CN105949952A - Method for manufacturing smooth coating on inner wall of tenebrio molitor breeding wood case - Google Patents

Method for manufacturing smooth coating on inner wall of tenebrio molitor breeding wood case Download PDF

Info

Publication number
CN105949952A
CN105949952A CN201610405627.4A CN201610405627A CN105949952A CN 105949952 A CN105949952 A CN 105949952A CN 201610405627 A CN201610405627 A CN 201610405627A CN 105949952 A CN105949952 A CN 105949952A
Authority
CN
China
Prior art keywords
parts
coating
tenebrio molitor
high pressure
wooden case
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610405627.4A
Other languages
Chinese (zh)
Inventor
张悦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610405627.4A priority Critical patent/CN105949952A/en
Publication of CN105949952A publication Critical patent/CN105949952A/en
Pending legal-status Critical Current

Abstract

The invention provides a method for manufacturing a smooth coating on the inner wall of a tenebrio molitor breeding wood case. The method comprises the steps that a coating material is pumped into a high-pressure steam spray gun; continuous stirring is carried out in the pumping-in process of the coating material; the coating material is scattered by high-pressure steam in the high-pressure steam spray gun and ejected out along with airflow; high-pressure airflow directly acts on the inner wall of the wood case in an even spraying mode, wherein the airflow speed is 500-510 m/s, the high-pressure gas temperature is 100-115 DEG C, the ejection distance is 35mm, and the included angle of the high-pressure gas acting on the inner wall of the wood case is 45-75 degrees; a high-compactness smooth coating with the thickness of 0.15-0.25 mm is formed on the inner wall of the wood case. The coating material will not volatilize hazardous gas, the high-compactness smooth coating can be formed, and the coating is nontoxic, produces no adverse influence on tenebrio molitor, is high in surface smoothness and can prevent tenebrio molitor from climbing upwards.

Description

A kind of cultivation tenebrio molitor makes lubricious method on wooden case inwall
Technical field
The present invention relates to tenebrio molitor cultivation field, particularly relate to a kind of system on tenebrio molitor cultivation wooden case inwall Make lubricious method.
Background technology
Tenebrio molitor not only protein content is high, and amino acid classes is complete, composition reasonable, possibly together with rich The nutritional labelings such as the unsaturated fatty acid of richness, vitamin, mineral, tenebrio molitor is also the food of a kind of high-quality Product resource insect, has the highest healthy nutritive value, and deep processing product have tenebrio molitor high protein powder, ammonia Base acid oral liquids etc., can be oriented quantitatively production.
Medicinal and live body moves primarily to allow larva fast-growth, its chief value be to raise tenebrio molitor Thing feedstuff, the additive of high protein, many universal culture benefits of raiser are the highest, due to unclear Solving the habit of tenebrio molitor, feedstuff environmental Kuznets Curves is unreasonable, the method not finding quickly weightening finish, leads Causing growth cycle longer, feed waste, benefit is low.
Tenebrio molitor is former is stored grain insects, and natural disposition is active.And the most all in activity, the energy of consumption is more, It is unfavorable for quickly increasing weight.
The physiological make-up of tenebrio molitor is highly susceptible to the injury of harmful gas, and the main source of harmful gas has Coating is harmful to source, and the coating great majority such as rendering in cultivation, paint contain volatile harmful gas, this Tenebrio molitor cultivation indirectly can be brought unnecessary loss by a little harmful gass, and insect is to these harmful gass Especially sensitive.In being currently used for breeding box body, coating can be to volatilizing toxic and harmful, to tenebrio molitor Cultivation bring loss.
Summary of the invention
It is an object of the invention to provide a kind of cultivation tenebrio molitor and make lubricious side on wooden case inwall Method, to solve above-mentioned technical problem.
The technical problem to be solved realizes by the following technical solutions:
A kind of cultivation tenebrio molitor makes lubricious method on wooden case inwall, it is characterised in that
Being pumped into by coating in high steam spray gun, coating is continuously stirred during pumping into, and coating steams at high pressure Being broken up by high steam in vapour spray gun and go out with jet-impingement, high pressure draught is straight in the way of uniformly strafing Connect and act on wooden case inwall, air velocity is 500m/s～510m/s, gases at high pressure temperature be 100 DEG C～ 115 DEG C, jet length be 35mm, it is 45 °～75 ° that high pressure draught acts on the angle of wooden case inwall, Forming thickness on wooden case inwall is high lubricious of 0.15mm～0.25mm compactness；
Coating used is made up of the raw material of following weight portion:
Epoxy resin 15 parts, 12 parts of phenolic resin, 6 parts of amino resins, 4 parts of paraffin, bentonite 0.2 part, Corn starch 3 parts, micro-crystal powder 1.2 parts, glass fiber powder 1.5 parts, Brazil wax 6 parts, forming agent 2.5 Part, tributyl citrate 1.5 parts, gas-phase silica 0.2 part, solvent 65 parts.
Described solvent is at least one in Ketohexamethylene, ethylene glycol monobutyl ether, butyl acetate, n-butyl alcohol.
Described forming agent is made up of the raw material of following weight portion:
Chlorinated paraffin 3 parts, sucrose ester 0.5 part, phthalic acid ester 6.4 parts, PE 2.5 parts, carboxymethyl are fine Dimension element 1.2 parts of sodium, cellulose acetate 0.2 part, maleic anhydride grafted monomers 0.35 part；
Preparation method:
Being proportionally added into above-mentioned raw materials in high-pressure bottle carrying out high pressure batch mixing, pressure is 2～3 times of atmospheric pressure, The temperature of high pressure batch mixing is 155-180 DEG C, and the time of high pressure batch mixing is 8-10 minute；It is subsequently adding extruder Complete to melt, the process of batch mixing, extrusion, the machine barrel of extruder includes four districts, by feed end to extrusion End, the temperature in four districts is followed successively by 185 DEG C, 230 DEG C, 205 DEG C, 195 DEG C, the machine barrel of described extruder Interior pressure is 0.06MPa.
The preparation method of inner-wall paint:
(1) solvent is placed in container and adds in container epoxy resin, stirring and dissolving, after filtering, Obtain solution mixture A；
(2) in solution mixture A, add phenolic resin, amino resins, stirring and dissolving, obtain solution Mixture B, and it is cooled to 50 DEG C；
(3) in solution mixture B, paraffin, bentonite, corn starch, micro-crystal powder, glass fibers are added Dimension powder, Brazil wax, forming agent, tributyl citrate and gas-phase silica, it is ensured that solution enough stirs Mix half an hour, while stirring, under the conditions of supersonic frequency 40kHz, power 45W, carry out supersound process, Stirring is cooled to 40 DEG C after terminating, and obtains coating.
Tenebrio molitor cultivates in wooden case, and bottom surface and side in wooden case are coated with the lubricious of densification, institute The bottom surface stating wooden case has several conical surface culture zones raised up, and tenebrio molitor is isolated in each conical surface Cultivating in culture zone, cultivate temperature 29 DEG C, relative humidity is 65%；
Conical surface culture zone includes the circular groove being located on wooden case bottom surface, and the middle part of circular groove raises up And formed domatic, domatic have the gradient that two sections are different, and wherein the gradient of hypomere is 1:3, epimere The gradient more than 2:3, tenebrio molitor is movable in being limited in circular groove and domatic hypomere region.
The invention has the beneficial effects as follows:
The present invention designs a kind of bottom wooden case with conical surface culture zone, and tenebrio molitor is separated into multiple region Cultivate, and the tenebrio molitor activity space in each culture zone is restricted, and can reduce tenebrio molitor Activity, is beneficial to quickly increase weight.
Epoxy resin is the thermosetting plastics that a class is important, is widely used in the purposes such as adhesive, coating, phenol Urea formaldehyde, is a kind of synthetic plastic, colourless or yellowish-brown transparent solid, thermostability, flame resistance, water-fast Property, alkali resistance, oil resistivity, corrosion resistance etc., the aqueous solution of amino resins has and hydrochloric acid, sulphuric acid etc. Equal highly acid, it has non-volatile, odorless and the feature minimum to tenebrio molitor toxicity, amino tree Fat aqueous solution is slower to the corrosion product effect of ferrum；
Comprise only in the coating of the present invention and the benzene of trace, free of toxic effects to tenebrio molitor, the present invention's Coating has extremely strong anticorrosive property and rustless property, has good antiacid sulfuration resistant performance, has relatively Strong resistance to elevated temperatures, will not volatilize toxic and harmful, reach Food Packaging Standards；The present invention's The method of stocking of coating is simple, and quickly, production efficiency is high.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from Solve, below in conjunction with specific embodiment, the present invention is expanded on further, but following embodiment is only the present invention Preferred embodiment, and not all.Based on the embodiment in embodiment, those skilled in the art are not having On the premise of making creative work, obtained other embodiments, broadly falls into protection scope of the present invention.
Tenebrio molitor cultivates in wooden case, and bottom surface and side in wooden case are coated with the lubricious of densification, institute The bottom surface stating wooden case has several conical surface culture zones raised up, and tenebrio molitor is isolated in each conical surface Cultivating in culture zone, cultivate temperature 29 DEG C, relative humidity is 65%；
Conical surface culture zone includes the circular groove being located on wooden case bottom surface, and the middle part of circular groove raises up And formed domatic, domatic have the gradient that two sections are different, and wherein the gradient of hypomere is 1:3, epimere The gradient more than 2:3, tenebrio molitor is movable in being limited in circular groove and domatic hypomere region；
Lubricious coating used is made up of the raw material of following weight portion:
Epoxy resin 15 parts, 12 parts of phenolic resin, 6 parts of amino resins, 4 parts of paraffin, bentonite 0.2 part, Corn starch 3 parts, micro-crystal powder 1.2 parts, glass fiber powder 1.5 parts, Brazil wax 6 parts, forming agent 2.5 Part, tributyl citrate 1.5 parts, gas-phase silica 0.2 part, solvent 65 parts.
At least one in Ketohexamethylene, ethylene glycol monobutyl ether, butyl acetate, n-butyl alcohol selected by solvent.
Forming agent is made up of the raw material of following weight portion:
Chlorinated paraffin 3 parts, sucrose ester 0.5 part, phthalic acid ester 6.4 parts, PE 2.5 parts, carboxymethyl are fine Dimension element 1.2 parts of sodium, cellulose acetate 0.2 part, maleic anhydride grafted monomers 0.35 part；
Preparation method:
Being proportionally added into above-mentioned raw materials in high-pressure bottle carrying out high pressure batch mixing, pressure is 2～3 times of atmospheric pressure, The temperature of high pressure batch mixing is 155-180 DEG C, and the time of high pressure batch mixing is 8-10 minute；It is subsequently adding extruder Complete to melt, the process of batch mixing, extrusion, the machine barrel of extruder includes four districts, by feed end to extrusion End, the temperature in four districts is followed successively by 185 DEG C, 230 DEG C, 205 DEG C, 195 DEG C, the machine barrel of described extruder Interior pressure is 0.06MPa.
The preparation method of coating, step is as follows:
(1) solvent is placed in container and adds in container epoxy resin, stirring and dissolving, after filtering, Obtain solution mixture A；
(2) in solution mixture A, add phenolic resin, amino resins, stirring and dissolving, obtain solution Mixture B, and it is cooled to 50 DEG C；
(3) in solution mixture B, paraffin, bentonite, corn starch, micro-crystal powder, glass fibers are added Dimension powder, Brazil wax, forming agent, tributyl citrate and gas-phase silica, it is ensured that solution enough stirs Mix half an hour, while stirring, under the conditions of supersonic frequency 40kHz, power 45W, carry out supersound process, Stirring is cooled to 40 DEG C after terminating, and obtains coating.
Wooden case inwall coats lubricious method:
Being pumped into by coating in high steam spray gun, coating is continuously stirred during pumping into, and coating steams at high pressure Being broken up by high steam in vapour spray gun and go out with jet-impingement, high pressure draught is straight in the way of uniformly strafing Connect and act on plank inwall, air velocity is 500m/s～510m/s, gases at high pressure temperature be 100 DEG C～ 115 DEG C, jet length be 35mm, it is 45 °～75 ° that high pressure draught acts on the angle of plank inwall, It is high lubricious of 0.15mm～0.25mm compactness that plank inwall forms thickness, and this coating is nontoxic, no Can have a negative impact tenebrio molitor, surface flatness is high, can stop that tenebrio molitor is upwards ascended.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.One's own profession Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation The preference being only the present invention described in book, is not intended to limit the present invention, without departing from present invention essence On the premise of god and scope, the present invention also has various changes and modifications, and these changes and improvements both fall within In scope of the claimed invention.Claimed scope by appending claims and etc. Effect thing defines.

Claims (3)

1. one kind makes lubricious method on tenebrio molitor cultivation wooden case inwall, it is characterised in that
Being pumped into by coating in high steam spray gun, coating is continuously stirred during pumping into, and coating steams at high pressure Being broken up by high steam in vapour spray gun and go out with jet-impingement, high pressure draught is straight in the way of uniformly strafing Connect and act on wooden case inwall, air velocity is 500m/s～510m/s, gases at high pressure temperature be 100 DEG C～ 115 DEG C, jet length be 35mm, it is 45 °～75 ° that high pressure draught acts on the angle of wooden case inwall, Forming thickness on wooden case inwall is high lubricious of 0.15mm～0.25mm compactness；
Coating used is made up of the raw material of following weight portion:
Epoxy resin 15 parts, 12 parts of phenolic resin, 6 parts of amino resins, 4 parts of paraffin, bentonite 0.2 part, Corn starch 3 parts, micro-crystal powder 1.2 parts, glass fiber powder 1.5 parts, Brazil wax 6 parts, forming agent 2.5 Part, tributyl citrate 1.5 parts, gas-phase silica 0.2 part, solvent 65 parts.
The most according to claim 1 cultivation tenebrio molitor makes lubricious method on wooden case inwall, It is characterized in that: described solvent be in Ketohexamethylene, ethylene glycol monobutyl ether, butyl acetate, n-butyl alcohol extremely Few one.
The most according to claim 1 cultivation tenebrio molitor makes lubricious method on wooden case inwall, It is characterized in that: described forming agent is made up of the raw material of following weight portion:
Chlorinated paraffin 3 parts, sucrose ester 0.5 part, phthalic acid ester 6.4 parts, PE 2.5 parts, carboxymethyl are fine Dimension element 1.2 parts of sodium, cellulose acetate 0.2 part, maleic anhydride grafted monomers 0.35 part；
Preparation method:
Being proportionally added into above-mentioned raw materials in high-pressure bottle carrying out high pressure batch mixing, pressure is 2～3 times of atmospheric pressure, The temperature of high pressure batch mixing is 155-180 DEG C, and the time of high pressure batch mixing is 8-10 minute；It is subsequently adding extruder Complete to melt, the process of batch mixing, extrusion, the machine barrel of extruder includes four districts, by feed end to extrusion End, the temperature in four districts is followed successively by 185 DEG C, 230 DEG C, 205 DEG C, 195 DEG C, the machine barrel of described extruder Interior pressure is 0.06MPa.
CN201610405627.4A 2016-06-08 2016-06-08 Method for manufacturing smooth coating on inner wall of tenebrio molitor breeding wood case Pending CN105949952A (en)