CN105969102A - Coating and preparation method thereof - Google Patents
Coating and preparation method thereof Download PDFInfo
- Publication number
- CN105969102A CN105969102A CN201610544259.1A CN201610544259A CN105969102A CN 105969102 A CN105969102 A CN 105969102A CN 201610544259 A CN201610544259 A CN 201610544259A CN 105969102 A CN105969102 A CN 105969102A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal
- water
- nonmetal
- aqueous coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a metal and non-metal universal ultraviolet light cured water-based coating and a preparation method thereof. The metal and non-metal universal ultraviolet light cured water-based coating comprises the following raw materials in parts by weight: 60-70 parts of vinyl ester resin, 38-46 parts of urethane acrylate, 1-2 parts of 2- hydroxyl-2-methyl-1-phenylacetone, 0.5-1 part of imarcaptoacetate dioctyltin, 35-40 parts of ethanol and 150-180 parts of water. The coating provided by the invention has relatively short curing time which is 3min, the adhesive force to a substrate is level I, the stability is good, and the coating can not layer after being stored for six months. The preparation method provided by the invention is simple and feasible and is suitable for being popularized and applied in a wide range.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of general ultraviolet solidified aqueous coating of metal and nonmetal and preparation method thereof.
Background technology
Ultraviolet-curing paint is more and more paid close attention to by people because of its good feature of environmental protection, but traditional photocureable coating is typically not fee from and can use volatile organic thing excitatory to human body, therefore existing ultraviolet-curing paint has used water to substitute zest organic diluent, ultraviolet solidified aqueous coating has enjoyed researcher to pay close attention to, but existing ultraviolet-curing paint still suffers from the deficiency that hardening time is longer, stability is the best.
In sum, the deficiencies in the prior art how are overcome to become paint field problem demanding prompt solution.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art to propose a kind of general ultraviolet solidified aqueous coating of metal and nonmetal and preparation method thereof, the paint solidification time of the present invention is shorter, and stability is preferable, and long storage time is difficult to layering.
Technical scheme is as follows: the general ultraviolet solidified aqueous coating of metal and nonmetal, the following raw material including according to mass fraction meter: vinyl ester resin 60-70 part, urethane acrylate 38-46 part, 2-hydroxy-2-methyl-1-phenylacetone 1-2 part, Imarcaptoacetate dioctyltin 0.5-1 part, ethanol 35-40 part, water 150-180 part.
The general ultraviolet solidified aqueous coating of described metal and nonmetal, the following raw material including according to mass fraction meter: vinyl ester resin 65 parts, urethane acrylate 40 parts, 2-hydroxy-2-methyl-1-phenylacetone 1.5 parts, Imarcaptoacetate dioctyltin 0.7 part, ethanol 37 parts, 160 parts of water.
The preparation method of the general ultraviolet solidified aqueous coating of described metal and nonmetal, comprise the following steps: according to quality proportioning, by vinyl ester resin and urethane acrylate mixing and stirring, add 2-hydroxy-2-methyl-1-phenylacetone and Imarcaptoacetate dioctyltin mixing, the mixed liquor of dropping second alcohol and water, rate of addition controls to be 2mL/min, drips complete stirring, obtains the general ultraviolet solidified aqueous coating of metal and nonmetal.
Beneficial effect: the paint solidification time of the present invention is shorter, hardening time is 3min, and the adhesive force to base material is 1 grade, has good stability, not stratified after depositing 6 months；Preparation method of the present invention is simple, is suitable to popularization and application on a large scale.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail.
The general ultraviolet solidified aqueous coating of embodiment 1 metal and nonmetal, the following raw material including according to mass fraction meter: vinyl ester resin 60 parts, urethane acrylate 38 parts, 2-hydroxy-2-methyl-1-phenylacetone 1 part, Imarcaptoacetate dioctyltin 0.5 part, ethanol 35 parts, 150 parts of water.
The present embodiment preparation method: according to quality proportioning, by vinyl ester resin and urethane acrylate mixing and stirring, add 2-hydroxy-2-methyl-1-phenylacetone and Imarcaptoacetate dioctyltin mixing, the mixed liquor of dropping second alcohol and water, rate of addition controls as 2mL/min, drip complete stirring, obtain the general ultraviolet solidified aqueous coating of metal and nonmetal.
Claims (3)
1. the general ultraviolet solidified aqueous coating of metal and nonmetal, it is characterized in that, the following raw material including according to mass fraction meter: vinyl ester resin 60-70 part, urethane acrylate 38-46 part, 2-hydroxy-2-methyl-1-phenylacetone 1-2 part, Imarcaptoacetate dioctyltin 0.5-1 part, ethanol 35-40 part, water 150-180 part.
The general ultraviolet solidified aqueous coating of metal and nonmetal the most according to claim 1, it is characterized in that, the following raw material including according to mass fraction meter: vinyl ester resin 65 parts, urethane acrylate 40 parts, 2-hydroxy-2-methyl-1-phenylacetone 1.5 parts, Imarcaptoacetate dioctyltin 0.7 part, ethanol 37 parts, 160 parts of water.
3. the preparation method of the general ultraviolet solidified aqueous coating of metal and nonmetal described in claim 1, it is characterized in that, comprise the following steps: according to quality proportioning, by vinyl ester resin and urethane acrylate mixing and stirring, adding 2-hydroxy-2-methyl-1-phenylacetone and Imarcaptoacetate dioctyltin mixing, the mixed liquor of dropping second alcohol and water, rate of addition controls as 2mL/min, drip complete stirring, obtain the general ultraviolet solidified aqueous coating of metal and nonmetal.