CN105926296A - Composite fabric applied to back of backpack - Google Patents
Composite fabric applied to back of backpack Download PDFInfo
- Publication number
- CN105926296A CN105926296A CN201610327074.5A CN201610327074A CN105926296A CN 105926296 A CN105926296 A CN 105926296A CN 201610327074 A CN201610327074 A CN 201610327074A CN 105926296 A CN105926296 A CN 105926296A
- Authority
- CN
- China
- Prior art keywords
- fabric
- composite material
- parts
- backpack
- processed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of bag materials, in particular to a composite fabric applied to the back of a backpack. By means of air texturing equipment, polyester industrial filaments are processed into air textured yarn, a fabric structure adopts plain weave, warp and weft adopt air textured yarn, and grey cloth is obtained through weaving by means of a warp sizing technology; water-proofing agent brushing treatment is conducted on the grey cloth; the surface of the fabric brushed with a water-proofing agent is brushed with a functional coating, and the functional coating is prepared by processing bamboo leaves, radix et rhizoma rhei, activated carbon, gypsum, herba taraxaci and ethyl alcohol; drying and plasticizing treatment are conducted on the fabric, and the composite fabric applied to the back of the backpack is obtained. The composite fabric has the advantages of being high in tensile strength, high in tearing strength, high in wear resistant property, clear in printing, excellent in color light and the like. Meanwhile, before drying treatment is conducted, due to the fact that the fabric is brushed with the functional coating with a health-preserving property, when people use the backpack, people can smell aroma, and the effects of relieving a fever, clearing fire and regulating a mood can be achieved.
Description
Technical field
The present invention relates to box material technical field, be specifically related to the composite material that a kind of both shoulders bag back uses.
Background technology
The performance requirement that case and bag fabric is general is that wearability is high, uses intensity preferable, so that the case and bag made can load more
Object, carries more weight, uses the more long time safely.Existing this kind of case and bag fabric, in preparation technology, typically uses tradition
Common material fabric process through traditional handicraft, the case and bag of this processing arise that hot strength is low, stamp conservation degree
The defect such as poor.
Meanwhile, for both shoulders bag, due to itself and the shoulder that contact site is human body of human body, if its back fabric uses
Conventional material, will certainly cause the defects such as caloric value is big.It addition, the fabric of existing both shoulders bag does not has the concept of health preserving, people
When using summer, the most flighty and impetuous, get angry.
Summary of the invention
It is an object of the invention to provide the composite material that a kind of both shoulders bag back uses, for achieving the above object, the present invention uses
Techniques below scheme:
The composite material that a kind of both shoulders bag back uses, manufacturing process comprises the steps:
1), utilize air-texturing equipment that the polyester industrial filament yarn that strength index is higher than 7.8cN/dtex is processed into air deformation yarn,
The air pressure adding man-hour is 5-10kg, and over feed rate(OFR) controls as 10-15%;
2), fabric construction select plain weave, use step 1 through, weft yarn) air deformation yarn processed, use warp thread sizing
Technique weaving obtains grey cloth, and slurry is that 1:1:1.5 mixes by polyvinyl alcohol, acrylic acid methyl ester. and silane coupler according to weight ratio
Conjunction forms;
3), to grey cloth carrying out brushing waterproofing agent process, waterproofing agent uses Japan AGC AG-710, and brushing amount is 150-200g/m2;
4), by the external coating functional paint of the fabric after brushing waterproofing agent, functional paint is by Folium Bambusae, Radix Et Rhizoma Rhei, activated carbon, stone
Cream, Herba Taraxaci and ethanol are processed into;
5), to fabric dry and plastics processing obtain the composite material that both shoulders bag back uses, dry temperature and be 140-175 DEG C,
Plasticization temperature is 190-220 DEG C.
Preferably, step 2) in the structural formula of silane coupler be:
Preferably, step 4) in the preparation method of functional paint be: 5 parts of Folium Bambusaes, 5 parts of Radix Et Rhizoma Rhei, 3 parts of Herba Taraxacis are put into appearance
In device, boiling 1 hour, amount of water is 10 times of solid three's weight sum, filters residue, adds 1 in gained liquid
Part activated carbon and 3 parts of Gypsum Fibrosum, after stirring, concentrate, and limit concentrates, while add ethanol, to remove moisture, until moisture
Content is less than 5%;Then solid abrasive is become powder, adds the ethanol of powder weight 3 times, form coating.
The composite material that the both shoulders bag back of the present invention uses, its beneficial effect shows:
The composite material that the both shoulders bag back of the present invention uses, by rational modification manufacture method, particularly at warp thread slashing technique
Weaving with the addition of the silane coupler containing special composition, so that the fabric manufactured possesses high tensile strength, height tears
Strongly, high-wear resistance, the advantage such as stamp is clear, coloured light is excellent.Meanwhile, before drying and processing, possess by having brushed
The functional coating of health preserving speciality, makes people when using both shoulders bag, can not only smell aromatic odor, additionally it is possible to have antipyretic dissipating
Fire, effect of conditioning mood.
Detailed description of the invention
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to institute of the present invention
The citing made and explanation, described specific embodiment is made various amendment or benefit by affiliated those skilled in the art
Fill or use similar mode to substitute, without departing from the design of invention or surmount scope defined in the claims, all
Protection scope of the present invention should be belonged to.
Embodiment 1
The composite material that a kind of both shoulders bag back uses, manufacturing process comprises the steps:
1), utilize air-texturing equipment that the polyester industrial filament yarn that strength index is higher than 7.8cN/dtex is processed into air deformation yarn,
The air pressure adding man-hour is 8kg, and it is 15% that over feed rate(OFR) controls.
2), fabric construction select plain weave, use step 1 through, weft yarn) air deformation yarn processed, use warp thread sizing
Technique weaving obtains grey cloth, and slurry is that 1:1:1.5 mixes by polyvinyl alcohol, acrylic acid methyl ester. and silane coupler according to weight ratio
Conjunction forms.
The structural formula of silane coupler is:
3), to grey cloth carrying out brushing waterproofing agent process, waterproofing agent uses Japan AGC AG-710, and brushing amount is 150g/m2。
4), by the external coating functional paint of the fabric after brushing waterproofing agent, functional paint is by Folium Bambusae, Radix Et Rhizoma Rhei, activated carbon, stone
Cream, Herba Taraxaci and ethanol are processed into.Preparation method is: put in container by 5 parts of Folium Bambusaes, 5 parts of Radix Et Rhizoma Rhei, 3 parts of Herba Taraxacis,
Boiling 1 hour, amount of water is 10 times of solid three's weight sum, filters residue, adds 1 part of activity in gained liquid
Charcoal and 3 parts of Gypsum Fibrosum, after stirring, concentrate, and limit concentrates, while add ethanol, to remove moisture, until moisture is little
In 5%;Then solid abrasive is become powder, adds the ethanol of powder weight 3 times, form coating.
5), to fabric drying and plastics processing obtains the composite material that both shoulders bag back uses, drying temperature is 160 DEG C,
Plasticization temperature is 190 DEG C.
Embodiment 2
The composite material that a kind of both shoulders bag back uses, manufacturing process comprises the steps:
1), utilize air-texturing equipment that the polyester industrial filament yarn that strength index is higher than 7.8cN/dtex is processed into air deformation yarn,
The air pressure adding man-hour is 5kg, and it is 12% that over feed rate(OFR) controls.
2), fabric construction select plain weave, use step 1 through, weft yarn) air deformation yarn processed, use warp thread sizing
Technique weaving obtains grey cloth, and slurry is that 1:1:1.5 mixes by polyvinyl alcohol, acrylic acid methyl ester. and silane coupler according to weight ratio
Conjunction forms.
The structural formula of silane coupler is:
3), to grey cloth carrying out brushing waterproofing agent process, waterproofing agent uses Japan AGC AG-710, and brushing amount is 200g/m2。
4), by the external coating functional paint of the fabric after brushing waterproofing agent, functional paint is by Folium Bambusae, Radix Et Rhizoma Rhei, activated carbon, stone
Cream, Herba Taraxaci and ethanol are processed into.Preparation method is: put in container by 5 parts of Folium Bambusaes, 5 parts of Radix Et Rhizoma Rhei, 3 parts of Herba Taraxacis,
Boiling 1 hour, amount of water is 10 times of solid three's weight sum, filters residue, adds 1 part of activity in gained liquid
Charcoal and 3 parts of Gypsum Fibrosum, after stirring, concentrate, and limit concentrates, while add ethanol, to remove moisture, until moisture is little
In 5%;Then solid abrasive is become powder, adds the ethanol of powder weight 3 times, form coating.
5), to fabric drying and plastics processing obtains the composite material that both shoulders bag back uses, drying temperature is 170 DEG C,
Plasticization temperature is 200 DEG C.
Embodiment 3
The composite material that a kind of both shoulders bag back uses, manufacturing process comprises the steps:
1), utilize air-texturing equipment that the polyester industrial filament yarn that strength index is higher than 7.8cN/dtex is processed into air deformation yarn,
The air pressure adding man-hour is 10kg, and it is 10% that over feed rate(OFR) controls.
2), fabric construction select plain weave, use step 1 through, weft yarn) air deformation yarn processed, use warp thread sizing
Technique weaving obtains grey cloth, and slurry is that 1:1:1.5 mixes by polyvinyl alcohol, acrylic acid methyl ester. and silane coupler according to weight ratio
Conjunction forms.
The structural formula of silane coupler is:
3), to grey cloth carrying out brushing waterproofing agent process, waterproofing agent uses Japan AGC AG-710, and brushing amount is 180g/m2。
4), by the external coating functional paint of the fabric after brushing waterproofing agent, functional paint is by Folium Bambusae, Radix Et Rhizoma Rhei, activated carbon, stone
Cream, Herba Taraxaci and ethanol are processed into.Preparation method is: put in container by 5 parts of Folium Bambusaes, 5 parts of Radix Et Rhizoma Rhei, 3 parts of Herba Taraxacis,
Boiling 1 hour, amount of water is 10 times of solid three's weight sum, filters residue, adds 1 part of activity in gained liquid
Charcoal and 3 parts of Gypsum Fibrosum, after stirring, concentrate, and limit concentrates, while add ethanol, to remove moisture, until moisture is little
In 5%;Then solid abrasive is become powder, adds the ethanol of powder weight 3 times, form coating.
5), to fabric drying and plastics processing obtains the composite material that both shoulders bag back uses, drying temperature is 145 DEG C,
Plasticization temperature is 220 DEG C.
Claims (3)
1. the composite material that a both shoulders bag back uses, it is characterised in that manufacturing process comprises the steps:
1), utilize air-texturing equipment that the polyester industrial filament yarn that strength index is higher than 7.8cN/dtex is processed into air deformation yarn,
The air pressure adding man-hour is 5-10kg, and over feed rate(OFR) controls as 10-15%;
2), fabric construction select plain weave, use step 1 through, weft yarn) air deformation yarn processed, use warp thread sizing
Technique weaving obtains grey cloth, and slurry is that 1:1:1.5 mixes by polyvinyl alcohol, acrylic acid methyl ester. and silane coupler according to weight ratio
Conjunction forms;
3), to grey cloth carrying out brushing waterproofing agent process, waterproofing agent uses Japan AGC AG-710, and brushing amount is
150-200g/m2;
4), by the external coating functional paint of the fabric after brushing waterproofing agent, functional paint is by Folium Bambusae, Radix Et Rhizoma Rhei, activated carbon, stone
Cream, Herba Taraxaci and ethanol are processed into;
5), to fabric drying and plastics processing obtains the composite material that both shoulders bag back uses, drying temperature is
140-175 DEG C, plasticization temperature is 190-220 DEG C.
2. the composite material that both shoulders bag back as claimed in claim 1 uses, it is characterised in that: step 2) in silane
The structural formula of coupling agent is:
3. the composite material that both shoulders bag back as claimed in claim 1 uses, it is characterised in that: step 4) in function be coated with
The preparation method of material is: put in container by 5 parts of Folium Bambusaes, 5 parts of Radix Et Rhizoma Rhei, 3 parts of Herba Taraxacis, and boiling 1 hour adds water
Amount is 10 times of solid three's weight sum, filters residue, adds 1 part of activated carbon and 3 parts of Gypsum Fibrosum, stirring in gained liquid
After Jun Yun, concentrating, limit concentrates, while add ethanol, to remove moisture, until moisture is less than 5%;Then by solid
Grind into powder, adds the ethanol of powder weight 3 times, forms coating.