CN105921387A - Coating process of outer surface of sculpture - Google Patents
Coating process of outer surface of sculpture Download PDFInfo
- Publication number
- CN105921387A CN105921387A CN201610283818.8A CN201610283818A CN105921387A CN 105921387 A CN105921387 A CN 105921387A CN 201610283818 A CN201610283818 A CN 201610283818A CN 105921387 A CN105921387 A CN 105921387A
- Authority
- CN
- China
- Prior art keywords
- paint
- sculpture
- coating process
- sprayed
- firming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating process of the outer surface of a sculpture. The coating process comprises the following steps that 1, the sculpture is integrally polished for several times by a 40-50-mesh sand tray until the surface roughness of the sculpture is 30-50 microns, and a treatment layer is uniformly smeared on the surface of the sculpture; 2, primer is sprayed by a high-pressure airless spraying device within 6 hours after the treatment layer is smeared, wherein the thickness of the primer is controlled to 30-40 microns, and the drying treatment is conducted for 8-12 hours after the spraying is completed; 3, defects of the surface, generated after the primer is sprayed, are remedied with unsaturated polyester resin putty, and after completely cured, the surface is polished with abrasive paper to be smooth; 4, intermediate paint is sprayed by the high-pressure airless spraying device, wherein the thickness of the intermediate paint is controlled to 30-40 microns, and the drying treatment is conducted for 8-12 hours after the spraying is completed; and 5, finish is sprayed by the high-pressure airless spraying device, wherein the thickness of the finish is controlled to 30-40 microns. The coating process has the advantages that the adhesive ability, the water resistance, the chemicals resistance, the light resistance and the temperature resistance of a paint film can be improved remarkably, and the paint film has a self-cleaning property and weather resistance.
Description
Technical field
The invention belongs to artistic sculpture field, particularly to a kind of sculpture outer surface coating process.
Background technology
The sculpture outer surface of the outer surface of sculpture particularly metal material typically can be coated with to protect long-acting color and color and luster
There is layer protecting film, prevent the corrosion of outer surface and coming off of surface color.But sculpture outer surface in prior art
Protecting film can only play the protection of a period of time, acid rain ultraviolet etc. is corroded for a long time and cannot be resisted.For putting
Put and easily cause coming off of rust staining and color at outdoor metal material sculpture, reduce aesthetic feeling and artistic effect, make
The life-span obtaining the art work is substantially reduced.Therefore one has high resistance to chemicals product, fast light, heat resistance and self has certainly
The external coating technique of clean property is particularly important.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the present invention provides a kind of can significantly improve paint film
Adhesive force, waterproof, chemicals-resistant, fast light, heat resistance, the sculpture outer surface application of himself self-cleaning and weatherability
Technique.
Technical scheme: for achieving the above object, the present invention provides a kind of sculpture outer surface coating process, comprises the steps:
Step one: some all over until surface roughness 30~50 μm and uniform on surface with 40~50 mesh emery disc entirety polishings
Smear process layer;The burning on metal carving surface it is prevented from by smearing process layer.
Step 2: process layer and smear spray-applied primer in latter 6 hours;Use high pressure airless spraying apparatus spray-applied primer, wherein
Base coat thickness controls, in 30~40 μm, to carry out the dried of 8~12 hours after having sprayed;By by base coat thickness control
In 30~40 μm so that base coat thickness can not only reach sufficiently thin, and it also is able to ensure between ground and paint film simultaneously
Adhesive force enough.
Step 3: use unsaturated polyester resin putty that the defect existed through basecoat paint rear surface is made up, complete
After all solidstate, use sand paper that surface is polished flat;By unsaturated polyester resin putty so that after priming paint
Surface reply smooth, more convenient follow-up middle paint and the spraying of finish paint.
Step 4: use in high pressure airless spraying apparatus and paint, wherein middle paint THICKNESS CONTROL is in 30~40 μm, after having sprayed
Carry out the dried of 8~12 hours;By by middle paint THICKNESS CONTROL in 30~40 μm so that middle paint thickness can not only reach
To sufficiently thin, and it also is able to ensure that it has enough chemical resistances and weatherability simultaneously.
Step 5: using high pressure airless spraying apparatus finish paint, wherein finish paint THICKNESS CONTROL is in 30~40 μm, after having sprayed
Color shade reaches consistent.By by finish paint THICKNESS CONTROL in 30~40 μm so that finish paint thickness can not only reach enough
Thin, and also be able to ensure that it improves the adhesive force of paint film, waterproof, chemicals-resistant, fast light, heat resistance, the most simultaneously
Prominent advantage is its self-cleaning and weatherability.Its self-cleaning and weatherability make typically need not to be carried out surface, energy
Keep color and color and luster long-effective protection ground for a long time.
Wherein process layer employing 2 described in step one~5% BTA is dissolved in alcohol and obtains.Employing 2~the benzo three of 5%
Nitrogen azoles is dissolved in ethanol just can play the effect of well oxidation anti-to outer metallic surface.
During wherein priming paint described in step 2 is epoxy zinc chromate primer add 15% firming agent and 5~20% diluent prepare.
The thermostability of priming paint, resistance to water, corrosion resistance can be strengthened by adding the firming agent of 15% in primers, be simultaneously introduced
5~20% diluent can more convenient spraying uniform.
During in wherein described in step 4, paint is polyurethane paint, firming agent and 20% diluent of addition 15% prepare.By
In middle paint add 15% firming agent can paint in strengthening thermostability, resistance to water, corrosion resistance, be simultaneously introduced 20% dilute
Release agent can more convenient spraying uniform.
During wherein finish paint described in step 5 is fluorine carbon finishing paint add 20% firming agent and 10~20% diluent prepare.Pass through
The firming agent adding 20% in finish paint can strengthen the thermostability of finish paint, resistance to water, corrosion resistance, is simultaneously introduced 10~20%
Diluent can more convenient spraying uniform.
Step 3 wherein adds in unsaturated polyester resin putty the firming agent of 2%.The firming agent of addition 2% can increase
The strong thermostability of unsaturated polyester resin putty, resistance to water, corrosion resistance.
Beneficial effect: the present invention compared with prior art has the advantage that
(1) present invention is prevented from the burning on metal carving surface by smearing process layer before spray-applied primer.
By base coat thickness being controlled in 30~40 μm so that base coat thickness can not only reach sufficiently thin, and also is able to simultaneously
Ensure that the adhesive force between ground and paint film is enough.By unsaturated polyester resin putty so that surface after priming paint
Reply smooth, more convenient follow-up middle paint and the spraying of finish paint.By by middle paint THICKNESS CONTROL in 30~40 μm so that middle paint
Thickness can not only reach sufficiently thin, and also be able to ensure that it has enough chemical resistances and weatherability simultaneously.Pass through
By finish paint THICKNESS CONTROL in 30~40 μm so that finish paint thickness can not only reach sufficiently thin, and it also is able to ensure simultaneously
It improves the adhesive force of paint film, waterproof, chemicals-resistant, fast light, heat resistance, the most prominent advantage be its self-cleaning and
Weatherability.Its self-cleaning and weatherability make typically to be carried out surface, can keep color and color and luster length for a long time
Effect protection ground.
(2) present invention just can play well outer metallic surface by using the BTA of 2~5% to be dissolved in ethanol
The effect of anti-oxidation.Can be strengthened by the firming agent using epoxy zinc chromate primer to be priming paint addition 15% in primers
The thermostability of priming paint, resistance to water, corrosion resistance, be simultaneously introduced 5~20% diluent can more convenient spraying uniform.Pass through
Polyurethane paint is used to be middle paint and add thermostability that the firming agent of 15% can paint in strengthening, resistance to water, resistance in middle paint
Corrosivity, be simultaneously introduced 20% diluent can more convenient spraying uniform.By using fluorine carbon finishing paint to be finish paint at finish paint
The firming agent of middle addition 20% can strengthen the thermostability of finish paint, resistance to water, corrosion resistance, is simultaneously introduced 10~20% and dilutes
Agent can more convenient spraying uniform.Unsaturation can be strengthened by adding the firming agent of 2% in unsaturated polyester resin putty
The thermostability of polyester resin putty, resistance to water, corrosion resistance.
Detailed description of the invention
Technical scheme is explained below with reference to specific embodiment.
Embodiment one: the present invention provides a kind of sculpture outer surface coating process, comprises the steps:
Step one: some all over until surface roughness 40 μm with 46 mesh emery disc entirety polishings, and at the uniform application of surface
Reason layer;The burning on metal carving surface it is prevented from by smearing process layer.Wherein process layer and use 2% benzo three nitrogen
Azoles is dissolved in alcohol and obtains.The BTA using 2% is dissolved in ethanol just can play well block anti-to outer metallic surface
The effect changed.
Step 2: process layer and smear spray-applied primer in latter 6 hours;Use high pressure airless spraying apparatus spray-applied primer, wherein
Base coat thickness controls, in 35 μm, to carry out the dried of 12 hours after having sprayed;By base coat thickness is controlled
35 μm so that base coat thickness can not only reach sufficiently thin, and also be able to ensure the attachment between ground and paint film simultaneously
Power is enough.During wherein priming paint is epoxy zinc chromate primer, firming agent and 15% diluent of addition 15% prepare.By at priming paint
The firming agent of middle addition 15% can strengthen the thermostability of priming paint, resistance to water, corrosion resistance, is simultaneously introduced 15% diluent
Can more convenient spraying uniform.
Step 3: use unsaturated polyester resin putty that the defect existed through basecoat paint rear surface is made up, complete
After all solidstate, use sand paper that surface is polished flat;By unsaturated polyester resin putty so that after priming paint
Surface reply smooth, more convenient follow-up middle paint and the spraying of finish paint.Wherein, unsaturated polyester resin putty adds
The firming agent of 2%.Add the firming agent of 2% and can strengthen the thermostability of unsaturated polyester resin putty, resistance to water, corrosion-resistant
Property.
Step 4: use in high pressure airless spraying apparatus and paint, wherein middle paint THICKNESS CONTROL is in 35 μm, carries out after having sprayed
The dried of 12 hours;By by middle paint THICKNESS CONTROL in 35 μm so that middle paint thickness can not only reach sufficiently thin,
And also be able to ensure that it has enough chemical resistances and weatherability simultaneously.In wherein, paint is for adding 15% in polyurethane paint
Firming agent and 20% diluent prepare.By in middle paint add 15% firming agent can paint in strengthening thermostability,
Resistance to water, corrosion resistance, be simultaneously introduced 20% diluent can more convenient spraying uniform.
Step 5: using high pressure airless spraying apparatus finish paint, wherein finish paint THICKNESS CONTROL is in 35 μm, has sprayed rear color
Color and luster reaches consistent.By by finish paint THICKNESS CONTROL in 35 μm so that finish paint thickness can not only reach sufficiently thin, and
Also being able to ensure that it improves the adhesive force of paint film, waterproof, chemicals-resistant, fast light, heat resistance, the most prominent is excellent simultaneously
Point is its self-cleaning and weatherability.Its self-cleaning and weatherability make typically to be carried out surface, can keep for a long time
Color and color and luster long-effective protection ground.Firming agent and the 15% diluent system of 20% is added during wherein finish paint is fluorine carbon finishing paint
?.The thermostability of finish paint, resistance to water, corrosion resistance can be strengthened, simultaneously by adding the firming agent of 20% in finish paint
Add 15% diluent can more convenient spraying uniform.
Embodiment two: a kind of sculpture outer surface coating process, comprises the steps:
Step one: some all over until surface roughness 30 μm with 40 mesh emery disc entirety polishings, and at the uniform application of surface
Reason layer;The burning on metal carving surface it is prevented from by smearing process layer.Wherein process layer and use 2% benzo three nitrogen
Azoles is dissolved in alcohol and obtains.The BTA using 2% is dissolved in ethanol just can play well block anti-to outer metallic surface
The effect changed.
Step 2: process layer and smear spray-applied primer in latter 6 hours;Use high pressure airless spraying apparatus spray-applied primer, wherein
Base coat thickness controls, in 30 μm, to carry out the dried of 8 hours after having sprayed;By base coat thickness being controlled in 30 μm,
Make base coat thickness can not only reach sufficiently thin, and also be able to the adhesive force foot ensureing between ground and paint film simultaneously
Enough.During wherein priming paint is epoxy zinc chromate primer, firming agent and 5% diluent of addition 15% prepare.By adding in primers
The firming agent of 15% can strengthen the thermostability of priming paint, resistance to water, corrosion resistance, and being simultaneously introduced 5% diluent can be more square
Just spraying is uniformly.
Step 3: use unsaturated polyester resin putty that the defect existed through basecoat paint rear surface is made up, complete
After all solidstate, use sand paper that surface is polished flat;By unsaturated polyester resin putty so that after priming paint
Surface reply smooth, more convenient follow-up middle paint and the spraying of finish paint.Wherein, unsaturated polyester resin putty adds
The firming agent of 2%.Add the firming agent of 2% and can strengthen the thermostability of unsaturated polyester resin putty, resistance to water, corrosion-resistant
Property.
Step 4: use in high pressure airless spraying apparatus and paint, wherein middle paint THICKNESS CONTROL is in 30 μm, carries out after having sprayed
The dried of 8 hours;By by middle paint THICKNESS CONTROL in 30 μm so that middle paint thickness can not only reach sufficiently thin,
And also be able to ensure that it has enough chemical resistances and weatherability simultaneously.In wherein, paint is for adding 15% in polyurethane paint
Firming agent and 20% diluent prepare.By in middle paint add 15% firming agent can paint in strengthening thermostability,
Resistance to water, corrosion resistance, be simultaneously introduced 20% diluent can more convenient spraying uniform.
Step 5: using high pressure airless spraying apparatus finish paint, wherein finish paint THICKNESS CONTROL is in 30 μm, has sprayed rear color
Color and luster reaches consistent.By by finish paint THICKNESS CONTROL in 30 μm so that finish paint thickness can not only reach sufficiently thin, and
Also being able to ensure that it improves the adhesive force of paint film, waterproof, chemicals-resistant, fast light, heat resistance, the most prominent is excellent simultaneously
Point is its self-cleaning and weatherability.Its self-cleaning and weatherability make typically to be carried out surface, can keep for a long time
Color and color and luster long-effective protection ground.Firming agent and the 10% diluent system of 20% is added during wherein finish paint is fluorine carbon finishing paint
?.The thermostability of finish paint, resistance to water, corrosion resistance can be strengthened, simultaneously by adding the firming agent of 20% in finish paint
Add 10% diluent can more convenient spraying uniform.
Embodiment three: a kind of sculpture outer surface coating process, comprises the steps:
Step one: some all over until surface roughness 50 μm with 50 mesh emery disc entirety polishings, and at the uniform application of surface
Reason layer;The burning on metal carving surface it is prevented from by smearing process layer.Wherein process layer and use 2% benzo three nitrogen
Azoles is dissolved in alcohol and obtains.The BTA using 2% is dissolved in ethanol just can play well block anti-to outer metallic surface
The effect changed.
Step 2: process layer and smear spray-applied primer in latter 6 hours;Use high pressure airless spraying apparatus spray-applied primer, wherein
Base coat thickness controls, in 40 μm, to carry out the dried of 12 hours after having sprayed;By base coat thickness is controlled
40 μm so that base coat thickness can not only reach sufficiently thin, and also be able to ensure the attachment between ground and paint film simultaneously
Power is enough.During wherein priming paint is epoxy zinc chromate primer, firming agent and 20% diluent of addition 15% prepare.By at priming paint
The firming agent of middle addition 15% can strengthen the thermostability of priming paint, resistance to water, corrosion resistance, is simultaneously introduced 20% diluent
Can more convenient spraying uniform.
Step 3: use unsaturated polyester resin putty that the defect existed through basecoat paint rear surface is made up, complete
After all solidstate, use sand paper that surface is polished flat;By unsaturated polyester resin putty so that after priming paint
Surface reply smooth, more convenient follow-up middle paint and the spraying of finish paint.Wherein, unsaturated polyester resin putty adds
The firming agent of 2%.Add the firming agent of 2% and can strengthen the thermostability of unsaturated polyester resin putty, resistance to water, corrosion-resistant
Property.
Step 4: use in high pressure airless spraying apparatus and paint, wherein middle paint THICKNESS CONTROL is in 40 μm, carries out after having sprayed
The dried of 12 hours;By by middle paint THICKNESS CONTROL in 40 μm so that middle paint thickness can not only reach sufficiently thin,
And also be able to ensure that it has enough chemical resistances and weatherability simultaneously.In wherein, paint is for adding 15% in polyurethane paint
Firming agent and 20% diluent prepare.By in middle paint add 15% firming agent can paint in strengthening thermostability,
Resistance to water, corrosion resistance, be simultaneously introduced 20% diluent can more convenient spraying uniform.
Step 5: using high pressure airless spraying apparatus finish paint, wherein finish paint THICKNESS CONTROL is in 40 μm, has sprayed rear color
Color and luster reaches consistent.By by finish paint THICKNESS CONTROL in 40 μm so that finish paint thickness can not only reach sufficiently thin, and
Also being able to ensure that it improves the adhesive force of paint film, waterproof, chemicals-resistant, fast light, heat resistance, the most prominent is excellent simultaneously
Point is its self-cleaning and weatherability.Its self-cleaning and weatherability make typically to be carried out surface, can keep for a long time
Color and color and luster long-effective protection ground.Firming agent and the 20% diluent system of 20% is added during wherein finish paint is fluorine carbon finishing paint
?.The thermostability of finish paint, resistance to water, corrosion resistance can be strengthened, simultaneously by adding the firming agent of 20% in finish paint
Add 20% diluent can more convenient spraying uniform.
The above is only the preferred embodiment of the present invention, it should be pointed out that: for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also
Should be regarded as protection scope of the present invention.
Claims (6)
1. a sculpture outer surface coating process, it is characterised in that comprise the steps:
Step one: some all over until surface roughness 30~50 μm and uniform on surface with 40~50 mesh emery disc entirety polishings
Smear process layer;
Step 2: process layer and smear spray-applied primer in latter 6 hours;Use high pressure airless spraying apparatus spray-applied primer, wherein
Base coat thickness controls, in 30~40 μm, to carry out the dried of 8~12 hours after having sprayed;
Step 3: use unsaturated polyester resin putty that the defect existed through basecoat paint rear surface is made up, complete
After all solidstate, use sand paper that surface is polished flat;
Step 4: use in high pressure airless spraying apparatus and paint, wherein middle paint THICKNESS CONTROL is in 30~40 μm, after having sprayed
Carry out the dried of 8~12 hours;
Step 5: using high pressure airless spraying apparatus finish paint, wherein finish paint THICKNESS CONTROL is in 30~40 μm, after having sprayed
Color shade reaches consistent.
A kind of sculpture outer surface coating process the most according to claim 1, it is characterised in that: described in step one
Process layer employing 2~5% BTA is dissolved in alcohol and obtains.
A kind of sculpture outer surface coating process the most according to claim 1, it is characterised in that: described in step 2
Priming paint be in epoxy zinc chromate primer add 15% firming agent and 5~20% diluent prepare.
4. according to a kind of sculpture outer surface coating process one of claims 1 to 3 Suo Shu, it is characterised in that: step
During in described in four, paint is polyurethane paint, firming agent and 20% diluent of addition 15% prepare.
A kind of sculpture outer surface coating process the most according to claim 4, it is characterised in that: described in step 5
Finish paint be in fluorine carbon finishing paint add 20% firming agent and 10~20% diluent prepare.
A kind of sculpture outer surface coating process the most according to claim 1, it is characterised in that: insatiable hunger in step 3
With the firming agent adding 2% in polyester resin putty.