CN105970665A - Automobile TPU instrument board leather and preparing method thereof - Google Patents

Automobile TPU instrument board leather and preparing method thereof Download PDF

Info

Publication number
CN105970665A
CN105970665A CN201610380961.9A CN201610380961A CN105970665A CN 105970665 A CN105970665 A CN 105970665A CN 201610380961 A CN201610380961 A CN 201610380961A CN 105970665 A CN105970665 A CN 105970665A
Authority
CN
China
Prior art keywords
tpu
instrument board
leather
automobile
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610380961.9A
Other languages
Chinese (zh)
Inventor
高金岗
王俊峰
周健
韩立业
李超
高义辉
裴莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Ruigao New Materials Co Ltd
Original Assignee
Suzhou Ruigao New Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Ruigao New Materials Co Ltd filed Critical Suzhou Ruigao New Materials Co Ltd
Priority to CN201610380961.9A priority Critical patent/CN105970665A/en
Publication of CN105970665A publication Critical patent/CN105970665A/en
Pending legal-status Critical Current

Abstract

The invention discloses an automobile TPU instrument board leather and a preparing method thereof. The TPU instrument board leather comprises PP foam and a TPU film coating one surface of the PP foam. The preparing method of the TPU instrument board leather comprises the following steps of 1, TPU extrusion molding processing, wherein by mass, 80-95 parts of thermoplastic polyurethane is dried at 90 DEG C and then mixed with 5-10 parts of a coloring agent and 0-20 parts of an additive at 120-200 DEG C, and then a sheet base material is formed through extrusion molding with an extruding machine; 2, preparation of the TPU film; 3, coating and rolling; 4, surface absorbing line treatment; 5, modification treatment. In this way, TPU replaces traditional polyvinyl chloride, operation and implementation are easy, the prepared automobile TPU instrument board leather has the excellent comprehensive performance of being high in hardness, antistatic, odorless, resistant to aging and the like, and the use requirement of high-end automobile instrument board leather can be met.

Description

A kind of automobile TPU instrument board leather and preparation method thereof
Technical field
The present invention relates to synthetic leather manufacturing technology field, particularly relate to a kind of automobile TPU instrument board leather and preparation method thereof.
Background technology
Instrument board is the topmost inside gadget of automobile, and at present in addition to a small amount of employing metal manufactures, almost all is made of plastic.
Polrvinyl chloride, owing to price is low, low cost of manufacture, is widely used in the manufacture of fascia leather.Polrvinyl chloride includes RPVC and soft PVC.The feature of both materials is respectively as follows: (1) RPVC: relative density is 1.38～1.43kg/m3, about the 1/5 of steel weight, mechanical strength is high, and electrical property is excellent, extremely strong to soda acid resistance, chemical stability is fine, and thermostability is low, linear expansion coefficient is bigger, but the shortcoming of RPVC material is poor heat stability, the degraded that can cause in various degree of being heated.(2) soft PVC: add substantial amounts of plasticizer in component, it is possible to prepare soft and limber soft polrvinyl chloride processed, due to the addition of plasticizer, make the plasticity of plastics, flexibility increase, but make mechanical properties decrease.Therefore soft PVC strain sensitive, can not restore after deformation completely, and its thermostability is more worse than RPVC, and becomes fragile when low temperature.
Therefore, it is badly in need of researching and developing a kind of there is the material of Good All-around Property to substitute polrvinyl chloride, meets the use requirement of high-end fascia leather.
Summary of the invention
Present invention mainly solves technical problem is that: for the deficiencies in the prior art, it is provided that a kind of automobile TPU instrument board leather and preparation method thereof, can solve the defect existing for existing polrvinyl chloride instrument board leather.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of automobile TPU instrument board leather and preparation method thereof, described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 80-95 mass parts, then at 120-200 DEG C, coloring agent, the additive of 0-20 mass parts with 5-10 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 1-5MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.1-0.3mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have a coating surface inorganic agent of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying, obtain finished product synthetic leather.
In a preferred embodiment of the present invention, in described step (1), described coloring agent is color masterbatch or toner.
In a preferred embodiment of the present invention, in described step (1), described additive includes fire retardant, antistatic additive, age resister and hydrolysis agent.
In a preferred embodiment of the present invention, in described step (5), described surface conditioning agent includes antistatic additive and age resister.
In a preferred embodiment of the present invention, in described step (5), described drying temperature is 90-120 DEG C.
The invention has the beneficial effects as follows: the present invention uses TPU to substitute traditional polrvinyl chloride, simple to operate, easily realize, the TPU instrument board leather prepared has high rigidity, antistatic, odorlessness, the Good All-around Property such as ageing-resistant, it is possible to meet the use requirement of high-end fascia leather.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
Embodiment one:
A kind of automobile TPU instrument board leather and preparation method thereof, described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 80 mass parts, then at 120 DEG C, color masterbatch, the fire retardant of 3% mass parts, 2% antistatic additive and 3% age resister with 5 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 1MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.1mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have one side coating antistatic additive and the age resister of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying at 90 DEG C, obtain high rigidity, antistatic, odorlessness, ageing-resistant finished automotive TPU instrument board leather.
Embodiment two:
A kind of automobile TPU instrument board leather and preparation method thereof, described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 95 mass parts, then at 160 DEG C, color masterbatch, the fire retardant of 1% mass parts, 1% antistatic additive and 1% age resister with 5 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 3MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.2mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have one side coating antistatic additive and the age resister of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying at 90 DEG C, obtain high rigidity, antistatic, odorlessness, ageing-resistant finished automotive TPU instrument board leather.
Embodiment three:
A kind of automobile TPU instrument board leather and preparation method thereof, described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 85 mass parts, then at 200 DEG C, toner, the fire retardant of 3% mass parts, 5% antistatic additive and 5% age resister with 5 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 5MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.3mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have one side coating antistatic additive and the age resister of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying at 100 DEG C, obtain high rigidity, antistatic, odorlessness, ageing-resistant finished automotive TPU instrument board leather.
Embodiment four:
A kind of automobile TPU instrument board leather and preparation method thereof, described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 80 mass parts, then at 200 DEG C, toner, the fire retardant of 6% mass parts, 6% antistatic additive and 4% age resister with 10 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 3MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.2mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have one side coating antistatic additive and the age resister of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying at 120 DEG C, obtain high rigidity, antistatic, odorlessness, ageing-resistant finished automotive TPU instrument board leather.
Present invention is disclosed a kind of automobile TPU instrument board leather and preparation method thereof, TPU is used to substitute traditional polrvinyl chloride, simple to operate, easily realize, the TPU instrument board leather prepared has high rigidity, antistatic, odorlessness, the Good All-around Property such as ageing-resistant, it is possible to meet the use requirement of high-end fascia leather.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical fields, the most in like manner it is included in the scope of patent protection of the present invention.

Claims (5)

1. automobile TPU instrument board leather and preparation method thereof, it is characterised in that described TPU instrument board leather includes that PP foam and the plastic-coated TPU membrane on described PP foam one surface, the preparation method of described TPU instrument board leather comprise the steps:
(1) extrusion processing of TPU:
Being dried at 90 DEG C by the thermoplastic polyurethane of 80-95 mass parts, then at 120-200 DEG C, coloring agent, the additive of 0-20 mass parts with 5-10 mass parts mixes, then is extruded into flat substrates through extruder；
(2) preparation of TPU membrane:
Adjust extruder gap, with the pressure of 1-5MPa, above-mentioned prepared flat substrates is made the thickness TPU membrane as 0.1-0.3mm；
(3) plastic-coated, rolling:
By above-mentioned prepared TPU membrane plastic-coated on PP foam one surface, after cooling, obtain primary synthetic leather；
(4) suction stricture of vagina in surface processes:
Use the surface suppressing primary synthetic leather with textured roller under vacuum conditions, it is thus achieved that there is the intermediate synthetic leather of clear textured pattern；
(5) modification:
Use roll coating model to have a coating surface inorganic agent of textured pattern to above-mentioned prepared intermediate synthetic leather, after drying, obtain finished product synthetic leather.
Automobile TPU instrument board leather the most according to claim 1 and preparation method thereof, it is characterised in that in described step (1), described coloring agent is color masterbatch or toner.
Automobile TPU instrument board leather the most according to claim 1 and preparation method thereof, it is characterised in that in described step (1), described additive includes fire retardant, antistatic additive, age resister and hydrolysis agent.
Automobile TPU instrument board leather the most according to claim 1 and preparation method thereof, it is characterised in that in described step (5), described surface conditioning agent includes antistatic additive and age resister.
Automobile TPU instrument board leather the most according to claim 1 and preparation method thereof, it is characterised in that in described step (5), described drying temperature is 90-120 DEG C.
CN201610380961.9A 2016-06-01 2016-06-01 Automobile TPU instrument board leather and preparing method thereof Pending CN105970665A (en)