CN105907136A - High-strength architectural powder coating - Google Patents
High-strength architectural powder coating Download PDFInfo
- Publication number
- CN105907136A CN105907136A CN201610488509.4A CN201610488509A CN105907136A CN 105907136 A CN105907136 A CN 105907136A CN 201610488509 A CN201610488509 A CN 201610488509A CN 105907136 A CN105907136 A CN 105907136A
- Authority
- CN
- China
- Prior art keywords
- parts
- strength
- strength building
- powder coating
- powder paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-strength architectural powder coating, prepared from the components: 100-200 parts of calcium carbonate filler, 100-150 parts of mica powder, 50-100 parts of wollastonite powder, 150-350 parts of titanium pigment, 1-1.5 parts of dispersant, 200-300 parts of de-ionized water, 3-5 parts of defoamer, 1.5-3 parts of thickener and 10-15 parts of curing agent. The high-strength architectural powder coating has the advantages of being better in strength, difficult of disbonding caused by weathering, better in overall use effect, longer in service life and suitable for popularization.
Description
Technical field
The present invention relates to a kind of high-strength building powder paint, relate generally to the formula technique of coating
Field.
Background technology
Coating, our the most described paint is one therein.Refer to coat body surface
Can form thin film under certain conditions and rise protection, decoration or other specific functions (insulation,
Antirust, mildew-resistant, heat-resisting etc.) a class I liquid I or solid material.Because of coating in early days mostly with
Vegetable oil is primary raw material, therefore also referred to as paint.Synthetic resin instead of vegetable oil now,
Therefore referred to as coating.Coating non-liquid, powdery paints is the big class of coating variety one.
Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound
Type.According to the classification of the chemical products that the modern times pass through, coating belongs to fine chemical product.Existing
The coating in generation the most progressively becomes a polyfunctional engineering material of class, is in chemical industry
Individual important industry.
The research and development of the research and development of the most all kinds of coating especially batch formula, are development paint industry institutes
Requisite.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high-strength building powder paint.
The present invention is achieved through the following technical solutions.
A kind of high-strength building powder paint, composition includes: calcium carbonate-filled material 100-200 part,
Mica powder 100-150 part, wollastonite part 50-100 part, titanium dioxide 150-350 part, dispersant
1-1.5 part, deionized water 200-300 part, defoamer 3-5 part, thickening agent 1.5-3 part, solid
Agent 10-15 part.
Further, defoamer includes silicone oil 2-3 part, vegetable oil 0.6-1 part, octylphenol polyethylene
Oxygen vinyl Ether 0.1-0.3 part, zinc soap salt 0.2-0.5 part, polyvinylether 0.1-0.2 part.
Further, thickening agent includes gelatin 1-2.5 part, sodium caseinate 0.1-0.3 part, Huang
Virgin rubber 0.2-0.8 part, carboxymethyl starch sodium 0.2-0.4 part.
Beneficial effects of the present invention:
Silicone oil, vegetable oil, OPEO, zinc soap salt, poly-second is included by use
The defoamer of alkene ether, can ensure that the reliable and stable of high-strength building powder paint, and thickening agent is effective
Improving the viscosity of coating, have preferable intensity, easy-weathering does not comes off, the overall effect used
Fruit preferably, extends service life, is suitable to promote.
Detailed description of the invention
Below according to embodiment, the present invention is described in further detail.
Case study on implementation 1:
A kind of high-strength building powder paint, composition includes: 200 parts of calcium carbonate-filled material, cloud
Female 100 parts of powder, wollastonite part 100 parts, titanium dioxide 150 parts, dispersant 1.5 parts, go from
200 parts of sub-water, defoamer 5 parts, thickening agent 1.5 parts, 15 parts of firming agent.
Further, defoamer includes silicone oil 2-3 part, vegetable oil 0.6-1 part, octylphenol polyethylene
Oxygen vinyl Ether 0.1-0.3 part, zinc soap salt 0.2-0.5 part, polyvinylether 0.1-0.2 part.
Further, thickening agent includes gelatin 1-2.5 part, sodium caseinate 0.1-0.3 part, Huang
Virgin rubber 0.2-0.8 part, carboxymethyl starch sodium 0.2-0.4 part.
Case study on implementation 2:
A kind of high-strength building powder paint, composition includes: 100 parts of calcium carbonate-filled material, cloud
Female 150 parts of powder, wollastonite part 50 parts, titanium dioxide 350 parts, dispersant 1 part, deionization
300 parts of water, defoamer 3 parts, thickening agent 3 parts, 10 parts of firming agent.
Further, defoamer includes silicone oil 2-3 part, vegetable oil 0.6-1 part, octylphenol polyethylene
Oxygen vinyl Ether 0.1-0.3 part, zinc soap salt 0.2-0.5 part, polyvinylether 0.1-0.2 part.
Further, thickening agent includes gelatin 1-2.5 part, sodium caseinate 0.1-0.3 part, Huang
Virgin rubber 0.2-0.8 part, carboxymethyl starch sodium 0.2-0.4 part.
Above-described embodiment, only for technology design and the feature of the explanation present invention, its object is to allow ripe
The personage knowing this art will appreciate that present invention and is carried out, and can not limit with this
Protection scope of the present invention processed.All equivalences made according to spirit of the invention change or repair
Decorations, all should contain within the scope of the present invention.
Claims (3)
1. a high-strength building powder paint, it is characterised in that composition includes: calcium carbonate-filled
Material 100-200 part, mica powder 100-150 part, wollastonite part 50-100 part, titanium dioxide 150-350
Part, dispersant 1-1.5 part, deionized water 200-300 part, defoamer 3-5 part, thickening agent
1.5-3 part, firming agent 10-15 part.
High-strength building powder paint the most according to claim 1, it is characterised in that froth breaking
Agent include silicone oil 2-3 part, vegetable oil 0.6-1 part, OPEO 0.1-0.3 part,
Zinc soap salt 0.2-0.5 part, polyvinylether 0.1-0.2 part.
High-strength building powder paint the most according to claim 1, it is characterised in that thickening
Agent includes gelatin 1-2.5 part, sodium caseinate 0.1-0.3 part, xanthan gum 0.2-0.8 part, carboxylic
Methyl starch sodium 0.2-0.4 part.