell, rocking of the final article affecting package interior.
The inwall of shell body and the outer wall of inner housing are correspondingly arranged several mounting grooves;Described first damper mechanism is embedded
It is installed in mounting groove, and the thickness/height of described first damper mechanism is right with on inner housing outer wall more than shell body inwall
The spacing of the mounting groove that should arrange.
Wherein, described first damper mechanism is shock-absorbing spring, air cushion or elastic ball;Second damper mechanism is vibration damping bullet
Spring, air cushion or elastic ball.
In the present embodiment, described hard plate is PVC hard plate.
In order to protect the most vibrated impact of precision instrument, the also cushion top layer in inner shell arranges elastic layer and in essence
Filling sponge liquid glue in gap between close part and elastic layer, and protecting film is to fit tightly on precision instrument,
When inner shell is vibrated, protecting film effectively slows down the vibrations of precision instrument;
Wherein protecting film is to use EVA resin, ethylenically unsaturated polyisocyanate, polyether polyols ester and unsaturated polyester resin
It is prepared from unsaturated group cage-type silsesquioxane, because the special cage structure of unsaturated group cage-type silsesquioxane makes
Must prepare protecting film have hard and become the skeleton matrix of a fixed structure, and EVA resin is flexible chain, during preparation one
The side chain of part EVA resin infiltrates in the cagelike structure of unsaturated group cage-type silsesquioxane, the master of another part EVA resin
Chain and attachment then reacts formation with unsaturated polyester resin, unsaturated isocyanate with polyether polyol and has hard segment with soft
The special construction that section combines so that the protecting film ultimately formed have basic unit be hard layer, intermediate layer be soft layer and top layer
The composite bed being combined with compliant section for hard segment, when inner shell is vibrated, vibration can be played further buffering by soft layer
Effect, precision instrument is then played buffering antihunt action by top layer.
Described elastic layer is that each material using following weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 1 part
EVA resin 4 parts
Ethylenically unsaturated polyisocyanate 4 parts
Polyether polyols ester 4 parts
Unsaturated polyester resin 2 parts.
In order to ensure that elastic layer not only possesses elastic but also possesses certain rigidity, in described EVA resin, VA content is 30%.
Described protecting film use following steps be prepared from, particularly as follows: a, at a temperature of 100 DEG C by EVA resin
Add unsaturated group cage-type silsesquioxane after Rong Rong, after mix homogeneously, obtain prefabrication;B, by unsaturated for ethylenic many isocyanides
Acid esters and polyether polyol are simultaneously introduced mixing and stirring in prefabrication, and react 0.5h under the vacuum of 120 DEG C, in obtaining
Between product;C, under conditions of 1.5 normal atmospheres, temperature are 60 DEG C, unsaturated polyurethanes added in intermediate products and mix
Closing uniformly, after standing 3h, compression molding obtains protecting film.
Embodiment 2
Difference with embodiment 1 is, described elastic layer is that each material using following weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 4 parts
EVA resin 16 parts
Ethylenically unsaturated polyisocyanate 16 parts
Polyether polyols ester 16 parts
Unsaturated polyester resin 8 parts.
In order to ensure that elastic layer not only possesses elastic but also possesses certain rigidity, in described EVA resin, VA content is 50%.
Described protecting film use following steps be prepared from, particularly as follows: a, at a temperature of 150 DEG C by EVA resin
Add unsaturated group cage-type silsesquioxane after Rong Rong, after mix homogeneously, obtain prefabrication;B, by unsaturated for ethylenic many isocyanides
Acid esters and polyether polyol are simultaneously introduced mixing and stirring in prefabrication, and react 5h under the vacuum of 130 DEG C, obtain centre
Product;C, unsaturated polyurethanes is added in intermediate products and mix all under conditions of 2 normal atmospheres, temperature are 90 DEG C
Even, after standing 5h, compression molding obtains protecting film.
Embodiment 3
Difference with embodiment 1 is, described elastic layer is that each material using following weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 2 parts
EVA resin 8 parts
Ethylenically unsaturated polyisocyanate 8 parts
Polyether polyols ester 8 parts
Unsaturated polyester resin 6 parts.
In order to ensure that elastic layer not only possesses elastic but also possesses certain rigidity, in described EVA resin, VA content is 40%.
Described protecting film use following steps be prepared from, particularly as follows: a, at a temperature of 120 DEG C by EVA resin
Add unsaturated group cage-type silsesquioxane after Rong Rong, after mix homogeneously, obtain prefabrication;B, by unsaturated for ethylenic many isocyanides
Acid esters and polyether polyol are simultaneously introduced mixing and stirring in prefabrication, and react 1h under the vacuum of 125 DEG C, obtain centre
Product;C, under conditions of 1.6 normal atmospheres, temperature are 78 DEG C, unsaturated polyurethanes added in intermediate products and mix
Uniformly, after standing 3.5h, compression molding obtains protecting film.
Embodiment 4
Difference with embodiment 1 is, described elastic layer is that each material using following weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 3 parts
EVA resin 10 parts
Ethylenically unsaturated polyisocyanate 10 parts
Polyether polyols ester 12 parts
Unsaturated polyester resin 6 parts.
In order to ensure that elastic layer not only possesses elastic but also possesses certain rigidity, in described EVA resin, VA content is 37%.
Described protecting film use following steps be prepared from, particularly as follows: a, at a temperature of 136 DEG C by EVA resin
Add unsaturated group cage-type silsesquioxane after Rong Rong, after mix homogeneously, obtain prefabrication;B, by unsaturated for ethylenic many isocyanides
Acid esters and polyether polyol are simultaneously introduced mixing and stirring in prefabrication, and react 4h under the vacuum of 127 DEG C, obtain centre
Product;C, under conditions of 1.5 normal atmospheres, temperature are 78 DEG C, unsaturated polyurethanes added in intermediate products and mix
Uniformly, after standing 4h, compression molding obtains protecting film.
Comparative example 5
Difference with embodiment 4 is, described elastic layer is that each material using following weight portion is prepared from:
Ethylenically unsaturated polyisocyanate 10 parts
Polyether polyols ester 12 parts
Unsaturated polyester resin 6 parts.
In order to ensure that elastic layer not only possesses elastic but also possesses certain rigidity, in described EVA resin, VA content is 37%.
Described protecting film use following steps be prepared from, particularly as follows: a, by ethylenically unsaturated polyisocyanate
With polyether polyol mixing and stirring, and under the vacuum of 127 DEG C react 4h, obtain intermediate products;C, big 1.5 standards
Unsaturated polyurethanes is added in intermediate products and mix homogeneously under conditions of being 78 DEG C by air pressure, temperature, is molded into after standing 4h
Type obtains protecting film.
The implementation result of embodiment 1-5
In table 1 Data Source in service life in: it is 5% and the number of times that do not deforms that protecting film is stretched to percentage elongation;
In table 1, vibrationproof performance is to be put in the ultrasonic washing unit of 50HZ by box body, the amplitude of detection tray interior placing articles
The performance test of box body is obtained prepared by table 1 embodiment 1-5
The Young's modulus (Mpa) of elastic layer | The service life of elastic layer | The ageing-resistant performance of elastic layer | Vibrationproof performance | |
Embodiment 1 | 4 | 165 | Unchanged | Without amplitude |
Embodiment 2 | 5 | 150 | Unchanged | Without amplitude |
Embodiment 3 | 4.5 | 155 | Unchanged | Without amplitude |
Embodiment 4 | 4.2 | 160 | Unchanged | Without amplitude |
Embodiment 5 | 3 | 100 | There is deformation | Amplitude 0.1cm |
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to the most real
Execute example the present invention has been described in detail, it will be understood by those within the art that, can be to the technical side of the present invention
Case is modified or equivalent, and without deviating from objective and the scope of technical solution of the present invention, it all should be contained in the present invention
Right in the middle of.
Claims (8)
1. a packing box for precision parts, including shell body and inner housing, uses first to subtract between shell body and inner housing
Shake mechanism connect;It is characterized in that, described inner housing includes supporting layer, cushion and the elastic layer set gradually from outside to inside;
Described supporting layer is hard plate;Described cushion includes several the second vibration dampings being uniformly arranged between supporting layer and elastic layer
Mechanism.
The packing box of a kind of precision parts the most according to claim 1, it is characterised in that the inwall of shell body and inner shell
The outer wall of body is correspondingly arranged several mounting grooves;Described first damper mechanism installation by adhering in mounting groove, and described
The thickness/height of one damper mechanism is more than the spacing of the mounting groove being correspondingly arranged on shell body inwall and inner housing outer wall.
The packing box of a kind of precision parts the most according to claim 1, it is characterised in that described first damper mechanism is
Shock-absorbing spring, air cushion or elastic ball;Second damper mechanism is shock-absorbing spring, air cushion or elastic ball.
The packing box of a kind of precision parts the most according to claim 1, it is characterised in that also include several sponge liquid
Body glue, described sponge liquid glue is positioned in the gap between precision component and elastic layer.
The packing box of a kind of precision parts the most according to claim 1, it is characterised in that described hard plate is that PVC is hard
Scutum.
The packing box of a kind of precision parts the most according to claim 1, it is characterised in that described elastic layer is to use such as
Each material of lower weight portion is prepared from:
Unsaturated group cage-type silsesquioxane 1-4 part
EVA resin 4-16 part
Ethylenically unsaturated polyisocyanate 4-16 part
Polyether polyols ester 4-16 part
Unsaturated polyester resin 2-8 part.
The packing box of a kind of precision parts the most according to claim 6, it is characterised in that in described EVA resin, VA contains
Amount is 30%-50%.
The packing box of a kind of precision parts the most according to claim 6, it is characterised in that described protecting film is to use such as
Lower step is prepared from, particularly as follows: a, add unsaturated group cage modle after melted for EVA resin at a temperature of 100-150 DEG C
Silsesquioxane, obtains prefabrication after mix homogeneously;B, ethylenically unsaturated polyisocyanate is added with polyether polyol simultaneously
Enter mixing and stirring in prefabrication, and under the vacuum of 120-130 DEG C, react 0.5-5h, obtain intermediate products;C, at 1.5-2
Unsaturated polyurethanes is added in intermediate products and mix homogeneously under conditions of being 60-90 DEG C by individual normal atmosphere, temperature, stands
After 3-5h, compression molding obtains protecting film.