CN105906292A - Wear-resistant corrosion-resistant cement for chemical stirring equipment - Google Patents
Wear-resistant corrosion-resistant cement for chemical stirring equipment Download PDFInfo
- Publication number
- CN105906292A CN105906292A CN201610266907.1A CN201610266907A CN105906292A CN 105906292 A CN105906292 A CN 105906292A CN 201610266907 A CN201610266907 A CN 201610266907A CN 105906292 A CN105906292 A CN 105906292A
- Authority
- CN
- China
- Prior art keywords
- wear
- corrosion
- resistant
- epoxy resin
- cerium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses wear-resistant corrosion-resistant cement for chemical stirring equipment. The wear-resistant corrosion-resistant cement is composed of, by weight, 20-40% of epoxy resin, 30-55% of lime powder, 1-10% of cerium oxide, 0.01-0.1% of benzene sulfonyl chloride, 10-20 parts of talcum powder and 0.1-1% of medical alcohol. The wear-resistant corrosion-resistant cement is prepared by adding the epoxy resin, the lime powder, cerium oxide, benzene sulfonyl chloride, the talcum powder and the medical alcohol into a stirring container according to a weight ratio and well stirring at 15-30 DEG C. The cement is environment-friendly, durable, less prone to shedding, resistant to corrosion, wear, high temperature and strong acid, simple and easy-to-understand in preparation process, short in curing period, long in service life, economical and practical and can be widely used for preventing corrosion of stirring tanks, stirring paddles and stirring shafts, and after raw materials are stirred and mixed, the cement can be ready for use within 24 h.
Description
Technical field
The present invention relates to chemical field, be specifically related to a kind of wear-and corrosion-resistant clay for chemical industry mixing plant.
Background technology
At present, in the whipping process of industrial chemicals, due to the corrosivity of raw material, often to agitator tank, stirrer paddle
And shaft produces corrosion reaction, have a strong impact on the service life of mixing plant.For the service life of extension device, prior art
In have by use stainless steel material antiseptical, also have employing clay carry out antiseptical.Owing to the big employing of mixing plant build is stainless
Steel material considerably increases production cost, existing clay there is also that antiseptic property is good but the most wear-resisting, wear-resisting but antiseptic property not
Good deficiency such as grade, owing to mixing plant is for continuous kinestate, is respectively provided with higher requirement to wear-resisting and corrosion resistant, the most existing
Clay there is also the deficiencies such as relatively costly, weak easy to fall off, the complex process of curing time length, non-refractory, cohesive force of price.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, and provide a kind of cheap, technique simple, solidification week
Phase strong acid short, high temperature resistant, resistance to, the wear-and corrosion-resistant clay for chemical industry mixing plant corrosion-resistant, anti abrasive.
For achieving the above object, the technical scheme is that a kind of wear-and corrosion-resistant clay for chemical industry mixing plant,
Mainly consist of the following components: epoxy resin, pulverized limestone, cerium oxide, benzene sulfonyl chloride.
As optimal technical scheme, the described wear-and corrosion-resistant clay for chemical industry mixing plant, by following weight proportion
Component forms, epoxy resin 20% ~ 40%, pulverized limestone 30 ~ 55%, cerium oxide 1% ~ 10%, benzene sulfonyl chloride 0.01% ~ 0.1%.
As optimal technical scheme, the described wear-and corrosion-resistant clay for chemical industry mixing plant, mainly by following components group
Become: epoxy resin, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol.
As optimal technical scheme, the described wear-and corrosion-resistant clay for chemical industry mixing plant, by following weight proportion
Component forms, epoxy resin 20% ~ 40%, pulverized limestone 30 ~ 55%, cerium oxide 1% ~ 10%, benzene sulfonyl chloride 0.01% ~ 0.1%, Pulvis Talci
10% ~ 20%, medical alcohol 0.1% ~ 1%.
As optimal technical scheme, the described wear-and corrosion-resistant clay for chemical industry mixing plant, by following weight proportion
Component forms, epoxy resin 35%, pulverized limestone 45%, cerium oxide 5%, benzene sulfonyl chloride 0.05%, Pulvis Talci 14%, medical alcohol
0.95%。
As optimal technical scheme, described pulverized limestone is set to 200 ~ 400 mesh.
As optimal technical scheme, the described wear-and corrosion-resistant clay processing method for chemical industry mixing plant is as follows: by institute
State in the epoxy resin of weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride addition stirring container, fully stir under 15 ~ 30 degrees Celsius
Mix uniformly, prepare finished product.
As optimal technical scheme, the described wear-and corrosion-resistant clay processing method for chemical industry mixing plant is as follows: by institute
State the epoxy resin of weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol add in stirring container, 15 ~
Stir under 30 degrees Celsius, prepare finished product.
The present invention uses technique scheme to provide the benefit that: Product Green environmental protection of the present invention, durable in use, is difficult to take off
Fall, have corrosion resistance and wearability simultaneously concurrently, can be high temperature resistant, resistance to strong acid, processing technology is easily understood, cure cycle is short, by former
After material stirring mixing, just can use in 24 hours, service life, length, economical and practical, can be widely used for agitator tank, stirrer paddle
And the anticorrosion of shaft.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated, but does not constitute any limitation of the invention.
Embodiment 1
A kind of wear-and corrosion-resistant clay for chemical industry mixing plant, is made up of the component of following weight proportion, epoxy resin 40%,
Pulverized limestone 50%, cerium oxide 9.95%, benzene sulfonyl chloride 0.05%.By the epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulphur
Acyl chlorides adds in stirring container, stirs under 15 ~ 30 degrees Celsius, prepares finished product.
Embodiment 2
A kind of wear-and corrosion-resistant clay for chemical industry mixing plant, is made up of the component of following weight proportion, epoxy resin 35%,
Pulverized limestone 55%, cerium oxide 9.9%, benzene sulfonyl chloride 0.1%.By the epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl
Chlorine adds in stirring container, stirs under 15 ~ 30 degrees Celsius, prepares finished product.
Embodiment 3
A kind of wear-and corrosion-resistant clay for chemical industry mixing plant, is mainly made up of the component of following weight proportion, epoxy resin
20%, pulverized limestone 50%, cerium oxide 9.9%, benzene sulfonyl chloride 0.1%, Pulvis Talci 20%, medical alcohol 1%.Described pulverized limestone is set to
200 mesh.The epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol are added stirring and hold
In device, stir under 15 ~ 30 degrees Celsius, prepare finished product.
Embodiment 4
A kind of wear-and corrosion-resistant clay for chemical industry mixing plant, is mainly made up of the component of following weight proportion, epoxy resin
35%, pulverized limestone 45%, cerium oxide 5%, benzene sulfonyl chloride 0.05%, Pulvis Talci 14%, medical alcohol 0.95%.Described pulverized limestone is set to
300 mesh.The epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol are added stirring and hold
In device, stir under 15 ~ 30 degrees Celsius, prepare finished product.
Embodiment 5
A kind of wear-and corrosion-resistant clay for chemical industry mixing plant, is mainly made up of the component of following weight proportion, epoxy resin
40%, pulverized limestone 40%, cerium oxide 5%, benzene sulfonyl chloride 0.05%, Pulvis Talci 14%, medical alcohol 0.95%.Described pulverized limestone is set to
400 mesh.The epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol are added stirring and hold
In device, stir under 15 ~ 30 degrees Celsius, prepare finished product.
In use, simple operation, technique is simple, is directly applied in by described clay and needs anticorrosion resistance to for product of the present invention
Mill product on, until described clay color by initial purple, through string color change after, eventually become black, painting
Product after smearing can use.Clay of the present invention can be widely used for industrial chemicals stirring agitator tank inwall and stirrer paddle,
The outer wall of shaft, can be greatly prolonged the service life of agitator tank, stirrer paddle, shaft, and the application of clay of the present invention includes
But it is not limited only to the said goods, also can be used for concrete-agitating field and other need on the product of anticorrosion antiwear.
Ultimate principle and the principal character of the present invention have more than been shown and described.Skilled person will appreciate that of the industry,
The present invention is not restricted to the described embodiments, the principle that the present invention is simply described described in above-described embodiment and description,
Without departing from the spirit and scope, the present invention also has various changes and modifications, and these changes and improvements all fall
Enter in scope of the claimed invention.Claimed scope is defined by appending claims and equivalent thereof.
Claims (8)
1. the wear-and corrosion-resistant clay for chemical industry mixing plant, it is characterised in that: mainly consist of the following components: asphalt mixtures modified by epoxy resin
Fat, pulverized limestone, cerium oxide, benzene sulfonyl chloride.
Wear-and corrosion-resistant clay for chemical industry mixing plant the most according to claim 1, it is characterised in that: main by following
The component composition of weight proportion, epoxy resin 20% ~ 40%, pulverized limestone 30 ~ 55%, cerium oxide 1% ~ 10%, benzene sulfonyl chloride 0.01% ~
0.1%。
Wear-and corrosion-resistant clay for chemical industry mixing plant the most according to claim 1, it is characterised in that: in described component
Also include Pulvis Talci, medical alcohol.
Wear-and corrosion-resistant clay for chemical industry mixing plant the most according to claim 3, it is characterised in that: main by following
The component composition of weight proportion, epoxy resin 20% ~ 40%, pulverized limestone 30 ~ 55%, cerium oxide 1% ~ 10%, benzene sulfonyl chloride 0.01% ~
0.1%, Pulvis Talci 10% ~ 20%, medical alcohol 0.1% ~ 1%.
Wear-and corrosion-resistant clay for chemical industry mixing plant the most according to claim 4, it is characterised in that: main by following
The component composition of weight proportion, epoxy resin 35%, pulverized limestone 45%, cerium oxide 5%, benzene sulfonyl chloride 0.05%, Pulvis Talci 14%, doctor
With ethanol 0.95%.
6. according to the wear-and corrosion-resistant clay for chemical industry mixing plant described in claim 2 or 4 or 5, it is characterised in that: described
Pulverized limestone is set to 200 ~ 400 mesh.
7. the wear-and corrosion-resistant clay processing method for chemical industry mixing plant according to claim 2, its feature exists
In: the epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride are added in stirring container, at 15 ~ 30 degrees Celsius
Under stir, prepare finished product.
8. the wear-and corrosion-resistant clay processing method for chemical industry mixing plant according to claim 4, its feature exists
In: the epoxy resin of described weight ratio, pulverized limestone, cerium oxide, benzene sulfonyl chloride, Pulvis Talci, medical alcohol are added stirring container
In, stir under 15 ~ 30 degrees Celsius, prepare finished product.