CN105969269A - High-elasticity storage battery sealing adhesive based on dimethylamino ethyl methacrylate and ethyleneglycol dimethacrylate and production method of high-elasticity storage battery sealing adhesive - Google Patents
High-elasticity storage battery sealing adhesive based on dimethylamino ethyl methacrylate and ethyleneglycol dimethacrylate and production method of high-elasticity storage battery sealing adhesive Download PDFInfo
- Publication number
- CN105969269A CN105969269A CN201610486502.9A CN201610486502A CN105969269A CN 105969269 A CN105969269 A CN 105969269A CN 201610486502 A CN201610486502 A CN 201610486502A CN 105969269 A CN105969269 A CN 105969269A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- diethylene glycol
- ethyl ester
- polyether rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-elasticity storage battery sealing adhesive based on dimethylamino ethyl methacrylate and ethyleneglycol dimethacrylate and a production method of the high-elasticity storage battery sealing adhesive. The high-elasticity storage battery sealing adhesive comprises a component A and a component B, wherein the component A comprises the dimethylamino ethyl methacrylate, solvent, propylene carbonate, high-thermal-conductivity composite powder, reinforcing filler, antioxidant and polyether rubber; the component B comprises the ethyleneglycol dimethacrylate, polyether rubber, fibrous talcum powder, bis(2-dimethylaminoethyl) ether, DEUCHEM2700 and tackifier. The adhesive of the component A and the adhesive of the component B are respectively prepared by sealed stirring, negative-pressure drying and temperature-controlled mixing. Compared with common adhesives, the high-elasticity storage battery sealing adhesive has the advantages that the sealing adhesive is high in elasticity, good in heat resistance, water resistance, heat conductivity and adhering performance, free of pollution, capable of achieving good adhering performance during use, good in sealing effect, little in internal air, and the like.
Description
Technical field
The present invention relates to chemical technology field, particularly to a kind of based on ethyl ester and diethylene glycol dilaurate the high resiliency accumulator sealant that accumulator is played sealing function
And manufacture method
。
Background technology
There is easily crystallization and glue the up time time of twice (the glue viscosity at a certain temperature be increased to) short problem in the amine curing agent of existing accumulator sealant water, up time embodies the response speed of glue, determine client join glue after glue can use and the length of operating time, after firming agent is produced, crystallization within the shelf-life causes client can not use this product.To accumulator sealant, in firming agent, each raw-material ratio is improper and under the original production process of firming agent, is easy for producing the problems referred to above.
Rising year by year along with the accumulator market demand, the process of old and useless battery is increasingly come into one's own with the maintenance of accumulator, and storage battery maintenance it is crucial that i.e. to open sealing lid can not damage battery cell case, more existing fluid sealants are if adhesive strength is high, battery cell case can be damaged owing to fluid sealant is difficult to stripping when opening sealing lid, and adhesive strength height all ratios of being easily peeled off are relatively low, how and to ensure that good adhesive strength does not damage battery cell case when opening sealing lid again be an anxious to be resolved difficult problem.
Summary of the invention
It is an object of the invention to provide
A kind of have good
High resiliency
,
Thermostability
,
Resistance to water
,
Heat conductivity
,
Cementability
,
Free of contamination a kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate
And manufacture method
, solve the use needs of problems of accumulator sealant.
In order to achieve the above object, the present invention provides following technical scheme:
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate, it is characterised in that: include
A
Component and
B
Component；Described
A
Component is made up of dimethylaminoethyl ethyl ester, solvent, Allyl carbonate, high heat conduction composite powder, reinforcing filler, antioxidant, polyether rubber；
B
Component by methacrylic acid diethylene glycol dilaurate, polyether rubber, fibrous talc, double dimethyl amine benzyl ethyl ethers,
DEUCHEM2700
, viscosifier form；Wherein said
A
In component, including:
50-70
The dimethylaminoethyl ethyl ester of part,
15-35
The solvent of part,
2-15
The Allyl carbonate of part,
10-15
The high heat conduction composite powder of part,
5-15
The reinforcing filler of part,
5-20
The antioxidant of part,
25-35
The polyether rubber composition of part；Described
B
In component, including:
60-80
The methacrylic acid diethylene glycol dilaurate of part,
30-35
The polyether rubber of part,
5-15
The fibrous talc of part,
3-15
Double dimethyl amine benzyl ethyl ethers of part,
10-25
Part
DEUCHEM2700
,
10-15
The viscosifier of part.
Described
A
In component, the mean molecule quantity of dimethylaminoethyl ethyl ester is
8000-10000
, described
B
In component, the mean molecule quantity of methacrylic acid diethylene glycol dilaurate is
10000-14000
。
Described
A
In component, including:
60
The dimethylaminoethyl ethyl ester of part,
25
The solvent of part,
10
The Allyl carbonate of part,
12
The high heat conduction composite powder of part,
10
The reinforcing filler of part,
12
The antioxidant of part,
30
The polyether rubber composition of part；Described
B
In component, including:
70
The methacrylic acid diethylene glycol dilaurate of part,
32
The polyether rubber of part,
10
The fibrous talc of part,
10
Double dimethyl amine benzyl ethyl ethers of part,
18
Part
DEUCHEM2700
,
12
The viscosifier of part.
Described solvent is the mixing of one or more in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene；Reinforcing filler is the mixing of one or more that fume colloidal silica, precipitated silica and surface process in white carbon；Antioxidant is
IrgastabPUR68
, antioxidant
1010
With
Irganox5057
In the mixing of one or more；Viscosifier be isopropyl titanate, butyl titanate,
r-
Aminopropyltriethoxywerene werene
,
1
、
2-
Epoxy ethyoxyl trimethoxy silane, carbonic ester ethyl acetoacetate chelate in the mixing of one or more.
Concretely comprise the following steps:
A
Component includes step: in closed reactor, adds the dimethylaminoethyl ethyl ester of above-mentioned ratio of weight and number, solvent, Allyl carbonate, polyether rubber, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, being passed through drying nitrogen and release vacuum, add above-mentioned ratio of weight and number height heat conduction composite powder, reinforcing filler, antioxidant, temperature controls
65
~
75
℃
, mix homogeneously, to obtain final product
A
Component fluid sealant.
B
Component includes step: in closed reactor, adds the methacrylic acid diethylene glycol dilaurate of above-mentioned ratio of weight and number, polyether rubber, fibrous talc, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, it is passed through drying nitrogen and releases vacuum, add double dimethyl amine benzyl ethyl ethers of above-mentioned ratio of weight and number,
DEUCHEM2700
, viscosifier, temperature controls
65
~
75
DEG C,
Mix homogeneously, to obtain final product
B
Component fluid sealant.
Beneficial effects of the present invention: the present invention is compared to general
Other adhesives have good
High resiliency
,
Thermostability
,
Resistance to water
,
Heat conductivity
,
Cementability
,
Pollution-free
Etc. advantage, it is possible to the best bonding, and good sealing effect, the effects such as inner air is few
。
Detailed description of the invention
Below in conjunction with embodiment, technical scheme is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment
1
:
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate, it is characterised in that: include
A
Component and
B
Component；Described
A
Component is made up of dimethylaminoethyl ethyl ester, solvent, Allyl carbonate, high heat conduction composite powder, reinforcing filler, antioxidant, polyether rubber；
B
Component by methacrylic acid diethylene glycol dilaurate, polyether rubber, fibrous talc, double dimethyl amine benzyl ethyl ethers,
DEUCHEM2700
, viscosifier form；Wherein said
A
In component, including:
50-70
The dimethylaminoethyl ethyl ester of part,
15-35
The solvent of part,
2-15
The Allyl carbonate of part,
10-15
The high heat conduction composite powder of part,
5-15
The reinforcing filler of part,
5-20
The antioxidant of part,
25-35
The polyether rubber composition of part；Described
B
In component, including:
60-80
The methacrylic acid diethylene glycol dilaurate of part,
30-35
The polyether rubber of part,
5-15
The fibrous talc of part,
3-15
Double dimethyl amine benzyl ethyl ethers of part,
10-25
Part
DEUCHEM2700
,
10-15
The viscosifier of part.
Described
A
In component, the mean molecule quantity of dimethylaminoethyl ethyl ester is
8000-10000
, described
B
In component, the mean molecule quantity of methacrylic acid diethylene glycol dilaurate is
10000-14000
。
Described
A
In component, including:
60
The dimethylaminoethyl ethyl ester of part,
25
The solvent of part,
10
The Allyl carbonate of part,
12
The high heat conduction composite powder of part,
10
The reinforcing filler of part,
12
The antioxidant of part,
30
The polyether rubber composition of part；Described
B
In component, including:
70
The methacrylic acid diethylene glycol dilaurate of part,
32
The polyether rubber of part,
10
The fibrous talc of part,
10
Double dimethyl amine benzyl ethyl ethers of part,
18
Part
DEUCHEM2700
,
12
The viscosifier of part.
Described solvent is the mixing of one or more in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene；Reinforcing filler is the mixing of one or more that fume colloidal silica, precipitated silica and surface process in white carbon；Antioxidant is
IrgastabPUR68
, antioxidant
1010
With
Irganox5057
In the mixing of one or more；Viscosifier be isopropyl titanate, butyl titanate,
r-
Aminopropyltriethoxywerene werene
,
1
、
2-
Epoxy ethyoxyl trimethoxy silane, carbonic ester ethyl acetoacetate chelate in the mixing of one or more.
Concretely comprise the following steps:
A
Component includes step: in closed reactor, adds the dimethylaminoethyl ethyl ester of above-mentioned ratio of weight and number, solvent, Allyl carbonate, polyether rubber, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, being passed through drying nitrogen and release vacuum, add above-mentioned ratio of weight and number height heat conduction composite powder, reinforcing filler, antioxidant, temperature controls
65
~
75
℃
, mix homogeneously, to obtain final product
A
Component fluid sealant.
B
Component includes step: in closed reactor, adds the methacrylic acid diethylene glycol dilaurate of above-mentioned ratio of weight and number, polyether rubber, fibrous talc, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, it is passed through drying nitrogen and releases vacuum, add double dimethyl amine benzyl ethyl ethers of above-mentioned ratio of weight and number,
DEUCHEM2700
, viscosifier, temperature controls
65
~
75
DEG C,
Mix homogeneously, to obtain final product
B
Component fluid sealant.
Embodiment
2
:
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate, it is characterised in that: include
A
Component and
B
Component；Described
A
Component is made up of dimethylaminoethyl ethyl ester, solvent, Allyl carbonate, high heat conduction composite powder, reinforcing filler, antioxidant, polyether rubber；
B
Component by methacrylic acid diethylene glycol dilaurate, polyether rubber, fibrous talc, double dimethyl amine benzyl ethyl ethers,
DEUCHEM2700
, viscosifier form；Wherein said
A
In component, including:
50-70
The dimethylaminoethyl ethyl ester of part,
15-35
The solvent of part,
2-15
The Allyl carbonate of part,
10-15
The high heat conduction composite powder of part,
5-15
The reinforcing filler of part,
5-20
The antioxidant of part,
25-35
The polyether rubber composition of part；Described
B
In component, including:
60-80
The methacrylic acid diethylene glycol dilaurate of part,
30-35
The polyether rubber of part,
5-15
The fibrous talc of part,
3-15
Double dimethyl amine benzyl ethyl ethers of part,
10-25
Part
DEUCHEM2700
,
10-15
The viscosifier of part.
Specifically
Production and processing
Step is:
A
Component includes step: in closed reactor, adds the dimethylaminoethyl ethyl ester of above-mentioned ratio of weight and number, solvent, Allyl carbonate, polyether rubber, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, being passed through drying nitrogen and release vacuum, add above-mentioned ratio of weight and number height heat conduction composite powder, reinforcing filler, antioxidant, temperature controls
65
~
75
℃
, mix homogeneously, to obtain final product
A
Component fluid sealant.
B
Component includes step: in closed reactor, adds the methacrylic acid diethylene glycol dilaurate of above-mentioned ratio of weight and number, polyether rubber, fibrous talc, and stirring heats up, and temperature controls
80
℃
~110
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, it is passed through drying nitrogen and releases vacuum, add double dimethyl amine benzyl ethyl ethers of above-mentioned ratio of weight and number,
DEUCHEM2700
, viscosifier, temperature controls
65
~
75
DEG C,
Mix homogeneously, to obtain final product
B
Component fluid sealant.
A
Component
With
B
Component
Respectively
Stand subpackage, directly will during use
A
Component,
B
Component is according to carrying out potting operation after weight ratio mix homogeneously.
Following table is the Data Comparison of the present invention and other series products:
Upper table shows that the properties of the present invention is better than like product, can meet the process requirements that accumulator seals.
Embodiment
3
:
In the present invention, optimum ratio is:
A
In component:
60
The dimethylaminoethyl ethyl ester of part,
25
The solvent of part,
10
The Allyl carbonate of part,
12
The high heat conduction composite powder of part,
10
The reinforcing filler of part,
12
The antioxidant of part,
30
The polyether rubber composition of part；
B
In component
:
70
The methacrylic acid diethylene glycol dilaurate of part,
32
The polyether rubber of part,
10
The fibrous talc of part,
10
Double dimethyl amine benzyl ethyl ethers of part,
18
Part
DEUCHEM2700
,
12
The viscosifier of part.
Preferably production and processing
Step is:
A
Component includes step: in closed reactor, adds the dimethylaminoethyl ethyl ester of above-mentioned ratio of weight and number, solvent, Allyl carbonate, polyether rubber, and stirring heats up, and temperature controls
90
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, being passed through drying nitrogen and release vacuum, add above-mentioned ratio of weight and number height heat conduction composite powder, reinforcing filler, antioxidant, temperature controls
70
℃
, mix homogeneously, to obtain final product
A
Component fluid sealant.
B
Component includes step: in closed reactor, adds the methacrylic acid diethylene glycol dilaurate of above-mentioned ratio of weight and number, polyether rubber, fibrous talc, and stirring heats up, and temperature controls
90
℃
, open vacuum pumping negative pressure, Stress control exists
-
0.1MPa
Below；Then cool to
65
℃
Hereinafter, it is passed through drying nitrogen and releases vacuum, add double dimethyl amine benzyl ethyl ethers of above-mentioned ratio of weight and number,
DEUCHEM2700
, viscosifier, temperature controls
70
DEG C,
Mix homogeneously, to obtain final product
B
Component fluid sealant.
A
Component
With
B
Component
Respectively
Stand subpackage, directly will during use
A
Component,
B
Component is according to carrying out potting operation after weight ratio mix homogeneously.
The above; being only the detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, any those familiar with the art is in the technical scope that the invention discloses; change can be readily occurred in or replace, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should described be as the criterion with scope of the claims.
Claims (5)
1. a high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate, it is characterised in that: include component A and B component；Described component A is made up of dimethylaminoethyl ethyl ester, solvent, Allyl carbonate, high heat conduction composite powder, reinforcing filler, antioxidant, polyether rubber；B component is made up of methacrylic acid diethylene glycol dilaurate, polyether rubber, fibrous talc, double dimethyl amine benzyl ethyl ethers, DEUCHEM2700, viscosifier；In wherein said component A, including: the dimethylaminoethyl ethyl ester of 50-70 part, the solvent of 15-35 part, the Allyl carbonate of 2-15 part, the high heat conduction composite powder of 10-15 part, the reinforcing filler of 5-15 part, the antioxidant of 5-20 part, the polyether rubber composition of 25-35 part；In described B component, including: the methacrylic acid diethylene glycol dilaurate of 60-80 part, the polyether rubber of 30-35 part, the fibrous talc of 5-15 part, double dimethyl amine benzyl ethyl ethers of 3-15 part, the viscosifier of the DEUCHEM2700 of 10-25 part, 10-15 part.
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate the most according to claim 1, it is characterized in that: in described component A, the mean molecule quantity of dimethylaminoethyl ethyl ester is 8000-10000, in described B component, the mean molecule quantity of methacrylic acid diethylene glycol dilaurate is 10000-14000.
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate the most according to claim 1, it is characterized in that: in described component A, including: the dimethylaminoethyl ethyl ester of 60 parts, the solvent of 25 parts, the Allyl carbonate of 10 parts, the high heat conduction composite powder of 12 parts, the reinforcing filler of 10 parts, the antioxidant of 12 parts, the polyether rubber composition of 30 parts；In described B component, including: the methacrylic acid diethylene glycol dilaurate of 70 parts, the polyether rubber of 32 parts, the fibrous talc of 10 parts, double dimethyl amine benzyl ethyl ethers of 10 parts, the DEUCHEM2700 of 18 parts, the viscosifier of 12 parts.
A kind of high resiliency accumulator sealant based on ethyl ester and diethylene glycol dilaurate the most according to claim 1, it is characterised in that: described solvent is the mixing of one or more in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene；Reinforcing filler is the mixing of one or more that fume colloidal silica, precipitated silica and surface process in white carbon；Antioxidant is the mixing of one or more in IrgastabPUR68, antioxidant 1010 and Irganox5057；Viscosifier are isopropyl titanate, butyl titanate, r-aminopropyltriethoxywerene werene, 1,2-epoxy ethyoxyl trimethoxy silane, carbonic ester ethyl acetoacetate chelate in the mixing of one or more.
5. according to the manufacture method of a kind of based on ethyl ester and diethylene glycol dilaurate the high resiliency accumulator sealant according to any one of claim 1-4, it is characterised in that: concretely comprise the following steps:
Component A includes step: in closed reactor, adds the dimethylaminoethyl ethyl ester of above-mentioned ratio of weight and number, solvent, Allyl carbonate, polyether rubber, stirring heats up, temperature controls at 80 DEG C ~ 110 DEG C, opens vacuum pumping negative pressure, and Stress control is at below-0.1MPa；Then cooling to less than 65 DEG C, be passed through drying nitrogen and release vacuum, add above-mentioned ratio of weight and number height heat conduction composite powder, reinforcing filler, antioxidant, temperature controls at 65～75 DEG C, and mix homogeneously obtains component A fluid sealant；
B component includes step: in closed reactor, adds the methacrylic acid diethylene glycol dilaurate of above-mentioned ratio of weight and number, polyether rubber, fibrous talc, stirring heats up, and temperature controls at 80 DEG C ~ 110 DEG C, opening vacuum pumping negative pressure, Stress control is at below-0.1MPa；Then cooling to less than 65 DEG C, be passed through drying nitrogen and release vacuum, add double dimethyl amine benzyl ethyl ethers of above-mentioned ratio of weight and number, DEUCHEM2700, viscosifier, temperature controls at 65～75 DEG C, and mix homogeneously obtains B component fluid sealant.