CN105885723A - High-temperature-resistant environment-friendly glue powder - Google Patents
High-temperature-resistant environment-friendly glue powder Download PDFInfo
- Publication number
- CN105885723A CN105885723A CN201410573306.6A CN201410573306A CN105885723A CN 105885723 A CN105885723 A CN 105885723A CN 201410573306 A CN201410573306 A CN 201410573306A CN 105885723 A CN105885723 A CN 105885723A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- temperature
- calcium carbonate
- glue powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature-resistant environment-friendly glue powder composed of, by weight, 10-20 parts of quartz powder, 15-20 parts of kaolin, 3-5 parts of expanded perlite, 5-10 parts of starfruit vine gum, 5-10 parts of latex powder, 5-10 parts of a viscosity improver, 1-5 parts of nano calcium carbonate, and 40-60 parts of hydroxymethyl cellulose. When the glue powder is dissolved in water, the high-molecular materials and the additives are attached to the light calcium carbonate to form a high-performance rubber compound, and a coating prepared therewith is convenient to construct, is free of urine-like flow, has good leveling property, is free of edge-wrinkle, has high film forming speed and is free of problems of edge-wrinkle and strip-off at high temperature.
Description
Technical field
The present invention relates to a kind of glue powder, particularly relate to a kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder.
Background technology
Building industry when used in glue different from common glue, its requirement has higher adhesive ability,
And keep the time long enough of viscosity.The building glue used on Vehicles Collected from Market has two kinds of modes of production, and one
City is thrown in after the flexible package punch that the chemical materials such as polyvinyl alcohol, acrylamide is directly produced by Zhong Shi manufacturer
?；The high molecular polymer rubber powders such as PVA, EVA, CMC are processed into building by manufacturer by another kind
After glue, packing is put on market.The packing material that both modes of production need is big, the most energy-conservation；Put on market
Storing cost is high, economical not；Produce product in-convenience in use；Its produce glue composition in have formaldehyde,
The noxious material such as ammonia, preservative, not environmentally；Product in transportation, cracky, can cause resource wave
Take；Glue quality is low, the putty poor adhesive force of modulation, easily rolls up skin, comes off；Make for base materials such as exterior walls
With the cement-based material of glue modulation, owing to cement base capillary suction reason easily causes expansion, cracking, wind
Change, pollute, go mouldy and cause the problems such as peeling during Frozen-thawed cycled.The most a lot of producers are all for building glue
Raw material components carried out improve and update, as Anhui Architectural Sci. Research & Design Inst. use latex powder, first
The novel environment friendly building putties rubber powder that the raw materials such as base cellulose, defoamer, binding agent, white cement produce, its
It is specifically designed to and replaces building glue configuration inner, external wall putty inferior.But the adhesive for building pigment of prior art
, except its adhesive ability power differs, the most generally there is the shortcoming polluting environment, have in (solid glue)
Long-time contact the health of builder can be caused damage.
Summary of the invention
The technical problem that present invention aims to above-mentioned existence provides a kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder.
For solving above-mentioned technical problem, the present invention is achieved through the following technical solutions:
A kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder, consists of the following composition: silica flour；Kaolin；Expanded perlite；
Carambola liana rubber；Latex powder；Viscosity-increasing agent；Nano-calcium carbonate；Hydroxymethyl cellulose.
Described a kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder each composition percentage composition is as follows: silica flour 10～20；
Kaolin 15～20；Expanded perlite 3～5；Carambola liana rubber 5～10；Latex powder 5～10；
Viscosity-increasing agent 5～10；Nano-calcium carbonate 1～5；Hydroxymethyl cellulose 40～60.
Described a kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder each composition percentage composition is as follows: silica flour 20；Kaolin
20；Expanded perlite 5；Carambola liana rubber 10；Latex powder 10；Viscosity-increasing agent 10；Nano-calcium carbonate
5；Hydroxymethyl cellulose 60.
Advantages of the present invention effect: after the present invention is dissolved in water, its macromolecular material and auxiliary agent depend on lightweight carbonic acid
Calcium forms a kind of high performance glue disjunctor, the coating prepared with it, easy construction, does not urinate line, good leveling property,
Not rolling up skin, film forming is fast, will not occur at high operating temperatures to roll up skin obscission.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is illustrated:
Embodiment 1:
Silica flour 20；Kaolin 20；Expanded perlite 5；Carambola liana rubber 10；Latex powder 10；Viscosity
Reinforcing agent 10；Nano-calcium carbonate 5；Hydroxymethyl cellulose 60.
Embodiment 2:
Silica flour 10；Kaolin 15；Expanded perlite 3；Carambola liana rubber 5；Latex powder 5；Viscosity strengthens
Agent 5；Nano-calcium carbonate 1；Hydroxymethyl cellulose 40.
Described above to the disclosed embodiments, makes professional and technical personnel in the field be capable of or uses this
Invention.Multiple amendment to these embodiments will be apparent for those skilled in the art
, generic principles defined herein can without departing from the spirit or scope of the present invention,
Other embodiments realizes.Therefore, the present invention is not intended to be limited to the embodiments shown herein, and
It is to fit to the widest scope consistent with principles disclosed herein and features of novelty.
Claims (3)
1. an Environment-friendlyhigh-temperature high-temperature resistant glue powder, consists of the following composition: silica flour；Kaolin；Expanded pearlite
Rock；Carambola liana rubber；Latex powder；Viscosity-increasing agent；Nano-calcium carbonate；Hydroxymethyl cellulose.
A kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder the most according to claim 1, it is characterised in that the most each
Composition percentage composition is as follows: silica flour 10～20；Kaolin 15～20；Expanded perlite 3～5；
Carambola liana rubber 5～10；Latex powder 5～10；Viscosity-increasing agent 5～10；Nano-calcium carbonate 1～
5；Hydroxymethyl cellulose 40～60.
A kind of Environment-friendlyhigh-temperature high-temperature resistant glue powder the most according to claim 1, it is characterised in that the most each
Composition percentage composition is as follows: silica flour 20；Kaolin 20；Expanded perlite 5；Carambola liana rubber 10；
Latex powder 10；Viscosity-increasing agent 10；Nano-calcium carbonate 5；Hydroxymethyl cellulose 60.