CN105969221A - Adhesive for cartons and preparation method thereof - Google Patents
Adhesive for cartons and preparation method thereof Download PDFInfo
- Publication number
- CN105969221A CN105969221A CN201610486148.XA CN201610486148A CN105969221A CN 105969221 A CN105969221 A CN 105969221A CN 201610486148 A CN201610486148 A CN 201610486148A CN 105969221 A CN105969221 A CN 105969221A
- Authority
- CN
- China
- Prior art keywords
- parts
- stabilizer
- sodium hydroxide
- binding agent
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an adhesive for cartons, made from the following materials according to parts by weight: 3-13 parts of sodium hydroxide, 2-10 parts of maleic acid, 4-12 parts of dibutyl phthalate, 3-9 parts of silicic acid, 2-12 parts of acrylic resin, 4-12 parts of polydimethylsiloxane, 3-9 parts of polyacrylamide, 5-15 parts of hydroxymethyl cellulose, 2-10 parts of an emulsifier, and 3-9 parts of a stabilizer. The adhesive has the advantages such as good adhesion and stable service performance.
Description
Technical field
The present invention relates to adhesive field, particularly relate to a kind of carton binding agent and preparation method thereof.
Background technology
At present, along with the fast development of packaging field, in packaging industry, the demand to carton is increasing, and existing
Carton in preparation process often use to binding agent, it is bondd, existing carton binding agent because of its material selection or
The problems such as processing technique, often occur bonding the shortcomings such as insecure, the situation that carton is damaged easily occur, be unfavorable for people's
Packaging.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of carton binding agent and preparation thereof
Method.
The present invention takes techniques below scheme to realize: a kind of carton binding agent, by following according to weight portion
Raw material forms: sodium hydroxide 3-13 part, maleic acid 2-10 part, dibutyl ester 4-12 part, silicic acid 3-9 part, acrylic resin 2-12 part,
Polydimethylsiloxane 4-12 part, polyacrylamide 3-9 part, hydroxymethyl cellulose 5-15 part, emulsifying agent 2-10 part, stabilizer 3-
9 parts.
Above-mentioned a kind of carton binding agent, is made up of according to the raw material of weight portion following: sodium hydroxide 3-11 part, Malaysia
Acid 2-8 part, dibutyl ester 4-10 part, silicic acid 3-7 part, acrylic resin 2-10 part, polydimethylsiloxane 4-10 part, polyacrylamide
Amine 3-7 part, hydroxymethyl cellulose 5-12 part, emulsifying agent 2-8 part, stabilizer 3-7 part.
Above-mentioned a kind of carton binding agent, is made up of according to the raw material of weight portion following: sodium hydroxide 8 parts, maleic acid 6
Part, dibutyl ester 8 parts, silicic acid 6 parts, acrylic resin 7 parts, polydimethylsiloxane 8 parts, polyacrylamide 6 parts, hydroxylmethyl cellulose
Element 10 parts, emulsifying agent 6 parts, stabilizer 6 parts.
The preparation method of above-mentioned a kind of carton binding agent, comprises the steps of:
(1) parts by weight of material in claim 3 are chosen, by m-diaminobenzene., sodium hydroxide, calcium carbonate part, hydroxylmethyl cellulose
Element, sodium carbonate and potassium permanganate are stirred, and add deionized water while stirring, and mixing time is 30min, is mixed
Material A；
(2) Borax, Nano sepiolite powder, stabilizer and catalyst are carried out mixing treatment, carry out heat treated simultaneously, mixed
Material B；
(3) batch mixing A and mixed material B are carried out sufficient mixed processing, obtain finished product.
The method have the advantages that the present invention has that cohesive is good and serviceability is stable etc. excellent in sum
Point, can effectively prevent the situation that packing crates is cracking during bonding, and the packaging making carton is more stable.
Detailed description of the invention
A kind of carton binding agent, is made up of according to the raw material of weight portion following: sodium hydroxide 3-13 part, maleic acid 2-10
Part, dibutyl ester 4-12 part, silicic acid 3-9 part, acrylic resin 2-12 part, polydimethylsiloxane 4-12 part, polyacrylamide 3-9
Part, hydroxymethyl cellulose 5-15 part, emulsifying agent 2-10 part, stabilizer 3-9 part.
Above-mentioned a kind of carton binding agent, is made up of according to the raw material of weight portion following: sodium hydroxide 3-11 part, Malaysia
Acid 2-8 part, dibutyl ester 4-10 part, silicic acid 3-7 part, acrylic resin 2-10 part, polydimethylsiloxane 4-10 part, polyacrylamide
Amine 3-7 part, hydroxymethyl cellulose 5-12 part, emulsifying agent 2-8 part, stabilizer 3-7 part.
Above-mentioned a kind of carton binding agent, is made up of according to the raw material of weight portion following: sodium hydroxide 8 parts, maleic acid 6
Part, dibutyl ester 8 parts, silicic acid 6 parts, acrylic resin 7 parts, polydimethylsiloxane 8 parts, polyacrylamide 6 parts, hydroxylmethyl cellulose
Element 10 parts, emulsifying agent 6 parts, stabilizer 6 parts.
The preparation method of above-mentioned a kind of carton binding agent, comprises the steps of:
(1) parts by weight of material in claim 3 are chosen, by m-diaminobenzene., sodium hydroxide, calcium carbonate part, hydroxylmethyl cellulose
Element, sodium carbonate and potassium permanganate are stirred, and add deionized water while stirring, and mixing time is 30min, is mixed
Material A；
(2) Borax, Nano sepiolite powder, stabilizer and catalyst are carried out mixing treatment, carry out heat treated simultaneously, mixed
Material B；
(3) batch mixing A and mixed material B are carried out sufficient mixed processing, obtain finished product.
The present invention has that cohesive is good and the advantage such as serviceability is stable, can effectively prevent packing crates in bonding
During cracking situation, the packaging making carton is more stable.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (4)
1. a carton binding agent, it is characterised in that be made up of according to the raw material of weight portion following: sodium hydroxide 3-13 part,
Maleic acid 2-10 part, dibutyl ester 4-12 part, silicic acid 3-9 part, acrylic resin 2-12 part, polydimethylsiloxane 4-12 part is poly-
Acrylamide 3-9 part, hydroxymethyl cellulose 5-15 part, emulsifying agent 2-10 part, stabilizer 3-9 part.
A kind of carton binding agent the most according to claim 1, it is characterised in that by the following raw material group according to weight portion
Become: sodium hydroxide 3-11 part, maleic acid 2-8 part, dibutyl ester 4-10 part, silicic acid 3-7 part, acrylic resin 2-10 part, poly-diformazan
Radical siloxane 4-10 part, polyacrylamide 3-7 part, hydroxymethyl cellulose 5-12 part, emulsifying agent 2-8 part, stabilizer 3-7 part.
A kind of carton binding agent the most according to claim 1, it is characterised in that by the following raw material group according to weight portion
Become: sodium hydroxide 8 parts, maleic acid 6 parts, dibutyl ester 8 parts, silicic acid 6 parts, acrylic resin 7 parts, polydimethylsiloxane 8 parts, poly-
Acrylamide 6 parts, hydroxymethyl cellulose 10 parts, emulsifying agent 6 parts, stabilizer 6 parts.
4. according to the preparation method of a kind of carton binding agent described in claim 1-3, it is characterised in that by following steps group
Become:
(1) parts by weight of material in claim 3 are chosen, by m-diaminobenzene., sodium hydroxide, calcium carbonate part, hydroxylmethyl cellulose
Element, sodium carbonate and potassium permanganate are stirred, and add deionized water while stirring, and mixing time is 30min, is mixed
Material A；
(2) Borax, Nano sepiolite powder, stabilizer and catalyst are carried out mixing treatment, carry out heat treated simultaneously, mixed
Material B；
(3) batch mixing A and mixed material B are carried out sufficient mixed processing, obtain finished product.