CN105970332A - Antiseptic and deodorant titanium polypropylene fiber and manufacturing method thereof - Google Patents
Antiseptic and deodorant titanium polypropylene fiber and manufacturing method thereof Download PDFInfo
- Publication number
- CN105970332A CN105970332A CN201610503263.3A CN201610503263A CN105970332A CN 105970332 A CN105970332 A CN 105970332A CN 201610503263 A CN201610503263 A CN 201610503263A CN 105970332 A CN105970332 A CN 105970332A
- Authority
- CN
- China
- Prior art keywords
- titanium
- polypropylene
- polypropylene fiber
- mesh
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antiseptic and deodorant titanium polypropylene fiber and a manufacturing method thereof and belongs to the technical field of textile. The antiseptic and deodorant titanium polypropylene fiber comprises a fiber body and is characterized in that the fiber body is composed of liquefied titanium masterbatch and polypropylene slice through fusing and mixing. The manufacturing method is characterized by including: mixing and stirring well the liquefied titanium masterbatch and the polypropylene slice according to a weight ratio of 2-10:90-98; putting a mixture into a dryer for heating and drying for 25-35 min; fusing and mixing by a screw extruder, and then feeding the mixture into a spinning box, accurate metering by a metering pump on the spinning box, and conveying the mixture to a spinning component for spinning and manufacturing. By using the manufacturing method, titanium metal can be organically incorporated into polypropylene fiber, so that the polypropylene fiber has antiseptic and deodorant efficacy, and the problem of substantial lowering in spinnability due to increase in mechanical impurities in fluid after the polypropylene slice and liquedified titanium are fused when the liquefied titanium masterbatch is added is solved.
Description
Technical field
The invention belongs to textile technology field, tool relates to titanium polypropylene fiber and the manufacture method thereof of a kind of smelly eliminating that sterilizes.
Background technology
Titanium is the most extremely stable, will not change, and titanium itself is nontoxic, to human body without anaphylaxis, so titanium quilt
It is referred to as the metal getting close to most human body, element safest to human body.Research finds titanium not only safety, and also has increase human body to exempt from
Epidemic disease ability, regulates many effects such as blood sugar for human body, blood pressure, blood fat, sterilization smelly eliminating.To this end, there has been proposed, titanium is applied to clothes
Technical scheme on dress fabric, as titanium material is dissolved in water by Japan through special liquefaction process, then soaks fiber cloth wherein
Make the microgranule of its fibers adsorption titanium, be finally made fabric.But the adhesion that the microgranule of fibers adsorption titanium is both it is limited, and it is not through
Play washing repeatedly.Therefore it is desirable to just titanium elements can will be organically combined into one both it when manufacturing fabric fibre
Body, can stand washing repeatedly with its cloth fabric titanium elements weaved out and not fall off.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes and
Manufacture method, its titanium polypropylene fiber can incorporate in polypropylene fiber by organic for titanium, makes polypropylene fiber have the merits such as sterilization smelly eliminating
Effect;Its manufacture method solves after with the addition of liquefied titanium master batch, and the machinery in polypropylene section and the melted rear fluid of liquefied titanium is miscellaneous
Matter increases, and spinnability is greatly reduced, it is impossible to produce a difficult problem for finished product liquefied titanium polypropylene fiber, overcomes titanium polypropylene fiber of knowing clearly raw
During product, owing to the elasticity of melt can be excessive, melt expanded coefficient when spinneret micropore jet ejecting plate face is excessive, causes strand
Rupture, it is impossible to the normal disadvantage producing finished product titanium polypropylene fiber continuously.
Above-mentioned goal of the invention is achieved through the following technical solutions, the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes, bag
Including fiber bodies, it is characterized by: described fiber bodies includes that liquefied titanium master batch and polypropylene section are through two kinds of melting mixing
Material component.
As preferentially, described fiber bodies includes liquefied titanium master batch and polypropylene section two kinds of material groups through melting mixing
The weight ratio of part is 2 ~ 10:90 ~ 98.
As preferentially, described liquefied titanium master batch is that liquefied titanium powder and polypropylene are cut into slices powder by 8 ~ 40:60 ~ 92 weight
Amount ratio stirs, and obtains through screw extruder melt-processed manufacture.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes, it is characterized by: it is by liquefied titanium master batch and polypropylene
Cut into slices according to the weight ratio mixing and stirring of 2 ~ 10:90 ~ 98, put into drying machine heat drying 25 ~ 35 minutes, then via
Deliver to casing of weaving after screw extruder melting mixing, by the dosing pump accurate measurement on weaving casing, be sent to assembly of weaving
Carry out spinning manufacture.
As preferentially, described liquefied titanium master batch is cut into slices powder according to 8 ~ 40:60 ~ 92 by liquefied titanium powder and polypropylene
Weight ratio mixing and stirring, forms through screw extruder melt-processed.
As preferentially, polypropylene is cut into slices and the dried moisture content of liquefied titanium master batch: 650ug/g ~ 700ug/g;
The draw ratio of screw extruder: 31:1;
The temperature of screw extruder divides 5 sections, is respectively as follows: to outlet from import
One section 170 ° ~ 185 ° of C;
Two sections 245 ° ~ 255 ° of C;
Three sections 255 ° ~ 265 ° of C;
Four sections 255 ° ~ 265 ° of C;
Five section 250 ~ 255 ° C;
Spinning body temperature: 250 ° of C ± 0.5 DEG C;
Spinning pressure: 13 ~ 15Mpa;
Coiling speed: 2000 ~ 2300m/Min;
Filtering metal sand: 60 ~ 100 mesh;
Seven layers of drainage screen are arranged by following mesh number: 50 ~ 100 mesh, 250 ~ 350 mesh, 450 ~ 500 mesh, 450 ~ 500 mesh, 450 ~ 500
Mesh, 250 ~ 350 mesh, 50 ~ 100 mesh;
Spinneret micropore draw ratio: 8:1.
As preferentially, the manufacture method of the described titanium polypropylene fiber i.e. draw textured yarn of its DTY is as follows: titanium polypropylene fiber exists
Place 68 ~ 76 hours in balance cylinder, eliminate the internal stress in titanium polypropylene fiber with balance, the titanium after 68 ~ 76 hours balances
Polypropylene fiber just can enter stretcher strain operation, and it is entered upper hot tank by elasticizer silk road one roller and heats, from upper hot tank
Silk out feeds scroll tube again and carries out false twisting modification, makes that tow is fluffy has certain elasticity, between upper hot tank and scroll tube
Draw ratio be 1:1.2 ~ 1.8;Derive frictional disk false twist yarn out hot tank through two rollers enter from scroll tube to shape,
Strand after sizing no longer bounces back;Reach after oiling roller oils through three rollers from lower hot tank tow out and be wound into through spindle
Type, i.e. prepares the finished product titanium i.e. draw textured yarn of polypropylene fiber DTY;More than go up heater temperature: 95 ~ 105 ° of C, lower heater temperature: 90 ~
100 ° of C, draw ratio: 1:1.3 ~ 1.5, roller rotating speed: a 430 ~ 470M/Min, two roller rotating speed: 450 ~ 500M/Min, three rollers
Rotating speed 460 ~ 500M/Min, ingot position package speed 440 ~ 480m/min, titanium polypropylene fiber draw textured yarn oil content: 3.5 ±
0.5%。
The beneficial effects of the present invention is: titanium polypropylene fiber makes the production of titanium functional health textile become a reality, by
Having titanium ion in titanium polypropylene fiber, it can produce the unbalanced of electric field, and the after birth metabolism of antibacterial can be made to be obstructed, and then
Cause bacterial death, therefore there is the antibiotic effect of excellence;And titanium ion has antibacterial and organic gas in extremely strong absorption air
Characteristic, and can fast decoupled organic gas, make fiber produce self-cleaning effect, eliminate abnormal flavour;It addition, titanium elements is for human body
Constant temperature often produces high-effect ultraviolet and natural ability anion.Its manufacture method solves and with the addition of liquefied titanium master batch
After, the mechanical admixture in polypropylene section and the melted rear fluid of liquefied titanium increases, and spinnability is greatly reduced, it is impossible to produce finished fluid
Changing a difficult problem for titanium polypropylene fiber, overcome and know clearly in titanium polypropylene fiber production process, owing to the elasticity of melt can be excessive, melt is through spray
During filament plate micropore jet ejecting plate face, expanded coefficient is excessive, causes strand to rupture, it is impossible to the normal finished product titanium polypropylene fiber of production continuously
Disadvantage.
Accompanying drawing explanation
Fig. 1: use the anionic textiles report of the woven socks of the present invention;
Fig. 2: use the anti-microbial property examining report of the woven socks of the present invention;
Fig. 3: use the Ti content examining report of the woven socks of the present invention.
Detailed description of the invention
Below in conjunction with the embodiment represented by 13, the invention will be further described.
The titanium polypropylene fiber of a kind of smelly eliminating that sterilizes, including fiber bodies, described fiber bodies includes liquefied titanium master batch
Cut into slices through two kinds of material components of melting mixing with polypropylene;Described fiber bodies includes that liquefied titanium master batch and polypropylene section are through molten
The weight ratio of the two kinds of material components melting mixing is 5: 95, and described liquefied titanium master batch is liquefied titanium powder and polypropylene to be cut into slices
Powder stirs by 15: 75 part by weight, obtains through screw extruder melt-processed manufacture.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes of above-described embodiment, it is cut by liquefied titanium master batch and polypropylene
Sheet, according to the weight ratio mixing and stirring of 5: 95, puts into drying machine heat drying 30 minutes, then via screw extruder
Deliver to casing of weaving after melting mixing, by the dosing pump accurate measurement on weaving casing, be sent to weaving assembly and carry out spinning system
Make;
Described liquefied titanium master batch by liquefied titanium powder and polypropylene cut into slices powder according to 15: 75 weight ratio mix and blend equal
Even, form through screw extruder melt-processed;
Polypropylene section and the dried moisture content of liquefied titanium master batch: 680ug/g;
The draw ratio of screw extruder: 31:1;
The temperature of screw extruder divides 5 sections, is respectively as follows: to outlet from import
One section 170 ° C;
Two section 245 ° C;
Three section 255 ° C;
Four section 255 ° C;
Five section 250 ° C;
Spinning body temperature: 250 ° of C ± 0.5 DEG C;
Spinning pressure: 13Mpa;
Coiling speed: 2000m/Min;
Filtering metal sand: 80 mesh;
Seven layers of drainage screen are arranged by following mesh number: 50 mesh, 250 mesh, 450 mesh, 450 mesh, 450 mesh, 250 mesh, 50 mesh;
Spinneret micropore draw ratio: 8:1.
The manufacture method of the described titanium polypropylene fiber i.e. draw textured yarn of its DTY is as follows: titanium polypropylene fiber is in balance cylinder
Placing 72 hours, eliminate the internal stress in titanium polypropylene fiber with balance, the titanium polypropylene fiber after 72 hours balances is the most permissible
Entering stretcher strain operation, it is entered upper hot tank by elasticizer silk road one roller and heats, and feeds from upper hot tank silk out again
Scroll tube carries out false twisting modification, makes that tow is fluffy has certain elasticity, and the draw ratio between upper hot tank and scroll tube is 1:
1.5;Deriving frictional disk false twist yarn out hot tank through two rollers enter from scroll tube to shape, the strand after sizing is not
Bounce back again;Reach through spindle coiling and molding after oiling roller oils from lower hot tank tow out through three rollers, i.e. prepare finished product titanium third
Synthetic fibre fiber low stretch yarn;More than go up heater temperature: 100 ° of C, lower heater temperature: 95 ° of C, draw ratio: 1:1.5, one roller rotating speed:
300M/Min, two roller rotating speed: 450M/Min, three roller rotating speed 460M/Min, ingot position package speed 450m/min, titanium polypropylene is fine
Tie up its draw textured yarn oil content: 3.5%.
Fig. 1-3 is the examining report with the titanium woven socks of polypropylene fiber draw textured yarn of above-described embodiment.
Claims (9)
1. a titanium polypropylene fiber for the smelly eliminating that can sterilize, including fiber bodies, it is characterised in that: described fiber bodies includes liquid
Change titanium master batch and polypropylene section two kinds of material components through melting mixing.
The titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 1, it is characterised in that: described fiber bodies
The weight ratio cut into slices through two kinds of material components of melting mixing including liquefied titanium master batch and polypropylene is 2 ~ 10:90 ~ 98.
The titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 1 and 2, it is characterised in that: described liquefaction
Titanium master batch is to stir, liquefied titanium powder and polypropylene section powder through screw extruder by 8 ~ 40:60 ~ 92 part by weight
Melt-processed manufacture obtains.
4. the manufacture method of the titanium polypropylene fiber of the smelly eliminating that can sterilize, it is characterised in that: it is cut by liquefied titanium master batch and polypropylene
Sheet, according to the weight ratio mixing and stirring of 2 ~ 10:90 ~ 98, puts into drying machine heat drying 25 ~ 35 minutes, then via spiral shell
Deliver to casing of weaving after bar extruder melting mixing, by the dosing pump accurate measurement on weaving casing, be sent to weaving assembly and enter
Row spinning manufactures.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 4, it is characterised in that: described
Liquefied titanium master batch cut into slices the powder weight ratio mixing and stirring according to 8 ~ 40:60 ~ 92 by liquefied titanium powder and polypropylene, warp
Screw extruder melt-processed forms.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 4, it is characterised in that: polypropylene
Section and the dried moisture content of liquefied titanium master batch: 600ug/g ~ 950ug/g;
The draw ratio of screw extruder: 30 ~ 31:1;
The temperature of screw extruder divides 5 sections, is respectively as follows: to outlet from import
One section 170 ° ~ 185 ° of C;
Two sections 245 ° ~ 255 ° of C;
Three sections 255 ° ~ 265 ° of C;
Four sections 255 ° ~ 265 ° of C;
Five section 250 ~ 255 ° C;
Spinning body temperature: 250 ° of C ± 0.5 DEG C;
Spinning pressure: 13 ~ 15Mpa;
Coiling speed: 2000 ~ 2300m/Min;
Filtering metal sand: 60 ~ 100 mesh;
Seven layers of drainage screen are arranged by following mesh number: 50 ~ 100 mesh, 250 ~ 350 mesh, 450 ~ 500 mesh, 450 ~ 500 mesh, 450 ~ 500
Mesh, 250 ~ 350 mesh, 50 ~ 100 mesh;
Spinneret micropore draw ratio: 6 ~ 8:1.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 5, it is characterised in that: polypropylene
Section and the dried moisture content of liquefied titanium master batch: 650ug/g ~ 700ug/g;
The draw ratio of screw extruder: 30 ~ 31:1;
The temperature of screw extruder divides 5 sections, is respectively as follows: to outlet from import
One section 170 ° ~ 185 ° of C;
Two sections 245 ° ~ 255 ° of C;
Three sections 255 ° ~ 265 ° of C;
Four sections 255 ° ~ 265 ° of C;
Five sections 250 DEG C ~ 255 ° of C;
Spinning body temperature: 250 ° of C ± 0.5 DEG C;
Spinning pressure: 13 ~ 15Mpa;
Coiling speed: 2000 ~ 2300m/Min;
Filtering metal sand: 60 ~ 100 mesh;
Seven layers of drainage screen are arranged by following mesh number: 50 ~ 100 mesh, 250 ~ 350 mesh, 450 ~ 500 mesh, 450 ~ 500 mesh, 450 ~ 500
Mesh, 250 ~ 350 mesh, 50 ~ 100 mesh;
Spinneret micropore draw ratio: 6 ~ 8:1.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 6, it is characterised in that: described
The manufacture method of the titanium polypropylene fiber i.e. draw textured yarn of its DTY as follows: it is little that titanium polypropylene fiber places 68 ~ 76 in balance cylinder
Time, eliminating the internal stress in titanium polypropylene fiber with balance, the titanium polypropylene fiber after 68 ~ 76 hours balances just can enter and draw
Stretching deformation operation, it is entered upper hot tank by elasticizer silk road one roller and heats, and feeds scroll tube again from upper hot tank silk out
Carrying out false twisting modification, make that tow is fluffy has certain elasticity, the draw ratio between upper hot tank and scroll tube is 1:1.2 ~ 1.8;
Deriving frictional disk false twist yarn out hot tank through two rollers enter from scroll tube to shape, the strand after sizing no longer returns
Contracting;Reach through spindle coiling and molding after oiling roller oils from lower hot tank tow out through three rollers, i.e. prepare finished product titanium polypropylene fine
Dimension DTY i.e. draw textured yarn;More than go up heater temperature: 95 ~ 105 ° of C, lower heater temperature: 90 ~ 100 ° of C, draw ratio: 1:1.3 ~
1.5, roller rotating speed: a 430 ~ 470M/Min, two roller rotating speed: 450 ~ 500M/Min, three roller rotating speed 460 ~ 500M/Min, ingot
Position package speed 440 ~ 480m/min, titanium polypropylene fiber draw textured yarn oil content: 3.5 ± 0.5%.
The manufacture method of the titanium polypropylene fiber of a kind of smelly eliminating that sterilizes the most according to claim 7, it is characterised in that: described
The manufacture method of the titanium polypropylene fiber i.e. draw textured yarn of its DTY as follows: it is little that titanium polypropylene fiber places 68 ~ 76 in balance cylinder
Time, eliminating the internal stress in titanium polypropylene fiber with balance, the titanium polypropylene fiber after 68 ~ 76 hours balances just can enter and draw
Stretching deformation operation, it is entered upper hot tank by elasticizer silk road one roller and heats, and feeds scroll tube again from upper hot tank silk out
Carrying out false twisting modification, make that tow is fluffy has certain elasticity, the draw ratio between upper hot tank and scroll tube is 1:1.2 ~ 1.8;
Deriving frictional disk false twist yarn out hot tank through two rollers enter from scroll tube to shape, the strand after sizing no longer returns
Contracting;Reach through spindle coiling and molding after oiling roller oils from lower hot tank tow out through three rollers, i.e. prepare finished product titanium polypropylene fine
Dimension DTY i.e. draw textured yarn;More than go up heater temperature: 95 ~ 105 ° of C, lower heater temperature: 90 ~ 100 ° of C, draw ratio: 1:1.3 ~
1.5, roller rotating speed: a 430 ~ 470M/Min, two roller rotating speed: 450 ~ 500M/Min, three roller rotating speed 460 ~ 500M/Min, ingot
Position package speed 440 ~ 480m/min, titanium polypropylene fiber draw textured yarn oil content: 3.5 ± 0.5%.