CN105908531A - Production technology of noctilucence blanket - Google Patents

Production technology of noctilucence blanket Download PDF

Info

Publication number
CN105908531A
CN105908531A CN201610386890.3A CN201610386890A CN105908531A CN 105908531 A CN105908531 A CN 105908531A CN 201610386890 A CN201610386890 A CN 201610386890A CN 105908531 A CN105908531 A CN 105908531A
Authority
CN
China
Prior art keywords
noctilucence
stamp
dyestuff
woollen blanket
district
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610386890.3A
Other languages
Chinese (zh)
Inventor
庄爱华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610386890.3A priority Critical patent/CN105908531A/en
Publication of CN105908531A publication Critical patent/CN105908531A/en
Pending legal-status Critical Current

Abstract

The invention discloses a production technology of a noctilucence blanket. The technology comprises the steps of drawing, white embryo weaving, printing, color fixing, softening treatment, drying, sizing and after treatment. The noctilucence blanket is characterized by comprising a normal printing region and a noctilucence printing region, and the two regions are subjected to printing treatment. The technology comprises the steps that soaking is performed in warm water with the temperature of 50 DEG C for 30 min, and printing treatment is performed on the condition that the temperature is 100 DEG C and the pressure is 3 kg/cm<2>, wherein dye adopted by the noctilucence printing region is prepared by uniformly mixing 3-5 parts of noctilucence powder with the mesh size being 2000-2500, 2-4 parts of textile dyestuff, 1-3 parts of sodium carboxymethyl starch and 80-85 parts of water.

Description

A kind of production technology of noctilucence woollen blanket
Technical field
The present invention relates to a kind of production technology, be specifically related to the production technology of a kind of noctilucence woollen blanket.Belong to printing technology neck Territory.
Background technology
Woollen blanket is a kind of conventional bedding, has heat-preserving function, its raw material many employings animal fiber or acrylon, viscose glue The chemical fibres such as fiber, or animal fiber makes with chemical fibre blending.The woollen blanket adding noctilucent function can the exhibition when night Show its exquisite pattern, and play the effect of indicating positions.If adding electronic light emitting devices, condition of storage is had by it strictly to be wanted Ask, need waterproof, moistureproof, and be inconvenient to clean.If arranging luminous substance layer, the sense of touch of carpeted surface can be directly affected, Further, luminous substance layer easily drops.Ideal method is to be printed and dyed on woollen blanket together with dyestuff by Noctilucent material, but Can Noctilucent material mix homogeneously with conventional textile dyestuff is a big problem, and it may directly affect color fastness and uniform coloring Property, it addition, the noctilucence luminescence persistence of gained woollen blanket is also very difficult to control.
Summary of the invention
It is an object of the invention to as overcoming above-mentioned the deficiencies in the prior art, it is provided that the production technology of a kind of noctilucence woollen blanket.
For achieving the above object, the present invention uses following technical proposals:
A kind of production technology of noctilucence woollen blanket, including drawing, the weaving of white embryo, stamp, fixation, soft treatment, drying and shaping and after Arrangement processes step, and this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region carries out stamp process respectively, Concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of carry out at stamp Reason, wherein, the dyestuff that luminous printing district is used is made up of the component mixing of following weight portion: 2000～2500 mesh noctilucence Powder 3～5 parts, textile dyestuff 2～4 parts, carboxymethyl starch sodium 1～3 parts, water 80～85 parts.
Conventional stamp district directly uses textile dyestuff to carry out stamp process.
Preferably, the preparation method of the used dyestuff in luminous printing district is: weigh the carboxymethyl starch sodium of weight portion, adds In water, after stirring 24 hours, add luminescent powder and textile dyestuff, sonic oscillation 4～5 hours of weight portion, to obtain final product.
Preferably, described textile dyestuff is natural dye.
It is further preferred that described textile dyestuff is vegetable colour (Radix Rubiae, Radix Arnebiae (Radix Lithospermi), indigo, Flos Carthami, Yellow Fructus Gardeniae, Galla Chinensis Deng natural plant dye).
Preferably, the concrete grammar of fixation step is: dry moisture content≤1.5% to product under the conditions of 200 DEG C, it After at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Beneficial effects of the present invention:
The luminescent powder of the present invention and conventional textile dyestuff are through sonic oscillation, it is possible to be sufficiently mixed, in conjunction with carboxymethyl starch sodium Thickening and cementation, it is ensured that the uniformity of gained dyestuff and upper Color uniformity and color fastness, it is possible to luminous printing is inhaled Attached firmly and do not affected by conventional wash, long-time use after still have good luminous effect.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further elaborated, it should explanation, the description below merely to Explain the present invention, its content is not defined.
Embodiment 1:
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2000 mesh luminescent powder 3kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 2kg, carboxymethyl starch sodium 1kg, water 80kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, stirring After 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 4 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Embodiment 2:
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2500 mesh luminescent powder 5kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 4kg, carboxymethyl starch sodium 3kg, water 85kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, stirring After 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 5 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Embodiment 3:
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2000 mesh luminescent powder 5kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 2kg, carboxymethyl starch sodium 3kg, water 80kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, stirring After 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 5 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Embodiment 4:
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2500 mesh luminescent powder 3kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 4kg, carboxymethyl starch sodium 1kg, water 85kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, stirring After 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 4 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Embodiment 5:
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2000 mesh luminescent powder 3kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 3kg, carboxymethyl starch sodium 2kg, water 83kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, stirring After 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 5 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Comparative example 1
A kind of production technology of noctilucence woollen blanket, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: at temperature 100 DEG C, pressure 3kg/cm2Under conditions of carry out stamp process, wherein, conventional stamp district is direct Using textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to carry out stamp process, luminous printing district is used Dyestuff be made up of following components mixing: 2000 mesh luminescent powder 3kg, textile dyestuff is (according to the stamp figure that daytime is to be shown Sample selects corresponding natural plant dye) 3kg, carboxymethyl starch sodium 2kg, water 83kg.The system of the used dyestuff in luminous printing district Preparation Method is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, after stirring 24 hours, add weight portion luminescent powder and Textile dyestuff, sonic oscillation 5 hours, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
Comparative example 2
A kind of production technology of the noctilucence woollen blanket of the present invention, including step:
One, drawing: computer color splitting；Computer goes out film；Photosensitive lithographic；Printing screen molding.
Two, white embryo weaving: silk at the bottom of DTY veil and FDY is woven into white embryo；White embryo sizing；White embryo arranges.
Three, stamp: this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is carried out at stamp respectively Reason, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Under conditions of print Flower processes, and wherein, conventional stamp district directly uses textile dyestuff (selecting corresponding natural plant dye according to stamp pattern) to enter Row stamp processes, and the dyestuff that luminous printing district is used is made up of following components mixing: 2000 mesh luminescent powder 3kg, weaving Dyestuff (selecting corresponding natural plant dye according to the stamp pattern that daytime is to be shown) 3kg, DR-72(acrylic type increases Thick dose) 2kg, water 83kg.The preparation method of the used dyestuff in luminous printing district is: weighs the carboxymethyl starch sodium of weight portion, adds Enter in water, after stirring 24 hours, add luminescent powder and textile dyestuff, the sonic oscillation 5 hours of weight portion, to obtain final product.
Four, fixation: dry moisture content≤1.5% to product under the conditions of 200 DEG C, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of process 40 minutes.
Five, soft treatment: washing processes；Softening agent processes.
Six, drying and shaping.
Seven, Final finishing processes: carding processes；Hot light processes.
Eight, cutting packaging.
To embodiment 1～5 and the luminous printing district color fastness index of comparative example 1 and comparative example 2 gained woollen blanket carry out Test, the results are shown in Table 1.
Table 1. color fastness test result
As it can be seen from table 1 the luminous printing district of gained woollen blanket of the present invention has a significantly higher color fastness, and comparative example 1 He In comparative example 2, the addition of luminescent powder has had a strong impact on color fastness.
By embodiment 1～5 and comparative example 1 and comparative example 2 be placed in the sending out of indoor observation luminous printing district of complete darkness Light situation, the results are shown in Table 2.
Table 2. luminous printing district's luminescence situation
Mix uneven from Table 2, it can be seen that comparative example 1 and comparative example 2 have been likely to occur luminescent powder with conventional textile dyestuff Situation, cause the noctilucence granular sensation observed strong, non-uniform light, and the present invention is completely absent this problem.
By embodiment 1～5 and comparative example 1 and comparative example 2 wash 100 times respectively after and use and within 2 years, be placed on completely The luminous situation in dark indoor observation luminous printing district, result is shown in Table 3 and table 4 respectively.
Table 3. washs 100 Ci Hou luminous printing district's luminescence situations
Embodiment 1 Embodiment 2 Embodiment 3 Embodiment 4 Embodiment 5 Comparative example 1 Comparative example 2
Send out Light Feelings Condition Uniformly light-emitting, nothing Grain sense, luminous intensity Do not weaken Uniformly light-emitting, nothing Grain sense, luminous intensity Do not weaken Uniformly light-emitting, nothing Grain sense, luminous intensity Do not weaken Uniformly light-emitting, nothing Grain sense, luminous intensity Do not weaken Uniformly light-emitting, nothing Grain sense, luminous intensity Do not weaken Only have three or four to send out Luminous point, and luminous strong Spend the most weak Only have three or four to send out Luminous point, and luminous strong Spend the most weak
Table 4. uses Liang Nianhou luminous printing district's luminescence situation
Embodiment 1 Embodiment 2 Embodiment 3 Embodiment 4 Embodiment 5 Contrast Example 1 Right Ratio Example 2
Luminous Situation Uniformly light-emitting, without granular sensation, Luminous intensity does not weakens Uniformly light-emitting, without granular sensation, Luminous intensity does not weakens Uniformly light-emitting, without granular sensation, Luminous intensity does not weakens Uniformly light-emitting, without granular sensation, Luminous intensity does not weakens Uniformly light-emitting, without granular sensation, Luminous intensity does not weakens Almost Without night Light Several ? Nothing Night Light
From table 3 and table 4 it can be seen that remain to keep preferable luminescent properties after the woollen blanket of the present invention is scrubbed, the most not by often Rule washing impact, still has good luminous effect after long-time use.
Although the above-mentioned detailed description of the invention to the present invention is described, but not limit to scope System, on the basis of technical scheme, those skilled in the art need not to pay that creative work can make is each Plant amendment or deformation still within protection scope of the present invention.

Claims (5)

1. a production technology for noctilucence woollen blanket, including drawing, the weaving of white embryo, stamp, fixation, soft treatment, drying and shaping and Final finishing processes step, it is characterised in that this noctilucence woollen blanket includes conventional stamp district and luminous printing district, and the two region is respectively Carrying out stamp process, concrete grammar is: soak 30 minutes in 50 DEG C of warm water, afterwards at temperature 100 DEG C, pressure 3kg/cm2Bar Carrying out stamp process under part, wherein, the dyestuff that luminous printing district is used is made up of the component mixing of following weight portion: 2000～2500 mesh luminescent powders 3～5 parts, textile dyestuff 2～4 parts, carboxymethyl starch sodium 1～3 parts, water 80～85 parts.
The production technology of a kind of noctilucence woollen blanket the most according to claim 1, it is characterised in that conventional stamp district directly uses Textile dyestuff carries out stamp process.
The production technology of a kind of noctilucence woollen blanket the most according to claim 1, it is characterised in that the used dye in luminous printing district The preparation method of material is: weighs the carboxymethyl starch sodium of weight portion, is added to the water, and after stirring 24 hours, adds the night of weight portion Light powder and textile dyestuff, sonic oscillation 4～5 hours, to obtain final product.
The production technology of a kind of noctilucence woollen blanket the most according to claim 1, it is characterised in that described textile dyestuff is natural Dyestuff.
The production technology of a kind of noctilucence woollen blanket the most according to claim 1, it is characterised in that the concrete grammar of fixation step It is: under the conditions of 200 DEG C, dry moisture content≤1.5% to product, afterwards at temperature 150 DEG C, pressure 3kg/cm2Under the conditions of locate Manage 40 minutes.
CN201610386890.3A 2016-06-03 2016-06-03 Production technology of noctilucence blanket Pending CN105908531A (en)