CN105984145A - Preparation method for surface-printed button - Google Patents
Preparation method for surface-printed button Download PDFInfo
- Publication number
- CN105984145A CN105984145A CN201510050157.XA CN201510050157A CN105984145A CN 105984145 A CN105984145 A CN 105984145A CN 201510050157 A CN201510050157 A CN 201510050157A CN 105984145 A CN105984145 A CN 105984145A
- Authority
- CN
- China
- Prior art keywords
- button
- preparation
- resin
- present
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method for a surface-printed button. The preparation method comprises the following steps: printing light-cured resin on the surface of a button having undergone oil removal so as to obtain a semi-finished product; and then subjecting the semi-finished product to curing so as to obtain the surface-printed button. The button prepared by using the method provided by the invention has obviously stereoscopic and variable color effect on its surface and can replace laser engraved buttons; and the preparation method can be used for surface treatment of other button materials without limitation by the button materials.
Description
Technical field
The invention belongs to garment production technical field, particularly relate to the preparation method of a kind of printout surface button.
Background technology
Button is exactly the fastener being connected for the both sides hem on clothes, and its initial effect is for connection to
The left front of clothes, the most gradually develop into and have more artistry and decoration in addition to keeping its original function
Property, also it is the personalized representative with multifunction of dress ornament.Along with fashion elements constantly substitutes, fashion dress ornament
Be continually changing, the processing technology of button is the most exquisite, and clothing button is the most exquisite,
Button, by the classification of its material, can be divided into natural class, chemical and other materials, this its
Middle chemical button be divided into again organic buckle, resin button, combination is buckled, carbamide is buckled, spray paint buckle, electroplate buckle,
Button etc. by the emperor himself.Along with the fast development of button industry, require the most day by day to improve to button, need to have wear-resisting
Property is good, heat-resisting quantity is good, good corrosion resistance and kind miscellaneous, and color of light is vivid beautiful etc.
Feature, and sometimes also need to tackle clothing and produce a lot of different style, the button that shape is very strange.Cause
And, go on the market the most one after another with the various button that various materials make, bucket victory strive very, as gold-plated button, silver-plated button,
Screw buckle, engraving button, enameling button, material button etc., the most valuable also has white jade Fructus Citri Sarcodactylis button, Margarita covered with gold leaf
Button, three inlaid with jade buttons, embedding gold Achates button and Corallium Japonicum Kishinouye button, Apis cerana Fabricius button, succinum button etc. even also have diamond
Button.The decorative pattern of button is the most rich and varied, and such as folding branch flowers, happiness,position and longevity are auspiciousness, it may be said that without institute not
Have, meet the different requirements of various fashion dress ornament.
Among these, surface engraving button is the button pattern that a class is emerging, and surface engraving button refers to
The surface of button is carved, and can be that intaglio may also be convex quarter, thus formation has vertical on button surface
The effect of body pattern.At present, along with the day by day fierce market competition and the development in pluralism of dress ornament color,
Engraving button has become one of indispensable element of a lot of trend dress ornament, and many stereoeffects are more easy to clothes fashion of arranging in pairs or groups,
Under different angles, obvious stereoeffect can be produced, novel brilliant.
But in prior art, in the preparation method of surface engraving button, many use laser can carve material
Character cut in bas-relief, type or the pattern that button surface is carved, font color is single, it is impossible to accomplish changeable color, and by
Easily it is heated excessively produces xanthochromia in the feature of laser, unsaturated-resin or plastic material button surface,
Particularly white button easily occurs.For making button attractive in appearance, must ultrasonic waves for cleaning after laser engraving
Processing, technique is loaded down with trivial details.Physical property additionally, due to button material is different, e.g., and hardness, fusing point etc.,
Also there is restriction to the material of button in laser engraving.
Therefore, the processing method on a kind of button surface can how be found, it is possible to substitute laser engraving
Button so that button surface has the effect of three-dimensional and changeable color, can be used for other button materials simultaneously
The surface of matter processes, and has become one of manufacturer's problem demanding prompt solution in field.
Summary of the invention
In view of this, the technical problem to be solved in the present invention is to provide the preparation of a kind of printout surface button
Method, button surface prepared by the method that the present invention provides has the most three-dimensional and color variable color effect,
Laser engraving button can be substituted completely, and the surface that can be used for other button materials processes,
Do not limited by button material.
The invention discloses the preparation method of a kind of printout surface button, it is characterised in that include following step
Rapid:
A) after the button printout surface light-cured resin after oil removal treatment, semi-finished product are obtained；
B), after being solidified by the semi-finished product that above-mentioned steps obtains, printout surface button is obtained.
Preferably, described light-cured resin includes fatty acid modified epoxy acrylate, aliphatic polyurethane
Acrylate, trimethylolpropane trimethacrylate, tripropylene glycol diacrylate fat, auxiliary agent and pigment.
Preferably, described auxiliary agent includes firming agent, diluent and dispersant.
Preferably, print to 3D described in print；Described it is cured as ultraviolet curing.
Preferably, described button is resin button, carbamide button, Cornu Bovis seu Bubali button, injection button, true shellfish
One or more in button and metal plating class button.
Preferably, described step B) also include afterwards,
C) after the surface spraying varnish of above-mentioned printout surface button, dry and obtain finished surface engraving button.
Preferably, described spraying is spray gun spraying, described in the bore that sprays paint be 1.1～1.3mm.
Preferably, described drying is that drying tunnel is dried, and the temperature of described drying is 60～90 DEG C, described drying
Time is 50～60 minutes.
Preferably, described varnish is mixed with resin paint.
Preferably, described mixed with resin paint is made up of the main paint of resin, firming agent and diluent；
The mass percent of the main paint of described resin, firming agent and diluent is (90～110): (20～50):
(50～600).
The invention discloses the preparation method of a kind of printout surface button, the present invention is first at oil removing
After button printout surface light-cured resin after reason, obtain semi-finished product；Then half above-mentioned steps obtained
After finished product solidifies, obtain printout surface button.Compared with prior art, present invention employs 3D to beat
The mode of print replaces laser artistic carving, is printed on button by light-cured resin, and specifically
Spray paint and post processing mode, obtained printout surface button.Printout surface button prepared by the present invention can
Print at button surface 3D and there is different colors, and can match colors each other, form difference
Pattern, thus there is obvious color variable color effect, and lower powered ultraviolet LED only need to be used to enter
Row solidification, during will not produce high heat, there is not button and burnt the phenomenon of Huang, without carrying out the later stage
Ultrasonic waves for cleaning processes, and simplifies operating procedure；Meanwhile, the knob needed for the preparation method that the present invention provides
Button material, do not restricted by hardness and fusing point, go for resin, carbamide, Cornu Bovis seu Bubali, injection,
True shellfish, metal plating class button.Thus, the printout surface button of the present invention can substitute laser radium completely
Penetrate engraving button, and the surface that can be used for other button materials processes, and is not limited by button material.
Test result indicate that, surface engraving button prepared by the present invention has obvious color variable color effect, does not deposits
Being burnt the defect of Huang at button, and can apply to multiple button material, product structure is various.
Accompanying drawing explanation
Fig. 1 is the outward appearance photo of laser engraving button prepared by prior art；
Fig. 2 is the outward appearance photo of the printout surface button of embodiment 1 preparation；
Fig. 3 is the outward appearance photo of the printout surface button of embodiment 2 preparation.
Detailed description of the invention
In order to further appreciate that the present invention, below in conjunction with embodiment, the preferred embodiments of the invention are carried out
Describe, but it is to be understood that these describe simply for further illustrate the features and advantages of the present invention and not
It it is the restriction to patent requirements of the present invention.
The all raw materials of the present invention, are not particularly limited its source, that commercially buy or according to ability
Prepared by the conventional method known to field technique personnel.
The all raw materials of the present invention, are not particularly limited its purity, present invention preferably employs analytical pure.
Printout surface button of the present invention, i.e. at button printout surface space pattern or the button of font.
The invention discloses the preparation method of a kind of printout surface button, it is characterised in that include following step
Rapid:
A) after the button printout surface light-cured resin after oil removal treatment, semi-finished product are obtained；
B), after being solidified by the semi-finished product that above-mentioned steps obtains, printout surface button is obtained.
First the present invention after the button printout surface light-cured resin after oil removal treatment, obtains half one-tenth
Product；Described printing is preferably 3D and prints；The method of described oil removal treatment is not particularly limited by the present invention,
Method with oil removal treatment well known to those skilled in the art；The equipment of described printing is not had by the present invention
Having restriction especially, with 3D printing device well known to those skilled in the art, the present invention is preferably 3D and beats
Print machine.The present invention is the stability ensureing to print, and preferably will come on fixture by button after oil removal treatment
After Gu Ding, then spray；Described fixture is not particularly limited by the present invention, with those skilled in the art
Known to button fixture.
Described light-cured resin preferably includes fatty acid modified epoxy acrylate, aliphatic polyurethane propylene
Acid esters, trimethylolpropane trimethacrylate, tripropylene glycol diacrylate fat, auxiliary agent and pigment；This
The bright curing performance for raising light-cured resin pair and effect, described light-cured resin is more preferably B-5292X
Fatty acid modified epoxy acrylate, TU-4500 aliphatic urethane acrylate, trimethylolpropane tris
Acrylate, tripropylene glycol diacrylate fat, auxiliary agent and pigment；Described auxiliary agent preferably include firming agent,
Diluent and dispersant；The present invention does not has spy to the specifically chosen of described firming agent, diluent and dispersant
Do not limit, with firming agent, diluent and dispersion used by light-cured resin well known to those skilled in the art
Agent, firming agent of the present invention is preferably methyl diethanolamine, diethylaminopropylamine, ethylenediamine,
One or more in hexamethylene diamine, diethylenetriamine and triethylene tetramine, more preferably methyl diethanolamine,
Diethylaminopropylamine, ethylenediamine, hexamethylene diamine, diethylenetriamine or triethylene tetramine, more preferably methyl
Diethanolamine, hexamethylene diamine or triethylene tetramine, most preferably methyl diethanolamine；Described diluent is preferred
For one or more in benzophenone, Ketohexamethylene and benzil, more preferably benzophenone and two
Benzene second diketone；Described dispersant is BYK3510 and/or BYK333.
The present invention is for making subsequent preparation process realize effect optimization, by the optimal set of described light-cured resin
Divide and be preferably the fatty acid modified epoxy acrylate of B-5292X, TU-4500 aliphatic polyurethane acrylic acid
Ester, trimethylolpropane trimethacrylate, tripropylene glycol diacrylate fat, methyl diethanolamine, hexichol
Ketone, benzil, BYK3510, BYK333 and pigment；The present invention is to above-mentioned optimal component
Mass fraction be not particularly limited, with the programs of light-cured resin well known to those skilled in the art
, the present invention be preferably the fatty acid modified epoxy acrylate of B-5292X of 10～30 weight portions, 5～20
The TU-4500 aliphatic urethane acrylate of weight portion, 0.1～0.4 trimethylolpropane tris of weight portion
Acrylate, 20～40 tripropylene glycol diacrylate fat, 0.5～3.0 methyl diethyls of weight portion of weight portion
Hydramine, 2～10 benzophenone, 2～10 benzil, 0.1～0.8 weight portions of weight portion of weight portion
BYK3510 and the 0.1～BYK333 of 0.3 weight portion, the B-5292X of more preferably 15～25 weight portions
Fatty acid modified epoxy acrylate, 5～15 weight portion TU-4500 aliphatic urethane acrylate,
The trimethylolpropane trimethacrylate of 0.1～0.3 weight portion, 25～35 tripropylene glycol two propylene of weight portion
Acid fat, 0.5～2.5 methyl diethanolamine, 3～7 benzophenone, 3～7 weight portions of weight portion of weight portion
Benzil, 0.2～0.5 BYK3510 and 0.1～the BYK333 of 0.2 weight portion of weight portion,
It is preferably the fatty acid modified epoxy acrylate of B-5292X of 20 weight portions, the TU-4500 of 10 weight portions
Aliphatic urethane acrylate, the trimethylolpropane trimethacrylate of 0.2 weight portion, 30 weight portions
Tripropylene glycol diacrylate fat, 1.0～2.0 methyl diethanolamine, 4～6 hexichol first of weight portion of weight portion
Ketone, 4～6 weight portion benzil, 0.3～0.4 weight portion BYK3510 and 0.15 weight portion
BYK333.Kind and the consumption of described pigment are not particularly limited, with people in the art by the present invention
Known to Yuan for the single of button or hybrid pigment, consumption can be according to practical condition or client
Requirement is allocated.
The model of above-mentioned concrete model raw material is not particularly limited by the present invention, ripe with those skilled in the art
Universal models raw material in the industry known；The present invention is the most special to the source of above-mentioned concrete model raw material
Limit, with method well known to those skilled in the art preparation or commercially.
The present invention uses 3D printer that photocuring color resin fixed point is sprayed on the knob after oil removal treatment
Button surface, obtains semi-finished product；After being solidified by the most above-mentioned semi-finished product, obtain surface engraving button；
Described solidification is not particularly limited by the present invention, with solidification light-cured resin well known to those skilled in the art
Method, solidification of the present invention is preferably ultraviolet curing；The present invention equipment to described solidification
It is not particularly limited, with the equipment of solidification light-cured resin well known to those skilled in the art, this
Bright described solidification is preferably uviol lamp；Other conditions of described solidification are not particularly limited by the present invention, with
The condition of solidification light-cured resin well known to those skilled in the art.
The present invention for strengthen stereoeffect or strengthen patterns, can the most above-mentioned spraying print and
The step of solidification, the number of times of above-mentioned repetition is not particularly limited by the present invention, real with technological requirement or production
Border situation is as the criterion, and the present invention is preferably 1～3 time.
The present invention is after above-mentioned steps obtains surface engraving button, for improving product appearance and wearability,
Preferably after the surface spraying varnish of described surface engraving button, dry and obtain finished surface engraving button.
Above-mentioned steps is not particularly limited by the present invention, with button post-processing step well known to those skilled in the art
?；The equipment of spraying of the present invention is not particularly limited, with spraying well known to those skilled in the art
Equipment, the present invention is preferably spray gun spraying；The described bore sprayed paint is preferably 1.1～1.3mm, more excellent
Elect 1.15～1.25mm as；Other conditions of described spraying are not particularly limited by the present invention, with this area skill
Spraying conditions known to art personnel.
Described varnish is not particularly limited by the present invention, with well known to those skilled in the art for spraying knob
The varnish of button, varnish of the present invention is preferably mixed with resin paint, and described mixed with resin paint is by resin
Main paint, firming agent and diluent composition, the addition of described epoxy resin is preferably 90～110 weight
Part, more preferably 95～105 weight portions, more preferably 98～102 weight portions；Described illusion-colour mica sheet
Addition is preferably 0.1～1.0 weight portions, more preferably 0.3～0.8 weight portion, most preferably 0.4～0.7 weight
Amount part；The addition of described amine curing agent is preferably 20～50 weight portions, more preferably 25～45 weight
Part, most preferably 30～40 weight portions；The addition of described diluent is preferably 50～600 weight portions, more
It is preferably 100～500 weight portions, more preferably 200～400 weight portions, most preferably 250～350 weight
Part.
The present invention is to improve the effect after lacquer varnish, described mixed with resin paint preferably include epoxy resin and/
Or acrylic resin, more preferably include epoxy resin and acrylic resin, most preferably 618 epoxy resin
With PJ23-65 acrylic resin；The present invention is to improve the paint film property of mixed with resin paint, the most also includes point
Powder and diluent, described dispersant and diluent are not particularly limited by the present invention, with art technology
The dispersant for lacquer type organic coating known to personnel and diluent, the preferred described diluent of the present invention is ring
Hexanone, dimethylbenzene and DAA；Described dispersant is BYK141 and/or BYK358.The present invention is
Make button product realize effect optimization, the optimal component of described mixed with resin paint is preferably 618 epoxies
Resin, PJ23-65 acrylic resin, Ketohexamethylene, dimethylbenzene, DAA, BYK141 and BYK358,
The mass fraction of above-mentioned optimal component is not particularly limited by the present invention, with well known to those skilled in the art
The programs of lacquer type organic coating, the present invention is preferably 618 epoxy resin, 22～26 of 20～40 weight portions
The PJ23-65 acrylic resin of weight portion, 10～20 Ketohexamethylene, 10～20 diformazans of weight portion of weight portion
Benzene, 10～20 weight portion DAA, 0.1～0.5 weight portion BYK141 and 0.1～0.5 weight portion
BYK358,618 epoxy resin of more preferably 25～35 weight portions, 23～25 PJ23-65 of weight portion
Acrylic resin, 13～17 Ketohexamethylene, 14～16 dimethylbenzene, 13～17 weight portions of weight portion of weight portion
DAA, 0.2～0.4 BYK141 and 0.2～the BYK358 of 0.4 weight portion of weight portion, optimum
Elect PJ23-65 acrylic resin, 13～17 of 618 epoxy resin of 30 weight portions, 24.5 weight portions as
The Ketohexamethylene of weight portion, the dimethylbenzene of 15 weight portions, the DAA of 15 weight portions, 0.3 weight portion
BYK141 and the BYK358 of 0.2 weight portion.
Described firming agent is preferably diethylaminopropylamine, ethylenediamine, hexamethylene diamine, diethylenetriamine and three second
One or more in alkene tetramine, more preferably diethylaminopropylamine, ethylenediamine, hexamethylene diamine, divinyl
Triamine or triethylene tetramine, more preferably diethylaminopropylamine, hexamethylene diamine or triethylene tetramine, most preferably
For diethylaminopropylamine；Described diluent is preferably dimethylbenzene, Ketohexamethylene and butanol；The present invention is to described
The ratio of diluent is not particularly limited, with well known to those skilled in the art for lacquer type organic coating mixing dilute
Releasing agent, the mass ratio of dimethylbenzene, Ketohexamethylene and butanol in described diluent is preferably 16 by the present invention:
1:3；The model of above-mentioned concrete model raw material is not particularly limited, with those skilled in the art by the present invention
Known to industry in universal models raw material；The present invention does not has spy to the source of above-mentioned concrete model raw material
Do not limit, with method well known to those skilled in the art preparation or commercially.
The method of described drying is not particularly limited by the present invention, with button well known to those skilled in the art
Furnace drying method, drying of the present invention is preferably drying tunnel and dries；The temperature of described drying is preferably
60～90 DEG C, more preferably 65～85 DEG C, most preferably 70～80 DEG C；The time of described drying is preferably 50～60
Minute, more preferably 53～58 minutes, most preferably 55 minutes；The present invention other conditions to described drying
It is not particularly limited, with button drying condition well known to those skilled in the art；The present invention is to described
The equipment dried is not particularly limited, with button drying plant well known to those skilled in the art.
The present invention obtains finished surface through above-mentioned steps and prints button, uses the method for the present invention not by hard
Degree and the restriction of fusing point, go for multiple button material；The material of button of the present invention is preferred
For one or more in resin, carbamide, Cornu Bovis seu Bubali, injection, Zhen Bei and metal plating class button, more excellent
Elect resin, carbamide, Cornu Bovis seu Bubali, injection, Zhen Bei or metal plating class button, most preferably resin, cattle as
Angle, Zhen Bei or metal plating class button.
Present invention employs the mode that 3D prints, light-cured resin is printed on button, and specifically
Spray paint and post processing mode, obtained printout surface button.Printout surface button prepared by the present invention can
Print at button surface 3D and there is different colors, and can match colors each other, form difference
Pattern, thus there is obvious color variable color effect, and lower powered ultraviolet LED only need to be used to enter
Row solidification, during will not produce high heat, there is not button and burnt the phenomenon of Huang, without carrying out the later stage
Ultrasonic waves for cleaning processes, and simplifies operating procedure；Meanwhile, the knob needed for the preparation method that the present invention provides
Button material, do not restricted by hardness and fusing point, go for resin, carbamide, Cornu Bovis seu Bubali, injection,
True shellfish, metal plating class button.Thus, the printout surface button of the present invention can substitute laser carving
Carve button, and the surface that can be used for other button materials processes, and is not limited by button material.Real
Testing result to show, printout surface button prepared by the present invention has obvious color variable color effect, does not exists
Button is burnt the defect of Huang, and can apply to multiple button material, and product structure is various.
In order to be further appreciated by the present invention, the printout surface button present invention provided below in conjunction with embodiment
Preparation method illustrate, protection scope of the present invention is not limited by the following examples.
Embodiment 1
Blank-making technology: add 10ml cobalt salt in 1.0kg unsaturated-resin and stir, then add
10ml methyl ethyl ketone peroxide and 20ml styrene, carry out making through rod machine bad, obtain button after stirring
Blank.
System button technique: first pass through deduction processed and button blank is made the shape of button, can be according to different
Examine that requirement carries out moulding.
Just polishing: the button blank worked it out by deduction processed, is poured in buffing machine, is carried out by rotten-stone
Water roll cast light, the burr stayed when removing system button and cutter foot unequal phenomenon.
Product inspection: reject defective button blank.
Polishing (cleaning): pour button blank into dry milling buffing machine, polish further, to reach
The luminosity needed, then by ultrasonic waves for cleaning, remove the dust on button surface and unnecessary burnishing oil, with
Increase paint fastness, finally obtain the button blank after polishing.
Surface 3D prints operation: first weigh the fatty acid modified epoxy acrylate of B-5292X 20%,
TU-4500 aliphatic urethane acrylate 10%, BYK35100.5%, BYK3330.2%, three hydroxyls
Propane tri 10%, tripropylene glycol diacrylate fat 30%, benzophenone 5%, hexichol second
Diketone 5%, methyl diethanolamine 2% and magenta pigment, obtain light-cured resin after mixing；Re-use
Above-mentioned light-cured resin is beaten on button surface by picture proof by printer, uses LED uviol lamp to carry out solid simultaneously
Change.
Spray treatment behind surface: the button after printing carries out epoxy-based lacquers spray coating.
Baking processes: toasted by the button after spraying, temperature 60 degrees Celsius, 60 minutes time,
The sold resin bar button of surface magenta pattern is obtained after lower button.
The sold resin bar button of the surface magenta pattern preparing embodiment 1 detects,
Test result indicate that, see the outward appearance of the printout surface button that Fig. 2, Fig. 2 are the embodiment of the present invention 1 preparation
Photo, as shown in Figure 2, the sold resin bar button of surface magenta pattern prepared by the present invention, phase
Ratio laser engraving button, has stereoeffect equally, but also has the effect of changeable color, meanwhile,
There is not button and burnt the defect of Huang, it is possible to be applied to low melting point button material.
See the outward appearance photo that Fig. 1, Fig. 1 are laser engraving button prepared by prior art, as shown in Figure 1,
Laser engraving button prepared by prior art is in the phenomenon of the marginal existence lighter of three-dimensional font, and this is
Due to the high temperature of laser, thus font edge is caused to occur being burnt yellow defect.
Embodiment 2
Blank-making technology: add 8ml cobalt salt in 1.0kg unsaturated-resin and stir, then add
10ml methyl ethyl ketone peroxide and 20ml styrene, carry out making sheet through centrifuge after stirring, after making sheet
Blank is taken under carrying out being carried out by blanking machine.
System button technique: first pass through deduction processed and button blank is made the shape of button, can be according to different
Examine that requirement carries out moulding.
Just polishing: the button blank worked it out by deduction processed, is poured in buffing machine, is carried out by rotten-stone
Water roll cast light, the burr stayed when removing system button and cutter foot unequal phenomenon.
Product inspection: reject defective button blank.
Polishing (cleaning): pour button blank into dry milling buffing machine, polish further, to reach
The luminosity needed, then by ultrasonic waves for cleaning, remove the dust on button surface and unnecessary burnishing oil, with
Increase paint fastness, finally obtain the button blank after polishing.
Surface 3D prints operation: first weigh the fatty acid modified epoxy acrylate of B-5292X 22%,
TU-4500 aliphatic urethane acrylate 8%, BYK35100.5%, BYK3330.2%, three hydroxyl first
Base propane triacrylate 12%, tripropylene glycol diacrylate fat 29%, benzophenone 4%, hexichol second two
Ketone 5%, methyl diethanolamine 2% and gorgeous blue pigment, obtain light-cured resin after mixing；Re-use and beat
Above-mentioned light-cured resin is beaten on button surface by picture proof by print machine, uses LED uviol lamp to solidify simultaneously.
Spray treatment behind surface: the button after printing carries out epoxy-based lacquers spray coating.
Baking processes: toasted by the button after spraying, temperature 60 degrees Celsius, 60 minutes time,
The sold resin sheet material button of gorgeous blue pattern is obtained after lower button.
The sold resin sheet material button of the surface gorgeous blue pattern preparing embodiment 2 detects,
Test result indicate that, see the outward appearance of the printout surface button that Fig. 2, Fig. 2 are the embodiment of the present invention 1 preparation
Photo, as shown in Figure 2, the sold resin sheet material button of surface gorgeous blue pattern prepared by the present invention, phase
Ratio laser engraving button, has stereoeffect equally, but also has the effect of changeable color, meanwhile,
There is not button and burnt the defect of Huang, it is possible to be applied to low melting point button material.
Embodiment 3
Blank-making technology: add 9ml cobalt salt in 1.0kg unsaturated-resin and stir, then add
10ml methyl ethyl ketone peroxide and 20ml styrene, carry out making sheet through centrifuge after stirring, after making sheet
Blank is taken under carrying out being carried out by blanking machine.
System button technique: first pass through deduction processed and button blank is made the shape of button, can be according to different
Examine that requirement carries out moulding.
Just polishing: the button blank worked it out by deduction processed, is poured in buffing machine, is carried out by rotten-stone
Water roll cast light, the burr stayed when removing system button and cutter foot unequal phenomenon.
Product inspection: reject defective button blank.
Polishing (cleaning): pour button blank into dry milling buffing machine, polish further, to reach
The luminosity needed, then by ultrasonic waves for cleaning, remove the dust on button surface and unnecessary burnishing oil, with
Increase paint fastness, finally obtain the button blank after polishing.
Coating process: use vacuum ion plating that button is carried out plated film.
Radium art: use laser machine to carry out the local laser in plated film district.
Again clean: use the radium-shine dust caused of ultrasonic waves for cleaning.
Surface 3D prints operation: first weigh the fatty acid modified epoxy acrylate of B-5292X 22%,
TU-4500 aliphatic urethane acrylate 9%, BYK35100.5%, BYK3330.2%, three hydroxyl first
Base propane triacrylate 11%, tripropylene glycol diacrylate fat 28%, benzophenone 5%, hexichol second two
Ketone 5%, methyl diethanolamine 2% and mineral black, obtain light-cured resin after mixing；Re-use printing
Above-mentioned light-cured resin is beaten on button surface by picture proof by machine, uses LED uviol lamp to solidify simultaneously.
Spray treatment behind surface: the button after printing carries out epoxy-based lacquers spray coating.
Baking processes: toasted by the button after spraying, temperature 60 degrees Celsius, 60 minutes time,
The sold resin plated film button of black pattern is obtained after lower button.
Above the preparation method of a kind of printout surface button provided by the present invention is described in detail.
Principle and the embodiment of the present invention are set forth by individual example specifically used herein, above enforcement
The explanation of example is only intended to help to understand method and the core concept thereof of the present invention.It should be pointed out that, for this
For the those of ordinary skill of technical field, under the premise without departing from the principles of the invention, it is also possible to this
Invention carries out some improvement and modification, and these improve and modify the protection model also falling into the claims in the present invention
In enclosing.
Claims (10)
1. the preparation method of a printout surface button, it is characterised in that comprise the following steps:
A) after the button printout surface light-cured resin after oil removal treatment, semi-finished product are obtained；
B), after being solidified by the semi-finished product that above-mentioned steps obtains, printout surface button is obtained.
Preparation method the most according to claim 1, it is characterised in that described light-cured resin includes
Fatty acid modified epoxy acrylate, aliphatic urethane acrylate, trimethylolpropane tris acrylic acid
Ester, tripropylene glycol diacrylate fat, auxiliary agent and pigment.
Preparation method the most according to claim 2, it is characterised in that described auxiliary agent include firming agent,
Diluent and dispersant.
Preparation method the most according to claim 1, it is characterised in that described in print to 3D print；
Described it is cured as ultraviolet curing.
Preparation method the most according to claim 1, it is characterised in that described button be resin button,
One or many in carbamide button, Cornu Bovis seu Bubali button, injection button, true shellfish button and metal plating class button
Kind.
Preparation method the most according to claim 1, it is characterised in that described step B) the most also
Including,
C) after the surface spraying varnish of above-mentioned printout surface button, dry and obtain finished surface engraving button.
Preparation method the most according to claim 6, it is characterised in that described spraying is spray gun spraying,
The described bore sprayed paint is 1.1～1.3mm.
Preparation method the most according to claim 6, it is characterised in that described drying is that drying tunnel is dried,
The temperature of described drying is 60～90 DEG C, and the time of described drying is 50～60 minutes.
Preparation method the most according to claim 6, it is characterised in that described varnish is mixed with resin
Paint.
Preparation method the most according to claim 9, it is characterised in that described mixed with resin paint by
The main paint of resin, firming agent and diluent composition；
The mass percent of the main paint of described resin, firming agent and diluent is (90～110): (20～50):
(50～600).