CN105970729B - A kind of infiltration solidification processing method of pseudo-classic book - Google Patents
A kind of infiltration solidification processing method of pseudo-classic book Download PDFInfo
- Publication number
- CN105970729B CN105970729B CN201610305438.XA CN201610305438A CN105970729B CN 105970729 B CN105970729 B CN 105970729B CN 201610305438 A CN201610305438 A CN 201610305438A CN 105970729 B CN105970729 B CN 105970729B
- Authority
- CN
- China
- Prior art keywords
- book
- infiltration
- temperature
- silver
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of infiltration solidification processing method of pseudo-classic book, and steps are as follows:In confined space, book is infiltrated after immersion fluid is atomized;Book after infiltration is placed in confined space and carries out curing process, increase the pressure in confined space to 1.5 times of atmospheric pressure, be placed in the environment of supersonic frequency 35kHz, power 85W and handle 30min, while utilizing steam moisturizing in confined space, relative humidity is maintained at 68%, and temperature is 46 DEG C.The present invention infiltrates book using immersion fluid, and the paper of immersion fluid and book is combined together by solidification means, increases the age sense of book, to produce pseudo-classic book, book paper surface yellowing is not faded, paper is more soft, and the age sense to people is stronger;It is corrosion-resistant.
Description
Technical field
The present invention relates to book production technical field more particularly to a kind of infiltration solidification processing methods of pseudo-classic book.
Background technology
Book or books are always a kind of carrier that very important knowledge is recorded and propagated, in the collection and transaction of antiques
Always there is a book, when Southern Song Dynasty has just occurred.Ancient book usually carries precious and wisdom emotion.Although modern book printing and
Binding technique is more than ancient times prosperity, but in order to meet some particular demands, can still produce some books for carrying pseudo-classic style
Volume, such as picture book, swordsman's class strip cartoon usually occur with the book of pseudo-classic style.Further for example, about Writing brush calligraphy, ancient poetry
The book with dense ancient culture such as word, distich also has much book appearance with pseudo-classic style.So how to utilize modern work
Industry production technology produces the book with pseudo-classic style, is the application problem to be solved.
Invention content
The purpose of the present invention is to provide a kind of infiltration solidification processing methods of pseudo-classic book, are asked with solving above-mentioned technology
Topic.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of infiltration solidification processing method of pseudo-classic book, which is characterized in that steps are as follows:
In confined space, book is infiltrated after immersion fluid is atomized, the immersion fluid by following parts by weight original
Material is made:10 parts of green tea, 500 parts of water, 0.2 part of emulsifier, 1.2 parts of silicon dioxide powder, carries silver-bearing copper silica gel 1.5 at 3 parts of smoke tar
Part, wherein silicon dioxide powder particle diameter distribution is between 1~25 micron;Carry silver-bearing copper silica gel be using silica gel be carrier adsorption copper ion with
Silver ion, copper content 2.0%, silver content 1.5%;
Book after infiltration is placed in confined space and carries out curing process, increases the pressure in confined space to 1.5 times
Atmospheric pressure is placed in processing 30mi n in the environment of supersonic frequency 35kHz, power 85W, while being protected using steam in confined space
Wet, relative humidity is maintained at 68%, and temperature is 46 DEG C.
Preferably, the steam used in steam moisturizing is mixed by water vapour and alcohol vapour, water vapour and ethyl alcohol
The volume ratio of steam mixing is 100:0.15.
Preferably, the preparation method of the immersion fluid is:Continuous heating in container is added water to, water temperature reaches 65 DEG C
When, green tea is added, stirring makes green tea be totally submerged in water;When water temperature reaches 90 DEG C, 6.5 hours are kept the temperature;Filtering, takes filtrate,
When temperature is down to 35-45 DEG C, emulsifier is added, stirring makes emulsifier be dispersed in filtrate, adds smoke tar, stirring makes
Smoke tar is dispersed in filtrate, is added silicon dioxide powder and is carried silver-bearing copper silica gel, is sufficiently stirred, makes silicon dioxide powder and load
Silver-bearing copper silica gel is uniformly dispersed in filtrate to get immersion fluid.
Infiltration processing is carried out to book,
The margin of pending book is clamped with clip, then book is suspended in infiltration by clip, between infiltration
It is a closed room, is provided in infiltration and persistently changes nyctitropic air outlet in the horizontal plane, air outlet is in vertical side
It is located at the lower section of book upwards, for air outlet against book, infiltration is interior to be additionally provided with atomizing humidifier, adds after immersion fluid is atomized
Air in immersion profit, it is 80-85% to keep the relative humidity in infiltration, and temperature is 52-55 DEG C, air outlet intensity
Book paper can be stirred by being subject to, and infiltration processing time is 7-9 hours;
It is dried after curing process,
Book is placed in hothouse, is dried using hot wind, hot blast temperature is 75-85 DEG C, drying time 0.5-2
Hour.
The beneficial effects of the invention are as follows:
The present invention infiltrates book using immersion fluid, and by solidification means by the paper of immersion fluid and book melt for
One increases the age sense of book, and to produce pseudo-classic book, book paper surface yellowing is not faded, paper is more soft
Soft, the age sense to people is stronger;It is corrosion-resistant.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained, but following embodiments are only the preferred embodiment of the present invention, and not all.
Based on the implementation example in the implementation mode, those skilled in the art's obtained other realities without making creative work
Example is applied, protection scope of the present invention is belonged to.
A kind of method that book increases pseudo-classic sense, steps are as follows:
Step 1 carries out infiltration processing to book,
The margin of pending book is clamped with clip, then book is suspended in infiltration by clip, between infiltration
It is a closed room, is provided in infiltration and persistently changes nyctitropic air outlet in the horizontal plane, air outlet is in vertical side
It is located at the lower section of book upwards, for air outlet against book, infiltration is interior to be additionally provided with atomizing humidifier, adds after immersion fluid is atomized
Air in immersion profit, it is 80-85% to keep the relative humidity in infiltration, and temperature is 52-55 DEG C, air outlet intensity
Book paper can be stirred by being subject to, and infiltration processing time is 7-9 hours;
The immersion fluid is made of the raw material of following parts by weight:10 parts of green tea, 3 parts of smoke tar, 500 parts of water, emulsifier 0.2
Part, carries 1.5 parts of silver-bearing copper silica gel at 1.2 parts of silicon dioxide powder, and wherein silicon dioxide powder particle diameter distribution is between 1~25 micron;Carry silver
Copper silica gel is copper content 2.0%, silver content 1.5% using silica gel as carrier adsorption copper ion and silver ion;Preparation method
For:Continuous heating in container is added water to, when water temperature reaches 65 DEG C, green tea is added, stirring makes green tea be totally submerged in water;Water
When temperature reaches 90 DEG C, 6.5 hours are kept the temperature;Filtering, takes filtrate, when temperature is down to 35-45 DEG C, emulsifier is added, stirring makes emulsification
Agent is dispersed in filtrate, adds smoke tar, and stirring makes smoke tar be dispersed in filtrate, adds silicon dioxide powder
It with load silver-bearing copper silica gel, is sufficiently stirred, silicon dioxide powder and load silver-bearing copper silica gel is made to be uniformly dispersed to get immersion fluid in filtrate;
Step 2, curing process,
Book after infiltration is placed in confined space, 1.5 times of atmospheric pressure is pressurized to, is placed in supersonic frequency 35kHz, work(
30mi n are handled in the environment of rate 85W, while utilizing steam moisturizing in confined space, and relative humidity is maintained at 68%, and temperature is
46℃;
Step 3 is dried,
Book is placed in hothouse, is dried using hot wind, hot blast temperature is 75-85 DEG C, drying time 0.5-2
Hour.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, described in the above embodiment and specification is only the present invention
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also has various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (1)
1. a kind of infiltration solidification processing method of pseudo-classic book, which is characterized in that steps are as follows:
Step 1 carries out infiltration processing to book,
The margin of pending book is clamped with clip, and then book is suspended in infiltration by clip, is one between infiltration
A closed room, interior be provided with of infiltration persistently change nyctitropic air outlet in the horizontal plane, and air outlet is in the vertical direction
Positioned at the lower section of book, for air outlet against book, infiltration is interior to be additionally provided with atomizing humidifier, and leaching is humidified after immersion fluid is atomized
Air in profit, it is 80-85% to keep the relative humidity in infiltration, and temperature is 52-55 DEG C, and air outlet intensity is with energy
Subject to book paper is stirred, infiltration processing time is 7-9 hours;
The immersion fluid is made of the raw material of following parts by weight:10 parts of green tea, 3 parts of smoke tar, 500 parts of water, 0.2 part of emulsifier,
1.2 parts of silicon dioxide powder carries 1.5 parts of silver-bearing copper silica gel, and wherein silicon dioxide powder particle diameter distribution is between 1~25 micron;Carry silver-bearing copper
Silica gel is copper content 2.0%, silver content 1.5% using silica gel as carrier adsorption copper ion and silver ion;Preparation method is:
Continuous heating in container is added water to, when water temperature reaches 65 DEG C, green tea is added, stirring makes green tea be totally submerged in water;Water temperature
When reaching 90 DEG C, 6.5 hours are kept the temperature;Filtering, takes filtrate, when temperature is down to 35-45 DEG C, emulsifier is added, stirring makes emulsifier
Be dispersed in filtrate, add smoke tar, stirring makes smoke tar be dispersed in filtrate, add silicon dioxide powder and
Silver-bearing copper silica gel is carried, is sufficiently stirred, silicon dioxide powder and load silver-bearing copper silica gel is made to be uniformly dispersed to get immersion fluid in filtrate;
Step 2, curing process,
Book after infiltration is placed in confined space, 1.5 times of atmospheric pressure is pressurized to, is placed in supersonic frequency 35kHz, power
30min is handled in the environment of 85W, while utilizing steam moisturizing in confined space, and relative humidity is maintained at 68%, temperature 46
℃;
Step 3 is dried,
Book is placed in hothouse, is dried using hot wind, hot blast temperature is 75-85 DEG C, and drying time is that 0.5-2 is small
When.