CN105906293B - A kind of desulfurated plaster high-strength crystal decorative panel and preparation method thereof - Google Patents
A kind of desulfurated plaster high-strength crystal decorative panel and preparation method thereof Download PDFInfo
- Publication number
- CN105906293B CN105906293B CN201610234652.0A CN201610234652A CN105906293B CN 105906293 B CN105906293 B CN 105906293B CN 201610234652 A CN201610234652 A CN 201610234652A CN 105906293 B CN105906293 B CN 105906293B
- Authority
- CN
- China
- Prior art keywords
- desulfurated plaster
- decorative panel
- powder
- micro mist
- photocatalysis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of desulfurated plaster high-strength crystal decorative panel and preparation method thereof:By the ripe powder of desulfurated plaster, rubber powder, crystal modifier, subtract swollen dose, water-loss reducer is by 95~99.6:0.1~1.2:0.02~0.05:0.2~1.0:0.1~2.8 weight activates micro mist than obtained desulfurated plaster;Desulfurated plaster is activated into micro mist, photocatalysis environmental mineral waste material, waterproofing agent, compounding glue, reinforcing fiber/grid cloth again and presses 100:0.5~12:0.1~1.8:60~75:0.8~7.0 weight after agitated, vibration, secondary agitation, the shaping of dual contact overlay film, the demoulding, cutting polishing, dry maintenance, the processing of facing handling process than being made decorative panel.The present invention solves the problem of setting time in the prior art is fast, intensity is unstable, expansion rate is high, particle compactness is big;There is obtained decorative panel purifying formaldehyde, negative oxygen ion to induce, automatic humidity-regulating it is ecological, realize industrial residue resource ecology utilize, realize full automatic standard metaplasia production, product appearance quality and performance are able to standardization control.
Description
Technical field
The present invention relates to a kind of high-strength crystal decorative panel and preparation method thereof, and in particular to a kind of desulfurated plaster high-strength crystal
Decorative panel and preparation method thereof, it is particularly a kind of containing desulfurated plaster activate micro mist desulfurated plaster high-strength crystal decorative panel and its
Preparation method, this method prepares ecological construction material using solid waste resource.
Background technology
" energy-saving and emission-reduction, recycling economy, sustainable development, green building material " etc. is the general character class of new normality new development approach
Topic, desulfurated plaster is as country to " dicontrolled area " (acid rain control district and sulfur dioxide control district) interior coal fired power plant flue gas desulfurization meter
The implementation drawn, its yield is also by the lasting rising with the continuous construction of flue gas desulfurization device.Building material industrial technology information
Director of the Institute Xu Luoyi is pointed out in 2014 annual desulfurated plaster utilization obstacles discuss forum:" China is coal mining and fire
Power generating big country, desulfurated plaster discharge capacity is huge, and the utilization rate of current desulfurated plaster is mainly used in building at present 70% or so
Building material industry, such as cement retarder, plaster of Paris, Thistle board, brushing gypsum.From the point of view of the whole country, utilized actual
During, exist as follows with urgent problem to be solved:(1) as interior coal-burning power plant side, based on flue gas desulphuization rate index, lack
Be dried to flue gas ash removal, to aqueous powdery desulfurated plaster, the technique Journal of Sex Research of calcined dehydration, it is and complete to desulfurated plaster
Understanding and control new technology, new technology lack;(2) as desulfurated plaster comprehensive utilization side, lack the corresponding regulation of desulfurated plaster,
Under policy, standard and the environmentally friendly attitude towards sex of recycling, it is confined to cement retarder, plaster of Paris, paper in traditional construction material industry
Plasterboard, answering for brushing gypsum are mixed or substituted, and cause the comprehensive utilization of desulfurated plaster to show low side added value, scattered shakiness
It is fixed, using it is insufficient the problem of.(3) interior coal-burning power plant side, desulfurated plaster comprehensive utilization side are to desulfurated plaster product technology, desulfurization
Gypsum does not form system maturation scheme using being formed, necessarily cause desulfurated plaster not to be inconsistent because of production technology, intermediate transition it is secondary
Pollution, production cost improve and influence utilization benefit.
The data gathered from China day flower prod in 2015 can see, and China's day flower prod is broadly divided into five at present
Major class:(1) Thistle board:To the north of Xinlong board, the new Mount Taishan in north, be resistant to good fortune, Lafarge, based on Saint-Gobain, the total market size is about
12.3 hundred million m2;(2) mineral wool ceiling (mineral wool sound absorption board):To be resistant to good fortune, northern Xinlong board, based on Jinyu Star, the total market size is about
For 400,000,000 m2;(3) metal ceiling (aluminium alloy smallpox):Based on Hunter Le Silong, Feisuo, western aluminium, Puffy that etc., dimensions of market is about
For 0.64 hundred million m2;(4) decorated gypsum board:Based on moist-proof board, calcium silicate board with microporous, high brilliant plate, dimensions of market is about 2.46 hundred million ㎡.The whole nation exists
The total market of the big alastrim product of the above four has surpassed 1,800,000,000 m2, usage amount is about in 1.2m per capita2/ people, takes with ripe adding
Big market 13m per capita2/ people, U.S. 8m2/ people, Japan 5.5m2/ people, France 4m2/ people, Britain 3m2/ people
Compare, still there is wide development space in Chinese day flower prod market.And be wherein rooted in the hearts of the people with green, ecological, health idea,
Meet under equivalents application, tend to using having ecological, ornamental decorated gypsum board concurrently.
Known patented technology high-strength crystal decorated gypsum board and preparation method (ZL201110232335.2) are taken in aquation
Reaction link breaches single mineral admixture and is modified to improve crystal morphology, crystal size, crystal distribution, microcellular structure
Technology, source is improved as with the essence of crystal unit structure, has both obtained good network structure, and it is unique not destroy gypsum base material
Porosity characteristic, make its give full play to good lightweight, attract noise reduction, damping fire prevention etc. environmental functional.In addition built-in waterproof
Technology, the introducing of one side water-proof system does not cause the degree and speed of hydration reaction, and another aspect monolithic article is thin from inside
All there is silicon-hydroxyl hydrophobic group to surface in micropore, so as to good moisture resistance and deformation resistance, solve gauge stuff
Plate makes moist deformation problem.But by production practices, such as with the ripe powder of scale application desulfurated plaster during, because of the ripe powder of desulfurated plaster
In the presence of serious batch unstability, it is in particular in:(1) setting time is extremely unstable, enters continuous in large-scale production
Link is stirred, when stirring blade is because running at full speed and more than 30 DEG C of frictional heat Biao Wenda (being only above 5 DEG C of normal temperature room temperature), is existed
Moment solidifies and causes mixer to block the production problem such as card machine, while when rapid hardening phenomenon turns brilliant to aquation crystalline product
Between, turn brilliant effect not notable;(2) there is the asymmetric of supply and demand, interior coal-burning power plant side in the supply chain of the ripe powder of desulfurated plaster
The many air storages of desulfurated plaster, moisture content is inconsistent, causes the ripe powder of desulfurated plaster to be difficult to set up technological standards in calcined dehydration,
Thing is mutually unstable, and the intensity for forming the ripe powder industry supply of whole desulfurated plaster is difficult to reach 80% stabilization, to manual production mould
Formula prepares the influence of high-strength crystal decorative panel and is confined to the unstable of product physical property, but for continuous automatic production pattern system
Standby high-strength crystal decorative panel is then present the production detrimental effects such as can not be stripped because of low intensity;(3) the ripe powder of existing desulfurated plaster
Industry is generally using Raymond mill, steel milling mill, and micro mist surface has crystal grain defect, rule and differed, and it is linearly swollen that common manifestation goes out 2h
Swollen rate is up to that 3.2 ‰ or so, loose thickness is big, as raw material product size is nonstandard, Unit Weight is big, products application
Later stage, which exists, deforms sagging quality problems.
So that in desulfurated plaster, or even natural gypsum application, reinforcing fiber, general mode can be all used in routine techniques
Be required for gypsum based gel material by being used after stirring, for ensure gypsum base gelling powder and liquid medium it is complete
Uniformly, the residence time for extending stirring under speed of agitator or low speed is either improved, for using the latter under manual production pattern
To extend the residence time of stirring under low speed, it is unobvious to beat the destruction of reinforcing fiber bundles assembling structure melting property, gypsum base gelling material
The mobility and enhancing effect of material meet the application of reinforcing fiber.But under consecutive production pattern, gypsum based gel material
Residence time is very short, to make its gypsum base gelling powder fully be stirred evenly with liquid, is only stirred for rotating speed raising, but thus will
The structure destruction completely of getting one's things ready of reinforcing fiber, which is beaten, melts, and the enhancement of one side reinforcing fiber greatly weakens, and on the other hand causes stone
The mobility of cream base gelling slurry significantly declines, and this almost has become restriction gypsum based gel material field continuous production
Disadvantage, and by fold level different rotating speeds agitating mode to die casting be molded when, its always stopping in mixing plants at different levels
The time is stayed to increase, any centre position occurs slightly blocking all pining down whole production system, in presently disclosed technology all
Without reference to and solve this problem.
In summary, only combination product application characteristic, is targetedly modified to the ripe powder of desulfurated plaster, could solve
Certainly current desulfurated plaster extensive style, the recycling application present situation without system maturation scheme;High-strength crystal dress is prepared with desulfurated plaster
Plaque, it is necessary to solve lot stability and turn brilliant preposition could obtain turns a brilliant good result;High-strength crystal decorative panel applies city
Field has broad space, in the case where keeping peculiar dicoration, need to have ecological, environmental protective feature concurrently;In its preparation method and technique
On, especially need to solve the stirring common fault broken without structure of reinforcing fiber under scale Sequential Production.
The content of the invention
The technical problems to be solved by the invention are to be directed to the deficiencies in the prior art, and provide a kind of desulfurated plaster
High-strength crystal decorative panel, by turning brilliant preposition and activation in microscopic appearance structure, solves condensation on desulfurated plaster micro mist
The problem of time is fast, intensity is unstable, expansion rate is high, particle compactness is big;And by with environmental photocatlytsis waste material processing after
Environmental photocatlytsis mineral powder is combined, and desulfurated plaster high-strength crystal decorative panel is made, induced with purifying formaldehyde, negative oxygen ion,
Automatic humidity-regulating etc. is ecological, realizes " ecological " utilization of resource of industrial residue.
The second object of the present invention is to provide a kind of preparation method of above-mentioned desulfurated plaster high-strength crystal decorative panel, realizes
Synchronous vibration shaping, secondary agitation, dual contact overlay film moulding process and reinforcing fiber in high-strength crystal decorated gypsum board field
Without damaged stirring technique, realize that full automatic standard metaplasia is produced, product appearance quality and performance are able to standardization control
To achieve these goals, the present invention is adopted the following technical scheme that:
A kind of desulfurated plaster high-strength crystal decorative panel, with desulfurated plaster activation micro mist, photocatalysis environmental mineral waste material, compounding
Solution, reinforcing fiber/grid cloth are raw material, and agitated, vibration, secondary agitation, overlay film shaping, the demoulding, cutting polish, dry and support
Described desulfurated plaster high-strength crystal decorative panel is formed after shield, the processing of facing handling process;Described desulfurated plaster activation micro mist,
Photocatalysis environmental mineral waste material, combination solution, the weight ratio of reinforcing fiber/grid cloth are 100:0.5~12:60~75:0.8~
7.0.Desulfurated plaster high-strength crystal decorative panel of the present invention, the more than single short cylinder calcium sulfate of its microcosmic crystal structure is brilliant
Body, also have in porous pattern environmental mineral crystal, macroscopically induced with purifying formaldehyde, negative oxygen ion, self-regulated it is moist
It is one or more ecological.
In above-mentioned technical proposal, described desulfurated plaster activation micro mist with the common ripe powder of β-desulfurated plaster, rubber powder, turns crystalline substance
Agent, subtract swollen dose, water-loss reducer as raw material, be prepared from after turning brilliant activation, homogenizing ageing through ball mill, described common β-de-
The ripe powder of sulphur gypsum, rubber powder, crystal modifier, subtract swollen dose, the weight ratio of water-loss reducer be 95~99.6:0.1~1.2:0.02~0.05:
0.2~1.0:0.1~2.8;
The described common ripe powder of β-desulfurated plaster is that steam power plant's desulfurated plaster waste residue is obtained general after drying and calcining grinding
Logical β powder (the common ripe powder of β-desulfurated plaster is existing, the exist or commercially available common ripe powder of β-desulfurated plaster);
Described rubber powder be preferably in polymer dispersion powder, the rubber powder of polyvinyl chloride 2488, plant gum powder any one, two
The mixture planted and mixed above with arbitrary proportion;
Described crystal modifier be preferably in aluminum sulfate, alum, sodium citrate, calcium chloride any one, two kinds and
The mixture mixed above with arbitrary proportion;
It is described subtract swollen dose be preferably in sodium pyrophosphate, sodium metaphosphate, trisodium citrate any one, two kinds and more than
The mixture mixed with arbitrary proportion;
Described water-loss reducer is preferably hydroxypropyl methyl cellulose HPMC, hydroxyethylmethylcellulose HEMC, Methyl cellulose
In plain MC, pre-gelatinized starch any one, the mixture that is mixed with arbitrary proportion of two kinds and the above;
The preparation method of described desulfurated plaster activation micro mist is:
1. ball mill turns brilliant activation:By the weight than the common ripe powder of β-desulfurated plaster, rubber powder, crystal modifier, subtract swollen dose,
After water-loss reducer is well mixed, it is added to ball milling in ball mill and entered at least after turning brilliant activation, 25~75min of material ball milling
In two storage tanks;
2. homogenizing ageing:Obtained material in step 1. at least two storage tanks is discharged simultaneously, and passes through helical feed
It is transported in the packaging with moisture resistance, is aged 3~15 days naturally after machine homogenizing, obtains the stably and controllable described desulfurization of performance
Gypsum activates micro mist;
In desulfurated plaster activation micro mist preparation process, setting time, each batch was adjustable, and setting strength batch is stably and controllable,
2h linear expansion rates can be by being reduced to 1.2 ‰ (common desulphurization land plaster 2h linear expansion rates > 3.2 ‰);Hydrated product is by fiber
It is short cylinder that shape, which turns brilliant, and its crystal draw ratio is reduced to 4.7 by 13.2;Be after ball milling it is microcosmic be ball shape, macroscopically desulfurization stone
Cream activation micro mist is loose, with natural fluidity.
In above-mentioned technical proposal, described photocatalysis environmental mineral waste material is production environmental photocatlytsis material, air cleaning
The useless clout (environmental mineral, micro photocatalyst component or photocatalysis component) produced in the inorganic environment-friendly material such as material is by de-
Water is dried, grinding, preferably oyster shell whiting, diatomite, activated carbon, negative ion powder, attapulgite, sepiolite, expansion leech
In stone any one, the mixture that is mixed with arbitrary proportion of two kinds and the above;
The preparation method of described photocatalysis environmental mineral waste material is:In view of the composition of the useless clout of photocatalysis environmental mineral,
Granular size, water content differ, and uniformly take using unit milling capacity as a batch, batch is carried out continuously drying and dehydrating;By iodine
The adsorption rate that distils characterizes photocatalysis environment miberal powder micro-porous adsorption ability or photocatalysis environment miberal powder anion-generating capacity is characterized and born
Ion induces the identical or approximate photocatalysis environmental mineral waste material of ability as same batch processed material, and batch is carried out continuously dry
Dry dehydration, carries out grinding again when described useless clout drying and dehydrating is to moisture content < 8.0%, grinding to fineness is 180 mesh and sieve
Surplus is less than 3%.
In above-mentioned technical proposal, described combination solution is with H2It is O, polymerized emulsion, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic
Plaque surface defoamer is formed as raw material compounding, described H2It is O, polymerized emulsion, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic
The weight ratio of plaque surface defoamer is 100:0.8~1.2:0.1~1.8:0.5~2.0;
Described polymerized emulsion is any in industrial-grade polyethylene alcohol emulsion, propyl benzene emulsion, silicone acrylic emulsion, biogel
The mixture that a kind of, two kinds and the above are mixed with arbitrary proportion;
Described inorganic decorating plate surface defoamer is by defoamer mother liquor, agricultural sodium sulphate and clear water according to 1.2:1.2:
97.6 weight is than compounding, or defoamer mother liquor, agricultural alum and clear water are according to 2.0:1.9:96.1
Weight is than compounding;Described defoamer mother liquor by fatty acid methyl ester ethoxylate, isomery alcohol ether, butyl glycol ether,
Organic silicon modified by polyether, clear water press 40:20:5:0.1:34.9 compoundings.
In above-mentioned technical proposal, described reinforcing fiber is preferably any in string, glass fibre, mineral fibres
The mixture that a kind of, two kinds and the above are mixed with arbitrary proportion;Described reinforcing fiber length is preferably 15~22mm;Institute
The grid cloth stated preferably glass fiber reticular cloth, grid cloth specification is preferably 4 × 4mm~10 × 10mm.
The present invention also provides a kind of preparation method of above-mentioned desulfurated plaster high-strength crystal decorative panel, comprises the following steps:
(1) desulfurated plaster activation micro mist is prepared:
1. ball mill turns brilliant activation:By the weight than the common ripe powder of β-desulfurated plaster, rubber powder, crystal modifier, subtract swollen dose,
After water-loss reducer is well mixed, it is added to ball milling in ball mill and entered at least after turning brilliant activation, 25~75min of material ball milling
In two storage tanks;
2. homogenizing ageing:Obtained material in step 1. at least two storage tanks is discharged simultaneously, and passes through helical feed
It is transported in the packaging with moisture resistance, is aged 3~15 days naturally after machine homogenizing, obtains the stably and controllable described desulfurization of performance
Gypsum activates micro mist;
(2) photocatalysis environmental mineral waste material is prepared:In view of photocatalysis environmental mineral gives up the composition of clout, granular size, contain
Water differs, and uniformly takes using unit milling capacity as a batch, batch is carried out continuously drying and dehydrating;By iodine distillation adsorption rate table
Levy photocatalysis environment miberal powder micro-porous adsorption ability or photocatalysis environment miberal powder anion-generating capacity characterizes anion and induces ability
Identical or approximate photocatalysis environmental mineral waste material is carried out continuously drying and dehydrating as same batch processed material, batch, to containing
Grinding is carried out during water rate < 8.0% again, grinding to fineness is 180 mesh and screen over-size is less than 3%;
(3) combination solution is prepared:By the weight than H2O, polymerized emulsion, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic dress
Plaque surface defoamer is well mixed, and produces described combination solution;
(4) once stir:The desulfurated plaster that step (1), (2), (3) are prepared from activates micro mist, photocatalysis environment ore deposit
Thing waste material and combination solution are stirred according to described weight ratio until uniformly, obtaining uniform net slurry;Speed of agitator is 280
~350r/min;
(5) synchronous vibration, secondary agitation, overlay film shaping:Step (4) is obtained into net slurry to be delivered in the bed die of shaping,
Simultaneously by the weight than reinforcing fiber/grid cloth be delivered in the bed die of shaping;By the net slurry described in bed die and increasing
Strong fibre/mesh lattice cloth carries out secondary agitation until uniform, and mixing speed is 25~38r/min;Obtained after being stirred in bed die
Product carries out vibration moulding, obtains the overlay film shaping wire body of two-sided overlay film, 20~50HZ of vibration frequency, 0.3~15mm of amplitude, shakes
Dynamic 8~15 seconds residence times;
(6) it is stripped and cuts polishing:By the overlay film shaping wire body demoulding described in step (5);By the overlay film shaping after the demoulding
Four side remnant fibrous of wire body are polished or neatly cut off its continuous grid cloth, four marginal rays are slided neatly;
(7) maintenance is dried:Kiln drying (is dried using natural air drying mode (drying time is 3~7 day), dry kiln drying mode
Dry temperature is 35~55 DEG C, drying time is 10~18h) in any one mode be dried;
(8) facing is handled:Through any in ecologic coating, metal baking finish, imitative stone baking vanish, F-C paint, gold stamping silk-screen, UV air brushing
A kind of mode surface coating, after after surface solidification, packaging can turn into product.
The advantage of technical solution of the present invention is
(1) desulfurated plaster activation micro mist, had both been connected Liao Nei coal-burning power plant sides, desulfurated plaster comprehensive utilization side to desulfurated plaster
Product technology, desulfurated plaster utilize the industrial chain disconnected;Solve again the ripe powder batch physical property of desulfurated plaster (setting time,
Intensity, appearance color, expansion rate) batch it is unstable the problem of;It is pressed for time while solving desulfurated plaster and turning crystalline substance in hydration stage
Brilliant preposition technical problem need to be turned by gathering;In addition, being activated by ball milling, improve the ripe powder industry of existing desulfurated plaster and generally use
There is crystal grain defect, rule and differ in Raymond mill, steel milling mill, micro mist surface, common manifestation goes out 2h linear expansion rates and is up to 3.2 ‰
The big technical problem of left and right, loose thickness, and desulfurated plaster application product unit unit weight it is exceeded the problem of.
(2) the photocatalysis ore deposit obtained after useless clout processing of the photocatalysis environmental mineral waste material to prepare photocatalysis environmentally conscious materialses
Thing miberal powder, based on photocatalysis environmentally conscious materialses technology, desulfurated plaster high-strength crystal decorated gypsum board, which is removed, has conventional high-strength crystal dress
Plaque is distinctive ornamental and the feature of environmental protection of gypsum base material outside, induced with more purifying formaldehyde, negative oxygen ion, automatic humidity-regulating, anti-
It is one or more ecological during bacterium is mould proof.
(3) present invention by crystal modifier and turn crystal technique it is preposition to desulfurated plaster activate the micro mist stage, solve high-strength crystal
In the hydration reaction stage in decorative panel and preparation method, because setting time is extremely unstable, enters in large-scale production and continuously stir
, when stirring blade is because running at full speed and more than 30 DEG C of frictional heat Biao Wenda (being only above 5 DEG C of normal temperature room temperature), there is moment in link
Solidify and cause mixer to block the production problems such as card machine, while rapid hardening phenomenon does not turn the brilliant time to aquation crystalline product,
Turn the inapparent technical difficulty of brilliant effect;In addition, the environmental mineral crystal in porous pattern is also introduced in crystal composition, and
Single short cylinder calcium sulphate crystal in non-traditional high-strength crystal decorative panel, is consequently formed two or more multiple elements design crystal,
Interlaced between crystal unit, mutual parcel, crystal structure is more densely cross-linked.
(4) the inventive method solves leading to without the stirring that structure is destroyed for reinforcing fiber under scale Sequential Production
Disease, compared with the once stirring in traditional preparation methods, moulding by casting, reinforcing fiber structure is not destroyed, slurry mobility
Do not lose, product enhancing effect does not fail, the product back side by two-sided overlay film, its back side can also realize grain decorating and
Product standard thickness is controlled.
Brief description of the drawings:
Fig. 1:The integrated artistic flow chart of the inventive method;
Fig. 2:The crystal morphology structure chart for the desulfurated plaster high-strength crystal decorative panel that the embodiment of the present invention 1 is obtained;
Fig. 3:The conventionally crystal morphology structure chart of high-strength crystal decorative panel made from (CN102408218A).
Embodiment
The embodiment to technical solution of the present invention is described in detail below, but the present invention is not limited in following description
Hold:
Embodiment 1:
A kind of desulfurated plaster high-strength crystal decorative panel, flow chart by following methods as shown in figure 1, be prepared from:
(1) desulfurated plaster activation micro mist is prepared:
1. ball mill turns brilliant activation:By 99.36 parts of the ripe powder of common β-desulfurated plaster, 0.3 part of polymer dispersion powder, aluminum sulfate
After 0.02 part of potassium, 0.02 part of sodium citrate, 0.2 part of sodium pyrophosphate, 0.1 part of hydroxypropyl methyl cellulose (HPMC) are well mixed,
It is added to ball milling in ball mill enter in two storage tanks after turning brilliant activation, material ball milling 50min or so;
2. homogenizing ageing:Obtained material in step 1. two storage tanks is discharged simultaneously, and it is equal by conveying worm
It is transported in the packaging with moisture resistance, is aged 10 days or so naturally after change, obtains the stably and controllable described desulfurization stone of performance
Cream activates micro mist;
(2) photocatalysis environmental mineral waste material is prepared:Centralized recovery utilizes the gloomy building material Science and Technology Ltd. of Hubei Green
The useless clout of preparation algae calcium air purification medium, containing diatomite 73%, through drying to grinding after moisture content < 8.0%, grinding is thin
Spend to be less than after 3% for 180 mesh sieve margins and obtain photocatalysis environmental mineral waste material;
(3) combination solution is prepared:By 100 parts of H2O, 0.8 part of polyvinyl alcohol, 0.1 part of methyl silicon sodium alcoholate waterproofing agent, 0.5 part
Inorganic decorating plate surface defoamer is (by defoamer mother liquor, agricultural sodium sulphate and clear water according to 1.2:1.2:97.6 weight ratio
Compounding is formed, and defoamer mother liquor is by fatty acid methyl ester ethoxylate, isomery alcohol ether, butyl glycol ether, polyether-modified organic
Silicon, clear water press 40:20:5:0.1:34.9 compoundings are formed) it is well mixed, produce described combination solution;
(4) once stir:Weigh step (1), 100 parts of the micro mist of desulfurated plaster activation that (2), (3) are prepared from, photocatalysis
68 parts of 3.0 parts of environmental mineral waste material and combination solution are stirred until uniformly, obtaining uniform net slurry, speed of agitator is 300
~320r/min;
(5) synchronous vibration, secondary agitation, overlay film shaping:Step (4) is obtained into net slurry to be delivered in the bed die of shaping,
1.2 parts of length are also delivered in the bed die of shaping for 18~20mm glass fiber leftover material simultaneously;Net slurry in bed die
Secondary agitation is carried out until uniform under 30~32r/min rotating speed with glass fibre;Product in bed die carries out vibration moulding
Obtain the overlay film shaping wire body of two-sided overlay film, 30~35HZ of vibration frequency, 5~6mm of amplitude, 10~12 seconds residence times of vibration;
(6) it is stripped and cuts polishing:The overlay film shaping wire body demoulding that step (5) is obtained, then by the overlay film after the demoulding
Four side remnant fibrous polishings of wire body, four marginal rays are molded to slide neatly;
(7) maintenance is dried:It is dried in natural air drying mode, drying time is 7 days;
(8) facing is handled:Through ecologic coating mode surface coating, after after surface solidification, packaging can turn into product.
Desulfurated plaster activation micro mist in the present embodiment step (1), the performance comparison with the common commercially available ripe powder of desulfurated plaster
As shown in table 1:
Table 1:Inventive desulfurization gypsum activates the performance comparison of micro mist and the ripe powder of common desulphurization gypsum
As shown in Table 1, desulfurated plaster of the invention activation micro mist performance is substantially better than the ripe powder of existing desulfurated plaster.
Desulfurated plaster high-strength crystal decorative panel manufactured in the present embodiment, powder activation turns brilliant preposition, and obtained crystalline phase is many
First crystal phase, as shown in Figure 2;And the product (turning crystalline substance in hydration stage) that conventionally prepared by CN102408218A, product
Crystalline phase be single crystal phase, as shown in Figure 3;The desulfurated plaster high-strength crystal decorative panel performance manufactured in the present embodiment such as institute of table 2
Show:
Table 2:The desulfurated plaster high-strength crystal decorative panel performance indications that the embodiment of the present invention 1 is prepared
As shown in Table 2, there is desulfurated plaster high-strength crystal decorative panel produced by the present invention purifying formaldehyde, negative oxygen ion to lure
Raw, automatic humidity-regulating it is ecological.
Embodiment 2:
A kind of desulfurated plaster high-strength crystal decorative panel, is prepared from by following methods:
(1) desulfurated plaster activation micro mist is prepared:
1. ball mill turns brilliant activation:By 95.75 parts of the ripe powder of common β-desulfurated plaster, 1.2 parts of plant gum powder, sodium citrate
0.02 part, 0.03 part of calcium chloride, 0.2 part of sodium pyrophosphate, 0.3 part of trisodium citrate, hydroxypropyl methyl cellulose (HPMC) 0.5
After part, 2.0 parts of pre-gelatinized starch are well mixed, it is added to ball milling progress turn crystalline substance in ball mill and activates, 50~55min of material ball milling
After enter in two storage tanks;
2. homogenizing ageing:Obtained material in step 1. two storage tanks is discharged simultaneously, and it is equal by conveying worm
It is transported in the packaging with moisture resistance, is aged 12 days naturally after change, obtains the stably and controllable described desulfurated plaster of performance and live
Change micro mist;
(2) photocatalysis environmental mineral waste material is prepared:Recycle load diatomite/TiO2Useless clout, containing diatomite
97.8%th, TiO21.8%;Drying and dehydrating, carries out grinding again during to moisture content < 8.0%, grinding to fineness is 180 mesh and tailed over
Amount produces photocatalysis environmental mineral waste material after being less than 3%;
(3) combination solution is prepared:By 100 parts of H2O, 1.2 parts of biogels, 1.3 parts of methyl silanol potassium waterproofing agents, 2.0 parts
(defoamer mother liquor, agricultural alum and clear water are according to 2.0 for inorganic decorating plate surface defoamer:1.9:96.1 weight ratio
Compounding is formed;Defoamer mother liquor by fatty acid methyl ester ethoxylate, isomery alcohol ether, butyl glycol ether, organic silicon modified by polyether,
Clear water presses 40:20:5:0.1:34.9 compoundings are formed) it is well mixed, produce described combination solution;
(4) once stir:100 parts of micro mist of desulfurated plaster activation, the photocatalysis ring that step (1), (2), (3) are prepared from
75 parts of 8.0 parts of border mineral waste and combination solution are stirred until uniform, obtain uniform net slurry, and speed of agitator is 300~
310r/min;
(5) synchronous vibration, secondary agitation, overlay film shaping:Step (4) is obtained into net slurry to be delivered in the bed die of shaping,
1.5 parts of grid cloths (specification is 5 × 5mm, grid cloth width 590mm) are delivered in the bed die of shaping simultaneously;In bed die
Net slurry and grid cloth carry out secondary agitation until uniform under 33~35r/min speed;Product in bed die is vibrated into
Type, obtains the overlay film shaping wire body of two-sided overlay film, 40~45HZ of vibration frequency, 8~10mm of amplitude, vibration residence time 12~13
Second;
(6) it is stripped and cuts polishing:The overlay film shaping wire body demoulding that step (5) is obtained, then by the overlay film after the demoulding
The continuous grid cloth in four sides of shaping wire body is neatly cut off, four marginal rays are slided neatly;
(7) maintenance is dried:To be dried in dry kiln drying mode;Temperature is 40~50 DEG C, the time is 13~14h;
(8) facing is handled:Through mode surface coating in UV air brushing, after after surface solidification, packaging can turn into product.
Desulfurated plaster high-strength crystal decorative panel performance manufactured in the present embodiment is as shown in table 3:
Table 3:The desulfurated plaster high-strength crystal decorative panel performance indications that the embodiment of the present invention 2 is prepared
As shown in Table 3, there is desulfurated plaster high-strength crystal decorative panel produced by the present invention purifying formaldehyde, negative oxygen ion to lure
Raw, automatic humidity-regulating it is ecological.
Examples detailed above is technical concept and technical characterstic to illustrate the invention, can not limit the present invention's with this
Protection domain.Equivalent transformation or modification that all essence according to the present invention is done, should all cover in protection scope of the present invention
Within.
Claims (7)
1. a kind of desulfurated plaster high-strength crystal decorative panel, it is characterised in that:With desulfurated plaster activation micro mist, photocatalysis environmental mineral
Waste material, combination solution, reinforcing fiber/grid cloth are raw material, and agitated, vibration, secondary agitation, overlay film shaping, the demoulding, cutting are beaten
Described desulfurated plaster high-strength crystal decorative panel is made after mill, dry maintenance, the processing of facing handling process;Described desulfurated plaster
It is 100 to activate micro mist, photocatalysis environmental mineral waste material, combination solution, the weight ratio of reinforcing fiber/grid cloth:0.5~12:60~
75:0.8~7.0;
Described desulfurated plaster activate micro mist using the common ripe powder of β-desulfurated plaster, rubber powder, crystal modifier, subtract swollen dose, water-loss reducer as
Raw material, is prepared from after turning brilliant activation, homogenizing ageing through ball mill ball milling, the described common ripe powder of β-desulfurated plaster, rubber powder,
Crystal modifier, subtract swollen dose, the weight ratio of water-loss reducer be 95 ~ 99.6:0.1~1.2:0.02~0.05:0.2~1.0:0.1~2.8;
The described common ripe powder of β-desulfurated plaster is steam power plant's desulfurated plaster waste residue obtained common β after drying and calcining grinding
Powder;
Described rubber powder is any one in polymer dispersion powder, the rubber powder of polyvinyl chloride 2488, plant gum powder or two or more
The mixture mixed with arbitrary proportion;
Described crystal modifier is any one in aluminum sulfate, alum, sodium citrate, calcium chloride or two or more with any
The mixture that ratio is mixed;
It is described subtract swollen dose be in sodium pyrophosphate, sodium metaphosphate, trisodium citrate any one or it is two or more arbitrarily to compare
The mixture that example is mixed;
Described water-loss reducer is in hydroxypropyl methyl cellulose, hydroxyethylmethylcellulose, methylcellulose, pre-gelatinized starch
Any one or the two or more mixtures mixed with arbitrary proportion;
Described photocatalysis environmental mineral waste material passes through for the useless clout produced in production environmental photocatlytsis material, material for air purification
The product obtained after drying and dehydrating, grinding;Described useless clout carries out grinding, powder again after drying and dehydrating to moisture content < 8.0%
Fineness is milled to for 180 mesh and screen over-size is less than the photocatalysis environmental mineral waste material described in being produced after 3%.
2. desulfurated plaster high-strength crystal decorative panel according to claim 1, it is characterised in that:Described photocatalysis environment ore deposit
Thing waste material be oyster shell whiting, diatomite, activated carbon, negative ion powder, attapulgite, sepiolite, expanded vermiculite in any one or
The two or more mixtures mixed with arbitrary proportion.
3. desulfurated plaster high-strength crystal decorative panel according to claim 1, it is characterised in that:Described combination solution with
H2O, polymerized emulsion/biogel, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic decorating plate surface defoamer are as raw material through compounding
It is prepared from afterwards;Described H2O, polymerized emulsion/biogel, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic decorating plate surface disappear
The weight ratio of infusion is 100:0.8~1.2:0.1~1.8:0.5~2.0.
4. desulfurated plaster high-strength crystal decorative panel according to claim 3, it is characterised in that:Described polymerized emulsion is work
Industry level polyvinyl alcohol emulsions, propyl benzene emulsion, in silicone acrylic emulsion any one or two or more mixed with arbitrary proportion
Mixture.
5. desulfurated plaster high-strength crystal decorative panel according to claim 1, it is characterised in that:Described reinforcing fiber is plant
Any one in fibres, glass fibre, mineral fibres or the two or more mixtures mixed with arbitrary proportion;It is described
Reinforcing fiber length be 15 ~ 22mm.
6. desulfurated plaster high-strength crystal decorative panel according to claim 1, it is characterised in that:Described grid cloth is glass
Grid cloth, grid cloth specification is the mm of 4 × 4 mm ~ 10 × 10.
7. the preparation method of the desulfurated plaster high-strength crystal decorative panel described in any one of claim 1 ~ 6, comprises the following steps:
(1)Prepare desulfurated plaster activation micro mist:
1. ball mill turns brilliant activation:
By the common ripe powder of β-desulfurated plaster, rubber powder, crystal modifier, subtract swollen dose, water-loss reducer it is well mixed after, be added to ball mill ball milling
It is middle entered after turning brilliant activation, 25~75min of material ball milling at least two storage tanks;
2. homogenizing ageing:
Obtained material in step 1. at least two storage tanks is discharged simultaneously, and be transported to tool after being homogenized by conveying worm
Have in the packaging of moisture resistance, be aged 3~15 days naturally, obtain the stably and controllable described desulfurated plaster activation micro mist of performance;
(2)Prepare photocatalysis environmental mineral waste material:
Dehydration is dried in the useless clout produced in production environment catalysis material, material for air purification, to moisture content <
Grinding is carried out after 8.0% again, grinding to fineness is 180 mesh and screen over-size is less than the photocatalysis environmental mineral described in being produced after 3% and given up
Material;
(3)Prepare combination solution:
By H2O, polymerized emulsion/biogel, methyl silicon sodium alcoholate/potassium waterproofing agent, inorganic decorating plate surface defoamer are well mixed,
Produce described combination solution;
(4)Once stir:
By step(1)、(2)、(3)Desulfurated plaster activation micro mist, photocatalysis environmental mineral waste material and the combination solution being prepared from
It is stirred according to described weight ratio until uniformly, obtaining uniform net slurry, speed of agitator is 280 ~ 350r/min;
(5)Synchronous vibration, secondary agitation, overlay film shaping:
By step(4)Net slurry is obtained to be delivered in the bed die of shaping, at the same by the weight than reinforcing fiber/grid cloth
It is delivered in the bed die of shaping;Net slurry and reinforcing fiber/grid cloth described in bed die is stirred until uniform, stirring
Speed is 25 ~ 38 r/min;The product obtained after being stirred in bed die carries out vibration moulding, obtains the overlay film shaping of two-sided overlay film
Wire body, 20 ~ 50HZ of vibration frequency, 0.3 ~ 15mm of amplitude, 8 ~ 15 seconds residence times of vibration;
(6)The demoulding and cutting polishing:By step(5)Overlay film after the demoulding, is then molded by the obtained overlay film shaping wire body demoulding
Four side remnant fibrous of wire body are polished or neatly cut off its continuous grid cloth, four marginal rays are slided neatly;
(7)Dry maintenance:It is dried in any one mode in natural air drying mode, dry kiln drying mode;Natural wind
When dry, drying time is 3 ~ 7 days;When drying kiln drying, dry kiln drying temperature is 35 ~ 55 DEG C, drying time is 10 ~ 18 small
When;
(8)Facing processing:Through any one in ecologic coating, metal baking finish, imitative stone baking vanish, F-C paint, gold stamping silk-screen, UV air brushing
Mode surface coating, after after surface solidification, packaging can turn into product.