CN105990033A - 一种润湿性佳耐高温的超级电容器隔膜材料 - Google Patents
一种润湿性佳耐高温的超级电容器隔膜材料 Download PDFInfo
- Publication number
- CN105990033A CN105990033A CN201610055301.3A CN201610055301A CN105990033A CN 105990033 A CN105990033 A CN 105990033A CN 201610055301 A CN201610055301 A CN 201610055301A CN 105990033 A CN105990033 A CN 105990033A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- ethanol
- concentration
- polyacrylonitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种润湿性佳耐高温的超级电容器隔膜材料，由下列重量份的原料制成：聚乙烯醇纤维35-40、聚丙烯纤维33-35、聚丙烯腈粉末10-13、丙酮30-32、N，N-二甲基甲酰胺72-75、70℃水溶PVA纤维8-10、聚乙烯吡咯烷酮7-8、正硅酸乙酯8-10、浓度为75wt%的乙醇9-10、二氧化硅6-7、沸石分子筛9-11、聚二甲基硅氧烷1-2、羧甲基纤维素2-3、大豆卵磷脂1.5-2。本发明将二氧化硅与沸石分子筛等成分通过适当的工艺改性添加到非织造布浆料的制备中，增加了产品的孔隙率，减小了孔径，提高了产品的耐高温性能以及破膜温度，还在成型前添加大豆卵磷脂等成分，增加了产品的润湿性。
Description
技术领域
本发明涉及电容器隔膜技术领域，尤其涉及一种润湿性佳耐高温的超级电容器隔膜材料。
背景技术
超级电容器是一种极具市场竞争力的储能器，由于它可以实现快速充电、大电流放电，且具有10万次以上的充电寿命，在一些需要短时高倍率放电的应用中占有重要地位。混合动力汽车和电动汽车对动力电源的要求也引起了全世界范围内对超级电容器这一新型储能装置的广泛重视。在超级电容器的组成中，电极、电解液和隔膜纸对超级电容器的性能起着决定性的影响。目前超级电容器的电极和电解液是研究的热点，但是人们对于隔膜的研究和关注度并不高。
超级电容器的隔膜纸位于两个多孔化碳电极之间，与电极一起完全浸润在电解液中，在反复充放电过程中起到隔离的作用，阻止电子传导，防止两极间接触造成的内部短路。这就要求隔膜材料是电子的绝缘体，具有良好的隔离性能，并且其孔隙应尽可能小于电极表面活性物质的最小粒径。隔离性能较好的隔膜纸必须孔径小，这样可使电解液的流通性下降，电池充放电性能下降；而电解液浸透率较高，离子通过性好的隔膜材料往往孔隙较大较多，容易造成两极之间接触造成的内部短路。超级电容器最大的优势在于充放电速度快、可以大功率放电，因此，隔膜材料将向着厚度更薄、孔隙率更高、孔径更小且分布更均匀等高性能趋势发展。
目前用于超级电容器隔膜的材料主要有纤维素隔膜纸和传统电池隔膜，高性能隔膜纸制造技术困难，价格高昂；传统电池隔膜厚度较厚，孔隙率低，对电解液亲和性差，而静电纺纳米纤维膜制造技术简单，成本低，隔膜孔隙率高达90%，对电解液亲和性良好，但是缺点是强度不高。如果能将纤维素隔膜纸与静电纺丝纤维膜进行复合，取长补短，可以得到成本低、孔隙率高、强度大的复合隔膜材料。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种润湿性佳耐高温的超级电容器隔膜材料。
本发明是通过以下技术方案实现的：
一种润湿性佳耐高温的超级电容器隔膜材料，由下列重量份的原料制成：聚乙烯醇纤维35-40、聚丙烯纤维33-35、聚丙烯腈粉末10-13、丙酮30-32、N，N-二甲基甲酰胺72-75、70℃水溶PVA纤维8-10、聚乙烯吡咯烷酮7-8、正硅酸乙酯8-10、浓度为75wt%的乙醇9-10、二氧化硅6-7、沸石分子筛9-11、聚二甲基硅氧烷1-2、羧甲基纤维素2-3、大豆卵磷脂1.5-2。
根据权利要求书1所述一种润湿性佳耐高温的超级电容器隔膜材料，由下列具体方法制备而成：
（1）将丙酮与N，N-二甲基甲酰胺在常温下混合均匀，加入聚丙烯腈粉末，以100转/分的速度在常温下搅拌3小时，形成聚丙烯腈纺丝溶液，在接收距离为20cm、电压为25kV、供液速率为1mL/h的条件下进行静电纺丝2小时，纺制出厚度为10μm的聚丙烯腈纳米纤维膜待用；
（2）将聚丙烯纤维与聚乙烯醇纤维混合，加入适量的水，放入打浆机中，按2%浓度进行分散成纤维悬浮液，加入70℃水溶PVA纤维，以1000转/分的速度边搅拌边加热至70℃，直至70℃水溶PVA纤维完全溶解形成混合悬浮液待用；
（3）将正硅酸乙酯溶于浓度为75wt%的乙醇中待用；将二氧化硅与沸石分子筛混合研磨60分钟后加入溶于3倍量水的羧甲基纤维素，继续研磨30分钟后倒出与上述正硅酸乙酯乙醇溶液混合，搅拌分散均匀后加热蒸发出乙醇，然后放入造粒机中挤出造粒，最后放入马弗炉中，以300℃的温度煅烧1小时，冷却至室温后粉碎，过800目筛，得到增强填料；
（4）将步骤（2）中得到的混合悬浮液中加入步骤（3）得到的增强填料、聚乙烯吡咯烷酮以及其余剩余成分，继续加入适量的水，以600转/分的速度搅拌30分钟，形成上网浓度为0.1wt%的浆料，采用湿法成型工艺将上述浆料送入造纸机经网部及压榨部脱水成形，然后用电热鼓风干燥10分钟，再采用热压成形机以135℃的温度热压粘合得到非织造布基布待用；
（5）将步骤（1）得到的聚丙烯腈纳米纤维膜覆盖在步骤（4）得到的非织造布基布上面，通过135℃的热辊进行热压结合，冷却后剪切、包装得到本发明。
本发明的优点是：本发明首先将聚丙烯腈进行静电纺丝制成聚丙烯腈纳米纤维膜，然后利用聚乙烯醇纤维与聚丙烯纤维混合，采用湿法无纺布工艺制成非织造布，将两者通过热压的方式很好的粘合在一起，可以得到强度高、透气性好的性能，而且更好的控制了隔膜材料的孔径以及分布，使得孔径更小分布更均匀、孔隙率高，从而能够更好的浸透电解液，使得放电电流更均匀；同时添加70℃水溶PVA纤维作为增强剂，制成的复合隔膜材料还具有较好的抗张强度、化学稳定性，吸液保液性以及隔离性能。
本发明将二氧化硅与沸石分子筛等成分通过适当的工艺改性添加到非织造布浆料的制备中，增加了产品的孔隙率，减小了孔径，提高了产品的耐高温性能以及破膜温度，还在非织造布基布成型前添加大豆卵磷脂等成分，增加了产品的润湿性，从而使得制成的超级电容器隔膜纸具有优异的电解液浸润性。
具体实施方式
一种润湿性佳耐高温的超级电容器隔膜材料，由下列重量份（公斤）的原料制成：聚乙烯醇纤维35、聚丙烯纤维33、聚丙烯腈粉末10、丙酮30、N，N二甲基甲酰胺72、70℃水溶PVA纤维8、聚乙烯吡咯烷酮7、正硅酸乙酯8、浓度为75wt%的乙醇9、二氧化硅6、沸石分子筛9、聚二甲基硅氧烷1、羧甲基纤维素2、大豆卵磷脂1.5。
根据权利要求书1所述一种润湿性佳耐高温的超级电容器隔膜材料，由下列具体方法制备而成：
（1）将丙酮与N，N二甲基甲酰胺在常温下混合均匀，加入聚丙烯腈粉末，以100转/分的速度在常温下搅拌3小时，形成聚丙烯腈纺丝溶液，在接收距离为20cm、电压为25kV、供液速率为1mL/h的条件下进行静电纺丝2小时，纺制出厚度为10μm的聚丙烯腈纳米纤维膜待用；
（2）将聚丙烯纤维与聚乙烯醇纤维混合，加入适量的水，放入打浆机中，按2%浓度进行分散成纤维悬浮液，加入70℃水溶PVA纤维，以1000转/分的速度边搅拌边加热至70℃，直至70℃水溶PVA纤维完全溶解形成混合悬浮液待用；
（3）将正硅酸乙酯溶于浓度为75wt%的乙醇中待用；将二氧化硅与沸石分子筛混合研磨60分钟后加入溶于3倍量水的羧甲基纤维素，继续研磨30分钟后倒出与上述正硅酸乙酯乙醇溶液混合，搅拌分散均匀后加热蒸发出乙醇，然后放入造粒机中挤出造粒，最后放入马弗炉中，以300℃的温度煅烧1小时，冷却至室温后粉碎，过800目筛，得到增强填料；
（4）将步骤（2）中得到的混合悬浮液中加入步骤（3）得到的增强填料、聚乙烯吡咯烷酮以及其余剩余成分，继续加入适量的水，以600转/分的速度搅拌30分钟，形成上网浓度为0.1wt%的浆料，采用湿法成型工艺将上述浆料送入造纸机经网部及压榨部脱水成形，然后用电热鼓风干燥10分钟，再采用热压成形机以135℃的温度热压粘合得到非织造布基布待用；
（5）将步骤（1）得到的聚丙烯腈纳米纤维膜覆盖在步骤（4）得到的非织造布基布上面，通过135℃的热辊进行热压结合，冷却后剪切、包装得到本发明。
通过对本实施例隔膜材料进行测试，厚度为52μm，平均孔径为0.26μm，孔隙率为59%，吸液率为581%，110℃下热收缩率小于1%，150℃下热收缩率小于1%。
Claims (2)
1.一种润湿性佳耐高温的超级电容器隔膜材料，其特征在于，由下列重量份的原料制成：聚乙烯醇纤维35-40、聚丙烯纤维33-35、聚丙烯腈粉末10-13、丙酮30-32、N，N-二甲基甲酰胺72-75、70℃水溶PVA纤维8-10、聚乙烯吡咯烷酮7-8、正硅酸乙酯8-10、浓度为75wt%的乙醇9-10、二氧化硅6-7、沸石分子筛9-11、聚二甲基硅氧烷1-2、羧甲基纤维素2-3、大豆卵磷脂1.5-2。
2.根据权利要求书1所述一种润湿性佳耐高温的超级电容器隔膜材料，其特征在于，由下列具体方法制备而成：
（1）将丙酮与N，N-二甲基甲酰胺在常温下混合均匀，加入聚丙烯腈粉末，以100转/分的速度在常温下搅拌3小时，形成聚丙烯腈纺丝溶液，在接收距离为20cm、电压为25kV、供液速率为1mL/h的条件下进行静电纺丝2小时，纺制出厚度为10μm的聚丙烯腈纳米纤维膜待用；
（2）将聚丙烯纤维与聚乙烯醇纤维混合，加入适量的水，放入打浆机中，按2%浓度进行分散成纤维悬浮液，加入70℃水溶PVA纤维，以1000转/分的速度边搅拌边加热至70℃，直至70℃水溶PVA纤维完全溶解形成混合悬浮液待用；
（3）将正硅酸乙酯溶于浓度为75wt%的乙醇中待用；将二氧化硅与沸石分子筛混合研磨60分钟后加入溶于3倍量水的羧甲基纤维素，继续研磨30分钟后倒出与上述正硅酸乙酯乙醇溶液混合，搅拌分散均匀后加热蒸发出乙醇，然后放入造粒机中挤出造粒，最后放入马弗炉中，以300℃的温度煅烧1小时，冷却至室温后粉碎，过800目筛，得到增强填料；
（4）将步骤（2）中得到的混合悬浮液中加入步骤（3）得到的增强填料、聚乙烯吡咯烷酮以及其余剩余成分，继续加入适量的水，以600转/分的速度搅拌30分钟，形成上网浓度为0.1wt%的浆料，采用湿法成型工艺将上述浆料送入造纸机经网部及压榨部脱水成形，然后用电热鼓风干燥10分钟，再采用热压成形机以135℃的温度热压粘合得到非织造布基布待用；
（5）将步骤（1）得到的聚丙烯腈纳米纤维膜覆盖在步骤（4）得到的非织造布基布上面，通过135℃的热辊进行热压结合，冷却后剪切、包装得到本发明。