CN105985591A - Polyvinyl chloride plain film - Google Patents
Polyvinyl chloride plain film Download PDFInfo
- Publication number
- CN105985591A CN105985591A CN201510063823.3A CN201510063823A CN105985591A CN 105985591 A CN105985591 A CN 105985591A CN 201510063823 A CN201510063823 A CN 201510063823A CN 105985591 A CN105985591 A CN 105985591A
- Authority
- CN
- China
- Prior art keywords
- parts
- plain film
- polyvinyl chloride
- resin
- heat stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyvinyl chloride plain film. The polyvinyl chloride plain film comprises the following components in parts by mass: 100 parts of PVC resin, 40-60 parts of a thickening agent, 20-40 parts of a heat stabilizer, 50-200 parts of a strengthening agent, 10-20 parts of reinforced resin, 0.5-1.5 parts of a lubricating agent, and 4-6 parts of an accelerant. By using a special formula, the plain film is the uniform to plasticize, flawless, good in toughness, resistant to impact, flame-retardant, good in low temperature performance, resistant to ageing and long in service life.
Description
Technical field
The present invention relates to a kind of polrvinyl chloride plain film.
Background technology
Polrvinyl chloride true qualities are slightly yellow translucent, glossy.Transparency is better than polyethylene, polyphenyl alkene, is worse than polyphenyl second
Alkene, different with auxiliary dosage, it is divided into soft, PVC-U, soft goods is soft and tough, and feel is glued, and the hardness of boardy product is higher than
Low Density Polyethylene, and less than polypropylene, at flexion, there will be albinism.Common product: sheet material, tubing,
The polrvinyl chloride such as sole, toy, door and window, wire outer skin, stationery are that a kind of one chlorine atom of use replaces polyethylene
In the macromolecular material of a hydrogen atom.
Polrvinyl chloride (PVC) plain film is the base material producing various drip water plates, is also used for other Blister products and secondary operations becomes
Matrix.Existing polrvinyl chloride plain film, sheet material plasticizing is uneven, have crackle, poor toughness, not impact resistance, the most fire-retardant, low
Temperature poor performance, aging life-span are short.
Summary of the invention
The technical problem to be solved in the present invention is the defect overcoming prior art, it is provided that a kind of polrvinyl chloride plain film.
In order to solve above-mentioned technical problem, the invention provides following technical scheme:
One polrvinyl chloride plain film of the present invention, its according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 40-60；
Heat stabilizer: 20-40；
Reinforcing agent: 50-200；
Strengthen resin: 10-20；
Lubricant: 0.5-1.5；
Accelerator: 4-6.
Further, according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 30；
Heat stabilizer: 20；
Reinforcing agent: 50；
Enhancing resin: 10；
Lubricant: 0.5；
Accelerator: 4.
Further, according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 50；
Heat stabilizer: 40；
Reinforcing agent: 200；
Enhancing resin: 20；
Lubricant: 1.5；
Accelerator: 4-6.
The present invention is reached to provide the benefit that:
The present invention uses special formula, the plasticizing of this sheet material uniformly, flawless, good toughness, impact resistance, fire-retardant, low temperature properties
Energy is good, aging life-span is long.
Detailed description of the invention
Hereinafter the preferred embodiments of the present invention are illustrated, it will be appreciated that preferred embodiment described herein is only used for
Bright and explain the present invention, be not intended to limit the present invention.
One polrvinyl chloride plain film of the present invention, its according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 40-60；
Heat stabilizer: 20-40；
Reinforcing agent: 50-200；
Strengthen resin: 10-20；
Lubricant: 0.5-1.5；
Accelerator: 4-6.
Further, according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 30；
Heat stabilizer: 20；
Reinforcing agent: 50；
Enhancing resin: 10；
Lubricant: 0.5；
Accelerator: 4.
Further, according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 50；
Heat stabilizer: 40；
Reinforcing agent: 200；
Enhancing resin: 20；
Lubricant: 1.5；
Accelerator: 4-6.
The present invention is reached to provide the benefit that:
The present invention uses special formula, the plasticizing of this sheet material uniformly, flawless, good toughness, impact resistance, fire-retardant, low temperature properties
Energy is good, aging life-span is long.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention, to the greatest extent
The present invention has been described in detail by pipe with reference to previous embodiment, and for a person skilled in the art, it is the most permissible
Technical scheme described in foregoing embodiments is modified, or wherein portion of techniques feature is carried out equivalent.All
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the present invention's
Within protection domain.
Claims (3)
1. a polrvinyl chloride plain film, it is characterised in that according to the mass fraction, it includes the composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 40-60；
Heat stabilizer: 20-40；
Reinforcing agent: 50-200；
Strengthen resin: 10-20；
Lubricant: 0.5-1.5；
Accelerator: 4-6.
A kind of polrvinyl chloride plain film the most according to claim 1, it is characterised in that according to the mass fraction, it includes
The composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 30；
Heat stabilizer: 20；
Reinforcing agent: 50；
Enhancing resin: 10；
Lubricant: 0.5；
Accelerator: 4.
A kind of polrvinyl chloride plain film the most according to claim 1, it is characterised in that according to the mass fraction, it includes
The composition of following proportioning:
Polyvinyl chloride resin: 100；
Viscosifier: 50；
Heat stabilizer: 40；
Reinforcing agent: 200；
Enhancing resin: 20；
Lubricant: 1.5；
Accelerator: 4-6.