CN105926269A - Preparation method for recombined finishing agent - Google Patents
Preparation method for recombined finishing agent Download PDFInfo
- Publication number
- CN105926269A CN105926269A CN201610362144.0A CN201610362144A CN105926269A CN 105926269 A CN105926269 A CN 105926269A CN 201610362144 A CN201610362144 A CN 201610362144A CN 105926269 A CN105926269 A CN 105926269A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- finishing agent
- composite finishing
- mixed liquor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for a recombined finishing agent. The preparation method comprises the following steps that firstly, 44-55 parts of fire retardant is taken and heated to a certain temperature, and 15-25 parts of etherifled hexamethylolmelamine resin is taken and shocked in a constant-temperature shocking pot for 20 minutes to be mixed fully; secondly, 3-7 parts of diamino diphenyl sulfone and 5-15 parts of an antibacterial agent are added into the mixed liquid to be heated to a certain temperature, a certain stirring speed is controlled, and stirring is carried out for 30 min; thirdly, 10-20 parts of phosphoric acid is added into the mixed liquid in the second step, and PH of the mixed liquid is adjusted to be 4-5; fourthly, 2-3 parts of a softening agent and 8-9 parts of octylphenyl salicylate are added into the mixed liquid in the third step, a certain stirring speed is controlled, and stirring is carried out for 30 min. The preparation method for the recombined finishing agent can prepare the recombined finishing agent with multiple good functions of preventing ultraviolet, resisting inflaming and bacteria and the like.
Description
Technical field
The disclosure relates generally to field of textiles, is specifically related to weaving additive preparation field, especially
It relates to the preparation method of a kind of composite finishing agent.
Background technology
Textile finishing is to apply a kind of finishing agent on fabric, and it can change the surface property of fabric,
Thus give the function that fabric is special.Such as hydrophobic and oil repellent arranges to have low surface tension
Finishing agent processes fabric, changes the surface characteristic of fiber, makes fabric face be difficult to by water or glossy
Wet and sprawl, thus reach the purpose of hydrophobic and oil repellent.Soil resistant finish and soil-releasing finiss are to pass through
Change surface property or the apparent condition of fiber, make fabric be difficult to be stained with under the conditions of dress, use
Attached dirt, or the dirt attached is prone to wash the processing technique of not recontamination.
Current finishing agent function is more single, prepares more complicated.
Summary of the invention
In view of drawbacks described above of the prior art or deficiency, it is desirable to provide one to prepare simple, many
The preparation method of the composite finishing agent of function.
First aspect, the preparation method of a kind of composite finishing agent, preparation method is by following steps group
Become:
Step one, takes fire retardant 45~55 parts, is heated to uniform temperature, takes etherificate hexamethylol
Melmac 15~25 parts, shake 20 minutes so that it is be sufficiently mixed in isothermal vibration pot;
Step 2, adds DADPS 3~7 parts, antibacterial 5~15 in above-mentioned mixed liquor
Part, it is heated to uniform temperature, controls certain mixing speed, stir 30min;
Step 3, adds phosphatase 11 0~20 parts, adjusts mixed liquor in the mixed liquor in step 2
PH to 4~5;
Step 4, adds softening agent 2~3 parts and salicylic acid to pungent in the mixed liquor of step 3 kind
Base phenylester 8~9 parts, control certain mixing speed, stirs 30min.
The technical scheme provided according to the embodiment of the present application, the preparation of the composite finishing agent of the application
Method can prepare have preferable anti-ultraviolet, the several functions such as fire-retardant, antibacterial compound
Finishing agent.
Detailed description of the invention
Below in conjunction with embodiment, the application is described in further detail.It is understood that
Specific embodiment described herein is used only for explaining related invention, rather than the limit to this invention
Fixed.
It should be noted that in the case of not conflicting, the embodiment in the application and embodiment
In feature can be mutually combined.The application is described in detail below with reference to embodiment.
Embodiment one
A kind of preparation method of composite finishing agent, preparation method is made up of following steps:
Step one, takes fire-retardant N TF-9045L45 part, is heated to 40 DEG C, takes etherificate six hydroxyl first
Base melmac 15 parts, shakes 20 minutes so that it is be sufficiently mixed in isothermal vibration pot;
Step 2, adds DADPS 3 parts, magnesium oxide, oxidation in above-mentioned mixed liquor
5 parts of the mixture of calcium, is heated to 30 DEG C, and controlling mixing speed is 100 revs/min, stirring
30min;
Step 3, adds phosphatase 11 0 part, adjusts mixed liquor in the mixed liquor in step 2
PH to 4;
Step 4, adds softening agent 2 parts and salicylic acid to octyl group in the mixed liquor of step 3 kind
Phenylester 8 parts, controlling mixing speed is 100 revs/min, stirs 30min.
Softening agent according to the mass fraction, comprises following components:
Organosilicon quaternary ammonium salt: 65 parts,
Amido silicon oil: 45 parts.
Embodiment two
A kind of preparation method of composite finishing agent, preparation method is made up of following steps:
Step one, takes fire-retardant N TF-9045L55 part, is heated to 60 DEG C, takes etherificate six hydroxyl first
Base melmac 25 parts, shakes 20 minutes so that it is be sufficiently mixed in isothermal vibration pot;
Step 2, adds DADPS 7 parts, zinc oxide, oxidation in above-mentioned mixed liquor
15 parts of the mixture of calcium, is heated to 50 DEG C, and controlling mixing speed is 200 revs/min, stirring
30min;
Step 3, adds phosphoric acid 20 parts, adjusts mixed liquor in the mixed liquor in step 2
PH to 5;
Step 4, adds softening agent 3 parts and salicylic acid to octyl group in the mixed liquor of step 3 kind
Phenylester 9 parts, controlling mixing speed is 200 revs/min, stirs 30min.
Softening agent according to the mass fraction, comprises following components:
Organosilicon quaternary ammonium salt: 85 parts,
Amido silicon oil: 55 parts.
Embodiment three
A kind of preparation method of composite finishing agent, preparation method is made up of following steps:
Step one, takes fire-retardant N TF-9045L50 part, is heated to 60 DEG C, takes etherificate six hydroxyl first
Base melmac 20 parts, shakes 20 minutes so that it is be sufficiently mixed in isothermal vibration pot;
Step 2, adds DADPS 5 parts, zinc oxide, oxidation in above-mentioned mixed liquor
10 parts of the mixture of calcium, is heated to 40 DEG C, and controlling mixing speed is 150 revs/min, stirring
30min;
Step 3, adds phosphatase 11 5 parts, adjusts mixed liquor in the mixed liquor in step 2
PH to 5;
Step 4, adds softening agent 3 parts and salicylic acid to octyl group in the mixed liquor of step 3 kind
Phenylester 9 parts, controlling mixing speed is 150 revs/min, stirs 30min.
Softening agent according to the mass fraction, comprises following components:
Organosilicon quaternary ammonium salt: 75 parts,
Amido silicon oil: 50 parts.
The composite finishing agent that the preparation method of the composite finishing agent of the present invention prepares has anti-purple
The features such as outside line, antibacterial, anti-flammability, and corresponding various aspects of performance is than single Use Limitation
Fruit is better, and preparation method is fairly simple.
Above description is only the preferred embodiment of the application and saying institute's application technology principle
Bright.It will be appreciated by those skilled in the art that invention scope involved in the application, do not limit
In the technical scheme of the particular combination of above-mentioned technical characteristic, also should contain simultaneously without departing from
In the case of described inventive concept, above-mentioned technical characteristic or its equivalent feature carry out combination in any
And other technical scheme formed.Such as features described above and (but not limited to) disclosed herein
The technical characteristic with similar functions is replaced mutually and the technical scheme that formed.
Claims (8)
1. the preparation method of a composite finishing agent, it is characterised in that described preparation method is by such as
Lower step forms:
Step one, takes fire retardant 45~55 parts, is heated to uniform temperature, takes etherificate hexamethylol
Melmac 15~25 parts, shake 20 minutes so that it is be sufficiently mixed in isothermal vibration pot;
Step 2, adds DADPS 3~7 parts, antibacterial 5~15 in above-mentioned mixed liquor
Part, it is heated to uniform temperature, controls certain mixing speed, stir 30min;
Step 3, adds phosphatase 11 0~20 parts, adjusts mixed liquor in the mixed liquor in step 2
PH to 4~5;
Step 4, adds softening agent 2~3 parts and salicylic acid to pungent in the mixed liquor of step 3 kind
Base phenylester 8~9 parts, control certain mixing speed, stirs 30min.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
The heating-up temperature of described step one is 40-60 DEG C.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
Heating-up temperature in described step 2 is 30-50 DEG C.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
The concussion speed of described step one is 100-200 rev/min.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
Mixing speed in described step 2 is 100-200 rev/min.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
Described antibacterial is one or more the combination in magnesium oxide, calcium oxide, zinc oxide.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
Described fire retardant is NTF-9045L.
The preparation method of composite finishing agent the most according to claim 1, it is characterised in that
Described softening agent according to the mass fraction, comprises following components:
Organosilicon quaternary ammonium salt: 65~85 parts,
Amido silicon oil: 45~55 parts.