CN105887259A - Polyvinyl flax wet spinning high count yarn or plied yarn produced through siro spinning - Google Patents
Polyvinyl flax wet spinning high count yarn or plied yarn produced through siro spinning Download PDFInfo
- Publication number
- CN105887259A CN105887259A CN201610499537.6A CN201610499537A CN105887259A CN 105887259 A CN105887259 A CN 105887259A CN 201610499537 A CN201610499537 A CN 201610499537A CN 105887259 A CN105887259 A CN 105887259A
- Authority
- CN
- China
- Prior art keywords
- yarn
- caulis
- polyvinyl
- folium lini
- strand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyvinyl flax wet spinning high count yarn or plied yarn produced through siro spinning. The polyvinyl flax wet spinning high count yarn or plied yarn is prepared by boiling and smelting crude yarns of long or short flax, bleaching, feeding yarns or long wires of water-soluble vinylon into a fine yarn machine so as to mix the yarns, and combining and kneading to form flax/vinylon blended yarns; boiling the blended yarns in a water solution, and dissolving to remove vinylon so as to obtain flax high count yarns; combining and kneading the blended yarns in an adverse direction so as to form high count yarns, removing the vinylon so as to obtain flax high count yarns, or dissolving the blended yarns to remove vinylon, and combining and kneading to form flax high count yarns, wherein after vinylon is removed, the water solution comprises sodium hexametaphosphate and citric acid of which the mole concentration is 7-9mmol/L; the mole concentration ratio of sodium hexametaphosphate to citric acid is (6-8):1. The produced polyvinyl flax wet spinning high count yarn has the best three-dimensional feeling.
Description
Technical field
The invention belongs to field of textiles, be specifically related to polyvinyl flax wet high grade cotton yarn or strand that a kind of SEILE textile produces.
Background technology
SEILE textile has another name called and twists with the fingers and spins, and domestic is referred to as A, B yarn.SEILE textile feeds two on spinning frame and keeps a determining deviation
Rove, after drawing-off, is exported this two single thread yarns by front roller, and makes due to the transmission of the twist on single thread yarn with few
The twist of amount, is added, after split, the yarn being twisted similar plying further, is wound on bobbin.
The initial designs purpose of SEILE textile is for wool spinning, and feature is that filoplume is few, and strength is high, and wearability is good, reaches wool yarn energy
The effect of single yarn weaving, to realize the lightening of wool fabric.Have bigger although SEILE textile compares similar conventional yarn in many aspects
Improvement, wool spinning single thread not starching to be really achieved weave, still have certain distance.Thereafter wool spinning also more abandons the method, on the contrary
At blending such as T/C, C.V.C etc. then uses the method, can produce the Flos Cannabis effect of doubling, good hand touch, therefore be subject to joyous after dyeing because of it
Meet, the most more because improving hairiness problems, as spun some fibers being easily generated filoplume, such as synthetic cotton, Modal, tencel, Semen sojae atricolor
Fiber, even cotton all produce by the method, and the feedstock grade used by Siro Yarn is splited than conventional ring and spun low, and its fabric is more normal
Rule ring ingot strand fabric filoplume is few, and soft, wear-resisting, permeability is good.
Caulis et Folium Lini is the natural fiber of a kind of function admirable, is referred to as fiber queen.Flax fiber humidity absorption and release is fast, good permeability,
It it is preferable wearing fabric in summer.At present, flax spinning mainly uses the form of wet spinning, owing to the ultimate fibre of Caulis et Folium Lini is long
Spending shorter, therefore, process of fiber (i.e. fibre bundle) thicker after can only using half deguming spins.Plus wet spinning work
Skill and the particularity of equipment so that the wet spinning of Caulis et Folium Lini is difficult to spin thinner yarn, can only make thick thick fabric.At present, Caulis et Folium Lini length
The spinning process of fiber crops wet spinning is mainly: scutched line (humidification health preserving) → hackling → one-tenth bar → drafting → rove → boil drift → spun yarn is wet
Spin → be dried → winder.And cast tow wet spinning is to use the noil produced in hackling in long fiber crops to carry out spinning processing, its spinning process
Before rove, each factory is different, but the later operation of rove is completely the same with long bast fibre spinning, simply tow system wet spinning frame
Drawing-off is spaced the shortest of longer bast fibre spinning.At present, Caulis et Folium Lini length fiber crops wet-spun yarn is typically 16-24 public affairs and props up, and cast tow wet-spun yarn is mainly 10-20
Public.In line, more than 36 public is exactly high grade cotton yarn.Especially 50 public and above yarn, want flax raw material
Ask high, and production efficiency is low, therefore actual production is few.Meanwhile, in addition to the fineness of yarn is thick, due to right in flax wet
The control of fiber movement is poor, and the bar evenness of its yarn is the poorest, and fiber crops grain is many, seriously limits line application on knitting.
Due to the existence of the problems referred to above, make existing flax wet to be difficult to produce height, expensive goods, be unfavorable for flax product
The diversified development of kind, limits the promotion and application of flax product to a great extent, constrains the development of Fiber Flax Industry.
Summary of the invention
It is an object of the invention to provide polyvinyl flax wet high grade cotton yarn or strand that a kind of SEILE textile produces.
The above-mentioned purpose of the present invention is achieved by techniques below scheme:
The polyvinyl flax wet high grade cotton yarn of a kind of SEILE textile production or strand, comprise the steps: Caulis et Folium Lini length fiber crops or tow roving
After boiling-off, bleaching, it jointly being fed on spinning frame with yarn or the long filament of water soluble vinylon and realize mixing, twisting forms Asia
Fiber crops/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves polyvinyl of decorporating, obtain Caulis et Folium Lini high grade cotton yarn；Mixed yarn is reverse
Doubling twisting is formed after strand, and polyvinyl of decorporating obtains Caulis et Folium Lini height and props up strand, or after mixed yarn is dissolved polyvinyl of decorporating, doubling twisting
Form Caulis et Folium Lini height and prop up strand；Wherein, mixed yarn is boiled in aqueous with dissolve decorporate polyvinyl time, containing mole dense in aqueous solution
Degree is sodium hexameta phosphate and the citric acid of 7～9mmol/L, and the molar concentration rate of sodium hexameta phosphate and citric acid is 6～8:1.
Further, mixed yarn is boiled in aqueous with dissolve decorporate polyvinyl time, in aqueous solution containing molar concentration be 8mmol/L
Sodium hexameta phosphate and the molar concentration rate of citric acid, sodium hexameta phosphate and citric acid be 7:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Further, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 4～14mm at front roller,
After front roller exports, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Further, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 0.9～1.3 with mixed yarn single twist multiplier ratio.
Further, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 20～40wt%, and remaining is Caulis et Folium Lini.
Further, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 1～3 hour.
Further, the fineness of Caulis et Folium Lini high grade cotton yarn is 50～150 public, and it is 50/2～150/2 public that Caulis et Folium Lini height props up the fineness of strand.
Further, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 0.8～1.2, and Caulis et Folium Lini height props up twist factor and the list of strand
The ratio of yarn twist factor is 0.9～1.1.
Advantages of the present invention:
The polyvinyl flax wet high grade cotton yarn third dimension that SEILE textile of the present invention produces is strong, and cloth style is fluffy, full, flexible, hands
It is the best to feel, and effect is significantly better than prior art.This effect with decorporate polyvinyl time method relevant, sodium hexameta phosphate in boiling water
When being 6～8:1 with the ratio of the molar concentration of citric acid, the polyvinyl flax wet high grade cotton yarn third dimension produced is the strongest.
Detailed description of the invention
Further illustrate the essentiality content of the present invention below in conjunction with embodiment, but do not limit scope with this.To the greatest extent
The present invention is explained in detail by pipe with reference to preferred embodiment, it will be understood by those within the art that, can be to the present invention
Technical scheme modify or equivalent, without deviating from the spirit and scope of technical solution of the present invention.
Embodiment 1: SEILE textile produces polyvinyl flax wet high grade cotton yarn
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 7:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
Embodiment 2: SEILE textile produces polyvinyl flax wet high grade cotton yarn
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 7mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 6:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
Embodiment 3: SEILE textile produces polyvinyl flax wet high grade cotton yarn
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 9mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 8:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
Embodiment 4: SEILE textile produces polyvinyl flax wet high grade cotton yarn
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 6:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
Embodiment 5: SEILE textile produces polyvinyl flax wet high grade cotton yarn
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 8:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
The molar concentration rate of embodiment 6: comparative example, sodium hexameta phosphate and citric acid is 5:1
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 5:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
The molar concentration rate of embodiment 7: comparative example, sodium hexameta phosphate and citric acid is 9:1
Comprise the steps:, by after Caulis et Folium Lini length fiber crops or tow roving boiling-off, bleaching, it to be existed with yarn or the long filament of water soluble vinylon
Jointly feeding on spinning frame and realize mixing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves
Decorporate polyvinyl, obtain Caulis et Folium Lini high grade cotton yarn；After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up stock
After line, or polyvinyl of mixed yarn dissolving being decorporated, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, by mixed yarn in aqueous
Boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, hexa metaphosphoric acid
The molar concentration rate of sodium and citric acid is 9:1.
Further, yarn or the long filament mixed method on spinning frame of Caulis et Folium Lini length fiber crops or tow roving and water soluble vinylon is: general
Caulis et Folium Lini length fiber crops or tow roving feed wet spinning frame from rear roller after tank, by the yarn of water soluble vinylon or long filament from wet spinning
Feed at the front roller of spinning frame, mix at front roller with Caulis et Folium Lini yarn after drawing-off.
Wherein, Caulis et Folium Lini yarn after water soluble vinylon yarn or long filament and drawing-off keeps the spacing of 9mm at front roller, through front roller
After output, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn.
Wherein, pure Caulis et Folium Lini height props up the reverse doublet cord twist factor of strand is 1.1 with mixed yarn single twist multiplier ratio.
Wherein, in described Caulis et Folium Lini/polyvinylalcohol blended yarn, water soluble vinylon content is 30wt%, and remaining is Caulis et Folium Lini.
Wherein, the solution temperature of described polyvinyl of decorporating is 100 DEG C, and the polyvinyl time of decorporating is 2 hours.
Wherein, the fineness of Caulis et Folium Lini high grade cotton yarn is 100 public, and it is 100/2 public that Caulis et Folium Lini height props up the fineness of strand.
Wherein, the single twist multiplier of described Caulis et Folium Lini/polyvinylalcohol blended yarn is 1.0, and Caulis et Folium Lini height props up the twist factor of strand and twists with the fingers system with single thread
The ratio of number is 1.0.
Embodiment 8: effect example
The polyvinyl flax wet high grade cotton yarn produced embodiment 1～7 SEILE textile respectively carries out marking and evaluates.Every full marks are 10 points,
By 5 professional judging panel marking, average.Result such as following table.
| Third dimension | Fluffy full style | Elasticity and feel | |
| Embodiment 1 | 10 | 10 | 10 |
| Embodiment 4 | 9.7 | 9.9 | 9.6 |
| Embodiment 5 | 9.5 | 9.7 | 9.6 |
| Embodiment 6 | 3.5 | 4.3 | 8.6 |
| Embodiment 7 | 3.8 | 4.6 | 8.8 |
Embodiment 2,3 evaluation result is basically identical with embodiment 4,5.
Result shows, the polyvinyl flax wet high grade cotton yarn third dimension that SEILE textile of the present invention produces is strong, cloth style is fluffy, full,
Flexible, feel is the best, and effect is significantly better than prior art.This effect with decorporate polyvinyl time method relevant, in boiling water
When the ratio of the molar concentration of sodium hexameta phosphate and citric acid is 6～8:1, the polyvinyl flax wet high grade cotton yarn third dimension produced is the strongest.
The effect of above-described embodiment indicates that the essentiality content of the present invention, but does not limit protection scope of the present invention with this.
It will be understood by those within the art that, technical scheme can be modified or equivalent, and not take off
Essence and protection domain from technical solution of the present invention.
Claims (9)
1. a SEILE textile produces polyvinyl flax wet high grade cotton yarn or strand, it is characterised in that comprise the steps: Caulis et Folium Lini
After long fiber crops or tow roving boiling-off, bleaching, by its with the yarn of water soluble vinylon or long filament on spinning frame common feeding and realize mixed
Closing, twisting forms Caulis et Folium Lini/polyvinylalcohol blended yarn；Mixed yarn is boiled in aqueous, dissolves polyvinyl of decorporating, obtain Caulis et Folium Lini high grade cotton yarn；
After reverse for mixed yarn doubling twisting is formed strand, polyvinyl of decorporating obtains Caulis et Folium Lini height and props up strand, or mixed yarn is dissolved polyvinyl of decorporating
After, doubling twisting forms Caulis et Folium Lini height and props up strand；Wherein, mixed yarn is boiled in aqueous with dissolve decorporate polyvinyl time, water-soluble
Liquid is 6～8:1 containing the sodium hexameta phosphate of molar concentration 7～9mmol/L and citric acid, sodium hexameta phosphate and citric acid molar concentration rate.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 or strand, it is characterised in that: by mixed yarn at aqueous solution
In boil with dissolve decorporate polyvinyl time, aqueous solution is sodium hexameta phosphate and the citric acid of 8mmol/L containing molar concentration, six inclined phosphorus
The molar concentration rate of acid sodium and citric acid is 7:1.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that Caulis et Folium Lini length is numb or short
Fiber crops rove with yarn or the long filament mixed method on spinning frame of water soluble vinylon is: by Caulis et Folium Lini length is numb or tow roving is through tank
After feed wet spinning frame from rear roller, yarn or the long filament of water soluble vinylon are fed at the front roller of wet spinning frame, and lead
Caulis et Folium Lini yarn after stretching mixes at front roller.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: water soluble vinylon yarn
Or Caulis et Folium Lini yarn after long filament and drawing-off keeps the spacing of 4～14mm at front roller, after front roller exports twisting formation Caulis et Folium Lini/
Polyvinylalcohol blended yarn.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: pure Caulis et Folium Lini height props up stock
The reverse doublet cord twist factor of line and the ratio of mixed yarn single twist multiplier are 0.9～1.3.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: described Caulis et Folium Lini/polyvinyl
In mixed yarn, water soluble vinylon content is 20～40wt%, and remaining is Caulis et Folium Lini.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: described dimension of decorporating
The solution temperature of synthetic fibre is 100 DEG C, and the polyvinyl time of decorporating is 1～3 hour.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: Caulis et Folium Lini high grade cotton yarn
Fineness is 50～150 public, and it is 50/2～150/2 public that Caulis et Folium Lini height props up the fineness of strand.
Polyvinyl flax wet high grade cotton yarn the most according to claim 1 and 2 or strand, it is characterised in that: described Caulis et Folium Lini/
The single twist multiplier of polyvinylalcohol blended yarn is 0.8～1.2, and the ratio of twist factor and single twist multiplier that Caulis et Folium Lini height props up strand is 0.9～1.1.