CN105970116A - Steel being good in plastic property - Google Patents
Steel being good in plastic property Download PDFInfo
- Publication number
- CN105970116A CN105970116A CN201610366556.1A CN201610366556A CN105970116A CN 105970116 A CN105970116 A CN 105970116A CN 201610366556 A CN201610366556 A CN 201610366556A CN 105970116 A CN105970116 A CN 105970116A
- Authority
- CN
- China
- Prior art keywords
- steel
- limonite
- carbon
- plasticity
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses steel being good in plastic property. The steel comprises the following raw material components in percentage by weight: not more than 0.075% of carbon, not more than 0.048% of phosphorus, not more than 0.036% of surplus, 9.67-12.5% of nickel, 18.44-19.57% of chromium, 3.3-4.3% of molybdenum, not more than 0.115% of nitrogen, not more than 0.82% of silicon, not more than 2.23% of manganese, and the balance of iron and impurities. Limonite is adopted as an ironmaking raw material for the steel, and the cut-off grade of the limonite is 24-27. By adoption of the above technical scheme, the steel disclosed by the invention can be subjected to permanent deformation stably, and the integrity of the steel is prevented from being broken; meanwhile, the steel has the very strong impact-bearing capability; and accordingly, various steel materials made of the steel are very wide in application.
Description
Technical field
The present invention relates to Steel material field, particularly relate to a kind of steel with the good performance of plasticity.
Background technology
Steel is a kind of iron-carbon alloy.Can classify according to chemical composition, including carbon steel, ordinary low-alloy steel and steel alloy.Carbon steel is the alloy of ferrum and carbon, in addition to ferrum and carbon, possibly together with elements such as silicon, manganese, p and ses.Ordinary low-alloy steel is to add a small amount of alloying element on the basis of low-carbon (LC) straight carbon steel and obtain the steel grade of preferable combination property, and wherein alloying element is silicon, calcium, titanium, niobium, boron and rare earth element etc., and its total amount is less than 3%.Steel alloy is the steel grade containing one or more appropriate alloying elements.Can there is the problem that plasticity is bad in existing steel, be not easy to keep after deforming upon, and impact uses.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of steel with the good performance of plasticity, can meet modern's demand to steel.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of steel with the good performance of plasticity, the material composition of described steel includes carbon, phosphorus, sulfur, nickel, chromium, molybdenum, nitrogen, silicon, manganese, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon≤0.075%, phosphorus≤0.048%, sulfur≤0.036%, nickel 9.67-12.5%, chromium 18.44-19.57%, molybdenum 3.3-4.3%, nitrogen≤0.115%, silicon≤0.82%, manganese≤2.23%, ferrum and impurity: surplus, the iron-smelting raw material of described steel is limonite, the border taste of described limonite is 24-27.
In a preferred embodiment of the present invention, described steel by weight percentage, including material composition have: carbon 0.056%, phosphorus 0.027%, sulfur 0.032%, nickel 10.77%, chromium 19.02%, molybdenum 3.78%, nitrogen 0.105%, silicon 0.73%, manganese 1.23%, ferrum and impurity: surplus.
In a preferred embodiment of the present invention, the beneficiation method of described limonite has washing, gravity treatment, the ore dressing of electromagnetism magnetic field or the ore dressing of permanent magnetic strong magnetic field.
In a preferred embodiment of the present invention, the industry taste of described limonite is 33-35.
The invention has the beneficial effects as follows: the steel with the good performance of plasticity of the present invention, under external force, steel can stable generation permanent deformation and do not destroy its integrity, the most described steel has the strongest ability withstood shocks, use this kind of steel to manufacture and obtain various Steel material, in application widely.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one:
A kind of steel with the good performance of plasticity is provided, the material composition of described steel includes carbon, phosphorus, sulfur, nickel, chromium, molybdenum, nitrogen, silicon, manganese, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.056%, phosphorus 0.027%, sulfur 0.032%, nickel 10.77%, chromium 19.02%, molybdenum 3.78%, nitrogen 0.105%, silicon 0.73%, manganese 1.23%, ferrum and impurity: surplus, the iron-smelting raw material of described steel is limonite, and the border taste of described limonite is 24.The beneficiation method of described limonite is the ore dressing of permanent magnetic strong magnetic field.The industry taste of described limonite is 35.
Embodiment two:
A kind of steel with the good performance of plasticity is provided, the material composition of described steel includes carbon, phosphorus, sulfur, nickel, chromium, molybdenum, nitrogen, silicon, manganese, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.035%, phosphorus 0.027%, sulfur 0.018%, nickel 12.5%, chromium 18.44%, molybdenum 4.3%, nitrogen 0.115%, silicon 0.77%, manganese 2.13%, ferrum and impurity: surplus, the iron-smelting raw material of described steel is limonite, and the border taste of described limonite is 25.The beneficiation method of described limonite is gravity treatment.The industry taste of described limonite is 34.
Embodiment three:
A kind of steel with the good performance of plasticity is provided, the material composition of described steel includes carbon, phosphorus, sulfur, nickel, chromium, molybdenum, nitrogen, silicon, manganese, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.075%, phosphorus 0.048%, sulfur 0.036%, nickel 9.67%, chromium 19.57%, molybdenum 3.3%, nitrogen 0.115%, silicon 0.82%, manganese 2.23%, ferrum and impurity: surplus, the iron-smelting raw material of described steel is limonite, and the border taste of described limonite is 27.The beneficiation method of described limonite is washing.The industry taste of described limonite is 33.
The invention has the beneficial effects as follows:
One, there is the steel of the good performance of plasticity under external force described in, steel can stable generation permanent deformation and do not destroy its integrity;
The steel described in two, with the good performance of plasticity has the strongest ability withstood shocks, and uses this kind of steel to manufacture and obtains various Steel material, in application widely.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.
Claims (4)
1. a steel with the good performance of plasticity, it is characterized in that, the material composition of described steel includes carbon, phosphorus, sulfur, nickel, chromium, molybdenum, nitrogen, silicon, manganese, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon≤0.075%, phosphorus≤0.048%, sulfur≤0.036%, nickel 9.67-12.5%, chromium 18.44-19.57%, molybdenum 3.3-4.3%, nitrogen≤0.115%, silicon≤0.82%, manganese≤2.23%, ferrum and impurity: surplus, the iron-smelting raw material of described steel is limonite, and the border taste of described limonite is 24-27.
The steel with the good performance of plasticity the most according to claim 1, it is characterised in that described steel by weight percentage, including material composition have: carbon 0.056%, phosphorus 0.027%, sulfur
0.032%, nickel 10.77%, chromium 19.02%, molybdenum 3.78%, nitrogen 0.105%, silicon
0.73%, manganese 1.23%, ferrum and impurity: surplus.
The steel with the good performance of plasticity the most according to claim 1, it is characterised in that the beneficiation method of described limonite has washing, gravity treatment, the ore dressing of electromagnetism magnetic field or the ore dressing of permanent magnetic strong magnetic field.
The steel with the good performance of plasticity the most according to claim 1, it is characterised in that the industry taste of described limonite is 33-35.