CN105906830A - Reflecting scratching-resistant release film - Google Patents
Reflecting scratching-resistant release film Download PDFInfo
- Publication number
- CN105906830A CN105906830A CN201610301041.3A CN201610301041A CN105906830A CN 105906830 A CN105906830 A CN 105906830A CN 201610301041 A CN201610301041 A CN 201610301041A CN 105906830 A CN105906830 A CN 105906830A
- Authority
- CN
- China
- Prior art keywords
- parts
- mould release
- reflective
- release membrance
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a reflecting scratching-resistant release film, which is characterized by comprising a base film layer, wherein a release layer is arranged on the base film layer; the release layer is formed by coating a release agent; the release agent is prepared from the following ingredients in parts by mass: 20 to 30 parts of reflecting powder, 10 to 25 parts of vinyl organic silicon resin, 5 to 10 parts of fluorocarbon resin, 3 to 8 parts of nanometer aluminum oxide, 1 to 5 parts of titanium dioxide, 0.1 to 3 parts of antioxidant, 0.5 to 1.5 parts of antifoaming agents, 0.1 to 1 part of adhesion promoters and 15 to 30 parts of solvents. The reflecting scratching-resistant release film has the advantages that the adhesion cannot be generated when the obtained release film is separated from a contact adhesion belt or bonding belt; meanwhile, fluorocarbon resin and nanometer aluminum oxide are contained, so that the release film has high scratching resistant capability; reflecting powder and the glass microbeads are added, so that the recognition degree of the release film is enhanced at night or in dark lamp light environment; the processing and the use of the release film are convenient.
Description
Technical field
The present invention relates to a kind of mould release membrance, particularly to a kind of reflective anti-scratch mould release membrance.
Background technology
Mould release membrance also known as antiadhesion barrier, be with polyethylene terephthalate plastics (be called for short PET),
Bidirectional stretching polypropylene film plastics (being called for short BOPP), vinyon (being called for short PE), carbonic acid
Ester plastics (being called for short PC), polystyrene plastics (being called for short PS), polypropylene plastics (being called for short CPP)
A kind of surface made for base material has the material of characteristic of low-surface-energy.By the viscose of next-door neighbour from release
When face is peeled off, can peel off or pipette separated type material easily, and not injure viscose physical property.Mould release membrance
Feature is surfacing, cleanliness factor height, following process dimensionally stable, and transparency and Color tunable are whole,
The thickness of thin film scope selectable with the kind of base material is wide.Utilize these features of mould release membrance can be to light
The deep processing learning the parts with electronic applications develops, thus it is the most automatic to adapt to this field
Changing production process, at present, mould release membrance can be widely applied for copper-clad plate, printed circuit board (PCB), electricity
The fields such as sub-adhesive.
Mould release membrance comprises base material film and release layer.Base material film surface at least one side is provided with release layer, with
Relatively low surface energy is provided.Base material film many employings paper, plastic sheeting are as material, and release layer is main
Silicon mixture is used to constitute.Typically it is used for industry adhesion zone or adhesive tape etc., to mould release membrance
Performance requirement relatively low, it is only necessary to its have high adherence and remain gluing rate, but be as industry neck
Developing rapidly of territory, the range of mould release membrance is increasingly wider, and there has also been its other performances must
Ask.
But, traditional mould release membrance mostly is transparent, translucent or coloured mould release membrance, due to its transparency
Height, is difficult to identification, at night or in the environment of the light is dusky, can affect processing and the use of mould release membrance.
Accordingly, it would be desirable to a kind of mould release membrance can in the environment of light intensity is more weak with strong reflecting effect, come
Strengthen the resolution of mould release membrance.
Summary of the invention
For solving the problem of above-mentioned existence, it is an object of the invention to provide a kind of reflective anti-scratch mould release membrance.
Described reflective Anti-static release liner, each component cooperates so that the release layer obtained can uniformly be coated with
It is distributed on base membrane layer, and then makes the mould release membrance obtained when separating with the adhesion zone contacted or adhesive tape
Do not produce adhesion, contain fluorocarbon resin and nano aluminium oxide simultaneously, make mould release membrance possess the strongest anti-scratch
Ability;And it is added with reflective powder glass microballoon, owing to the high refraction action of glass microballoon and optically focused are at glass
On the special reflecting layer of glass microballon focus, light is reflexed to light by transparent microballon by reflecting layer again
Near source, so very bright reflection light can be seen at light source, at night or the ring that the light is dusky
Under border, strengthen the resolution of mould release membrance, it is simple to the processing of mould release membrance and use.
For reaching above-mentioned purpose, the technical scheme is that
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 20-30 part;Vinyl organosilicon resin: 10-25 part;Fluorocarbon resin: 5-10 part;Nanometer
Aluminium oxide: 3-8 part;Titanium dioxide: 1-5 part;Antioxidant: 0.1-3 part;Defoamer: 0.5-1.5
Part;Adhesion promoter: 0.1-1 part;Solvent: 15-30 part.
Further, described mould release comprises each component of following weight percent: reflective powder: 20-26
Part;Vinyl organosilicon resin: 10-20 part;Fluorocarbon resin: 5-8 part;Nano aluminium oxide: 5-8
Part;Titanium dioxide: 1-3.5 part;Antioxidant: 0.1-1.6 part;Defoamer: 0.5-1 part;Attachment
Power accelerator: 0.1-0.7 part;Solvent: 19-30 part.
Further, described mould release comprises each component of following weight percent: reflective powder: 24
Part;Vinyl organosilicon resin: 16 parts;Fluorocarbon resin: 6.5 parts;Nano aluminium oxide: 6 parts;Two
Titanium oxide: 2.5 parts;Antioxidant: 0.8 part;Defoamer: 0.6 part;Adhesion promoter: 0.3
Part;Solvent: 28 parts.
Further, described base membrane layer material is in PE, PET, TPX, PMMA, BOPP or PS
Any one.
Separately, described reflective powder is glass microsphere light-reflecting powder, and the granularity of described glass microsphere light-reflecting powder is
300-500 mesh.
And have, the particle diameter of described nano aluminium oxide is 50-150nm.
Meanwhile, described antioxidant is DI-tert-butylphenol compounds or Butylated hydroxyanisole;Described defoamer
For glycol distearate or polyoxyethylene polyoxypropylene glycerin ether;Described adhesion promoter is chlorine
For any one in resin or polyester resin or organic silane compound.
The beneficial effects of the present invention is:
The reflective Anti-static release liner of one that the present invention provides, each component cooperates so that obtain
Release layer can be spread evenly across on base membrane layer, so make the mould release membrance obtained with the adhesion zone contacted
Or adhesive tape does not produce adhesion when separating, and contains fluorocarbon resin and nano aluminium oxide, makes release simultaneously
Film possesses the strongest anti-scratch ability;And it is added with reflective powder glass microballoon, due to the high folding of glass microballoon
The effect of penetrating and optically focused on the special reflecting layer of glass microballoon focus, reflecting layer by light by transparent micro-
Pearl reflexes near light source again, so can see very bright reflection light at light source, at night
Evening or in the environment of the light is dusky, strengthen the resolution of mould release membrance, it is simple to the processing of mould release membrance and use.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with enforcement
Example further describes.
Embodiment 1
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 20 parts;Vinyl organosilicon resin: 10 parts;Fluorocarbon resin: 6 parts;Nano aluminium oxide: 3
Part;Titanium dioxide: 2 parts;Antioxidant: 0.1 part;Defoamer: 0.8 part;Adhesion promoter:
0.1 part;Solvent: 15 parts.
Wherein, described base membrane layer material is PE, and described reflective powder is glass microsphere light-reflecting powder, described glass
The granularity of the reflective powder of glass microballon is 300 mesh, and the particle diameter of described nano aluminium oxide is 100nm, described anti-
Oxidant is DI-tert-butylphenol compounds,;Described defoamer is polyoxyethylene polyoxypropylene glycerin ether;Described attached
Adhesion promoter is chloro resin.
Embodiment 2
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 22 parts;Vinyl organosilicon resin: 15 parts;Fluorocarbon resin: 5 parts;Nano aluminium oxide: 4
Part;Titanium dioxide: 1 part;Antioxidant: 0.5 part;Defoamer: 0.5 part;Adhesion promoter:
0.2 part;Solvent: 18 parts.
Wherein, described base membrane layer material is TPX, and described reflective powder is glass microsphere light-reflecting powder, described
The granularity of glass microsphere light-reflecting powder is 300 mesh, and the particle diameter of described nano aluminium oxide is 50nm, described anti-
Oxidant is Butylated hydroxyanisole;Described defoamer is glycol distearate;Described adhesive force
Accelerator is polyester resin.
Embodiment 3
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 24 parts;Vinyl organosilicon resin: 16 parts;Fluorocarbon resin: 6.5 parts;Nano aluminium oxide:
6 parts;Titanium dioxide: 2.5 parts;Antioxidant: 0.8 part;Defoamer: 0.6 part;Adhesive force promotes
Agent: 0.3 part;Solvent: 28 parts.
Wherein, described base membrane layer material is PMMA, and described reflective powder is glass microsphere light-reflecting powder, institute
The granularity stating glass microsphere light-reflecting powder is 400 mesh, and the particle diameter of described nano aluminium oxide is 50nm, described
Antioxidant is Butylated hydroxyanisole;Described defoamer is glycol distearate;Described attachment
Power accelerator is chloro resin.
Embodiment 4
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 27 parts;Vinyl organosilicon resin: 20 parts;Fluorocarbon resin: 10 parts;Nano aluminium oxide:
7 parts;Titanium dioxide: 4 parts;Antioxidant: 2.2 parts;Defoamer: 1.5 parts;Adhesion promoter:
1 part;Solvent: 25 parts.
Wherein, described base membrane layer material is BOPP, and described reflective powder is glass microsphere light-reflecting powder, institute
The granularity stating glass microsphere light-reflecting powder is 500 mesh, and the particle diameter of described nano aluminium oxide is 150nm, institute
Stating antioxidant is DI-tert-butylphenol compounds or Butylated hydroxyanisole;Described defoamer is that ethylene glycol bisthioglycolate is hard
Fat acid ester or polyoxyethylene polyoxypropylene glycerin ether;Described adhesion promoter is polyester resin.
Embodiment 5
A kind of reflective anti-scratch mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, institute
Stating release layer to be formed by mould release coating, described mould release comprises each component of following mass fraction: anti-
Light powder: 30 parts;Vinyl organosilicon resin: 25 parts;Fluorocarbon resin: 8 parts;Nano aluminium oxide: 8
Part;Titanium dioxide: 5 parts;Antioxidant: 3 parts;Defoamer: 1 part;Adhesion promoter: 0.8
Part;Solvent: 30 parts.
Wherein, described base membrane layer material is PS, and described reflective powder is glass microsphere light-reflecting powder, described glass
The granularity of the reflective powder of glass microballon is 500 mesh, and the particle diameter of described nano aluminium oxide is 50-150nm, described
Antioxidant is Butylated hydroxyanisole;Described defoamer is polyoxyethylene polyoxypropylene glycerin ether;Institute
Stating adhesion promoter is chloro resin.
In order to the off-type force of reflective anti-scratch mould release membrance a kind of in embodiment 1-5 is tested, use
FINAT-10, the index zone of the wide 50mm × long 175mm of attachment on each embodiment mould release membrance
(TESA7475-acryloyl chloride class).Then, FINAT-10 test roller (2Kg load) is utilized,
Come and go twice index zone with the speed of 10mm/sec to compress, clamp release with two pieces of smooth metallic plates
Film, plus 70g/cm2Pressure, at a temperature of about 25 DEG C keep 20h.Afterwards, lay down
Pressure, is fixed to tool mould release membrance after 4h, by index zone from the direction of 180 ° according to 300mm/min
Speed peel off, test, repeatedly test average for 5 times, the results are shown in Table 1.
The mould release membrance of embodiment 1-5 is scratched hardness test, in five road scratches, if having two
More than road or twice do not scrape when scratching mould release membrance, then use the pencil test of previous hardness label instead, until
Find out mould release membrance and scratched the pencil of more than twice or twice, a rear mark of this pencil hardness label
Number it is the pencil hardness scratching mould release membrance, the results are shown in Table 1.
The mould release membrance scratch hardness of embodiment 1-5 is tested, in five road scratches, if having two
When road or the above mould release membrance of twice do not abrade, then use the pencil test of previous hardness label instead, until looking for
Go out mould release membrance and be scratched the pencil of more than twice or twice, a rear label of this pencil hardness label
It is the abrasive pencil hardness of mould release membrance, the results are shown in Table 1.
The mould release membrance reflecting rate of embodiment 1-5 is tested, the results are shown in Table 1.
The performance test results of mould release membrance in table 1 embodiment 1-5
As can be known from the above table, in embodiment 1-5, the hardness that scratches of reflective anti-scratch mould release membrance reaches H level, wipes
Hinder hardness and reach B level, show that mould release membrance possesses the strongest anti-scratch ability;And reflecting rate reach 88% with
On, show that this mould release membrance has good reflecting effect;Meanwhile, each component cooperates so that
To release layer can be spread evenly across on base membrane layer, and then make the mould release membrance obtained viscous with contact
Band or adhesive tape does not produce adhesion when separating.
It should be noted that above example is only in order to illustrate technical scheme and unrestricted.
Although being described in detail the present invention with reference to preferred embodiment, those of ordinary skill in the art should
Work as understanding, the technical scheme of invention can be modified or equivalent, without deviating from the present invention
The scope of technical scheme, it all should be contained in scope of the presently claimed invention.
Claims (7)
1. a reflective anti-scratch mould release membrance, it is characterised in that include base membrane layer, described base membrane layer is provided with release layer, and described release layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder: 20-30 part;Vinyl organosilicon resin: 10-25 part;Fluorocarbon resin: 5-10 part;Nano aluminium oxide: 3-8 part;Titanium dioxide: 1-5 part;Antioxidant: 0.1-3 part;Defoamer: 0.5-1.5 part;Adhesion promoter: 0.1-1 part;Solvent: 15-30 part.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that described mould release comprises each component of following weight percent: reflective powder: 20-26 part;Vinyl organosilicon resin: 10-20 part;Fluorocarbon resin: 5-8 part;Nano aluminium oxide: 5-8 part;Titanium dioxide: 1-3.5 part;Antioxidant: 0.1-1.6 part;Defoamer: 0.5-1 part;Adhesion promoter: 0.1-0.7 part;Solvent: 19-30 part.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that described mould release comprises each component of following weight percent: reflective powder: 24 parts;Vinyl organosilicon resin: 16 parts;Fluorocarbon resin: 6.5 parts;Nano aluminium oxide: 6 parts;Titanium dioxide: 2.5 parts;Antioxidant: 0.8 part;Defoamer: 0.6 part;Adhesion promoter: 0.3 part;Solvent: 28 parts.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that described base membrane layer material is any one in PE, PET, TPX, PMMA, BOPP or PS.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that described reflective powder is glass microsphere light-reflecting powder, the granularity of described glass microsphere light-reflecting powder is 300-500 mesh.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that the particle diameter of described nano aluminium oxide is 50-150nm.
The reflective anti-scratch mould release membrance of one the most according to claim 1, it is characterised in that described antioxidant is DI-tert-butylphenol compounds or Butylated hydroxyanisole;Described defoamer is glycol distearate or polyoxyethylene polyoxypropylene glycerin ether;Described adhesion promoter is any one in chloro resin or polyester resin or organic silane compound.