CN105970627A - Anti-oil fabric of down jacket and manufacturing technique thereof - Google Patents
Anti-oil fabric of down jacket and manufacturing technique thereof Download PDFInfo
- Publication number
- CN105970627A CN105970627A CN201610568212.9A CN201610568212A CN105970627A CN 105970627 A CN105970627 A CN 105970627A CN 201610568212 A CN201610568212 A CN 201610568212A CN 105970627 A CN105970627 A CN 105970627A
- Authority
- CN
- China
- Prior art keywords
- oil
- fabric
- proofing agent
- water
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides an anti-oil fabric of a down jacket and a manufacturing technique thereof and relates to the technical field of down jacket processing. The anti-oil fabric comprises a fabric layer main body, wherein the fabric layer main body is processed by taking warps and wefts according to the present textile technique; the surfaces of the warps and wefts are coated with an anti-oil agent; and the anti-oil agent is composed of the following components in parts by weight: 30-50 parts of perfluoroalkyl acrylate copolymers, 5-15 parts of vinylite, 5-15 parts of butyl methacrylate, 10-20 parts of polyvinylidene chloride and 30-50 parts of water. The anti-oil property of the present down jacket is improved, the cleaning frequency is reduced, and the service life of the down jacket is greatly prolonged.
Description
Technical field
The present invention relates to down jackets processing technique field, be specifically related to a kind of down jackets Oilproof fabric and processing technology thereof.
Background technology
Filling the jacket of eider down filler in down jackets, profile is huge mellow and full.Down jackets general duck's down amount accounts for more than half, simultaneously
Can mix some tiny feathers, be cleaned up by duck's down, through high-temperature sterilization, being filled in afterwards in clothes is exactly down jackets
?.Down jackets warmth retention property is best.It mostly is people's dress of cold district, is also commonly used by polar expedition personnel.
Implant in down jackets, is most commonly that goose down and duck's down, and both is divided by color, can be divided into again white floss and ash
Floss.From the point of view of down jackets on the market are according to price, be ordered as: white goose down grey goose down > white duck down > grey duck down.May be sold
The impact of valency sequence, therefore a lot of people are considered as these flosss is also so sequence in quality, and actually this is not so.By to eider down side
The theoretical research in face and real experiences, in general the goose down of equal in quality and down content is than the warmth retention property of duck's down, loft etc.
Quite a lot of.
Floss and feather is comprised inside down jackets.Floss is that the long neck aquatic birds such as goose ducks obstructs without plumage between chest and abdomen
Hair, owing to the hair at this position is often soaked in water, so not only having certain water proofing property, and its warming cold-resistant energy
Power is also best in whole body hair.It addition, because the fine hair at this position does not has plumage to obstruct, the most soft, fiber length and loft is high,
Equivalent small volume, is to make down jackets material of the highest excellence.Feather in down jackets, refer to except fine hair described above it
The hair at other positions on outer whole body, is usually in the form of sheets, and centre has plumage to obstruct.The thermal ressistance of feather is relatively limited, does not has fine hair good.
Loft is the important indicator measuring down thermal degree in the world, refers to the most each ounce
The numerical value of volume cubic inch shared by (30 grams) eider down.Such as, the space shared by the eider down of an ounce be 600 cubic inches then
The loft of this eider down is called 600.It is said that in general, fertile, ripe birds, the loft of its eider down is high, on the contrary, and little birds
Loft is relatively low.
Owing to down jackets often cleaning can cause its thermal property to decline, it is therefore necessary to improve the performance that bears dirty of its fabric.
Summary of the invention
Present invention aims to defect and the deficiency of prior art, it is provided that a kind of simple in construction, reasonable in design
Down jackets Oilproof fabric and processing technology thereof, improve current feather dress fabric oil preventing performance, reduces cleaning rate, is greatly prolonged eider down
The service life of clothes.
For achieving the above object, the technical solution used in the present invention is: it comprises precoat body;Described precoat is originally
Body is processed according to existing textile technology by through parallel;The described surface through parallel is coated with oil-proofing agent;Described is grease proofing
Agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 30-50 part, vinylite 5-15 part, metering system
Acid butyl ester 5-15 part, Vingon 10-20 part, water 30-50 part.
Described oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 40-50 part, vinyl tree
Fat 10-15 part, butyl methacrylate 10-15 part, Vingon 15-20 part, water 40-50 part.
Oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 45-50 part, vinylite 12-
15 parts, butyl methacrylate 12-15 part, Vingon 15-20 part, water 45-50 part.
Its processing process is as follows:
One, the textile fabric needed for parallel is immersed in by fluoroalkyl copolymer 30-50 part, vinylite 5-
15 parts, butyl methacrylate 5-15 part, Vingon 10-20 part, water 30-50 part composition oil-proofing agent in, soak 24-
36h, soaking temperature is 30-50 DEG C;
Two, being pulled out by the textile fabric soaking oil-proofing agent and drain away the water, send in baking oven and dry, drying temperature is 100-150
DEG C, drying time is 10-12h;
Three, the textile fabric after drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
The operation principle of the present invention: by the raw material of feather dress fabric is entered in oil-proofing agent, make raw material appearance and
Inside is all mutually merged with oil-proofing agent, improves the grease proofing effect of finished product.
Present invention have the beneficial effect that a kind of down jackets Oilproof fabric of the present invention and processing technology thereof, improve at present
Feather dress fabric oil preventing performance, reduces cleaning rate, is greatly prolonged the service life of down jackets, and the present invention has simple in construction, if
Put rationally, the advantages such as cost of manufacture is low.
Detailed description of the invention
This detailed description of the invention (embodiment one) the technical scheme is that it comprises precoat body;Described fabric
Layer body is processed according to existing textile technology by through parallel;The described surface through parallel is coated with oil-proofing agent;Described
Oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 30-50 part, vinylite 5-15 part, methyl
Butyl acrylate 5-15 part, Vingon 10-20 part, water 30-50 part.
Its processing process is as follows:
One, the textile fabric needed for parallel is immersed in by fluoroalkyl copolymer 30-50 part, vinylite 5-
15 parts, butyl methacrylate 5-15 part, Vingon 10-20 part, water 30-50 part composition oil-proofing agent in, soak 24h,
Soaking temperature is 50 DEG C;
Two, being pulled out by the textile fabric soaking oil-proofing agent and drain away the water, send in baking oven and dry, drying temperature is 120 DEG C, dries
The dry time is 10h;
Three, the textile fabric after drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
The operation principle of this detailed description of the invention: by being entered in oil-proofing agent by the raw material of feather dress fabric, make raw material
Appearance and inside all mutually merge with oil-proofing agent, improve finished product grease proofing effect.
This detailed description of the invention has the beneficial effect that a kind of down jackets Oilproof fabric described in this detailed description of the invention and system thereof
Make technique, improve current feather dress fabric oil preventing performance, reduce cleaning rate, be greatly prolonged the service life of down jackets, the present invention
There is simple in construction, arrange rationally, the advantages such as cost of manufacture is low
Embodiment two:
The present embodiment the technical scheme is that it comprises precoat body;Described precoat body by through parallel according to existing
Textile technology is had to process;The described surface through parallel is coated with oil-proofing agent;Described oil-proofing agent is become by following weight portion
It is grouped into: described oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 40-50 part, vinyl tree
Fat 10-15 part, butyl methacrylate 10-15 part, Vingon 15-20 part, water 40-50 part.
Its processing process is as follows:
One, the textile fabric needed for parallel is immersed in it is made up of following parts by weight ingredient described oil-proofing agent: fluoroalkyl
Acrylate copolymer 40-50 part, vinylite 10-15 part, butyl methacrylate 10-15 part, Vingon 15-20
In the oil-proofing agent that part, water 40-50 part form, soaking 30h, soaking temperature is 30 DEG C;
Two, being pulled out by the textile fabric soaking oil-proofing agent and drain away the water, send in baking oven and dry, drying temperature is 150 DEG C, dries
The dry time is 10h;
Three, the textile fabric after drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
Embodiment three:
The present embodiment the technical scheme is that it comprises precoat body;Described precoat body by through parallel according to existing
Textile technology is had to process;The described surface through parallel is coated with oil-proofing agent;Described oil-proofing agent is become by following weight portion
It is grouped into: oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 45-50 part, vinylite 12-15
Part, butyl methacrylate 12-15 part, Vingon 15-20 part, water 45-50 part.
Its processing process is as follows:
One, the textile fabric needed for parallel is immersed in it is made up of following parts by weight ingredient oil-proofing agent: perfluoroalkyl acrylic
Ester copolymer 45-50 part, vinylite 12-15 part, butyl methacrylate 12-15 part, Vingon 15-20 part, water
In the oil-proofing agent of 45-50 part composition, soaking 36h, soaking temperature is 40 DEG C;
Two, being pulled out by the textile fabric soaking oil-proofing agent and drain away the water, send in baking oven and dry, drying temperature is 130 DEG C, dries
The dry time is 12h;
Three, the textile fabric after drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
Embodiment four:
The present embodiment the technical scheme is that it comprises precoat body;Described precoat body by through parallel according to existing
Textile technology is had to process;The described surface through parallel is coated with oil-proofing agent;Described oil-proofing agent is become by following weight portion
It is grouped into: oil-proofing agent is made up of following parts by weight ingredient: fluoroalkyl copolymer 50 parts, vinylite 15 parts, first
Base butyl acrylate 15 parts, Vingon 15 parts, 40 parts of water.
Its processing process is as follows:
One, the textile fabric needed for parallel is immersed in it is made up of following parts by weight ingredient oil-proofing agent: perfluoroalkyl acrylic
Preventing of ester copolymer 50 parts, vinylite 15 parts, butyl methacrylate 15 parts, Vingon 15 parts, 40 parts of water composition
In oil preparation, soaking 36h, soaking temperature is 45 DEG C;
Two, being pulled out by the textile fabric soaking oil-proofing agent and drain away the water, send in baking oven and dry, drying temperature is 140 DEG C, dries
The dry time is 10h;
Three, the textile fabric after drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
The above, only in order to technical scheme to be described and unrestricted, those of ordinary skill in the art are to this
Other amendment or equivalent that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
All should contain in the middle of scope of the presently claimed invention.
Claims (4)
1. a down jackets Oilproof fabric, it comprises precoat body;Described precoat body is spun according to existing by through parallel
Weaving process processes;The described surface through parallel is coated with oil-proofing agent;It is characterized in that: described oil-proofing agent is by weighing as follows
Amount part becomes to be grouped into: fluoroalkyl copolymer 30-50 part, vinylite 5-15 part, butyl methacrylate 5-15
Part, Vingon 10-20 part, water 30-50 part.
2. the processing technology of a down jackets Oilproof fabric, it is characterised in that: its processing process is as follows:
(1), the textile fabric needed for parallel is immersed in by fluoroalkyl copolymer 30-50 part, vinylite
In the oil-proofing agent that 5-15 part, butyl methacrylate 5-15 part, Vingon 10-20 part, water 30-50 part form, soak 24-
36h, soaking temperature is 30-50 DEG C;
(2), by the textile fabric soaking oil-proofing agent pulling out and drain away the water, send in baking oven and dry, drying temperature is 100-
150 DEG C, drying time is 10-12h;
(3) textile fabric after, drying is sent in fabric machining production line and is processed into fabric, finally according to template cutting, i.e.
?.
A kind of down jackets Oilproof fabric the most according to claim 1, it is characterised in that: described oil-proofing agent is by following weight
Part becomes to be grouped into: fluoroalkyl copolymer 40-50 part, vinylite 10-15 part, butyl methacrylate 10-15
Part, Vingon 15-20 part, water 40-50 part.
A kind of down jackets Oilproof fabric the most according to claim 1, it is characterised in that: oil-proofing agent is by following parts by weight ingredient
Composition: fluoroalkyl copolymer 45-50 part, vinylite 12-15 part, butyl methacrylate 12-15 part, poly-partially
Vinyl chloride 15-20 part, water 45-50 part.