CN105907235A - Flame-retardant iron oxide red anticorrosive paint and manufacturing method thereof - Google Patents
Flame-retardant iron oxide red anticorrosive paint and manufacturing method thereof Download PDFInfo
- Publication number
- CN105907235A CN105907235A CN201610294560.1A CN201610294560A CN105907235A CN 105907235 A CN105907235 A CN 105907235A CN 201610294560 A CN201610294560 A CN 201610294560A CN 105907235 A CN105907235 A CN 105907235A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- oxide red
- hour
- paint
- improved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses flame-retardant iron oxide red anticorrosive paint. After being modified, chaff is used as a binding agent and is added into raw materials, so that the binding property and the affinity of the chaff and a polymer are improved; nano silicon dioxide and superfine iron oxide red powder are further uniformly mixed and are organically modified, so that on one hand, the surface of the iron oxide red powder is organized, the lipophilic property and the compatibility of the iron oxide red powder and organic matters are improved, a phenomenon that the iron oxide red powder is easily agglomerated is solved and waterproof and anticorrosive properties of the paint are also improved; on the other hand, the modified nano silicon dioxide, an inorganic SiO2 network and a polymer chain form a mutually-crossed interpenetrating structure, so that the motion of a polymer molecular chain is inhibited and the heat resistance of the paint is improved; the prepared paint has the advantages of flame retarding, high-temperature resistance, bacteria resistance and environment friendliness; the product can be used for reducing or avoiding pores in the surfaces of castings so as to improve the appearance of the castings.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of flame retardant type iron oxide red anticorrosive paint and preparation method thereof.
Background technology
Development along with China's modern industry, particularly in industries such as metallurgy, petrochemical industry, the energy, new material and military projects, the application of high-temperature service and auxiliary facility gets more and more, metal material oxygen generation oxidation reaction easily and in air in hot environment, produce corrosion phenomena, make metal material gradually lose intensity and cause structural disappearance, become the hidden danger of various accident.Therefore, high-temperature service surface the most all needs application fire-resistant anticorrosion paint to protect, and to prevent metal material oxide etch, extends the service life of high-temperature service.
Iron oxide red is also referred to as become rusty red, red oxidization iron powder, because of it is nontoxic, chemical stability is good and have excellence fast light, high temperature resistant, acidproof, alkaline-resisting, antirust, the advantages such as ultraviolet can be absorbed and become usage amount and be only second to the second largest inorganic pigment of titanium dioxide.Iron oxide red is largely used to antirusting paint and has physical property antirust function, and moisture in air etc. is impermeable in metal level, and can increase compactness and the mechanical strength of coating.
Epoxy resin has excellent adhesion, wearability, electrical insulating property, resistant of high or low temperature, chemical proofing, have that adhesive force is good simultaneously, good mechanical performance and shrinkage factor machine-shaping low, easy and the advantage such as with low cost, be the good material as anti-corrosion of metal erosion resisting coating.But in tridimensional network after pure epoxy resin solidification, crosslink density is high, the problem such as have that internal stress is relatively big, quality is the most crisp, resistance to cracking is poor, resistance to impact is strong and wet-heat resisting is the best.
" preparation of new type silica sol modified epoxy composite coating and performance evaluation " prepares amino modified Ludox by sol-gel process, and by its mixing modification epoxy resin to obtain silica sol modified epoxy composite coating.Result shows: when add improved silica Ludox account for epoxy resin content be 2%-5% time, the adhesive force of coating, hardness, resistance to impact, pliability etc. are preferable, and the gasoline acidproof, alkaline-resisting, resistance to of coating, resistance to distilled water, salt water resistance effect also reach actually used standard simultaneously.Silicon dioxide and alternate chemical bond and the hydrogen bond action of existing of epoxy resin two in hybrid coating, the result of hybrid inorganic-organic crosslinking, can improve the high temperature resistant of coating and Corrosion Protection.
Although but iron oxide red superfine powder body has the advantages such as granularity is little, specific surface area is big, surface activity is strong, chemical reaction velocity is fast in literary composition, but it has thermodynamic phase simultaneously, easily reunite, so that application performance is severely impacted, so we need to improve the dispersive property of superfine iron oxide Hydrargyri Oxydum Rubrum body;Binding agent commonly used in the prior art is organic or inorganic class Chemical Felter mostly, to have coated the most of long duration easy to fall off but also there is corrosion metal and pollutes the hidden danger of environment, the present invention also needs to be improved existing coating binding agent, optimizes existing production technology and formula proportion and then prepares the iron oxide red anticorrosive paint of Multifunctional environment friendly.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of flame retardant type iron oxide red anticorrosive paint and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of flame retardant type iron oxide red anticorrosive paint, is prepared by the raw materials in: epoxy resin 36-38, polyvinyl acetate 10-12, sepiolite powder 10-12, Oleum Verniciae fordii 5-6, Jojoba oil 3-5, Phaeoporus obliquus extract 2-4, bran coat 9-12, methacryloxypropyl trimethoxy silane 7-9, NPE 4-6, nano silicon 2.3-2.7, iron oxide red superfine powder body 12-14, n-butyl alcohol 23-24.
The manufacture method of described a kind of flame retardant type iron oxide red anticorrosive paint, comprises the following steps:
(1) bran coat is added sodium hydrate aqueous solution steaming and decocting 5-8 hour that appropriate mass concentration is 1-2%, cooling flowing water rinsed clean, addition Phaeoporus obliquus extract, NPE ultrasonic grinding 1-3 hour at 85-95 DEG C, dry to obtain modified bran coat starch;
(2) by hydrochloric acid solution that sepiolite powder spray concentration after high-temperature process is 1-2mol/L in 60-80 DEG C of ultrasonic disperse 1-2 hour, washing, to neutral, adds Oleum Verniciae fordii magnetic agitation 2-3 hour, dries;
(3) under nitrogen protection by methacryloxypropyl trimethoxy silane heated and boiled; adding nano silicon keeps temperature to stir 15-20 minute; add iron oxide red superfine powder body, Jojoba oil continues stirring and evenly mixing ultrasonic grinding 40-50 minute, is dried and to obtain modified oxidized iron oxide red superfine powder;
(4) n-butyl alcohol put in agitator stir, be warming up to 90-100 DEG C and add epoxy resin, polyvinyl acetate and step (1) material stirring 1-2 hour, be cooled to 45-50 DEG C add step (2), (3) material stirring grinds 2-3 hour, discharging.
The invention have the advantage that the present invention adds in raw material using modified for bran coat as binding agent, improve caking property and the affinity with polymer thereof;The present invention passes through organically-modified after also nano silicon and superfine iron oxide Hydrargyri Oxydum Rubrum body being mixed, on the one hand iron oxide red surface organic is made, improve its lipophile and with the organic compatibility, not only solve the easy agglomeration of iron oxide red superfine powder body, further improve the waterproof of coating and antiseptic property, nano silicon the most after modified, its inorganic SiO2Network and polymer chain form the interpenetrating structure being cross-linked with each other, it is suppressed that the motion of polymer molecular chain, improve the thermostability of coating, and prepared coating flame-resistant high-temperature-resistant, antibacterial environment protection, this product can reduce or stop cast(ing) surface pore, improving casting of appearance of cast.
Detailed description of the invention
A kind of flame retardant type iron oxide red anticorrosive paint, is prepared by the raw materials in: epoxy resin 36, polyvinyl acetate 10, sepiolite powder 10, Oleum Verniciae fordii 5, Jojoba oil 3, Phaeoporus obliquus extract 2, bran coat 9, methacryloxypropyl trimethoxy silane 7, NPE 4, nano silicon 2.3, iron oxide red superfine powder body 12, n-butyl alcohol 23.
The manufacture method of described a kind of flame retardant type iron oxide red anticorrosive paint, comprises the following steps:
(1) bran coat is added sodium hydrate aqueous solution steaming and decocting 5-8 hour that appropriate mass concentration is 1-2%, cooling flowing water rinsed clean, addition Phaeoporus obliquus extract, NPE ultrasonic grinding 1-3 hour at 85-95 DEG C, dry to obtain modified bran coat starch;
(2) by hydrochloric acid solution that sepiolite powder spray concentration after high-temperature process is 1-2mol/L in 60-80 DEG C of ultrasonic disperse 1-2 hour, washing, to neutral, adds Oleum Verniciae fordii magnetic agitation 2-3 hour, dries;
(3) under nitrogen protection by methacryloxypropyl trimethoxy silane heated and boiled; adding nano silicon keeps temperature to stir 15-20 minute; add iron oxide red superfine powder body, Jojoba oil continues stirring and evenly mixing ultrasonic grinding 40-50 minute, is dried and to obtain modified oxidized iron oxide red superfine powder;
(4) n-butyl alcohol put in agitator stir, be warming up to 90-100 DEG C and add epoxy resin, polyvinyl acetate and step (1) material stirring 1-2 hour, be cooled to 45-50 DEG C add step (2), (3) material stirring grinds 2-3 hour, discharging.
The iron oxide red anticorrosive paint utilizing the present invention to prepare has a following technical specification:
(1) coating of the present invention being heated beyond 300 DEG C just to thermally decompose, heat-resisting quantity highlights;
(2) contact angle of coating surface is 53.12 °, and coating hydrophobicity substantially increases;
(3) pencil hardness: 2H.
Claims (2)
1. a flame retardant type iron oxide red anticorrosive paint, it is characterized in that, be prepared by the raw materials in: epoxy resin 36-38, polyvinyl acetate 10-12, sepiolite powder 10-12, Oleum Verniciae fordii 5-6, Jojoba oil 3-5, Phaeoporus obliquus extract 2-4, bran coat 9-12, methacryloxypropyl trimethoxy silane 7-9, NPE 4-6, nano silicon 2.3-2.7, iron oxide red superfine powder body 12-14, n-butyl alcohol 23-24.
The manufacture method of a kind of flame retardant type iron oxide red anticorrosive paint the most according to claim 1, it is characterised in that comprise the following steps:
(1) bran coat is added sodium hydrate aqueous solution steaming and decocting 5-8 hour that appropriate mass concentration is 1-2%, cooling flowing water rinsed clean, addition Phaeoporus obliquus extract, NPE ultrasonic grinding 1-3 hour at 85-95 DEG C, dry to obtain modified bran coat starch;
(2) by hydrochloric acid solution that sepiolite powder spray concentration after high-temperature process is 1-2mol/L in 60-80 DEG C of ultrasonic disperse 1-2 hour, washing, to neutral, adds Oleum Verniciae fordii magnetic agitation 2-3 hour, dries;
(3) under nitrogen protection by methacryloxypropyl trimethoxy silane heated and boiled; adding nano silicon keeps temperature to stir 15-20 minute; add iron oxide red superfine powder body, Jojoba oil continues stirring and evenly mixing ultrasonic grinding 40-50 minute, is dried and to obtain modified oxidized iron oxide red superfine powder;
(4) n-butyl alcohol put in agitator stir, be warming up to 90-100 DEG C and add epoxy resin, polyvinyl acetate and step (1) material stirring 1-2 hour, be cooled to 45-50 DEG C add step (2), (3) material stirring grinds 2-3 hour, discharging.