CN105888142A - Novel asphalt shingle for buildings - Google Patents
Novel asphalt shingle for buildings Download PDFInfo
- Publication number
- CN105888142A CN105888142A CN201410697695.3A CN201410697695A CN105888142A CN 105888142 A CN105888142 A CN 105888142A CN 201410697695 A CN201410697695 A CN 201410697695A CN 105888142 A CN105888142 A CN 105888142A
- Authority
- CN
- China
- Prior art keywords
- self
- asphalt
- colored
- novel
- novel architecture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of novel waterproof building materials, and particularly relates to a novel asphalt shingle for buildings. The novel asphalt shingle comprises glass fiber felt, modified petroleum asphalt, colored mineral aggregates, an isolation material and a self-adhesion material, wherein the glass fiber felt serves as the base, and after the glass fiber felt is soaked in the modified petroleum asphalt, the surface layer of the glass fiber felt is covered with the colored mineral aggregates, and the other side is scattered with the isolation material and dipcoated with the self-adhesion material; the modified petroleum asphalt is prepared from, by weight, 40-90 parts of petroleum asphalt, 15-50 parts of powder filler, 5-18 parts of modifier and 4-14 parts of auxiliary, and all the raw materials are placed in a material reaction still for stirring reaction lasting 60-180 min at 180-200 DEG C so that the modified petroleum asphalt can be obtained; the colored mineral aggregates are colored nanometer fluorinated siloxane-acrylate; the self-adhesion material is self-adhesion glue. The novel asphalt shingle has the advantages of being capable of achieving heat insulation and sound absorption and insulation and resisting water and dust, convenient to pave, rich in color and high in flexibility and corrosion resistance.
Description
Technical field
The invention belongs to new waterproof building material technical field, especially relate to a kind of novel architecture drip
Grey tile.
Background technology
Along with the fast development of building industry and improving constantly of people's living standard, the building construction of China is also
There occurs bigger change, in order to reduce the temperature of building top layer light radiation in summer, raising is lived
Comfort level, what original plane roof was more transform domatic roof as.For this reason, it may be necessary to be applicable in a large number
The tile waterproof material of sloping roof, thus the endurance quality etc. of waterproof material is used requirement increasingly
High.From all kinds of waterproof rolls of three felt two oil tech in five sixties to the nineties, constructing and making
During with, they are not had special protective measure, so that their high and low temperature, durability, resistance to
Compaction capacity is the most poor, and traditional domatic roof is that the cinerous clay of curved shape is fired
Watt, colour glazed tile and orange colour plain tile and the cement casting of firing belt grooves with clay of modern development
Watt, although the test that the tile of these kinds attacks through wind and rain for many years, there is preferable practicality.But
Being to there is also many shortcomings, 1. density is high big from weight, from producing, transporting to application and construction all
Need to pay a lot of labours and financial resources, and also add the deadweight of building；2. color is dull, removes
Glazed tiles have a small amount of several color and to fire the plain tile of belt grooves with clay be outside orange colour, remaining tile fragment
It is all caesious, basic no decoration effect；The most either clay shingle, glazed tiles or cement tile all in
Rigid state, broken during firing and using, cause bigger loss；The most often there will be tile fragment
Deform and there is trachoma pitted skin aperture, causing rainy day Seepage.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, it is provided that a kind of insulation, sound-absorbing sound insulation, water proof and dust proof,
Mat formation simplicity, rich color, the flexible and novel architecture bituminized shingle of good corrosion resistance.
One novel architecture bituminized shingle of the present invention, including glass mat, modified oil pitch, colour
Mineral pellet, isolated material and self adhesive material；Described glass mat is tire base, through being impregnated with modified petroleum
After Colophonium, surface layer covers colored mineral pellet, and another side spreads with isolated material and dip-coating strip self adhesive material；
Described modified oil pitch proportioning and weight portion be: asphalt 40-90 part, powder stuffing 15-50
Part, modifying agent 5-18 part, auxiliary agent 4-14 part；Above-mentioned whole raw materials are put in material reaction still,
At a temperature of 180-200 DEG C, stirring reaction 60-180 minute, obtains modified oil pitch.
Described Colophonium is No. 90 asphalt；Described powder stuffing is Pulvis Talci or light calcium powder；
Described modifying agent is SBS or rubber powder；Described auxiliary agent is rubber oil；
Described colored mineral pellet is color nano fluorine-silicon-acrylate.
Described self adhesive material is self-adhesion sizing material.
Advantages of the present invention and good effect be: (1) novel architecture of the present invention bituminized shingle is flexible,
It is applicable to the villa roofing that complex geometrical body is constituted；(2) product heat conductivity is low, energy
Intercept summer hot cold with winter, it is ensured that the indoor life that resident family is comfortable；Effectively absorb environmental noise,
Ensure the living environment that resident family is quiet；(3) bituminized shingle surface covers colored mineral pellet, and color is various,
Coordinate surrounding and different building group style, meet various esthetic sentiment；(4) malthoid can be protected
Direct sunlight and wind and rain, ice and snow is avoided to corrode so that it is to be difficult to aging；(5) asphalt shingle roofing is equivalent to
Two-layer watt overlap, watt groove water guide is smooth, and drainage performance is good, is difficult to the existing stain of dust stratification, after rain-out more
Clean bright and beautiful；(6) bituminized shingle deadweight is relatively light, easy construction, short construction period.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated, and following each embodiment is merely to illustrate this
Invention, does not limit the present invention.
Embodiment 1:
One novel architecture bituminized shingle of the present invention, including glass mat, modified oil pitch, colour
Mineral pellet, isolated material and self adhesive material；Described glass mat is tire base, through being impregnated with modified petroleum
After Colophonium, surface layer covers colored mineral pellet, and another side spreads with isolated material and dip-coating strip self adhesive material；
Described modified oil pitch proportioning and weight portion be: 90 parts of asphalt, powder stuffing 50 parts,
Modifying agent 18 parts, auxiliary agent 14 parts；Above-mentioned whole raw materials are put in material reaction still, 200 DEG C of temperature
The lower stirring reaction of degree 150 minutes, obtains modified oil pitch.
Described Colophonium is No. 90 asphalt；Described powder stuffing is Pulvis Talci；Described modification
Agent is rubber powder；Described auxiliary agent is rubber oil；
Described colored mineral pellet is color nano fluorine-silicon-acrylate.
Described self adhesive material is self-adhesion sizing material.
Embodiment 2:
One novel architecture bituminized shingle of the present invention, including glass mat, modified oil pitch, colour
Mineral pellet, isolated material and self adhesive material；Described glass mat is tire base, through being impregnated with modified petroleum
After Colophonium, surface layer covers colored mineral pellet, and another side spreads with isolated material and dip-coating strip self adhesive material；
Described modified oil pitch proportioning and weight portion be: 40 parts of asphalt, powder stuffing 15 parts,
Modifying agent 5 parts, auxiliary agent 4 parts；Above-mentioned whole raw materials are put in material reaction still, 180 DEG C of temperature
Lower stirring reaction 80 minutes, obtains modified oil pitch.
Described Colophonium is No. 90 asphalt；Described powder stuffing is Pulvis Talci；Described modification
Agent is SBS；Described auxiliary agent is rubber oil；
Described colored mineral pellet is color nano fluorine-silicon-acrylate.
Described self adhesive material is self-adhesion sizing material.
The technical specification such as table 1 below of the novel architecture bituminized shingle that the employing present invention obtains:
The technical specification of table 1 novel architecture of the present invention bituminized shingle
Above embodiments of the invention are described in detail, but described content has been only the preferable of the present invention
Embodiment, it is impossible to be considered the practical range for limiting the present invention.All according to the scope of the invention made equal
Deng change and improvement etc., within all should still belonging to this patent covering scope.
Claims (5)
1. a novel architecture bituminized shingle, it is characterised in that: include that glass mat, modified petroleum drip
Mineral pellet blue or green, colored, isolated material and self adhesive material；Described glass mat is tire base, through being impregnated with
After modified oil pitch, surface layer covers colored mineral pellet, and another side spreads with isolated material and dip-coating strip
Self adhesive material.
Novel architecture bituminized shingle the most according to claim 1, it is characterised in that: described modified stone
Oil asphalt proportioning and weight portion be: asphalt 40-90 part, powder stuffing 15-50 part, modifying agent 5-18
Part, auxiliary agent 4-14 part；Above-mentioned whole raw materials are put in material reaction still, at a temperature of 180-200 DEG C
Stirring reaction 60-180 minute, obtains modified oil pitch.
Novel architecture bituminized shingle the most according to claim 2, it is characterised in that: described Colophonium
It is No. 90 asphalt；Described powder stuffing is Pulvis Talci or light calcium powder；Described modifying agent is
SBS or rubber powder；Described auxiliary agent is rubber oil.
Novel architecture bituminized shingle the most according to claim 1, it is characterised in that: described colored ore deposit
Thing pellet is color nano fluorine-silicon-acrylate.
Novel architecture bituminized shingle the most according to claim 1, it is characterised in that: described self-adhesion material
Material is self-adhesion sizing material.