CN105970205A - Air conditioner aluminum foil surface passivation solution - Google Patents
Air conditioner aluminum foil surface passivation solution Download PDFInfo
- Publication number
- CN105970205A CN105970205A CN201610331642.9A CN201610331642A CN105970205A CN 105970205 A CN105970205 A CN 105970205A CN 201610331642 A CN201610331642 A CN 201610331642A CN 105970205 A CN105970205 A CN 105970205A
- Authority
- CN
- China
- Prior art keywords
- air conditioner
- aluminum foil
- aluminium foil
- passivation solution
- surface passivation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an air conditioner aluminum foil surface passivation solution. The passivation solution is prepared from yttrium oxide, GdCl3.6H2O, nanometer bentonite, sodium silicate, inositol hexaphosphate, silica sol, epoxy resin, hydrogen peroxide, deionized water, phospholipid fatty acid, sodium alkyl sulfate and auxiliary agents. The passivation solution is environmentally friendly, safe, wide in raw material source and low in cost; and in the using process of the passivation solution, a bath solution is stable, components are safe and environmentally friendly, and various later-stage reprocessing properties of an air conditioner aluminum foil product are not influenced. A passivation film formed by the air conditioner aluminum foil passivation solution is high in stability and corrosion resistance, good in oxidation resistance and capable of effectively protecting an air conditioner aluminum foil material from external corrosion; the service life of the air conditioner aluminum foil material is effectively prolonged; and the air conditioner aluminum foil surface passivation solution is convenient to use, practical and suitable for being applied and popularized. An air conditioner heat exchanger made of air conditioner aluminum foil treated through the passivation solution is more excellent in performance; and compared with that of a common air conditioner heat exchanger, the service life of the air conditioner heat exchanger is prolonged by one time or above.
Description
Technical field
The present invention relates to chemical field, particularly relate to a kind of air conditioner aluminium foil surface passivation liquid.
Background technology
Aluminum is that nature stores one of the abundantest metallic element, owing to aluminum and alloy thereof have little, good the leading of proportion
Heat and electric conductivity, reflective is strong, be prone to processing and forming and the physical and chemical performance of excellence, the advantage such as cheap, and aluminium foil is
One metallic aluminium directly rolls sheet thermoprint material, and its hot stamping effects is similar to the effect of pure silver foil thermoprint, therefore also known as
White alloy paper tinsel.Owing to the quality of aluminum is soft, ductility is good, there is argenteous gloss, if by the thin slice after calendering, using sodium silicate
Mount Deng material on offset paper, make aluminium foil, also can print.But aluminium foil itself is oxidizable and colour-darkening, rubs, touch
Touching etc. and all can fade, be not therefore suitable for the thermoprint of the Front cover of book and periodical etc. preserved for a long time, in recent years, the use of air-conditioning is increasingly
Many, make air-conditioning heat exchanger heat transmission fin material, commonly referred to as air conditioner aluminium foil with aluminium foil, it needs enough surface corrosion resistance
Can, accordingly, it would be desirable to through Passivation Treatment.
Along with people's enhancing to environmental protection consciousness, chromic application is the most severely limited.In February, 2003
13, European Union issued " waste electronic andelectrical equipment instruction " and " has used some to be harmful to about limiting in electronic electric equipment
Substances Directive ".The former came into force from August 13rd, 2004, be to the effect that exported to 10 big classes of European Union totally 99 kinds electric
Product recycling and processing cost will be born by manufacturer oneself;The latter was then come into force from 1 day July in 2006, mainly forbade to Europe
The electronic and electrical equipment of 6 kinds of harmful substances such as leaded, hydrargyrum, cadmium, Cr VI, poly-dibromodiphenyl ether and poly-bromo biphenyl is sold by alliance, this
Instruction will relate to 8 big class totally 64 kinds of products.Research and develop nontoxic or low toxicity material to exist to substitute chromating technique gesture
Must go.
Summary of the invention
It is an object of the invention to provide a kind of air conditioner aluminium foil surface passivation liquid, be achieved through the following technical solutions:
A kind of air conditioner aluminium foil surface passivation liquid, is made up of following component: yittrium oxide 0.5 part, GdCl3 6H2O by weight
1.4 parts, nano-bentonite 0.01 part, sodium silicate 0.9 part, inositol hexaphosphate 1.5 parts, Ludox 25 parts, epoxy resin 1 part,
Hydrogen peroxide 18 parts, deionized water 50 parts, lipoid fatty acid 1 part, sodium alkyl sulfate 0.8 part, auxiliary agent 0.5 part;Described auxiliary agent is pressed
Percentages is made up of following component: 20.5% cyclohexanhexanol phosphate ester, 0.5% sodium chloride, 47% chitosan, 32% acrylic acid;Institute
The manufacture method stating auxiliary agent is: sodium chloride, cyclohexanhexanol phosphate ester are mixed with chitosan, control temperature at 8-10 DEG C,
After continuing 40 minutes, then dripping acrylic acid, control to drip off at 25 minutes, dropping limit, limit is stirred, and mixing speed is 250r/min,
Rear standing 5-8 minute,;By adding auxiliary agent, it is possible to strengthening air conditioner aluminium foil passivation effect, reduce the Passivation Treatment time.
Further, described epoxy resin is through silane coupler kh560 modification.
Further, the PH of described air conditioner aluminium foil passivating solution is 1.0-1.3.
A kind of manufacture method of air conditioner aluminium foil surface passivation liquid, including:
1) yittrium oxide, GdCl3 6H2O, nano-bentonite, sodium silicate are joined in deionized water, heating in water bath, temperature 72
DEG C, by ultrasonic wave concussion 15 minutes, supersonic frequency was 112.5KHZ;
2) adding hydrogen peroxide, lipoid fatty acid in above-mentioned mixed solution, stirring while adding, mixing speed is 300r/min;
3) above-mentioned mixed liquor is put at room temperature, add inositol hexaphosphate, Ludox, epoxy resin, after mix homogeneously 5 points
Clock, is centrifuged processing 10 minutes, and centrifugal speed is 278r/min;
4) above-mentioned mixed solution temperature is controlled to 15-18 DEG C, add sodium alkyl sulfate, auxiliary agent, after mix homogeneously, stir
Mixing, mixing speed is 525r/min, and mixing time is 30 minutes,.
The passivating solution prepared by yittrium oxide, GdCl3 6H2O, nano-bentonite, after Passivation Treatment air conditioner aluminium foil,
The passivating film defining continuous print fine and close has high stability and corrosion resisting property, and antioxygenic property is strong, by adding inositol six phosphorus
Acid esters, sodium alkyl sulfate, the epoxy resin of process modification can improve the film property of passivating film and the seriality of film greatly, logical
The cooperation crossing Ludox and lipoid fatty acid can further improve the seriality of passivating film and the adhesion property of passivating film, it is possible to has
Effect protection air conditioner aluminium foil material, it is to avoid corroded by the external world, through the air conditioner aluminium foil surface passivation that passivating solution of the present invention processes
The life-span of the passivating film that film is formed than general passivating solution under same environment is long 1 times, and passivation time is the 78-84 second, through blunt
After change, the salt spray resistance of air conditioner aluminium foil is more than 120 hours (6.8%NaCl solution is sprayed continuously, temperature 35 DEG C).
By adding nano-bentonite and auxiliary agent synergism, the reaction rate of hydrogen peroxide oxidation aluminum can be improved, permissible
Obtain oxide-film finer and close, firm, and the decay resistance of oxide-film can be improved.
The invention has the beneficial effects as follows: the passivating solution green safety of the present invention, raw material sources is extensive, and cost is relatively low, its
In use, tank liquor is stable, component safety and environmental protection, does not affect the various cycling processabilities in air conditioner aluminium foil goods later stage, this
The passivating film that the air conditioner aluminium foil passivating solution that invention provides is formed, has high stability and corrosion resisting property, and antioxygenic property is good, energy
Enough effectively protection air conditioner aluminium foil materials, it is to avoid corroded by the external world, effectively extend its service life convenient and practical, suitably push away
Extensively applying, the air conditioner aluminium foil processed through passivating solution of the present invention makes heat exchanger of air condition, and performance is more excellent, and the life-span is relative
General heat exchanger of air condition is doubled.
Detailed description of the invention
A kind of air conditioner aluminium foil surface passivation liquid, is made up of following component: yittrium oxide 0.5 part, GdCl3 by weight
6H2O 1.4 parts, nano-bentonite 0.01 part, sodium silicate 0.9 part, inositol hexaphosphate 1.5 parts, Ludox 25 parts, epoxy resin
1 part, hydrogen peroxide 18 parts, deionized water 50 parts, lipoid fatty acid 1 part, sodium alkyl sulfate 0.8 part, auxiliary agent 0.5 part;Described help
Agent is made up of following component in percentage terms: 20.5% cyclohexanhexanol phosphate ester, 0.5% sodium chloride, 47% chitosan, 32% propylene
Acid;The manufacture method of described auxiliary agent is: sodium chloride, cyclohexanhexanol phosphate ester are mixed with chitosan, controls temperature at 8-
10 DEG C, after continuing 40 minutes, then dripping acrylic acid, control to drip off at 25 minutes, dropping limit, limit is stirred, and mixing speed is 250r/
Min, finally stands 5-8 minute,;By adding auxiliary agent, it is possible to strengthening air conditioner aluminium foil passivation effect, when reducing Passivation Treatment
Between.
Further, described epoxy resin is through silane coupler kh560 modification.
Further, the PH of described air conditioner aluminium foil passivating solution is 1.0-1.3.
A kind of manufacture method of air conditioner aluminium foil surface passivation liquid, including:
1) yittrium oxide, GdCl3 6H2O, nano-bentonite, sodium silicate are joined in deionized water, heating in water bath, temperature 72
DEG C, by ultrasonic wave concussion 15 minutes, supersonic frequency was 112.5KHZ;
2) adding hydrogen peroxide, lipoid fatty acid in above-mentioned mixed solution, stirring while adding, mixing speed is 300r/min;
3) above-mentioned mixed liquor is put at room temperature, add inositol hexaphosphate, Ludox, epoxy resin, after mix homogeneously 5 points
Clock, is centrifuged processing 10 minutes, and centrifugal speed is 278r/min;
4) above-mentioned mixed solution temperature is controlled to 15-18 DEG C, add sodium alkyl sulfate, auxiliary agent, after mix homogeneously, stir
Mixing, mixing speed is 525r/min, and mixing time is 30 minutes,.
The passivating solution prepared by yittrium oxide, GdCl3 6H2O, nano-bentonite, after Passivation Treatment air conditioner aluminium foil,
The passivating film defining continuous print fine and close has high stability and corrosion resisting property, and antioxygenic property is strong, by adding inositol six phosphorus
Acid esters, sodium alkyl sulfate, the epoxy resin of process modification can improve the film property of passivating film and the seriality of film greatly, logical
The cooperation crossing Ludox and lipoid fatty acid can further improve the seriality of passivating film and the adhesion property of passivating film, it is possible to has
Effect protection air conditioner aluminium foil material, it is to avoid corroded by the external world, through the air conditioner aluminium foil surface passivation that passivating solution of the present invention processes
The life-span of the passivating film that film is formed than general passivating solution under same environment is long 1 times, and passivation time is the 78-84 second, through blunt
After change, the salt spray resistance of air conditioner aluminium foil is more than 120 hours (6.8%NaCl solution is sprayed continuously, temperature 35 DEG C).
Claims (4)
1. an air conditioner aluminium foil surface passivation liquid, it is characterised in that be made up of following component by weight: yittrium oxide 0.5 part,
GdCl3 6H2O 1.4 parts, nano-bentonite 0.01 part, sodium silicate 0.9 part, inositol hexaphosphate 1.5 parts, Ludox 25 parts,
Epoxy resin 1 part, hydrogen peroxide 18 parts, deionized water 50 parts, lipoid fatty acid 1 part, sodium alkyl sulfate 0.8 part, auxiliary agent 0.5
Part;Described auxiliary agent is made up of following component in percentage terms: 20.5% cyclohexanhexanol phosphate ester, 0.5% sodium chloride, 47% chitosan,
32% acrylic acid;The manufacture method of described auxiliary agent is: sodium chloride, cyclohexanhexanol phosphate ester are mixed with chitosan, controls temperature
Degree, at 8-10 DEG C, after continuing 40 minutes, then drips acrylic acid, controls to drip off at 25 minutes, and dropping limit, limit is stirred, and mixing speed is
250r/min, finally stands 5-8 minute,.
A kind of air conditioner aluminium foil surface passivation liquid the most according to claim 1, it is characterised in that described epoxy resin is through silicon
Alkane coupling agent kh560 modification.
A kind of air conditioner aluminium foil surface passivation liquid the most according to claim 1, it is characterised in that described air conditioner aluminium foil passivating solution
PH be 1.0-1.3.
4. according to the manufacture method of a kind of air conditioner aluminium foil surface passivation liquid described in claim 1-3, it is characterised in that including:
1) yittrium oxide, GdCl3 6H2O, nano-bentonite, sodium silicate are joined in deionized water, heating in water bath, temperature 72
DEG C, by ultrasonic wave concussion 15 minutes, supersonic frequency was 112.5KHZ;
2) adding hydrogen peroxide, lipoid fatty acid in above-mentioned mixed solution, stirring while adding, mixing speed is 300r/min;
3) above-mentioned mixed liquor is put at room temperature, add inositol hexaphosphate, Ludox, epoxy resin, after mix homogeneously 5 points
Clock, is centrifuged processing 10 minutes, and centrifugal speed is 278r/min;
4) above-mentioned mixed solution temperature is controlled to 15-18 DEG C, add sodium alkyl sulfate, auxiliary agent, after mix homogeneously, stir
Mixing, mixing speed is 525r/min, and mixing time is 30 minutes,.