CN105907185A - Resin coating - Google Patents
Resin coating Download PDFInfo
- Publication number
- CN105907185A CN105907185A CN201610307353.5A CN201610307353A CN105907185A CN 105907185 A CN105907185 A CN 105907185A CN 201610307353 A CN201610307353 A CN 201610307353A CN 105907185 A CN105907185 A CN 105907185A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- coating
- weight
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a resin coating, prepared from the following components by weight percent: 10-20 percent of a component A and 80-90 percent of a component B, wherein the component A is prepared from the following components in parts by weight: 10-24 parts of epoxy resin, 10-20 parts of amino resin, 15-20 parts of ethyl acetate, 6-11 parts of dimethylbenzene, 34-55 parts of acetone and 1-5 parts of a plasticizer; the component B is prepared from the following components in parts by weight: 10-20 parts of barium sulfate, 21-23 parts of talcum powder, 15-18 parts of an HDI tripolymer, 30-35 parts of titanium dioxide, 10-20 parts of a curing agent, 5-8 parts of zinc phosphate, 10-12 parts of aluminum tripolyphosphate and 1-3.5 parts of composite titanium. The resin coating is stable in quality and good in use effect, has good physical properties, chemical properties, luster-preserving performance, color retention and durability, and does not easily fall off; furthermore, after the epoxy resin is added into the resin coating, the pressure on the environment is reduced, and the corrosion resistance is greatly improved; after the amino resin is added into the resin coating, the temperature resistance and the acid resistance of the coating are improved.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of cold coating.
Background technology
With the coating that synthetic resin is main film forming matter.Its mechanical performance, decorate and the combination property such as protection is superior to grease paint and natural resin coating.Since within 1909, there is phenolic resin coating, synthetic resin coating develops quickly.At the beginning of the eighties, U.S.'s synthetic resin coating has accounted for the 90% of coating total output.1984, China's synthetic resin coating accounted for the 50% of coating total output.
Existing cold coating, rarer a kind of combination property preferably coating, existing coating Heat-stable, artificial ageing resistance performance and resistance to metal erosion performance are poor.
Summary of the invention
Goal of the invention: it is an object of the invention to solve the problem that existing coating Heat-stable, artificial ageing resistance performance and resistance to metal erosion performance are poor.
Technical scheme: for achieving the above object, the present invention provides techniques below scheme: a kind of cold coating, its component consists of the following composition by weight percentage: 10~the component A of 20% and 80~the B component of 90%;Described component A includes following component by weight: epoxy resin 10~24 parts, polyvinyl resin 36~44 parts, ethyl acetate 15~20 parts, dimethylbenzene 6~11 parts, acetone 34~55 parts, plasticizer 1~5 parts;Described B component includes following component, 10~20 parts of barium sulfate, 21~23 parts of Pulvis Talci, 15~18 parts of HDI trimer, 30~35 parts of titanium dioxides, 10~20 parts of firming agent, 5~8 parts of zinc phosphates, 10~12 parts of aluminium triphosphates and 1~3.5 part of composite titanium by weight.
As optimization, described plasticizer includes one or several in triethyl citrate, acetyl triethyl citrate or tributyl citrate.
As optimization, described epoxy resin is bisphenol A type epoxy resin.
As optimization, described firming agent is phenol, formaldehyde and the Nitrogen-containing Phenolic Resins of tripolycyanamide synthesis.
Beneficial effect: the present invention compared with prior art: the coating quality that the present invention provides is stable, using effect is good, there is good physical property, chemical property and protect light colour retention and durability, difficult drop-off, artificial ageing resistance, and after replacing epoxy resin, substantially increase the friendly to environment and metal subunits, the Heat-stable of coating is improve after adding amino resins, simultaneously, use the Nitrogen-containing Phenolic Resins of phenol, formaldehyde and tripolycyanamide synthesis as firming agent, there is good anti-flammability.
Detailed description of the invention
Below in conjunction with specific embodiment, it is further elucidated with the present invention, it should be understood that these embodiments are merely to illustrate this utility model rather than limit the scope of the present invention, after having read the present invention, those skilled in the art all fall within the application claims limited range to the amendment of the various equivalent form of values of the present invention.
Embodiment 1
A kind of cold coating, its component consists of the following composition by weight percentage: the component A of 10% and the B component of 90%;Described component A includes following component by weight: epoxy resin 10 parts, polyvinyl resin 36 parts, ethyl acetate 15 parts, dimethylbenzene 6 parts, 34 parts of acetone, plasticizer 1 part;Described B component includes following component, 10 parts of barium sulfate, 21 parts of Pulvis Talci, 15 parts of HDI trimer, 30 parts of titanium dioxides, 10 parts of firming agent, 5 parts of zinc phosphates, 10 parts of aluminium triphosphates and 1 part of composite titanium by weight.
Described plasticizer includes triethyl citrate.
Described epoxy resin is bisphenol A type epoxy resin.
Described firming agent is phenol, formaldehyde and the Nitrogen-containing Phenolic Resins of tripolycyanamide synthesis.
Prepared by employing the present embodiment i.e. obtains finished product paint with B component according to the allotment of paint vehicle ratio by component A, has good metal subunits, and environmentally friendly.
Embodiment 2
A kind of cold coating, its component consists of the following composition by weight percentage: the component A of 20% and the B component of 80%;Described component A includes following component by weight: epoxy resin 24 parts, polyvinyl resin 44 parts, ethyl acetate 20 parts, dimethylbenzene 11 parts, 55 parts of acetone, plasticizer 5 parts;Described B component includes following component, 20 parts of barium sulfate, 23 parts of Pulvis Talci, 18 parts of HDI trimer, 35 parts of titanium dioxides, 20 parts of firming agent, 8 parts of zinc phosphates, 12 parts of aluminium triphosphates and 3.5 parts of composite titanium by weight.
Described plasticizer includes triethyl citrate, acetyl triethyl citrate and tributyl citrate.
Described epoxy resin is bisphenol A type epoxy resin.
Described firming agent is phenol, formaldehyde and the Nitrogen-containing Phenolic Resins of tripolycyanamide synthesis.
Prepared by employing the present embodiment i.e. obtains finished product paint with B component according to the allotment of paint vehicle ratio by component A, has good metal subunits, and environmentally friendly.
Claims (4)
1. a cold coating, it is characterised in that: its component consists of the following composition by weight percentage: 10~20%
Component A and 80~the B component of 90%;Described component A includes following component by weight: epoxy resin 10~
24 parts, amino resins 10~20 parts, ethyl acetate 15~20 parts, dimethylbenzene 6~11 parts, acetone 34~55 parts,
Plasticizer 1~5 parts;Described B component include by weight following component, 10~20 parts of barium sulfate, 21~23 parts
Pulvis Talci, 15~18 parts of HDI trimer, 30~35 parts of titanium dioxides, 10~20 parts of firming agent, 5~8 parts of zinc phosphates,
10~12 parts of aluminium triphosphates and 1~3.5 part of composite titanium.
Cold coating the most according to claim 1, it is characterised in that: described plasticizer include triethyl citrate,
One or several in acetyl triethyl citrate or tributyl citrate.
Cold coating the most according to claim 1, it is characterised in that: described epoxy resin is bisphenol type epoxy tree
Fat.
Cold coating the most according to claim 1, it is characterised in that: described firming agent is phenol, formaldehyde and three
The Nitrogen-containing Phenolic Resins of poly cyanamid synthesis.