CN105968859A - Wood-plastic wall panel and production method thereof - Google Patents
Wood-plastic wall panel and production method thereof Download PDFInfo
- Publication number
- CN105968859A CN105968859A CN201610462869.7A CN201610462869A CN105968859A CN 105968859 A CN105968859 A CN 105968859A CN 201610462869 A CN201610462869 A CN 201610462869A CN 105968859 A CN105968859 A CN 105968859A
- Authority
- CN
- China
- Prior art keywords
- wood
- shingle nail
- wall panel
- moulded
- plastic wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wood-plastic wall panel and a production method thereof. Through adding of bamboo fiber/bamboo powder and oxidized starch, a network structure is formed under the curing cross-linking action of hydroxyl cellulose sodium. Firstly, the network structure can effectively buffer external impact, so that the fragility of the wood-plastic wall panel is reduced; secondly, the gaps among PCV resin particles can be filled with bamboo fiber/bamboo powder particles, so that the strength of the wood-plastic wall panel is greatly improved, and can be higher and higher as time goes on, and the wood-plastic wall panel is resistant to acid, alkali, light and rain erosion, low in aging possibility, and mould-proof/mothproof; thirdly, the consumption of calcium carbonate and wood flour can be greatly reduced, and the water absorption rate of the wood-plastic wall panel is reduced.
Description
Technical field
The present invention relates to building board technical field, particularly relate to a kind of wood and mould shingle nail and production method thereof.
Background technology
Shingle nail moulded by wood, and wood is moulded, i.e. wood plastic composite, is that the class being in recent years surging forward both at home and abroad is novel
Composite, refers to utilize polyethylene, polypropylene and polrvinyl chloride etc., replaces common resin adhesive, with
The useless Plant fiber such as wood powder more than more than 35%-70%, rice husk, straw are mixed into new wood materials, then
Through the plastic processings such as extruding, mold pressing, injection mo(u)lding, the sheet material produced or section bar.It is mainly used in building
The industries such as material, furniture, logistics packaging.Through being hot extruded into after plastics and wooden powder are mixed by a certain percentage
The sheet material of type, referred to as extrudes wood-plastic composite panel.
Shingle nail moulded by wood the most on the market, and life-time service is the most aging, additionally, materials water-resistant is poor,
It is easily deformed after water suction, tympanites.
Summary of the invention
In view of this, the present invention proposes and a kind of be difficult to wood aging, water-tolerant and mould shingle nail and production thereof
Method.
The technical scheme is that and be achieved in that: on the one hand, the invention provides a kind of wood and mould shingle nail,
It is as follows that shingle nail raw material components mass fraction moulded by described wood,
On the basis of above technical scheme, it is preferred that described wood moulds shingle nail raw material components mass fraction such as
Under,
Second aspect, the invention provides wood described in first aspect and moulds the preparation method of shingle nail, including following
Step,
S1, is crushed to bamboo fibre or bamboo powder more than 40 mesh, then mixes with PVC-8s resin, Oxytarch
Uniformly;
S2, adds ACR401, CPE, paraffin, yellow hair infusion, foaming control agent-100, PE wax, hard
Fat acid is warming up to 60~85 DEG C, adds the aqueous solution of sodium hydroxyl cellulose, reacts 1~2 hour, is dried;
S3, extrusion molding obtains wood and moulds shingle nail.
Shingle nail moulded by the wood of the present invention and production method has the advantages that relative to prior art
By adding bamboo fibre or bamboo powder and Oxytarch, shape under the solidification crosslinked action of sodium hydroxyl cellulose
Reticulate structure, on the one hand, this network structure can effective absorbing external impulsive force, reduce sheet material fragility;The
Two aspects, described bamboo fibre or bamboo powder granule can be filled in the gap of PCV resin particle so that sheet material is strong
Degree increases substantially, and As time goes on, timber intensity can be more and more higher, acid and alkali-resistance, illumination and
Raindrop erosion, is difficult to aging, prevents mouldy or damages by worms;3rd, calcium carbonate and wood powder can be greatly lowered
Consumption, reduce sheet material water absorption rate.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, below will be to enforcement
In example or description of the prior art, the required accompanying drawing used is briefly described, it should be apparent that, describe below
In accompanying drawing be only some embodiments of the present invention, for those of ordinary skill in the art, do not paying
On the premise of going out creative work, it is also possible to obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 is the flow chart that the preparation method of shingle nail moulded by wood of the present invention.
Detailed description of the invention
Below in conjunction with the accompanying drawing in embodiment of the present invention, the technical scheme in embodiment of the present invention is entered
Row clearly and completely describes, it is clear that described embodiment is only a part of embodiment of the present invention,
Rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not having
Have and make the every other embodiment obtained under creative work premise, broadly fall into the model of present invention protection
Enclose.
Embodiment 1
Shingle nail moulded by the wood of the present embodiment, and its preparation comprises the following steps,
50 parts of bamboo fibres are crushed to more than 40 mesh by S1, then with 50 parts of PVC-8s resins, 30 parts of oxidations
Starch mix homogeneously;
S2, adds 1 part of ACR401,3 parts of CPE, 0.1 part of paraffin, 0.5 part of yellow hair infusion, 3 parts of foaming
Regulator-100,0.1 part of PE wax, 0.5 part of stearic acid are warming up to 60 DEG C, add 3 parts of sodium hydroxyl cellulose
Aqueous solution, reacts 1 hour, is dried;
S3, extrusion molding obtains wood and moulds shingle nail.
After testing, shingle nail moulded by the wood that the present embodiment prepares,
Pull tensile strength: >=8.0%;
Water absorption rate (normal atmosphere) :≤3%;
Shao Er hardness (a): >=47;
Apparent density: >=0.45g/ml;
Impact strength: >=14.4KJ/m2。
Embodiment 2
Shingle nail moulded by the wood of the present embodiment, and its preparation comprises the following steps,
S1, more than 65 parts of bamboo fibres and bamboo powder co-grinding to 40 mesh, then with 50 parts of PVC-8s resins,
30~50 parts of Oxytarch mix homogeneously;
S2, add 1~3 part of ACR401,3~5 parts of CPE, 0.1~1 part of paraffin, 0.8 part of yellow hair infusion, 5
Part foaming control agent-100,0.5 part of PE wax, 1 part of stearic acid are warming up to 75 DEG C, add 4 parts of hydroxyl fibers
The aqueous solution of element sodium, reacts 1.5 hours, is dried;
S3, extrusion molding obtains wood and moulds shingle nail.
After testing, shingle nail moulded by the wood that the present embodiment prepares,
Pull tensile strength: >=8.0%;
Water absorption rate (normal atmosphere) :≤3%;
Shao Er hardness (a): >=47;
Apparent density: >=0.45g/ml;
Impact strength: >=14.4KJ/m2。
Embodiment 3
Shingle nail moulded by the wood of the present embodiment, and its preparation comprises the following steps,
80 parts of bamboo powder are crushed to more than 40 mesh, then form sediment with 50 parts of PVC-8s resins, 50 parts of oxidations by S1
Powder mix homogeneously;
S2, adds 3 parts of ACR401,5 parts of CPE, 1 part of paraffin, 1 part of yellow hair infusion, 7 parts of foaming tune
Joint agent-100,1 part of PE wax, 1.5 parts of stearic acid are warming up to 85 DEG C, add the water of 5 parts of sodium hydroxyl cellulose
Solution, reacts 2 hours, is dried;
S3, extrusion molding obtains wood and moulds shingle nail.
After testing, shingle nail moulded by the wood that the present embodiment prepares,
Pull tensile strength: >=8.0%;
Water absorption rate (normal atmosphere) :≤3%;
Shao Er hardness (a): >=47;
Apparent density: >=0.45g/ml;
Impact strength: >=14.4KJ/m2。
The foregoing is only the better embodiment of the present invention, not in order to limit the present invention, all at this
Within the spirit of invention and principle, any modification, equivalent substitution and improvement etc. made, should be included in this
Within the protection domain of invention.
Claims (3)
1. shingle nail moulded by a wood, it is characterised in that: it is as follows that shingle nail raw material components mass fraction moulded by described wood,
2. shingle nail moulded by wood as claimed in claim 1, it is characterised in that: shingle nail raw material group moulded by described wood
Divide mass fraction as follows,
3. the preparation method of shingle nail moulded by wood as claimed in claim 1, it is characterised in that: include following step
Suddenly,
S1, is crushed to bamboo fibre or bamboo powder more than 40 mesh, then mixes with PVC-8s resin, Oxytarch
Uniformly;
S2, adds ACR401, CPE, paraffin, yellow hair infusion, foaming control agent-100, PE wax, hard
Fat acid is warming up to 60~85 DEG C, adds the aqueous solution of sodium hydroxyl cellulose, reacts 1~2 hour, is dried;
S3, extrusion molding obtains wood and moulds shingle nail.